Swift-heavy-ion-irradiation-induced enhancement in electrical conductivity of chemical solution deposited La0.7Ba0.3MnO3 thin films
Authors:
R. N. Parmar,
J. H. Markna,
D. G. Kuberkar,
Ravi Kumar,
D. S. Rana,
Vivas C. Bagve,
S. K. Malik
Abstract:
Epitaxial thin films of La0.7Ba0.3MnO3 manganite, deposited using Chemical Solution Deposition technique, were irradiated by 200 MeV Ag+15 ions with a maximum ion dose up to 1x10^12 ions/cm2. Temperature- and magnetic field-dependent resistivity measurements on all the films (before and after irradiation) reveal a sustained decrease in resistivity with increasing ion dose. A maximum dose of 1x10…
▽ More
Epitaxial thin films of La0.7Ba0.3MnO3 manganite, deposited using Chemical Solution Deposition technique, were irradiated by 200 MeV Ag+15 ions with a maximum ion dose up to 1x10^12 ions/cm2. Temperature- and magnetic field-dependent resistivity measurements on all the films (before and after irradiation) reveal a sustained decrease in resistivity with increasing ion dose. A maximum dose of 1x10^12 ions/cm2 suppresses resistivity by factors of 3 and 10, at 330 K [insulator-metal (I-M) transition] and at 10 K, respectively. On the other hand, with increasing ion dose, the magnetoresistance (MR) enhances in the vicinity of I-M transition but decreases at low temperatures. These results, corroborated by surface morphology of films, suggest that the origin of such properties lies in the irradiation induced improved crystallinity and epitaxial orientation, enhanced connectivity between grains, and conglomeration of grains which result in better conductivity at grain boundaries.
△ Less
Submitted 24 September, 2006;
originally announced September 2006.
-
200 MeV Ag+15 ion irradiation created columnar defects and enhanced critical current density of La-2125 type superconducting thin films
Authors:
K. R. Mavani,
D. S. Rana,
S. Rayaprol,
R. N. Parmar,
D. G. Kuberkar,
Ravi Kumar,
M. Tonouchi,
J. John,
R. Nagarajan
Abstract:
We have deposited c-axis oriented thin films of La1.5Dy0.5CaBa2Cu5Oz (La-2125) tetragonal superconductor on LaAlO3 (001) by Pulsed Laser Deposition. These films were irradiated with 200 MeV Ag+15 ions. Atomic Force Microscopy and Elastic Recoil Detection Analysis indicate that the irradiation has created columnar defects along the entire thickness (2000 A) of these films. With ion irradiation up…
▽ More
We have deposited c-axis oriented thin films of La1.5Dy0.5CaBa2Cu5Oz (La-2125) tetragonal superconductor on LaAlO3 (001) by Pulsed Laser Deposition. These films were irradiated with 200 MeV Ag+15 ions. Atomic Force Microscopy and Elastic Recoil Detection Analysis indicate that the irradiation has created columnar defects along the entire thickness (2000 A) of these films. With ion irradiation up to 1*10^11 ions/cm2, the critical current density (Jc(H)) is found to enhance by almost five folds, which is attributed to the augmented flux pinning by the columnar defects. A further increase in irradiation to 1*10^12 ions/cm2 causes reduction in Jc(H) due to distorted morphology of the film. Our work shows that the enhancement in Jc (H) of the irradiated La-2125 film is comparable to that in irradiated RE-123. Also, as the La-2125 type films have greater chemical stability than RE-123 (RE = rare earth ion), La-2125 type superconductors are potential candidates for applications. Interesting to note that there are partial flux jumps observed to occur symmetrically in the magnetic hysteresis of irradiated La-2125 thin films with enhanced Jc(H).
△ Less
Submitted 9 August, 2006;
originally announced August 2006.
