Temperature dependence of the Raman spectrum of orthorhombic Bi2Se3
Authors:
Irene Mediavilla-Martinez,
Christian Kramberger,
Shabnam Dadgostar,
Juan Jimenez,
Paola Ayala,
Thomas Pichler,
Francisco J. Manjon,
Placida Rodriguez-Hernandez,
Alfonso Muñoz,
Nadezhda Serebryanaya,
Sergei Buga,
Jorge Serrano
Abstract:
Bismuth selenide, a benchmark topological insulator, grows in a trigonal structure at ambient conditions and exhibits a number of enticing properties related to the formation of Dirac surface states. Besides this polytype, a metastable orthorhombic modification with Pnma space group has been produced by electrodeposition and high-pressure high-temperature synthesis displaying upon Sb do** signif…
▽ More
Bismuth selenide, a benchmark topological insulator, grows in a trigonal structure at ambient conditions and exhibits a number of enticing properties related to the formation of Dirac surface states. Besides this polytype, a metastable orthorhombic modification with Pnma space group has been produced by electrodeposition and high-pressure high-temperature synthesis displaying upon Sb do** significant thermoelectric properties in the midtemperature range. However, very little experimental information is available on the fundamental properties of this polytype, such as, e.g., the electronic band gap and the lattice dynamics. We report here the temperature dependence of the Raman spectra of orthorhombic Bi2Se3 between 10 K and 300 K, which displays an anharmonic behavior of the optical phonons that can be modelled with a two-phonon decay channel. In order to analyze the data we performed ab initio calculations of the electronic bandstructure, the phonon frequencies at the center of the Brillouin zone, and the phonon dispersion relations along the main symmetry directions, examining the effect of spin-orbit coupling in both phonon and electronic energies. Lastly, we report here cathodoluminescence experiments at 83 K that set a lower limit to the electronic bandgap at 0.835 eV, pointing to an indirect nature, in agreement with our calculations. These results shed light to essential properties of orthorhombic Bi2Se3 for further understanding of the potential of this semiconductor for thermoelectrics and new applications.
△ Less
Submitted 11 February, 2024;
originally announced February 2024.
-
Structural and vibrational study of Zn(IO3)2 combining high-pressure experiments and density-functional theory
Authors:
A. Liang,
C. Popescu,
F. J. Manjon,
P. Rodriguez-Hernandez,
A. Munoz,
Z. Hebboul,
D. Errandonea
Abstract:
We report a characterization of the high-pressure behavior of zinc-iodate, Zn(IO3)2. By the combination of x-ray diffraction, Raman spectroscopy, and first-principles calculations we have found evidence of two subtle isosymmetric structural phase transitions. We present arguments relating these transitions to a non-linear behavior of phonons and changes induced by pressure on the coordination sphe…
▽ More
We report a characterization of the high-pressure behavior of zinc-iodate, Zn(IO3)2. By the combination of x-ray diffraction, Raman spectroscopy, and first-principles calculations we have found evidence of two subtle isosymmetric structural phase transitions. We present arguments relating these transitions to a non-linear behavior of phonons and changes induced by pressure on the coordination sphere of the iodine atoms. This fact is explained as a consequence of the formation of metavalent bonding at high-pressure which is favored by the lone-electron pairs of iodine. In addition, the pressure dependence of unit-cell parameters, volume, and bond is reported. An equation of state to describe the pressure dependence of the volume is presented, indicating that Zn(IO3)2 is the most compressible iodate among those studied up to now. Finally, phonon frequencies are reported together with their symmetry assignment and pressure dependence.
△ Less
Submitted 24 January, 2024;
originally announced January 2024.
-
Structural, Vibrational, and Electronic Behavior of Two GaGeTe Polymorphs under compression
Authors:
Enrico Bandiello,
Samuel Gallego-Parra,
Akun Liang,
Juan Ángel Sans,
Vanesa Cuenca-Gotor,
Estelina Lora da Silva,
Rosario Vilaplana,
Plácida. Rodríguez-Hernández,
Alfonso Muñoz,
Daniel Diaz-Anichtchenko,
Catalin Popescu,
Frederico Gil Alabarse,
Carlos Rudamas,
Čestmír Drašar,
Alfredo Segura,
Daniel Errandonea,
Francisco Javier Manjón
Abstract:
GaGeTe is a layered topological semimetal that has been recently found to exist in at least two different polytypes, $α$-GaGeTe ($R\bar{3}m$) and $β$-GaGeTe ($P6_3 mc$). Here we report a joint experimental and theoretical study of the structural, vibrational, and electronic properties of these two polytypes at high pressure. Both polytypes show anisotropic compressibility and two phase transitions…
▽ More
GaGeTe is a layered topological semimetal that has been recently found to exist in at least two different polytypes, $α$-GaGeTe ($R\bar{3}m$) and $β$-GaGeTe ($P6_3 mc$). Here we report a joint experimental and theoretical study of the structural, vibrational, and electronic properties of these two polytypes at high pressure. Both polytypes show anisotropic compressibility and two phase transitions, above 7 and 15 GPa, respectively, as confirmed by XRD and Raman spectroscopy measurements. Although the nature of the high-pressure phases is not confirmed, comparison with other chalcogenides and total-energy calculations allow us to propose possible high-pressure phases for both polytypes with an increase in coordination for Ga and Ge atoms from 4 to 6. In particular, the simplification of the X-ray patterns for both polytypes above 15 GPa suggests a transition to a structure of relatively higher symmetry than the original one. This result is consistent with the rocksalt-like high-pressure phases observed in parent III-VI semiconductors, such as GaTe, GaSe, and InSe. Pressure-induced amorphization is observed upon pressure release. The electronic band structures of $α$-GaGeTe and $β$-GaGeTe and their pressure dependence also show similarities to III-VI semiconductors, thus suggesting that the germanene-like sublayer induces a semimetallic character in both GaGeTe polytypes. Above 3 GPa, both polytypes lose their topological features, due to the opening of the direct band gap, while the reduction of the interlayer space increases the thermal conductivity at high pressure.
△ Less
Submitted 3 July, 2023; v1 submitted 4 May, 2023;
originally announced May 2023.
-
Layered topological semimetal GaGeTe: new polytype with non-centrosymmetric structure
Authors:
S. Gallego-Parra,
E. Bandiello,
A. Liang,
E. Lora da Silva,
P. Rodríguez-Hernández,
A. Muñoz,
S. Radescu,
A. H. Romero,
C. Drasar,
D. Errandonea,
F. J. Manjón
Abstract:
GaGeTe is a layered material composed of germanene and GaTe sublayers that has been recently predicted to be a basic Z2 topological semimetal. To date, only one polytype of GaGeTe is known with trigonal centrosymmetric structure (alpha phase, space group R-3m, No. 166). Here we show that as-grown samples of GaGeTe show traces of at least another polytype with hexagonal non-centrosymmetric structur…
▽ More
GaGeTe is a layered material composed of germanene and GaTe sublayers that has been recently predicted to be a basic Z2 topological semimetal. To date, only one polytype of GaGeTe is known with trigonal centrosymmetric structure (alpha phase, space group R-3m, No. 166). Here we show that as-grown samples of GaGeTe show traces of at least another polytype with hexagonal non-centrosymmetric structure (beta phase, space group P63mc, No. 186). Moreover, we suggest that another bulk hexagonal polytype (gamma phase, space group P-3m1, No. 164) could also be found near room conditions. Both alpha and beta polytypes have been identified and characterized by means of X-ray diffraction and Raman scattering measurements with the support of ab initio calculations. We provide the vibrational properties of both polytypes and show that the Raman spectrum reported for GaGeTe almost forty years ago and attributed to the alpha phase, was, in fact, that of the secondary beta phase. Additionally, we show that a Fermi resonance occurs in alpha-GaGeTe under non-resonant excitation conditions, but not under resonant excitation conditions. Theoretical calculations show that bulk beta-GaGeTe is a non-centrosymmetric weak topological semimetal with even smaller lattice thermal conductivity than centrosymmetric bulk alpha-GaGeTe. In perspective, our work paves the way for the control and engineering of GaGeTe polytypes to design and implement complex van der Waals heterostructures formed by a combination of centrosymmetric and non-centrosymmetric layers of up to three different polytypes in a single material, suitable for a number of fundamental studies and technological applications.
