In-situ reduction by Joule heating and measurement of electrical conductivity of graphene oxide in a transmission electron microscope
Authors:
Simon Hettler,
David Sebastian,
Mario Pelaez-Fernandez,
Ana M. Benito,
Wolfgang K. Maser,
Raul Arenal
Abstract:
Graphene oxide (GO) is reduced by Joule heating using in-situ transmission electron microscopy (TEM). The approach allows the simultaneous study of GO conductivity by electrical measurements and of its composition and structural properties throughout the reduction process by TEM, electron diffraction and electron energy-loss spectroscopy. The small changes of GO properties observed at low applied…
▽ More
Graphene oxide (GO) is reduced by Joule heating using in-situ transmission electron microscopy (TEM). The approach allows the simultaneous study of GO conductivity by electrical measurements and of its composition and structural properties throughout the reduction process by TEM, electron diffraction and electron energy-loss spectroscopy. The small changes of GO properties observed at low applied electric currents are attributed to the promotion of diffusion processes. The actual reduction process starts from an applied power density of about 2 1014 Wm-3 and occurs in a highly uniform and localized manner. The conductivity increases more than 4 orders of magnitude reaching a value of 3 103 Sm-1 with a final O content of less than 1%. We discuss differences between the reduction by thermal annealing and Joule heating.
△ Less
Submitted 14 April, 2021;
originally announced April 2021.
-
Detailed thermal reduction analyses of Graphene Oxide via in-situ TEM/EELS studies
Authors:
M. Pelaez-Fernandez,
A. Bermejo,
A. M. Benito,
W. K. Maser,
R. Arenal
Abstract:
We report an in-depth study of the reduction of graphene oxide (GO) by in-situ thermal transmission electron microscopy (TEM) analysis. In-situ heating high-resolution TEM (HRTEM) imaging and electron energy-loss spectroscopy (EELS) measurements have been combined to identify the transformations of different oxygen functional groups, the desorption of physisorbed and chemisorbed water and the grap…
▽ More
We report an in-depth study of the reduction of graphene oxide (GO) by in-situ thermal transmission electron microscopy (TEM) analysis. In-situ heating high-resolution TEM (HRTEM) imaging and electron energy-loss spectroscopy (EELS) measurements have been combined to identify the transformations of different oxygen functional groups, the desorption of physisorbed and chemisorbed water and the graphitization as a function of the temperature in the range from 70 up to 1200°C. A model for the general removal of water and OFGs is proposed based on different chemical and physical parameters that have been monitored. All this unique information provides a detailed roadmap of the thermal behaviour of GO at an extended range of temperature. This is not only of interest to understand the thermal reduction process of GO but also of critical relevance to the response of GO in applications when exposed to thermal effects.
△ Less
Submitted 14 April, 2021;
originally announced April 2021.
-
Optical properties and carrier dynamics in Co-doped ZnO nanorods
Authors:
Aswathi K. Sivan,
Alejandro Galan-Gonzalez,
Lorenzo Di Mario,
Nicolas Tappy,
Javier Hernandez-Ferrer,
Daniele Catone,
Stefano Turchini,
Ana M. Benito,
Wolfgang K. Maser,
Simon Escobar Steinvall,
Anna Fontcuberta i Morral,
Andrew Gallant,
Dagou A. Zeze,
Del Atkinson,
Faustino Martelli1
Abstract:
The controlled modification of the electronic properties of ZnO nanorods via transition metal do** is reported. A series of ZnO nanorods were synthesized by chemical bath growth with varying Co content from 0 to 20 atomic % in the growth solution. Optoelectronic behavior was probed using cathodoluminescence, time-resolved luminescence, transient absorbance spectroscopy, and the incident photon-t…
▽ More
The controlled modification of the electronic properties of ZnO nanorods via transition metal do** is reported. A series of ZnO nanorods were synthesized by chemical bath growth with varying Co content from 0 to 20 atomic % in the growth solution. Optoelectronic behavior was probed using cathodoluminescence, time-resolved luminescence, transient absorbance spectroscopy, and the incident photon-to-current conversion efficiency (IPCE). Analysis indicates the crucial role of surface defects in determining the electronic behavior. Significantly, Co-do** extends the light absorption of the nanorods into the visible region, increases the surface defects, shortens the non-radiative lifetimes, while leaving the radiative lifetime constant. Furthermore, for 1 atomic % Co-do** the IPCE of the ZnO nanorods is enhanced. These results demonstrate that do** can controllably tune the functional electronic properties of ZnO nanorods for applications.
△ Less
Submitted 30 June, 2020;
originally announced June 2020.