-
On the role of Calcium in inducing superconductivity - the study of La-2125 superconductors
Authors:
S. Rayaprol,
D. G. Kuberkar
Abstract:
Ever since high Tc superconductivity was discovered in La-based mixed oxide system by Bednorz and Muller, enormous efforts have been put in by several researchers around the world in understanding the origin and mechanism of superconductivity in these, as well as in systems derived from them. It is a proven fact that the superconductivity in RE-123 superconductors is governed by the oxygen conte…
▽ More
Ever since high Tc superconductivity was discovered in La-based mixed oxide system by Bednorz and Muller, enormous efforts have been put in by several researchers around the world in understanding the origin and mechanism of superconductivity in these, as well as in systems derived from them. It is a proven fact that the superconductivity in RE-123 superconductors is governed by the oxygen content, which in turn is responsible for the carrier concentration in the system. Due to their dependence on oxygen content, RE-123 superconductors undergo structural transformation from orthorhombic to tetragonal as a function of oxygen content making them very difficult compounds to work with, in terms of technological applications, such as device fabrication. Hence, it would be interesting to obtain a stable compound whose superconducting properties, are not only insensitive directly to oxygen content but, having dependence of its carrier concentration and Tc on the nature and amount of the substituted cation. In the present work, we focus our investigations for such a compound, which has been derived from a tetragonal RE-123 superconducting system.
In this chapter, we present a brief review of the studies carried out on La-2125 compounds to elucidate the role of dopants in modifying the superconducting properties and establish a structure-property correlation in them.
△ Less
Submitted 20 October, 2005; v1 submitted 14 July, 2005;
originally announced July 2005.
-
Large magnetoresistance in low temperature metallic region of manganite compounds (La0.7-2xEux)(Ca0.3Srx)MnO3 (0.05<x<0.15)
Authors:
D. S. Rana,
C. M. Thaker,
K. R. Mavani,
D. G. Kuberkar,
S. K. Malik
Abstract:
Magnetoresistance (MR) and magnetization (d.c and a.c) measurements have been carried out on the manganites, (La0.7-2xEux)(Ca0.3Srx)MnO3 (0.05<x<0.15), in the temperature range of 5K-320K. At 5K, an unusually large MR of almost 98% is observed in the x=0.15 sample, nearly up to fields of 4-5 Tesla. This large high-field MR occurs in the metallic region, far below the insulator-metal transition t…
▽ More
Magnetoresistance (MR) and magnetization (d.c and a.c) measurements have been carried out on the manganites, (La0.7-2xEux)(Ca0.3Srx)MnO3 (0.05<x<0.15), in the temperature range of 5K-320K. At 5K, an unusually large MR of almost 98% is observed in the x=0.15 sample, nearly up to fields of 4-5 Tesla. This large high-field MR occurs in the metallic region, far below the insulator-metal transition temperature, and does not vary linearly with applied field. The unusual magnetoresistance is explained the light of various possibilities of phase segregation and cluster spin-glass behavior. Keywords: Manganites, High field MR, Phase segregation.
△ Less
Submitted 16 December, 2004;
originally announced December 2004.
-
Structural and Magnetic Studies on La2-xDyxCa2xBa2Cu4+2xOz Type Superconducting Oxides
Authors:
S. Rayaprol,
Darshan C. Kundaliya,
C. M. Thaker,
D. G. Kuberkar,
Keka R. Chakraborty,
P. S. R. Krishna,
M. Ramanadham
Abstract:
The La-2125 type La2-xDyxCa2xBa2Cu4+2xOz (0.1 < x < 0.5; LDBO) compounds have been synthesized and studied for their structural and superconducting properties by room temperature neutron diffraction, high field dc magnetization, four-probe resistivity and iodometric double titration. The Rietveld analysis of the neutron diffraction data reveals tetragonal structure for all the samples, which cry…
▽ More
The La-2125 type La2-xDyxCa2xBa2Cu4+2xOz (0.1 < x < 0.5; LDBO) compounds have been synthesized and studied for their structural and superconducting properties by room temperature neutron diffraction, high field dc magnetization, four-probe resistivity and iodometric double titration. The Rietveld analysis of the neutron diffraction data reveals tetragonal structure for all the samples, which crystallizes into La-123 type tetragonal structure in P4/mmm space group. Iodometric double titrations were performed to determine the oxygen content values and calculate mobile charge carrier (holes) density. The superconducting transition temperatures (Tc) increases from ~ 20 K for x = 0.1 to a maximum of 75 K for x = 0.5. Flux pinning force (Fp) and critical current density (Jc), calculated from the low temperature hysteresis loops, also increases with increasing dopant concentration. The paper presents the studies on structure and superconducting properties of all LDBO compounds in light of the role of calcium in inducing superconductivity in the tetragonal non-superconducting oxide.