△ Less
Submitted 6 July, 2022;
originally announced July 2022.
-
Theoretical study of the stability of the tetradymite-like phases of Sb$_2$S$_3$, Bi$_2$S$_3$, and Sb$_2$Se$_3$
Authors:
E. Lora da Silva,
J. M. Skelton,
P. Rodríguez-Hernández,
A. Muñoz,
M. C. Santos,
D. Martínez-García,
R. Vilaplana,
F. J. Manjón
Abstract:
We report a comparative theoretical study of the \textit{Pnma} and \textit{R-3m} phases of Sb$_2$S$_3$, Bi$_2$S$_3$, and Sb$_2$Se$_3$ close to ambient pressure.
Our enthalpy calculations at 0 K show that at ambient pressure the \textit{R-3m} (tetradymite-like) phase of Sb$_2$Se$_3$ is energetically more stable than the \textit{Pnma} phase, contrary to what is observed for Sb$_2$S$_3$ and Bi$_2$S…
▽ More
We report a comparative theoretical study of the \textit{Pnma} and \textit{R-3m} phases of Sb$_2$S$_3$, Bi$_2$S$_3$, and Sb$_2$Se$_3$ close to ambient pressure.
Our enthalpy calculations at 0 K show that at ambient pressure the \textit{R-3m} (tetradymite-like) phase of Sb$_2$Se$_3$ is energetically more stable than the \textit{Pnma} phase, contrary to what is observed for Sb$_2$S$_3$ and Bi$_2$S$_3$, and irrespective of the exchange-correlation functional employed in the calculations.
The result for Sb$_2$Se$_3$ is in contradiction to experiments where all three compounds are usually grown in the \textit{Pnma} phase.
This result is further confirmed by free-energy calculations taking into account the temperature dependence of the unit-cell volumes and phonon frequencies.
Lattice dynamics and elastic tensor calculations further show that both \textit{Pnma} and \textit{R-3m} phases of Sb$_2$Se$_3$ are dynamically and mechanically stable at zero applied pressure.
Since these results suggest that the formation of the \textit{R-3m} phase for Sb$_2$Se$_3$ should be feasible at close to ambient conditions, we provide a theoretical crystal structure and simulated Raman and infrared spectra to help in its identification. We also discuss the results of the two published works that have claimed to have synthesized tetradymite-like Sb$_2$Se$_3$.
Finally, the stability of the \textit{R-3m} phase across the three group-15 \textit{A$_2$X$_3$} sesquichalcogenides is analysed based on their van der Waals gap and X-X in-plane geometry.
△ Less
Submitted 2 June, 2022;
originally announced June 2022.
-
Anomalous Raman Modes in Tellurides
Authors:
F. J. Manjón,
S. Gallego-Parra,
P. Rodríguez-Hernández,
A. Muñoz,
C. Drasar,
V. Muñoz-Sanjosé,
O. Oeckler
Abstract:
Two broad bands are usually found in the Raman spectrum of many Te-based chalcogenides, which include binary compounds, like ZnTe, CdTe, HgTe, GaTe, GeTe, SnTe, PbTe, GeTe2, As2Te3, Sb2Te3, Bi2Te3, NiTe2, IrTe2, TiTe2, as well as ternary compounds, like GaGeTe, SnSb2Te4, SnBi2Te4, and GeSb2Te5. Many different explanations have been proposed in the literature for the origin of these two anomalous b…
▽ More
Two broad bands are usually found in the Raman spectrum of many Te-based chalcogenides, which include binary compounds, like ZnTe, CdTe, HgTe, GaTe, GeTe, SnTe, PbTe, GeTe2, As2Te3, Sb2Te3, Bi2Te3, NiTe2, IrTe2, TiTe2, as well as ternary compounds, like GaGeTe, SnSb2Te4, SnBi2Te4, and GeSb2Te5. Many different explanations have been proposed in the literature for the origin of these two anomalous broad bands in tellurides, usually located between 119 and 145 cm-1. They have been attributed to the own sample, to oxidation, to the folding of Brillouin-edge modes onto the zone center, to the existence of a double resonance, like that of graphene, or to the formation of Te precipitates. In this paper, we provide arguments to demonstrate that such bands correspond to clusters or precipitates of trigonal Te in form of nanosize or microsize grains or layers that are segregated either inside or at the surface of the samples. Several mechanisms for Te segregation are discussed and sample heating caused by excessive laser power during Raman scattering measurements is emphasized. Finally, we show that anomalous Raman modes related to Se precipitates also occur in selenides, thus providing a general vision for a better characterization of selenides and tellurides by means of Raman scattering measurements and for a better understanding of chalcogenides in general.
△ Less
Submitted 23 February, 2021;
originally announced February 2021.
-
Experimental and theoretical study of SbPO4 under compression
Authors:
André Luis de Jesus Pereira,
David Santamaría-Pérez,
Rosário Vilaplana,
Daniel Errandonea,
Catalin Popescu,
Estelina Lora da Silva,
Juan Angel Sans,
Juan Rodríguez-Carvajal,
Alfonso Muñoz,
Plácida Rodríguez-Hernández,
Andres Mujica,
Silvana Elena Radescu,
Armando Beltrán,
Alberto Otero de la Roza,
Marcelo Nalin,
Miguel Mollar,
Francisco Javier Manjón
Abstract:
SbPO4 is a complex monoclinic layered material characterized by a strong activity of the non-bonding lone electron pair (LEP) of Sb. The strong cation LEP leads to the formation of layers piled up along the a-axis and linked by weak Sb-O electrostatic interactions. In fact, Sb is 4-fold coordination with O similar to what occurs with the P-O coordination, despite the large difference of ionic radi…
▽ More
SbPO4 is a complex monoclinic layered material characterized by a strong activity of the non-bonding lone electron pair (LEP) of Sb. The strong cation LEP leads to the formation of layers piled up along the a-axis and linked by weak Sb-O electrostatic interactions. In fact, Sb is 4-fold coordination with O similar to what occurs with the P-O coordination, despite the large difference of ionic radii and electronegativity between both elements. Here we report a joint experimental and theoretical study of the structural and vibrational properties of SbPO4 at high pressure. We show that SbPO4 is not only one of the most compressible phosphates but also one of the most compressible compounds of the ABO4 family. Moreover, it has a considerable anisotropic compression behavior with the largest compression occurring along a direction close to a-axis and governed by the compression of the LEP and the weak inter-layer Sb-O bonds. The strong compression along the a-axis leads to a subtle modification of the monoclinic crystal structure above 3 GPa leading from a 2D to a 3D material. Moreover, the onset of a reversible pressure-induced phase transition is observed above 9 GPa, which is completed above 20 GPa. We propose that the high-pressure phase is a triclinic distortion of the original monoclinic phase. The understanding of the compression mechanism of SbPO4 can aid in understanding the importance of the ion intercalation and catalytic properties of this layered compound.
△ Less
Submitted 19 February, 2021;
originally announced February 2021.
-
GdBO$_3$ and YBO$_3$ Nanocrystals under Compression
Authors:
Robin Turnbull,
Daniel Errandonea,
Juan Ángel Sans,
Vanesa Paula Cuenca-Gotor,
Rosario Isabel Vilaplana,
Jordi Ibáñez,
Catalin Popescu,
Agata Szczeszak,
Stefan Lis,
Francisco Javier Manjón
Abstract:
High-pressure X-ray diffraction studies on nanocrystals of the pseudo-vaterite-type borates GdBO$_3$ and YBO$_3$ are herein reported up to 17.4(2) and 13.4(2) GPa respectively. The subsequent determination of the room-temperature pressure-volume equations of state is presented and discussed in the context of contemporary publications which contradict the findings of this work. In particular, the i…
▽ More
High-pressure X-ray diffraction studies on nanocrystals of the pseudo-vaterite-type borates GdBO$_3$ and YBO$_3$ are herein reported up to 17.4(2) and 13.4(2) GPa respectively. The subsequent determination of the room-temperature pressure-volume equations of state is presented and discussed in the context of contemporary publications which contradict the findings of this work. In particular, the isothermal bulk moduli of GdBO$_3$ and YBO$_3$ are found to be 170(13) and 163(13) GPa respectively, almost 50% smaller than recent findings. Our experimental results provide an accurate revision of the high-pressure compressibility behaviour of GdBO$_3$ and YBO$_3$ which is consistent with the known systematics in isomorphic borates and previous ab initio calculations. Finally we discuss how experimental/analytical errors could have led to unreliable conclusions reported elsewhere.
