Chemical heterogeneity enhances hydrogen resistance in high-strength steels
Authors:
Binhan Sun,
Wenjun Lu,
Ran Ding,
Surendra Kumar Makineni,
Baptiste Gault,
Chun-Hung Wu,
Di Wan,
Hao Chen,
Dirk Ponge,
Dierk Raabe
Abstract:
When H, the lightest, smallest and most abundant atom in the universe, makes its way into a high-strength alloy (>650 MPa), the material's load-bearing capacity is abruptly lost. This phenomenon, known as H embrittlement, was responsible for the catastrophic and unpredictable failure of large engineering structures in service. The inherent antagonism between high strength requirements and H embrit…
▽ More
When H, the lightest, smallest and most abundant atom in the universe, makes its way into a high-strength alloy (>650 MPa), the material's load-bearing capacity is abruptly lost. This phenomenon, known as H embrittlement, was responsible for the catastrophic and unpredictable failure of large engineering structures in service. The inherent antagonism between high strength requirements and H embrittlement susceptibility strongly hinders the design of lightweight yet reliable structural components needed for carbon-free hydrogen-propelled industries and reduced-emission transportation solutions. Inexpensive and scalable alloying and microstructural solutions that enable both, an intrinsically high resilience to H and high mechanical performance, must be found. Here we introduce a counterintuitive strategy to exploit typically undesired chemical heterogeneity within the material's microstructure that allows the local enhancement of crack resistance and local H trap**, thereby enhancing the resistance against H embrittlement. We deploy this approach to a lightweight, high-strength steel and produce a high-number density Mn-rich zones dispersed within the microstructure. These solute-rich buffer regions allow for local micro-tuning of the phase stability, arresting H-induced microcracks thus interrupting the H-assisted damage evolution chain, regardless of how and when H is introduced and also regardless of the underlying embrittling mechanisms. A superior H embrittlement resistance, increased by a factor of two compared to a reference material with a homogeneous solute distribution within each microstructure constituent, is achieved at no expense of the material's strength and ductility.
△ Less
Submitted 30 August, 2023;
originally announced August 2023.
-
Microstructural engineering of medium entropy NiCo(CrAl) alloy for enhanced room and high-temperature mechanical properties
Authors:
Nithin Baler,
Abdulla Samin M V,
Akshat Godha,
Surendra Kumar Makineni
Abstract:
This work demonstrates the development of a strong and ductile medium entropy alloy by employing conventional alloying and thermomechanical processing to induce partial recrystallization (PR) and precipitation strengthening in the microstructure. The combined usage of electron microscopy and atom probe tomography reveals the sequence of microstructural evolution during the process. First, the cold…
▽ More
This work demonstrates the development of a strong and ductile medium entropy alloy by employing conventional alloying and thermomechanical processing to induce partial recrystallization (PR) and precipitation strengthening in the microstructure. The combined usage of electron microscopy and atom probe tomography reveals the sequence of microstructural evolution during the process. First, the cold working of homogenized alloy resulted in a highly deformed microstructure. On annealing at 700°C, B2 ordered precipitates heterogeneously nucleate on the highly misoriented sites. These B2 promotes particle stimulated nucleation (PSN) of new recrystallized strain-free grains. The migration of recrystallized grain boundaries leads to discontinuous precipitation of L12 ordered regions in highly dense lamellae structures. Atomic-scale compositional analysis reveals a significant amount of Ni confined to the GB regions between B2 and L12 precipitates, indicating Ni as a rate-controlling element for coarsening the microstructure. On 20 hours of annealing, the alloy comprises a composite microstructure of soft recrystallized and hard non-recrystallized zones, B2 particles at the grain boundaries (GBs), and coherent L12 precipitates inside the grains. The B2 pins the GB movement during recrystallization while the latter provides high strength. The microstructure results in a 0.2% yield stress (YS) value of 1030 MPa with 32% elongation at ambient temperature and retains up to 910 MPa at 670°C. Also, it shows exceptional microstructural stability at 700 °C and resistance to deformation at high temperatures up to 770°C. Examination of deformed microstructure reveals excessive twinning, formation of stacking faults, shearing of L12 precipitates, and accumulation of dislocations at around the B2 precipitates and GBs attributed to high strain hardening of the alloy.
△ Less
Submitted 28 September, 2021; v1 submitted 18 September, 2021;
originally announced September 2021.