△ Less
Submitted 14 August, 2004;
originally announced August 2004.
-
Neutron Diffraction Studies on La2-xDyxCa2xBa2Cu4+2xOz Superconductors
Authors:
S. Rayaprol,
Rohini Parmar,
D. G. Kuberkar,
Keka R. Chakraborty,
P. S. R. Krishna,
M. Ramanadham
Abstract:
Structural studies on Dy-substituted La-2125 type superconductors have been carried out by neutron diffraction experiments at room temperature using a monochromatic neutron beam of wavelength lambda = 1.249 Angstroms. A series of samples with La2-xDyxCa2xBa2Cu4+2xOz stoichiometric composition, for x = 0.1 - 0.5, have been studied for their structural properties. A tetragonal Y-123 unit cell was…
▽ More
Structural studies on Dy-substituted La-2125 type superconductors have been carried out by neutron diffraction experiments at room temperature using a monochromatic neutron beam of wavelength lambda = 1.249 Angstroms. A series of samples with La2-xDyxCa2xBa2Cu4+2xOz stoichiometric composition, for x = 0.1 - 0.5, have been studied for their structural properties. A tetragonal Y-123 unit cell was taken as the starting model for the Rietveld analysis. All the samples fit into the starting model, exhibiting no structural transition taking place with increasing dopant concentration. The results of Rietveld analysis and structural properties are discussed in detail.
△ Less
Submitted 14 August, 2004;
originally announced August 2004.
-
Critical current density and flux pinning in La2-xPrxCa2xBa2Cu4+2xOz (x = 0.1 - 0.5) superconductors
Authors:
S. Rayaprol,
C. M. Thaker,
N. A. Shah,
D. G. Kuberkar
Abstract:
Polycrystalline La2-xPrxCa2xBa2Cu4+2xOz (LPCaBCO) compounds with x = 0.1 - 0.5 were synthesized by solid-state reaction method and studied by room temperature X-ray diffraction, dc resistivity, dc magnetization and iodometry. The superconducting transition temperatures in these tetragonal triple perovskite compounds increases from 32 to 62 K (Tconset values) with increasing dopant concentration.…
▽ More
Polycrystalline La2-xPrxCa2xBa2Cu4+2xOz (LPCaBCO) compounds with x = 0.1 - 0.5 were synthesized by solid-state reaction method and studied by room temperature X-ray diffraction, dc resistivity, dc magnetization and iodometry. The superconducting transition temperatures in these tetragonal triple perovskite compounds increases from 32 to 62 K (Tconset values) with increasing dopant concentration. The mixing of rare earth La3+ and Pr3+/4+ ions at rare earth site (La3+) along with substitution of divalent Ca2+ results in the shrinkage of unit cell volume. The contraction of unit cell volume due to larger ion being substituted by smaller ions, gives rise to creation of pinning centers in the unit cell leading to increase in critical current density and flux pinning
△ Less
Submitted 21 May, 2004;
originally announced May 2004.
-
Effect of Co-Ga paired substitution on superconductivity in YBa2Cu3O7-d
Authors:
Anjana Dogra,
S. Rayaprol,
N. A. Shah,
D. G. Kuberkar
Abstract:
The effect of Co-Ga paired substitution on the superconducting properties of YBa2Cu3O7-d (Y-123) has been investigated by X-ray diffraction, ac susceptibility,dc resistivity and oxygen content measurements. We report in this paper the results of our studies on the paired substitution of a magnetic and non-magnetic ion at Cu site in Y-123, while kee** the total dopant concentration fixed. The s…
▽ More
The effect of Co-Ga paired substitution on the superconducting properties of YBa2Cu3O7-d (Y-123) has been investigated by X-ray diffraction, ac susceptibility,dc resistivity and oxygen content measurements. We report in this paper the results of our studies on the paired substitution of a magnetic and non-magnetic ion at Cu site in Y-123, while kee** the total dopant concentration fixed. The simultaneous substitution of Co and Ga at Cu site shows variation in the transition temperature (Tc), oxygen content and hole concentration as a function of change in the balance of magnetic (Co) and non-magnetic (Ga) concentration. Orthorhombicity (D), given as (b-a)/a, also varies as a function of increasing dopant concentration. The variation in Tc due to Co-Ga substitution is discussed in the light of dopant valency and hole filling mechanism.