△ Less
Submitted 24 September, 2020;
originally announced September 2020.
-
$β$-As$_2$Te$_3$: Pressure-Induced 3D Dirac Semi-Metal
Authors:
E. Lora da Silva,
A. Leonardo,
Tao Yang,
M. C. Santos,
R. Vilaplana,
S. Gallego-Parra,
A. Bergara,
F. J. Manjón
Abstract:
We report a theoretical \textit{ab-initio} study of $β$-As$_2$Te$_3$ ($R\bar{3}m$ symmetry) at hydrostatic pressures up to 12 GPa. We have systematically characterized the vibrational and electronic changes of the system induced by the pressure variation. The electronic band dispersions calculated at different pressures using \textit{QS}GW show an insulator-metal transition. At room pressure the s…
▽ More
We report a theoretical \textit{ab-initio} study of $β$-As$_2$Te$_3$ ($R\bar{3}m$ symmetry) at hydrostatic pressures up to 12 GPa. We have systematically characterized the vibrational and electronic changes of the system induced by the pressure variation. The electronic band dispersions calculated at different pressures using \textit{QS}GW show an insulator-metal transition. At room pressure the system is a semiconductor with small band-gap, and the valence and conduction bands present a parabolic conventional dispersion. However around 2 GPa the parabolic shape of the bands become linear and touch at the Fermi level. This means that this compound undergoes a pressure-induced topological phase transition to a 3D analog of graphene, known as a 3D Dirac semi-metal, with gapless electronic excitations. At increasing pressures the gap reopens and variation of the character of the electronic band-gap from direct to indirect is evidenced. At 7 GPa we observe the formation of a negative band-gap character, which persists for pressures up to 12 GPa. Topological insulating features are evidenced from 2 to 12 GPa with a Z$_4$=3 topological index. Moreover by investigating the lattice thermal-conductivity at different pressures, we observe an ultra low value of $κ_\textrm{L}$ at 300 K for 0.5 GPa (0.294 and 0.486 Wm$^{-1}$K$^{-1}$ for the $x$-$y$-axis and for the $z$-axis, respectively) which is the result of existing low-frequency optical modes. At 2 GPa $κ_\textrm{L}$ increases to 1.170 and 0.669 Wm$^{-1}$K$^{-1}$, for the $x$-$y$-axis and for the $z$-axis, respectively. At 4 GPa the thermal-conductivity values between the two distinct crystallographic axis tend to approximate, with 1.495 and 1.433 Wm$^{-1}$K$^{-1}$, along the $x$-$y$-axis and the $z$-axis, respectively.
△ Less
Submitted 27 November, 2020; v1 submitted 22 August, 2020;
originally announced August 2020.
-
Structural and lattice-dynamical properties of Tb2O3 under compression: a comparative study with rare-earth and related sesquioxides
Authors:
Jordi Ibáñez,
Juan Ángel Sans,
Vanesa Cuenca-Gotor,
Robert Oliva,
Óscar Gomis,
Plácida Rodríguez-Hernández,
Alfonso Muñoz,
Ulises Rodríguez-Mendoza,
Matías Velázquez,
Philippe Veber,
Catalin Popescu,
Francisco Javier Manjón
Abstract:
We report a joint experimental and theoretical investigation of the high-pressure structural and vibrational properties of terbium sesquioxide (Tb2O3). Powder x-ray diffraction and Raman scattering measurements show that cubic (C-type) Tb2O3 undergoes two phase transitions up to 25 GPa. We observe a first irreversible reconstructive transition to the monoclinic (B-type) phase at ~7 GPa and a subse…
▽ More
We report a joint experimental and theoretical investigation of the high-pressure structural and vibrational properties of terbium sesquioxide (Tb2O3). Powder x-ray diffraction and Raman scattering measurements show that cubic (C-type) Tb2O3 undergoes two phase transitions up to 25 GPa. We observe a first irreversible reconstructive transition to the monoclinic (B-type) phase at ~7 GPa and a subsequent reversible displacive transition from the monoclinic to the trigonal (A-type) phase at ~12 GPa. Thus, Tb2O3 is found to follow the well-known C-B-A phase transition found in other cubic rare-earth sesquioxides with cations of larger atomic mass than Tb. Our ab initio theoretical calculations predict phase transition pressures and bulk moduli for the three phases in rather good agreement with experimental results. Moreover, Raman-active modes of the three phases have been monitored as a function of pressure and lattice-dynamics calculations have allowed us to confirm the assignment of the experimental phonon modes in the C-type phase as well as to make a tentative assignment of the symmetry of most vibrational modes in the B- and A-type phases. Finally, we extract the bulk moduli and the Raman-active modes frequencies together with their pressure coefficients for the three phases of Tb2O3. These results are thoroughly compared and discussed in relation to those reported for rare-earth and other related sesquioxides. It is concluded that the evolution of the volume and bulk modulus of all the three phases of these technologically relevant compounds exhibit a nearly linear trend with respect to the third power of the ionic radii of the cations.
△ Less
Submitted 26 May, 2020;
originally announced May 2020.
-
High-pressure characterization of multifunctional CrVO4
Authors:
P. Botella,
S. Lopez-Moreno,
D. Errandonea,
F. J. Manjon,
J. A. Sans,
D. Vie,
A. Vomiero
Abstract:
The structural stability and physical properties of CrVO4 under compression were studied by X-ray diffraction, Raman spectroscopy, optical absorption, resistivity measurements, and ab initio calculations up to 10 GPa. High-pressure X-ray diffraction and Raman measurements show that CrVO4 undergoes a phase transition from the ambient pressure orthorhombic CrVO4-type structure (Cmcm space group, pha…
▽ More
The structural stability and physical properties of CrVO4 under compression were studied by X-ray diffraction, Raman spectroscopy, optical absorption, resistivity measurements, and ab initio calculations up to 10 GPa. High-pressure X-ray diffraction and Raman measurements show that CrVO4 undergoes a phase transition from the ambient pressure orthorhombic CrVO4-type structure (Cmcm space group, phase III) to the high-pressure monoclinic CrVO4-V phase, which is isomorphic to the wolframite structure. Such a phase transition (CrVO4-type - wolframite), driven by pressure, also was previously observed in indium vanadate. The crystal structure of both phases and the pressure dependence in unit-cell parameters, Raman-active modes, resistivity, and electronic band gap, is reported. Vanadium atoms are sixth-fold coordinated in the wolframite phase, which is related to the collapse in the volume at the phase transition. Besides, we also observed drastic changes in the phonon spectrum, a drop of the band-gap, and a sharp decrease of resistivity. All the observed phenomena are explained with the help of first-principles calculations.
△ Less
Submitted 17 April, 2020;
originally announced April 2020.
-
Orpiment under compression: metavalent bonding at high pressure
Authors:
V. P. Cuenca-Gotor,
J. A. Sans,
O. Gomis,
A. Mujica,
S. Radescu,
A. Muñoz,
P. Rodríguez-Hernández,
E. Lora da Silva,
C. Popescu,
J. Ibañez,
R. Vilaplana,
F. J. Manjón
Abstract:
We report a joint experimental and theoretical study of the structural, vibrational, and electronic properties of layered monoclinic arsenic sulfide (alpha-As2S3), aka mineral orpiment, under compression. X-ray diffraction and Raman scattering measurements performed in orpiment samples at high pressure and combined with ab initio calculations have allowed us to determine the equation of state and…
▽ More
We report a joint experimental and theoretical study of the structural, vibrational, and electronic properties of layered monoclinic arsenic sulfide (alpha-As2S3), aka mineral orpiment, under compression. X-ray diffraction and Raman scattering measurements performed in orpiment samples at high pressure and combined with ab initio calculations have allowed us to determine the equation of state and the tentative assignment of the symmetry of many Raman-active modes of orpiment. From our results, we conclude that no first-order phase transition occurs up to 25 GPa at room temperature; however, compression leads to an isostructural phase transition above 20 GPa. In fact, As coordination increases from threefold at room pressure to more than fivefold above 20 GPa. This increase in coordination can be understood as the formation of metavalent bonding at high pressure, which results in a progressive decrease of the electronic and optical bandgap, an increase of the dielectric tensor and Born effective charges, and a considerable softening of many high-frequency optical modes with pressure. The formation of metavalent bonding may also explain the behavior of other group-15 sesquichalcogenides under compression. Moreover, our results suggest that group-15 sesquichalcogenides either show metavalent bonding at room pressure or undergo a transition from p-type covalent bonding at room pressure towards metavalent bonding at high pressure, as a preceding phase towards metallic bonding at very high pressure.