-
Understanding creep of a single-crystalline Co-Al-W-Ta superalloy by studying the deformation mechanism, segregation tendency and stacking fault energy
Authors:
Nicklas Volz,
Fei Xue,
Christopher H. Zenk,
Andreas Bezold,
Stefan Gabel,
Aparna P. A. Subramanyam,
Ralf Drautz,
Thomas Hammerschmidt,
Surendra K. Makineni,
Baptiste Gault,
Mathias Göken,
Steffen Neumeier
Abstract:
A systematic study of the compression creep properties of a single-crystalline Co-base superalloy (Co-9Al-7.5W-2Ta) was conducted at 950 °C, 975 °C and 1000 °C to reveal the influence of temperature and the resulting diffusion velocity of solutes like Al, W and Ta on the deformation mechanisms. Two creep rate minima are observed at all temperatures indicating that the deformation mechanisms causin…
▽ More
A systematic study of the compression creep properties of a single-crystalline Co-base superalloy (Co-9Al-7.5W-2Ta) was conducted at 950 °C, 975 °C and 1000 °C to reveal the influence of temperature and the resulting diffusion velocity of solutes like Al, W and Ta on the deformation mechanisms. Two creep rate minima are observed at all temperatures indicating that the deformation mechanisms causing these minima are quite similar. Atom-probe tomography analysis reveals elemental segregation to stacking faults, which had formed in the $γ\prime$ phase during creep. Density-functional-theory calculations indicate segregation of W and Ta to the stacking fault and an associated considerable reduction of the stacking fault energy. Since solutes diffuse faster at a higher temperature, segregation can take place more quickly. This results in a significantly faster softening of the alloy, since cutting of the $γ\prime$ precipitate phase by partial dislocations is facilitated through segregation already during the early stages of creep. This is confirmed by transmission electron microscopy analysis. Therefore, not only the smaller precipitate fraction at higher temperatures is responsible for the worse creep properties, but also faster diffusion-assisted shearing of the $γ\prime$ phase by partial dislocations. The understanding of these mechanisms will help in future alloy development by offering new design criteria.
△ Less
Submitted 1 June, 2021; v1 submitted 31 May, 2021;
originally announced May 2021.
-
On the effect of Re addition on microstructural evolution of a CoNi-based superalloy
Authors:
P. Pandey,
A. K. Sawant,
B. Nithin,
Z. Peng,
S. K. Makineni,
B. Gault,
K. Chattopadhyay
Abstract:
In this study, the effect of rhenium (Re) addition on microstructural evolution of a new low-density Co-Ni-Al-Mo-Nb based superalloy is presented. Addition of Re significantly influences the γ' precipitate morphology, the γ/γ' lattice misfit and the γ/γ' microstructural stability during long term aging. An addition of 2 at.% Re to a Co-30Ni-10Al-5Mo-2Nb (all in at.%) alloy, aged at 900°C for 50 ho…
▽ More
In this study, the effect of rhenium (Re) addition on microstructural evolution of a new low-density Co-Ni-Al-Mo-Nb based superalloy is presented. Addition of Re significantly influences the γ' precipitate morphology, the γ/γ' lattice misfit and the γ/γ' microstructural stability during long term aging. An addition of 2 at.% Re to a Co-30Ni-10Al-5Mo-2Nb (all in at.%) alloy, aged at 900°C for 50 hours, reduces the γ/γ' lattice misfit by {\approx} 40% (from +0.32% to +0.19%, measured at room temperature) and hence alters the γ' morphology from cuboidal to round-cornered cuboidal precipitates. The composition profiles across the γ/γ' interface by atom probe tomography (APT) reveals Re partitions to the γ phase (K_Re=0.34) and also results in the partitioning reversal of Mo to the γ phase (K_Mo=0.90) from the γ' precipitate. An inhomogeneous distribution of Gibbsian interfacial excess for the solute Re (Γ_Re, ranging from 0.8 to 9.6 atom.nm-2) has been observed at the γ/γ' interface. A coarsening study at 900°C (up to 1000 hours) suggests that the coarsening of γ' precipitates occurs solely by an evaporation--condensation (EC) mechanism. This is contrary to that observed in the Co-30Ni-10Al-5Mo-2Nb alloy as well as in some of the Ni-Al based and high mass density Co-Al-W based superalloys, where γ' precipitates coarsen by coagulation/coalescence mechanism with extensive alignment of γ' along <100> directions as a sign of microstructural instability. The γ' coarsening rate exponent (K_r) and γ/γ' interfacial energy are estimated to be 1.41 x 10-27 m3/s and 8.4 mJ/m2, which are comparable and lower than Co-Al-W based superalloys.
△ Less
Submitted 3 February, 2019;
originally announced February 2019.
-
On the segregation of Re at dislocations in the γ' phase of Ni-based single crystal superalloys
Authors:
Xiaoxiang Wu,
Surendra Kumar Makineni,
Paraskevas Kontis,
Gerhard Dehm,
Dierk Raabe,
Baptiste Gault,
Gunther Eggeler
Abstract:
We report evidence of Re and Mo segregation (up to 2.6 at.% and 1 at.%) along with Cr and Co to the dislocations inside of γ' precipitates in a second generation Ni-based single crystal superalloy, after creep deformation at 750°C under an applied stress of 800 MPa. The observed segregation effects can be rationalized through bridging the solute partitioning behavior across the γ/γ' interface and…
▽ More
We report evidence of Re and Mo segregation (up to 2.6 at.% and 1 at.%) along with Cr and Co to the dislocations inside of γ' precipitates in a second generation Ni-based single crystal superalloy, after creep deformation at 750°C under an applied stress of 800 MPa. The observed segregation effects can be rationalized through bridging the solute partitioning behavior across the γ/γ' interface and the pipe diffusion mechanism along the core of the dislocation line. This understanding can provide new insights enabling improved alloy design.
△ Less
Submitted 24 September, 2018;
originally announced September 2018.