△ Less
Submitted 23 April, 2004;
originally announced April 2004.
-
Studies on La2-xPrxCayBa2Cu4+yOz (0.1 < x < 0.5) type mixed oxide superconductors
Authors:
S Rayaprol,
K R Mavani,
D S Rana,
C M Thaker,
Manglesh Dixit,
Shovit Bhattacharya,
D G Kuberkar
Abstract:
The La2-xPrxCayBa2Cu4+yOz (LaPrCaBCO) mixed oxides have been studied for their structural and superconducting properties using X-ray diffraction (XRD), d. c. resistivity, d. c. susceptibility and iodometric double titration. All the LaPrCaBCO samples for x = 0.1 - 0.5, exhibit tetragonal crystalline structure with P 4/mmm space group as determined by Rietveld analysis of the X-ray diffraction da…
▽ More
The La2-xPrxCayBa2Cu4+yOz (LaPrCaBCO) mixed oxides have been studied for their structural and superconducting properties using X-ray diffraction (XRD), d. c. resistivity, d. c. susceptibility and iodometric double titration. All the LaPrCaBCO samples for x = 0.1 - 0.5, exhibit tetragonal crystalline structure with P 4/mmm space group as determined by Rietveld analysis of the X-ray diffraction data. With increasing x, enhancement in Tc is observed, which is quite interesting for Pr substituted high Tc oxides. Maximum Tc ~ 58 K has been observed for x = 0.5(La-2125 stoichiometry). The results of structural studies and superconducting property measurements are presented in light of increase in Tc in LaPrCaBCO system with increasing Pr concentration.
△ Less
Submitted 24 May, 2003;
originally announced May 2003.
-
Effect of Mo-Substitution on Superconductivity, Flux Pinning and Critical Currents of la(1.5)Nd(0.5)Ca(1)Ba(2)Cu(5)O(z0
Authors:
S. Rayaprol,
Krushna Mavani,
C. M. Thaker,
D. S. Rana,
R. G. Kulkarni,
D. G. Kuberkar,
Darshan Kundaliya,
S. K. Malik
Abstract:
Mo-substituted triple perovskite superconducting samples with the stoichiometric composition La(1.5)Nd(0.5)Ca(1)Ba(2)[Cu(1-x)Mo(x)](5)O(z), [LNCBCuMO] with x = 0.00, 0.01, 0.03, 0.05 and 0.10, have been investigated using X-ray diffraction, electrical resistivity, magnetic susceptibility, magnetization and oxygen content measurements. The observed reduction in Tc with increasing Mo content (x) i…
▽ More
Mo-substituted triple perovskite superconducting samples with the stoichiometric composition La(1.5)Nd(0.5)Ca(1)Ba(2)[Cu(1-x)Mo(x)](5)O(z), [LNCBCuMO] with x = 0.00, 0.01, 0.03, 0.05 and 0.10, have been investigated using X-ray diffraction, electrical resistivity, magnetic susceptibility, magnetization and oxygen content measurements. The observed reduction in Tc with increasing Mo content (x) in LNCBCuMO, can be attributed to the decrease in hole concentration. Magnetization measurements as a function of temperature and field (H), exhibit an M-H hysteresis loop, which indicates moderate flux pinning, which can be attributed to the pinning centers created by Mo substitution at Cu sites. The critical current density, Jc, deduced from the M-H data satisfies the flux creep model.
△ Less
Submitted 26 April, 2003;
originally announced April 2003.