△ Less
Submitted 25 July, 2019;
originally announced July 2019.
-
Characterization and decomposition of the natural van der Waals heterostructure SnSb2Te4 under compression
Authors:
Juan A. Sans,
Rosario Vilaplana,
E. Lora Da Silva,
Catalin Popescu,
Vanesa P. Cuenca-Gotor,
Adrián Andrada-Chacón,
Javier Sánchez-Benitez,
Oscar Gomis,
André L. J. Pereira,
Plácida Rodríguez-Hernández,
Alfonso Muñoz,
Dominik Daisenberger,
Braulio García-Domene,
Alfredo Segura,
Daniel Errandonea,
Ravhi S. Kumar,
Oliver Oeckler,
Julia Contreras-García,
Francisco J. Manjón
Abstract:
This joint experimental and theoretical study of the structural, vibrational and electrical properties of rhombohedral SnSb2Te4 at high pressure unveils the internal mechanisms of its compression. The equation of state and the internal polyhedral compressibility, the symmetry and behavior of the Raman-active modes and the electrical behavior of this topological insulator under compression have bee…
▽ More
This joint experimental and theoretical study of the structural, vibrational and electrical properties of rhombohedral SnSb2Te4 at high pressure unveils the internal mechanisms of its compression. The equation of state and the internal polyhedral compressibility, the symmetry and behavior of the Raman-active modes and the electrical behavior of this topological insulator under compression have been discussed and compared with the parent binary alpha-Sb2Te3 and SnTe compounds and with related ternary compounds. Our X-ray diffraction and Raman measurements together with theoretical calculations, which include topological electron density and electronic localization function analysis, evidence the presence of an isostructural phase transition around 2 GPa and a Fermi resonance around 3.5 GPa. The Raman spectrum of SnSb2Te4 shows vibrational modes that are forbidden in rocksalt SnTe; thus showing a novel way to experimentally observe the forbidden vibrational modes of some compounds. Additionally, since SnSb2Te4 is an incipient metal, like its parent binary compounds, we establish a new criterion to identify the recently proposed metavalent bonding in complex materials when different bond characters coexist in the system. Finally, SnSb2Te4 exhibits a pressure-induced decomposition into the high-pressure phases of its parent binary compounds above 7 GPa, which is supported by an analysis of their formation enthalpies. We have framed the behavior of SnSb2Te4 within the extended orbital radii map of BA2Te4 compounds, which paves the way to understand the pressure behavior and stability ranges of other layered van der Waals-type compounds with similar stoichiometry.
△ Less
Submitted 18 July, 2019;
originally announced July 2019.
-
Theoretical study of phase transitions in Sb2S3, Bi2S3 and Sb2Se3 under compression
Authors:
E. Lora da Silva,
J. M. Skelton,
P. Rodríguez-Hernández,
A. Muñoz,
D. Martínez-García,
F. J. Manjón
Abstract:
We report a theoretical study of Sb2S3, Sb2Se3 and Bi2S3 sesquichalcogenides at hydrostatic pressures up to 60 GPa. We explore the possibility that the R-3m, C2/m, C2/c and Im-3m phases observed in sesquichalcogenides with heavier cations, viz. Bi2Se3, Bi2Te3 and Sb2Te3, could also be formed in the former compounds as suggested by recent experiments. Our calculations show that the C2/m and C2/c ph…
▽ More
We report a theoretical study of Sb2S3, Sb2Se3 and Bi2S3 sesquichalcogenides at hydrostatic pressures up to 60 GPa. We explore the possibility that the R-3m, C2/m, C2/c and Im-3m phases observed in sesquichalcogenides with heavier cations, viz. Bi2Se3, Bi2Te3 and Sb2Te3, could also be formed in the former compounds as suggested by recent experiments. Our calculations show that the C2/m and C2/c phases are energetically unstable in any of the three compounds and over the entire range of pressures examined. In contrast, the disordered bcc-like Im-3m phase is energetically stable at high pressures, but only the Sb2Se3 phase does not show dynamical instabilities below 60 GPa. Our calculations show that the Pnma structure is the most energetically stable Sb2S3 and Bi2S3 phase at ambient pressure whereas, surprisingly, the R-3m phase of Sb2Se3 is predicted to have the lowest enthalpy energy at 0 GPa, in contradiction to experimental evidence. Our calculations show that both Pnma and R-3m phases are dynamical and mechanically stable at room pressure. These results suggest that the formation of the R-3m phase in Sb2Se3 could be feasible at close to ambient conditions. To aid its identification, we provide a theoretical crystal structure (lattice and atomic parameters) and complete infrared and Raman spectra for this phase.
△ Less
Submitted 16 November, 2019; v1 submitted 19 April, 2019;
originally announced April 2019.
-
Helium ordered trap** in arsenolite under compression: Synthesis of He2As4O6
Authors:
Juan Angel Sans,
Francisco Javier Manjón,
Catalin Popescu,
Vanesa Paula Cuenca-Gotor,
Oscar Gomis,
Alfonso Muñoz,
Plácida Rodríguez-Hernández,
Julio Pellicer-Porres,
Andre Luis de Jesus Pereira,
David Santamaría-Pérez,
Alfredo Segura
Abstract:
The compression of arsenolite (cubic As2O3) has been studied from a joint experimental and theoretical point of view. Experimental X-ray diffraction and Raman scattering measurements of this molecular solid at high pressures with different pressure-transmitting media have been interpreted with the help of ab initio calculations. Our results confirm arsenolite as one of the softest minerals in abse…
▽ More
The compression of arsenolite (cubic As2O3) has been studied from a joint experimental and theoretical point of view. Experimental X-ray diffraction and Raman scattering measurements of this molecular solid at high pressures with different pressure-transmitting media have been interpreted with the help of ab initio calculations. Our results confirm arsenolite as one of the softest minerals in absence of hydrogen bonding and provide evidence for helium trap** above 3 GPa between adamantane-type As4O6 cages, thus leading to a new compound with stoichiometry He2As4O6. Helium trap** alters all properties of arsenolite. In particular, pressure-induced amorphization, which occurs in pure arsenolite above 15 GPa, is impeded when He is trapped between the As4O6 cages; thus resulting in a mechanical stability of He2As4O6 beyond 30 GPa. Our work paves the way for the modification of the properties of other molecular solids by compression depending on their ability to trap relatively small atomic or molecular species and form new compounds. Furthermore, our work suggests that compression of molecular solids with noble gases as helium could result in unexpected results compared to other pressure-transmitting media.
△ Less
Submitted 14 February, 2015;
originally announced February 2015.
-
High-pressure structural and elastic properties of Tl2O3
Authors:
O. Gomis,
D. Santamaria-Perez,
J. Ruiz-Fuertes,
J. A. Sans,
R. Vilaplana,
H. M. Ortiz,
B. Garcia-Domene,
F. J. Manjon,
D. Errandonea,
P. Rodriguez-Hernandez,
A. Muñoz,
M. Mollar
Abstract:
The structural properties of Thallium (III) oxide (Tl2O3) have been studied both experimentally and theoretically under compression at room temperature. X-ray powder diffraction measurements up to 37.7 GPa have been complemented with ab initio total-energy calculations. The equation of state of Tl2O3 has been determined and compared to related compounds. It has been found experimentally that Tl2O3…
▽ More
The structural properties of Thallium (III) oxide (Tl2O3) have been studied both experimentally and theoretically under compression at room temperature. X-ray powder diffraction measurements up to 37.7 GPa have been complemented with ab initio total-energy calculations. The equation of state of Tl2O3 has been determined and compared to related compounds. It has been found experimentally that Tl2O3 remains in its initial cubic bixbyite-type structure up to 22.0 GPa. At this pressure, the onset of amorphization is observed, being the sample fully amorphous at 25.2 GPa. The sample retains the amorphous state after pressure release. To understand the pressure-induced amorphization process, we have studied theoretically the possible high-pressure phases of Tl2O3. Although a phase transition is predicted at 5.8 GPa to the orthorhombic Rh2O3-II-type structure and at 24.2 GPa to the orthorhombic a-Gd2S3-type structure, neither of these phases were observed experimentally, probably due to the hindrance of the pressure-driven phase transitions at room temperature. The theoretical study of the elastic behavior of the cubic bixbyite-type structure at high-pressure shows that amorphization above 22 GPa at room temperature might be caused by the mechanical instability of the cubic bixbyite-type structure which is theoretically predicted above 23.5 GPa.