-
Revisiting Graphene Oxide Chemistry via Spatially-Resolved Electron Energy Loss Spectroscopy
Authors:
Anna Tararan,
Alberto Zobelli,
Ana M. Benito,
Wolfgang K. Maser,
Odile Stéphan
Abstract:
The type and distribution of oxygen functional groups in graphene oxide (GO) and reduced graphene oxide (RGO) remain still a subject of great debate. Local analytic techniques are required to access the chemistry of these materials at a nanometric scale. Electron energy loss spectroscopy in a scanning transmission electron microscope can provide the suitable resolution, but GO and RGO are extremel…
▽ More
The type and distribution of oxygen functional groups in graphene oxide (GO) and reduced graphene oxide (RGO) remain still a subject of great debate. Local analytic techniques are required to access the chemistry of these materials at a nanometric scale. Electron energy loss spectroscopy in a scanning transmission electron microscope can provide the suitable resolution, but GO and RGO are extremely sensitive to electron irradiation. In this work we employ a dedicated experimental setup to reduce electron illumination below damage limit. GO oxygen maps obtained at a few nanometers scale show separated domains with different oxidation levels. The C/O ratio varies from about 4:1 to 1:1, the latter corresponding to a complete functionalization of the graphene flakes. In RGO the residual oxygen concentrates mostly in regions few tens nanometers wide. Specific energy-loss near-edge structures are observed for different oxidation levels. By combining these findings with first-principles simulations we propose a model for the highly oxidized domains where graphene is fully functionalized by hydroxyl groups forming a 2D-sp$^3$ carbon network analogous to that of graphane.
△ Less
Submitted 12 December, 2016;
originally announced December 2016.
-
The effect of the thermal reduction on the kinetics of low temperature 4He sorption and the structural characteristics of graphene oxide
Authors:
A. V. Dolbin,
M. V. Khlistuck,
V. B. Esel'son,
V. G. Gavrilko,
N. A. Vinnikov,
R. M. Basnukaeva,
A. I. Prokhvatilov,
I. V. Legchenkova,
V. V. Meleshko,
W. K. Maser,
A. M. Benito
Abstract:
The kinetics of the sorption and the subsequent desorption of 4He by the starting graphite oxide (GtO) and the thermally reduced graphene oxide samples (TRGO, Treduction = 200, 300, 500, 700 and 900 C) have been investigated in the temperature interval 1.5 - 20 K. The effect of the annealing temperature on the structural characteristics of the samples was examined by the X-ray diffraction (XRD) te…
▽ More
The kinetics of the sorption and the subsequent desorption of 4He by the starting graphite oxide (GtO) and the thermally reduced graphene oxide samples (TRGO, Treduction = 200, 300, 500, 700 and 900 C) have been investigated in the temperature interval 1.5 - 20 K. The effect of the annealing temperature on the structural characteristics of the samples was examined by the X-ray diffraction (XRD) technique. On lowering the temperature from 20 K to 11-12 K, the time of 4He sorption increased for all the samples, which is typically observed under the condition of thermally activated diffusion. Below 5 K the characteristic times of 4He sorption by the GtO and TRGO-200 samples were only weakly dependent on temperature, suggesting the dominance of the tunnel mechanism. In the same region (T<5 K) the characteristic times of the TRGOs reduced at higher temperatures (300, 500, 700 and 900 C) were growing with lowering temperature, presumably due to the defects generated in the carbon planes on removing the oxygen functional groups (oFGs). The estimates of the activation energy (Ea) of 4He diffusion show that in the TRGO-200 sample the Ea value is 2.9 times lower as compared to the parent GtO, which is accounted for by GtO exfoliation due to evaporation of the water intercalated in the interlayer space of carbon. The nonmonotonic dependences Ea vs T for the GtO samples treated above 200 C are determined by a competition between two processes - the recovery of the graphite carbon structure, which increases the activation energy, and the generation of defects, which decreases the activation energy by opening additional surface areas and ways for sorption. The dependence of the activation energy on treatment temperature correlates well with the contents of the crystalline phase in GtO varying with a rise of the annealing temperature.
△ Less
Submitted 25 November, 2016;
originally announced November 2016.
-
Sorption of 4He, H2, Ne, N2, CH4 and Kr impurities in graphene oxide at low temperatures. Quantum effects
Authors:
A. V. Dolbin,
V. B. Esel'son,
V. G. Gavrilko,
V. G. Manzhelii,
N. A. Vinnikov,
R. M. Basnukaeva,
V. V. Danchuk,
N. S. Mysko,
E. V. Bulakh,
W. K. Maser,
A. M. Benito
Abstract:
Sorption and the subsequent desorption of 4He, H2,Ne, N2, CH4 and Kr gas impurities by graphene oxide (GO), glucose-reduced GO (RGO-Gl) and hydrazine-reduced GO (RGO-Hz) powders have been investigated in the temperature interval 2-290 K. It has been found that the sorptive capacity of the reduced sample RGO-Hz is three to six times higher than that of GO. The reduction of GO with glucose has only…
▽ More
Sorption and the subsequent desorption of 4He, H2,Ne, N2, CH4 and Kr gas impurities by graphene oxide (GO), glucose-reduced GO (RGO-Gl) and hydrazine-reduced GO (RGO-Hz) powders have been investigated in the temperature interval 2-290 K. It has been found that the sorptive capacity of the reduced sample RGO-Hz is three to six times higher than that of GO. The reduction of GO with glucose has only a slight effect on its sorptive properties. The temperature dependences of the diffusion coefficients of the GO, RGO-Gl and RGO-Hz samples have been obtained using the measured characteristic times of sorption. It is assumed that the temperature dependences of the diffusion coefficients are determined by the competition of the thermally activated and tunneling mechanisms, the tunneling contribution being dominant at low temperatures.
△ Less
Submitted 17 July, 2013;
originally announced July 2013.