△ Less
Submitted 9 January, 2015;
originally announced January 2015.
-
Structural study of alfa-Bi2O3 under pressure
Authors:
A. L. J. Pereira,
D. Errandonea,
A. Beltrán,
L. Gracia,
O. Gomis,
J. A. Sans,
B. Garcia-Domene,
A. Miquel-Veyrat,
F. J. Manjón,
A. Muñoz,
C. Popescu
Abstract:
An experimental and theoretical study of the structural properties of monoclinic bismuth oxide (alfa-Bi2O3) under high pressures is here reported. Both synthetic and mineral bismite powder samples have been compressed up to 45 GPa and their equations of state have been determined with angle-dispersive x-ray diffraction measurements. Experimental results have been also compared to theoretical calcu…
▽ More
An experimental and theoretical study of the structural properties of monoclinic bismuth oxide (alfa-Bi2O3) under high pressures is here reported. Both synthetic and mineral bismite powder samples have been compressed up to 45 GPa and their equations of state have been determined with angle-dispersive x-ray diffraction measurements. Experimental results have been also compared to theoretical calculations which suggest the possibility of several phase transitions below 10 GPa. However, experiments reveal only a pressure-induced amorphisation between 15 and 25 GPa, depending on sample quality and deviatoric stresses. The amorphous phase has been followed up to 45 GPa and its nature discussed.
△ Less
Submitted 10 February, 2014;
originally announced February 2014.
-
Room-temperature vibrational properties of multiferroic MnWO4 under quasi-hydrostatic compression up to 39 GPa
Authors:
J. Ruiz-Fuertes,
D. Errandonea,
O. Gomis,
A. Friedrich,
F. J. Manjon
Abstract:
The multiferroic manganese tungstate (MnWO4) has been studied by high-pressure Raman spectroscopy at room temperature under quasi-hydrostatic conditions up to 39.3 GPa. The low-pressure wolframite phase undergoes a phase transition at 25.7 GPa, a pressure around 8 GPa higher than that found in previous works which used less hydrostatic pressure-transmitting media. The pressure dependence of the Ra…
▽ More
The multiferroic manganese tungstate (MnWO4) has been studied by high-pressure Raman spectroscopy at room temperature under quasi-hydrostatic conditions up to 39.3 GPa. The low-pressure wolframite phase undergoes a phase transition at 25.7 GPa, a pressure around 8 GPa higher than that found in previous works which used less hydrostatic pressure-transmitting media. The pressure dependence of the Raman active modes of both the low- and high-pressure phases are reported and discussed comparing with the results available in the literature for MnWO4 and related wolframites. A gradual pressure-induced phase transition from the low- to the high- pressure phase is suggested on the basis of the linear intensity decrease of the Raman mode with the lowest frequency up to the end of the phase transition.
△ Less
Submitted 27 January, 2014;
originally announced January 2014.
-
Pbca-type In2O3: the lost pressure-induced post-corundum phase
Authors:
Braulio García-Domene,
Juan A. Sans,
Óscar Gomis,
Francisco J. Manjón,
Henry M. Ortiz,
Daniel Errandonea,
David Santamaría-Pérez,
Domingo Martínez-García,
Rosario Vilaplana,
André L. J. Pereira,
Ángel Morales-García,
Plácida Rodríguez-Hernández,
Alfonso Muñoz,
Catalin Popescu,
Alfredo Segura
Abstract:
Contradictory results of high-pressure studies in cubic bixbyite-type indium oxide (c-In2O3) at room temperature (RT) have motivated us to perform high-pressure powder x-ray diffraction and Raman scattering measurements in this material. On increasing pressure c-In2O3 undergoes a transition to the Rh2O3-II structure. On decreasing pressure Rh2O3-II-type In2O3 undergoes a transition to a previously…
▽ More
Contradictory results of high-pressure studies in cubic bixbyite-type indium oxide (c-In2O3) at room temperature (RT) have motivated us to perform high-pressure powder x-ray diffraction and Raman scattering measurements in this material. On increasing pressure c-In2O3 undergoes a transition to the Rh2O3-II structure. On decreasing pressure Rh2O3-II-type In2O3 undergoes a transition to a previously unknown phase which is isostructural to Rh2O3-III. On further decrease of pressure, another phase transition to corundum-type In2O3, which is metastable at room conditions, is observed. Recompression of metastable corundum-type In2O3 shows that the Rh2O3-III phase is the post-corundum phase. Our results are supported by theoretical ab initio calculations which show that the Rh2O3-III phase could be present in other sesquioxides, thus leading to a revision of the pressure-temperature phase diagrams of sesquioxides.
△ Less
Submitted 26 November, 2013;
originally announced November 2013.
-
New high-pressure phase and equation of state of Ce2Zr2O8
Authors:
D. Errandonea,
R. S. Kumar,
S. N. Achary,
O. Gomis,
F. J. Manjon,
R. Shukla,
A. K. Tyagi
Abstract:
In this paper we report a new high-pressure rhombohedral phase of Ce2Zr2O8 observed from high-pressure angle-dispersive x-ray diffraction and Raman spectroscopy studies up to nearly 12 GPa. The ambient-pressure cubic phase of Ce2Zr2O8 transforms to a rhombohedral structure beyond 5 GPa with a feeble distortion in the lattice. Pressure evolution of unit-cell volume showed a change in compressibilit…
▽ More
In this paper we report a new high-pressure rhombohedral phase of Ce2Zr2O8 observed from high-pressure angle-dispersive x-ray diffraction and Raman spectroscopy studies up to nearly 12 GPa. The ambient-pressure cubic phase of Ce2Zr2O8 transforms to a rhombohedral structure beyond 5 GPa with a feeble distortion in the lattice. Pressure evolution of unit-cell volume showed a change in compressibility above 5 GPa. The unit-cell parameters of the high-pressure rhombohedral phase at 12.1 GPa are ah = 14.6791(3) Å, ch = 17.9421(5) Å, V = 3348.1(1) Å3. The structure relation between the parent cubic (P2_13) and rhombohedral (P3_2) phases were obtained by group-subgroup relations. All the Raman modes of the cubic phase showed linear evolution with pressure with the hardest one at 197 cm-1. Some Raman modes of the high-pressure phase have a non-linear evolution with pressure and softening of one low-frequency mode with pressure is found. The compressibility, equation of state, and pressure coefficients of Raman modes of Ce2Zr2O8 are also reported.
△ Less
Submitted 9 March, 2012;
originally announced March 2012.
-
Effects of high-pressure on the structural, vibrational, and electronic properties of monazite-type PbCrO4
Authors:
E. Bandiello,
D. Errandonea,
D. Martinez-Garcia,
D. Santamaria-Perez,
F. J. Manjon
Abstract:
We have performed an experimental study of the crystal structure, lattice-dynamics, and optical properties of PbCrO4 (the mineral crocoite) at ambient and high pressures. In particular, the crystal structure, Raman-active phonons, and electronic band-gap have been accurately determined. X-ray-diffraction, Raman, and optical-absorption experiments have allowed us also to completely characterize two…
▽ More
We have performed an experimental study of the crystal structure, lattice-dynamics, and optical properties of PbCrO4 (the mineral crocoite) at ambient and high pressures. In particular, the crystal structure, Raman-active phonons, and electronic band-gap have been accurately determined. X-ray-diffraction, Raman, and optical-absorption experiments have allowed us also to completely characterize two pressure-induced structural phase transitions. The first transition is isostructural, maintaining the monoclinic symmetry of the crystal, and having important consequences in the physical properties; among other a band-gap collapse is induced. The second one involves an increase of the symmetry of the crystal, a volume collapse, and probably the metallization of PbCrO4. The results are discussed in comparison with related compounds and the effects of pressure in the electronic structure explained. Finally, the room-temperature equation of state of the low-pressure phases is also obtained.
△ Less
Submitted 16 November, 2011;
originally announced November 2011.
-
High-pressure Raman spectroscopy and lattice-dynamics calculations on scintillating MgWO4: A comparison with isomorphic compounds
Authors:
J. Ruiz-Fuertes,
D. Errandonea,
S. Lopez-Moreno,
J. Gonzalez,
O. Gomis,
R. Vilaplana,
F. J. Manjon,
A. Munoz,
P. Rodriguez-Hernandez,
A. Friedrich,
I. A. Tupitsyna,
L. L. Nagornaya
Abstract:
Raman scattering measurements and lattice-dynamics calculations have been performed on magnesium tungstate under high pressure up to 41 GPa. Experiments have been carried out under a selection of different pressure-media. The influence of non-hydrostaticity on the structural properties of MgWO4 and isomorphic compounds is examined. Under quasi-hydrostatic conditions a phase transition has been fou…
▽ More
Raman scattering measurements and lattice-dynamics calculations have been performed on magnesium tungstate under high pressure up to 41 GPa. Experiments have been carried out under a selection of different pressure-media. The influence of non-hydrostaticity on the structural properties of MgWO4 and isomorphic compounds is examined. Under quasi-hydrostatic conditions a phase transition has been found at 26 GPa in MgWO4. The high-pressure phase has been tentatively assigned to a triclinic structure similar to that of CuWO4. We also report and discuss the Raman symmetries, frequencies, and pressure coefficients in the low- and high-pressure phases. In addition, the Raman frequencies for different wolframites are compared and the variation of the mode frequency with the reduced mass across the family is investigated. Finally, the accuracy of theoretical calculations is systematically discussed for MgWO4, MnWO4, FeWO4, CoWO4, NiWO4, ZnWO4, and CdWO4.
△ Less
Submitted 1 July, 2011;
originally announced July 2011.
-
Zircon to monazite phase transition in CeVO4
Authors:
V. Panchal,
S. Lopez-Moreno,
D. Santamaria-Perez,
D. Errandonea,
F. J. Manjon,
P. Rodriguez-Hernandez,
A. Munoz,
S. N. Achary,
A. K. Tyagi
Abstract:
X-ray diffraction and Raman-scattering measurements on cerium vanadate have been performed up to 12 and 16 GPa, respectively. Experiments reveal that at 5.3 GPa the onset of a pressure-induced irreversible phase transition from the zircon to the monazite structure. Beyond this pressure, diffraction peaks and Raman-active modes of the monazite phase are measured. The zircon to monazite transition i…
▽ More
X-ray diffraction and Raman-scattering measurements on cerium vanadate have been performed up to 12 and 16 GPa, respectively. Experiments reveal that at 5.3 GPa the onset of a pressure-induced irreversible phase transition from the zircon to the monazite structure. Beyond this pressure, diffraction peaks and Raman-active modes of the monazite phase are measured. The zircon to monazite transition in CeVO4 is distinctive among the other rare-earth orthovanadates. We also observed softening of external translational Eg and internal B2g bending modes. We attributed it to mechanical instabilities of zircon phase against the pressure-induced distortion. We additionally report lattice-dynamical and total-energy calculations which are in agreement with the experimental results. Finally, the effect of non-hydrostatic stresses on the structural sequence is studied and the equations of state of different phases are reported.
△ Less
Submitted 2 May, 2011;
originally announced May 2011.
-
Post-spinel transformations and equation of state in ZnGa2O4: Determination at high-pressure by in situ x-ray diffraction
Authors:
D. Errandonea,
Ravhi S. Kumar,
F. J. Manjon,
V. V. Ursaki,
E. V. Rusu
Abstract:
Room temperature angle-dispersive x-ray diffraction measurements on spinel ZnGa2O4 up to 56 GPa show evidence of two structural phase transformations. At 31.2 GPa, ZnGa2O4 undergoes a transition from the cubic spinel structure to a tetragonal spinel structure similar to that of ZnMn2O4. At 55 GPa, a second transition to the orthorhombic marokite structure (CaMn2O4-type) takes place. The equation o…
▽ More
Room temperature angle-dispersive x-ray diffraction measurements on spinel ZnGa2O4 up to 56 GPa show evidence of two structural phase transformations. At 31.2 GPa, ZnGa2O4 undergoes a transition from the cubic spinel structure to a tetragonal spinel structure similar to that of ZnMn2O4. At 55 GPa, a second transition to the orthorhombic marokite structure (CaMn2O4-type) takes place. The equation of state of cubic spinel ZnGa2O4 is determined: V0 = 580.1(9) A3, B0 = 233(8) GPa, B0'= 8.3(4), and B0''= -0.1145 GPa-1 (implied value); showing that ZnGa2O4 is one of the less compressible spinels studied to date. For the tetragonal structure an equation of state is also determined: V0 = 257.8(9) A3, B0 = 257(11) GPa, B0'= 7.5(6), and B0''= -0.0764 GPa-1 (implied value). The reported structural sequence coincides with that found in NiMn2O4 and MgMn2O4.
△ Less
Submitted 3 May, 2010;
originally announced May 2010.
-
High-pressure structural phase transitions in CuWO4
Authors:
J. Ruiz-Fuertes,
D. Errandonea,
R. Lacomba-Perales,
A. Segura,
J. Gonzalez,
F. Rodriguez,
F. J. Manjon,
S. Ray,
P. Rodriguez-Hernandez,
A. Munoz,
Zh. Zhu,
C. Y. Tu
Abstract:
We study the effects of pressure on the structural, vibrational, and magnetic behavior of cuproscheelite. We performed powder x-ray diffraction and Raman spectroscopy experiments up to 27 GPa as well as ab initio total-energy and lattice-dynamics calculations. Experiments provide evidence that a structural phase transition takes place at 10 GPa from the low-pressure triclinic phase (P-1) to a mono…
▽ More
We study the effects of pressure on the structural, vibrational, and magnetic behavior of cuproscheelite. We performed powder x-ray diffraction and Raman spectroscopy experiments up to 27 GPa as well as ab initio total-energy and lattice-dynamics calculations. Experiments provide evidence that a structural phase transition takes place at 10 GPa from the low-pressure triclinic phase (P-1) to a monoclinic wolframite-type structure (P2/c). Calculations confirmed this finding and indicate that the phase transformation involves a change in the magnetic order. In addition, the equation of state for the triclinic phase is determined: V0 = 132.8(2) A3, B0 = 139 (6) GPa and = 4. Furthermore, experiments under different stress conditions show that non-hydrostatic stresses induce a second phase transition at 17 GPa and reduce the compressibility of CuWO4, B0 = 171(6) GPa. The pressure dependence of all Raman modes of the triclinic and high-pressure phases is also reported and discussed.
△ Less
Submitted 3 May, 2010;
originally announced May 2010.
-
High-pressure x-ray diffraction study on the structure and phase transitions of the defect-stannite ZnGa2Se4 and defect-chalcopyrite CdGa2S4
Authors:
D. Errandonea,
R. S. Kumar,
F. J. Manjon,
V. V. Ursaki,
I. M. Tiginyanu
Abstract:
X-ray diffraction measurements on the sphalerite-derivatives ZnGa2Se4 and CdGa2S4 have been performed upon compression up to 23 GPa in a diamond-anvil cell. ZnGa2Se4 exhibits a defect tetragonal stannite-type structure (I-42m) up to 15.5 GPa and in the range from 15.5 GPa to 18.5 GPa the low-pressure phase coexists with a high-pressure phase, which remains stable up to 23 GPa. In CdGa2S4, we fin…
▽ More
X-ray diffraction measurements on the sphalerite-derivatives ZnGa2Se4 and CdGa2S4 have been performed upon compression up to 23 GPa in a diamond-anvil cell. ZnGa2Se4 exhibits a defect tetragonal stannite-type structure (I-42m) up to 15.5 GPa and in the range from 15.5 GPa to 18.5 GPa the low-pressure phase coexists with a high-pressure phase, which remains stable up to 23 GPa. In CdGa2S4, we find the defect tetragonal chalcopyrite-type structure (I-4) is stable up to 17 GPa. Beyond this pressure a pressure-induced phase transition takes place. In both materials, the high-pressure phase has been characterized as a defect-cubic NaCl-type structure (Fm-3m). The occurrence of the pressure induced phase transitions is apparently related with an increase of the cation disorder on the semiconductors investigated. In addition, the results allow the evaluation of the axial compressibility and the determination of the equation of state for each compound. The obtained results are compared with those previously reported for isomorphic digallium sellenides. Finally, a systematic study of the pressure-induced phase transition in twenty-three different sphalerite-related ABX2 and AB2X4 compounds indicates that the transition pressure increases as the ratio of the cationic radii and anionic radii of the compounds increases.
△ Less
Submitted 26 September, 2008;
originally announced September 2008.
-
Combined Raman scattering and ab initio investigation of pressure-induced structural phase transitions in the scintillator ZnWO4
Authors:
D. Errandonea,
F. J. Manjon,
N. Garro,
P. Rodriguez-Hernandez,
S. Radescu,
A. Mujica,
A. Munoz,
C. Y. Tu
Abstract:
Room-temperature Raman scattering was measured in ZnWO4 up to 45 GPa. We report the pressure dependence of all the Raman-active phonons of the low-pressure wolframite phase. As pressure increases new Raman peaks appear at 30.6 GPa due to the onset of a reversible structural phase transition to a distorted monoclinic b-fergusonite-type phase. The low- and high-pressure phases coexist from 30.6 GP…
▽ More
Room-temperature Raman scattering was measured in ZnWO4 up to 45 GPa. We report the pressure dependence of all the Raman-active phonons of the low-pressure wolframite phase. As pressure increases new Raman peaks appear at 30.6 GPa due to the onset of a reversible structural phase transition to a distorted monoclinic b-fergusonite-type phase. The low- and high-pressure phases coexist from 30.6 GPa to 36.5 GPa. In addition to the Raman measurements we also report ab initio total-energy and lattice-dynamics calculations for the two phases. These calculations helped us to determine the crystalline structure of the high-pressure phase and to assign the observed Raman modes in both the wolframite and b-fergusonite phases. Based upon the ab initio calculations we propose the occurrence of a second phase transition at 57.6 GPa from the b-fergusonite phase to an orthorhombic Cmca phase. The pressure evolution of the lattice parameters and the atomic positions of wolframite ZnWO4 are also theoretically calculated and an equation of state reported.
△ Less
Submitted 1 September, 2008;
originally announced September 2008.
-
Pressure effects on the structural and electronic properties of ABX4 scintillating crystals
Authors:
Daniel Errandonea,
Francisco Javier Manjon
Abstract:
Studies at high pressures and temperatures are helpful for understanding the physical properties of the solid state, including such classes of materials as, metals, semiconductors, superconductors, or minerals. In particular, the phase behaviour of ABX4 scintillating materials is a challenging problem with many implications for other fields including technological applications and Earth and plan…
▽ More
Studies at high pressures and temperatures are helpful for understanding the physical properties of the solid state, including such classes of materials as, metals, semiconductors, superconductors, or minerals. In particular, the phase behaviour of ABX4 scintillating materials is a challenging problem with many implications for other fields including technological applications and Earth and planetary sciences. A great progress has been done in the last years in the study of the pressure-effects on the structural and electronic properties of these compounds. In particular, the high-pressure structural sequence followed by these compounds seems now to be better understood thanks to recent experimental and theoretical studies. Here, we will review studies on the phase behaviour of different ABX4 scintillating materials. In particular, we will focus on discussing the results obtained by different groups for the scheelite-structured orthotungstates, which have been extensively studied up to 50 GPa. We will also describe different experimental techniques for obtaining reliable data at simultaneously high pressure and high temperature. Drawbacks and advantages of the different techniques are discussed along with recent developments involving synchrotron x-ray diffraction, Raman scattering, and ab initio calculations. Differences and similarities of the phase behaviour of these materials will be discussed, on the light of the Fukunaga and Yamaoka and the Bastide diagrams, aiming to improve the actual understanding of their high-pressure behaviour. Possible technological and geophysical implications of the reviewed results will be also commented.
△ Less
Submitted 1 February, 2008;
originally announced February 2008.
-
High-pressure effects on the optical-absorption edge of CdIn2S4, MgIn2S4, and MnIn2S4 thiospinels
Authors:
J. Ruiz-Fuertes,
D. Errandonea,
F. J. Manjon,
D. Martinez-Garcia,
A. Segura,
V. V. Ursaki,
I. M. Tiginyanu
Abstract:
The effect of pressure on the optical-absorption edge of CdIn2S4, MgIn2S4, and MnIn2S4 thiospinels at room temperature is investigated up to 20 GPa. The pressure dependence of their band-gaps has been analyzed using the Urbach rule. We have found that, within the pressure-range of stability of the low-pressure spinel phase, the band-gap of CdIn2S4 and MgIn2S4 exhibits a linear blue-shift with pr…
▽ More
The effect of pressure on the optical-absorption edge of CdIn2S4, MgIn2S4, and MnIn2S4 thiospinels at room temperature is investigated up to 20 GPa. The pressure dependence of their band-gaps has been analyzed using the Urbach rule. We have found that, within the pressure-range of stability of the low-pressure spinel phase, the band-gap of CdIn2S4 and MgIn2S4 exhibits a linear blue-shift with pressure, whereas the band-gap of MnIn2S4 exhibits a pronounced non-linear shift. In addition, an abrupt decrease of the band-gap energies occurs in the three compounds at pressures of 10 GPa, 8.5 GPa, and 7.2 GPa, respectively. Beyond these pressures, the optical-absorption edge red-shifts upon compression for the three studied thiospinels. All these results are discussed in terms of the electronic structure of each compound and their reported structural changes.
△ Less
Submitted 23 November, 2007;
originally announced November 2007.
-
Lattice dynamics study in PbWO4 under high pressure
Authors:
F. J. Manjon,
D. Errandonea,
N. Garro,
J. Pellicer-Porres,
J. Lopez-Solano,
P. Rodriguez-Hernandez,
S. Radescu,
A. Mujica,
A. Munoz
Abstract:
Room-temperature Raman scattering has been measured in lead tungstate up to 17 GPa. We report the pressure dependence of all the Raman modes of the tetragonal scheelite phase (PbWO4-I, space group I41/a), which is stable at ambient conditions. Upon compression the Raman spectrum undergoes significant changes around 6.2 GPa due to the onset of a partial structural phase transition to the monoclin…
▽ More
Room-temperature Raman scattering has been measured in lead tungstate up to 17 GPa. We report the pressure dependence of all the Raman modes of the tetragonal scheelite phase (PbWO4-I, space group I41/a), which is stable at ambient conditions. Upon compression the Raman spectrum undergoes significant changes around 6.2 GPa due to the onset of a partial structural phase transition to the monoclinic PbWO4-III phase (space group P21/n). Further changes in the spectrum occur at 7.9 GPa, related to a scheelite-to-fergusonite transition. This transition is observed due to the sluggishness and kinetic hindrance of the I-to-III transition. Consequently, we found the coexistence of the scheelite, PbWO4-III, and fergusonite phases from 7.9 to 9 GPa, and of the last two phases up to 14.6 GPa. Further to the experiments, we have performed ab initio lattice dynamics calculations which have greatly helped us in assigning the Raman modes of the three phases and discussing their pressure dependence.
△ Less
Submitted 21 June, 2006;
originally announced June 2006.
-
High-pressure lattice dynamics in bulk single-crystal BaWO4
Authors:
F. J. Manjon,
D. Errandonea,
N. Garro,
J. Pellicer-Porres,
P. Rodriguez-Hernandez,
S. Radescu,
J. Lopez-Solano,
A. Mujica,
A. Munoz
Abstract:
Room-temperature Raman scattering has been measured in barium tungstate (BaWO4) up to 16 GPa. We report the pressure dependence of all the Raman-active first-order phonons of the tetragonal scheelite phase (BaWO4-I, space group I41/a), which is stable at normal conditions. As pressure increases the Raman spectrum undergoes significant changes around 6.9 GPa due to the onset of the structural pha…
▽ More
Room-temperature Raman scattering has been measured in barium tungstate (BaWO4) up to 16 GPa. We report the pressure dependence of all the Raman-active first-order phonons of the tetragonal scheelite phase (BaWO4-I, space group I41/a), which is stable at normal conditions. As pressure increases the Raman spectrum undergoes significant changes around 6.9 GPa due to the onset of the structural phase transition to the monoclinic BaWO4-II phase (space group P21/n). This transition is only completed above 9.5 GPa. A further change in the spectrum is observed at 7.5 GPa related to a scheelite-to-fergusonite transition. The scheelite, BaWO4-II, and fergusonite phases coexist up to 9.0 GPa due to the sluggishness of the I?II phase transition. Further to the experimental study, we have performed ab initio lattice dynamics calculations that have greatly helped us in assigning and discussing the pressure behaviour of the observed Raman modes of the three phases.
△ Less
Submitted 26 May, 2006;
originally announced May 2006.
-
Determination of the high-pressure crystal structure of BaWO4 and PbWO4
Authors:
D. Errandonea,
J. Pellicer-Porres,
F. J. Manjon,
2 A. Segura,
Ch. Ferrer-Roca,
R. S. Kumar,
O. Tschauner,
J. Lopez-Solano,
P. Rodriguez-Hernandez,
S. Radescu,
A. Mujica,
A. Munoz,
G. Aquilanti
Abstract:
We report the results of both angle-dispersive x-ray diffraction and x-ray absorption near-edge structure studies in BaWO4 and PbWO4 at pressures of up to 56 GPa and 24 GPa, respectively. BaWO4 is found to undergo a pressure-driven phase transition at 7.1 GPa from the tetragonal scheelite structure (which is stable under normal conditions) to the monoclinic fergusonite structure whereas the same…
▽ More
We report the results of both angle-dispersive x-ray diffraction and x-ray absorption near-edge structure studies in BaWO4 and PbWO4 at pressures of up to 56 GPa and 24 GPa, respectively. BaWO4 is found to undergo a pressure-driven phase transition at 7.1 GPa from the tetragonal scheelite structure (which is stable under normal conditions) to the monoclinic fergusonite structure whereas the same transition takes place in PbWO4 at 9 GPa. We observe a second transition to another monoclinic structure which we identify as that of the isostructural phases BaWO4-II and PbWO4-III (space group P21/n). We have also performed ab initio total energy calculations which support the stability of this structure at high pressures in both compounds. The theoretical calculations further find that upon increase of pressure the scheelite phases become locally unstable and transform displacively into the fergusonite structure. The fergusonite structure is however metastable and can only occur if the transition to the P21/n phases were kinetically inhibited. Our experiments in BaWO4 indicate that it becomes amorphous beyond 47 GPa.
△ Less
Submitted 2 June, 2006; v1 submitted 27 February, 2006;
originally announced February 2006.
-
High-pressure structural study of the scheelite tungstates CaWO4 and SrWO4
Authors:
D. Errandonea,
J. Pellicer-Porres,
F. J. Manjon,
A. Segura,
Ch. Ferrer,
R. S. Kumar,
O. Tschauner,
P. Rodriguez-Hernandez,
J. Lopez-Solano,
S. Radescu,
A. Mujica,
A. Munoz,
G. Aquilanti
Abstract:
Angle-dispersive x-ray diffraction (ADXRD) and x-ray absorption near edge structure (XANES) measurements have been performed in the AWO4 tungstates CaWO4 and SrWO4 under high pressure up to approximately 20 GPa. Similar phase transitions and phase transition pressures have been observed for both tungstates using the two techniques in the studied pressure range. Both materials are found to underg…
▽ More
Angle-dispersive x-ray diffraction (ADXRD) and x-ray absorption near edge structure (XANES) measurements have been performed in the AWO4 tungstates CaWO4 and SrWO4 under high pressure up to approximately 20 GPa. Similar phase transitions and phase transition pressures have been observed for both tungstates using the two techniques in the studied pressure range. Both materials are found to undergo a pressure-induced scheelite-to-fergusonite phase transition under sufficiently hydrostatic conditions. Our results are compared to those found previously in the literature and supported by ab initio total energy calculations. From the total energy calculations we have also predicted a second phase transition from the fergusonite structure to a new structure identified as Cmca. Finally, a linear relationship between the charge density in the AO8 polyhedra of ABO4 scheelite-related structures and the bulk modulus is discussed and used to predict the bulk modulus of other materials, like zircon.
△ Less
Submitted 17 November, 2005; v1 submitted 6 April, 2005;
originally announced April 2005.
-
Effect of isotopic mass on the photoluminescence spectra of beta zinc sulfide
Authors:
F. J. Manjon,
M. Mollar,
B. Mari,
N. Garro,
A. Cantarero,
R. Lauck,
M. Cardona
Abstract:
Zinc sulfide is a wide bandgap semiconductor which crystallizes in either the wurtzite modification (a-ZnS), the zincblende modification (b-ZnS) or as one of several similar tetrahedrally coordinated polytypes. In this work, we report a photoluminescence study of different samples of isotopically pure b-ZnS crystals, and crystals with the natural isotopic abundances, at 15 and 77 K. The derivati…
▽ More
Zinc sulfide is a wide bandgap semiconductor which crystallizes in either the wurtzite modification (a-ZnS), the zincblende modification (b-ZnS) or as one of several similar tetrahedrally coordinated polytypes. In this work, we report a photoluminescence study of different samples of isotopically pure b-ZnS crystals, and crystals with the natural isotopic abundances, at 15 and 77 K. The derivatives of the free and bound exciton energies on isotopic mass have been obtained. They allow us to estimate the contribution of the zinc and sulfur vibrations to the bandgap renormalization energy by electron-phonon interaction. A two-oscillator model based on the zinc and sulfur renormalization energies has been used to account for the temperature dependence of the bandgap energy in ZnS. The results are compared with those found for other tetrahedrally coordinated semiconductors.
△ Less
Submitted 11 October, 2004;
originally announced October 2004.
-
Effects of pressure on the local atomic structure of CaWO4 and YLiF4: Mechanism of the scheelite-to-wolframite and scheelite-to-fergusonite transitions
Authors:
D. Errandonea,
F. J. Manjon,
M. Somayazulu,
D. Hausermann
Abstract:
The pressure response of the scheelite phase of CaWO4 (YLiF4) and the occurrence of the pressure induced scheelite-to-wolframite (M-fergusonite) transition are reviewed and discussed. It is shown that the change of the axial parameters under compression is related with the different pressure dependence of the W-O (Li-F) and Ca-O (Y-F) interatomic bonds. Phase transition mechanisms for both compo…
▽ More
The pressure response of the scheelite phase of CaWO4 (YLiF4) and the occurrence of the pressure induced scheelite-to-wolframite (M-fergusonite) transition are reviewed and discussed. It is shown that the change of the axial parameters under compression is related with the different pressure dependence of the W-O (Li-F) and Ca-O (Y-F) interatomic bonds. Phase transition mechanisms for both compounds are proposed. Furthermore, a systematic study of the phase transition in 16 different scheelite ABX4 compounds indicates that the transition pressure increases as the packing ratio of the anionic BX4 units around the A cations increases.
△ Less
Submitted 8 March, 2004; v1 submitted 9 June, 2003;
originally announced June 2003.
-
Modellization of RGB lasers based on QPM structures with independent control of laser intensities by electrooptic effect
Authors:
R. Vilaplana,
F. J. Manjon
Abstract:
Recently simultaneous generation of continuous-wave visible laser light in the three fundamental colors has been experimentally demonstrated in Nd3+-doped LiNbO3 and Sr0.6Ba0.4(NbO3)2 by quasi-phase matching intracavity self-frequency conversion. In this work, we report the modelization of RGB lasers operating under similar experimental conditions but designed in the simplest quasi-periodically…
▽ More
Recently simultaneous generation of continuous-wave visible laser light in the three fundamental colors has been experimentally demonstrated in Nd3+-doped LiNbO3 and Sr0.6Ba0.4(NbO3)2 by quasi-phase matching intracavity self-frequency conversion. In this work, we report the modelization of RGB lasers operating under similar experimental conditions but designed in the simplest quasi-periodically poled ferroelectric form by using the Fourier Transform technique. The aim of this work is to analyse the possibility of controlling the three laser intensities in an independent and novel way by means of the linear electrooptic (Pockels) effect in these non-linear materials. Our results suggest that the application of electrooptic effect for this purpose, according to our proposed scheme, is better adapted to Sr0.6Ba0.4(NbO3)2 than to Nd3+-doped LiNbO3.
△ Less
Submitted 30 May, 2003;
originally announced May 2003.