Evolution of local atomic structure accompanying devitrification of amorphous Ni-Zr alloy thin films
Authors:
Debarati Bhattacharya,
Nidhi Tiwari,
P. S. R. Krishna,
Dibyendu Bhattacharyya
Abstract:
Thin film metallic glasses undergoing devitrification can form partially crystallized or fully crystallized materials with novel structural and magnetic properties. The development of desired and tunable properties of such systems drives the need to understand the mechanism of their thermal evolution at the atomic level. Co-sputtered amorphous Ni-Zr alloy thin films which were thermally annealed i…
▽ More
Thin film metallic glasses undergoing devitrification can form partially crystallized or fully crystallized materials with novel structural and magnetic properties. The development of desired and tunable properties of such systems drives the need to understand the mechanism of their thermal evolution at the atomic level. Co-sputtered amorphous Ni-Zr alloy thin films which were thermally annealed in steps of 200 deg C from room temperature up to 800 deg C, were observed to undergo an amorphous-to-crystalline transformation. Evolutions in local atomic structure, including oxide formation and depletion during this devitrification process, were determined using a combination of X-ray reflectivity (XRR), grazing incidence X-ray diffraction (GIXRD) and Extended X-ray Absorption Fine Structure (EXAFS) techniques. The most probable phase of the alloy was determined as Ni7Zr2; undergoing a polymorphous transformation. The slight oxide content in the films was also noted to decrease rapidly as annealing proceeded; leaving the crystallization pathway unhindered. Modelling and analyses of XRR and GIXRD data showed that film thickness decreased with annealing while long range order increased. Pair distribution function peak widths were observed to decrease with annealing, indicating a control over structural disorder in the system as it transitioned from the amorphous to crystalline state. Partial atomic distribution in the environment of each constituent was examined at every stage of annealing through EXAFS measurements, which gave proper insight into atomic scale changes to the order present. Detailed analyses through these techniques gave coherent results, thus providing a true picture of the thermal evolution process of devitrification in this technologically useful material.
△ Less
Submitted 19 October, 2022;
originally announced October 2022.
-
Structure-property relations characterizing the devitrification of Ni-Zr glassy alloy thin films
Authors:
Debarati Bhattacharya,
S. Rayaprol,
Kawsar Ali,
T. V. Chandrasekhar Rao,
P. S. R. Krishna,
R. B. Tokas,
S. Singh,
C. L. Prajapat,
A. Arya
Abstract:
The investigation of devitrification in thermally annealed nanodimensional glassy alloy thin films provides a comprehensive understanding of their thermal stability, which can be used to explore potential applications. The amorphous to crystalline polymorphous transformation of cosputtered NiZr alloy (Ni78Zr22 at%) films, with a thickness lower than the reported critical limit of devitrification,…
▽ More
The investigation of devitrification in thermally annealed nanodimensional glassy alloy thin films provides a comprehensive understanding of their thermal stability, which can be used to explore potential applications. The amorphous to crystalline polymorphous transformation of cosputtered NiZr alloy (Ni78Zr22 at%) films, with a thickness lower than the reported critical limit of devitrification, was studied through detailed structural characterization and molecular dynamics (MD) simulations. Devitrification to a nanocrystalline state (Ni7Zr2 structure) was observed at 800 degC, with an increase in density (approx 3.6%) much higher than that achieved in bulk alloys. Variation in the magnetic property of the films and the overall physical structure including morphology and composition were examined before and after annealing. MD simulations were employed to effectively elucidate not only the high densification but also the increased magnetic moment after annealing, which was correlated with the simulated change in the coordination number around Ni atoms. The structural relaxation process accompanying devitrification was described as a disorder-to-order transformation while highlighting the crucial role played by chemical short range order prevalent in glassy materials.
△ Less
Submitted 29 September, 2021;
originally announced September 2021.
-
Neutron-Irradiation Induced Magnetization and Persistent Defects at High Temperatures in Graphite
Authors:
Ranjan Mittal,
Mayanak K. Gupta,
Sanjay K. Mishra,
Sourabh Wajhal,
Peram Delli Babu,
Baltej Singh,
Anil Bhimrao Shinde,
Poluri Siva Rama Krishna,
Rakesh K. Singhal,
Rakesh Ranjan,
Samrath Lal Chaplot
Abstract:
Structural as well as magnetization studies have been carried out on graphite samples irradiated by neutrons over 50 years in the CIRUS research reactor at Trombay. Neutron diffraction studies reveal that the defects in irradiated graphite samples are not well annealed and remain significant up to high temperatures much greater than 653 K where the Wigner energy is completely released. We infer th…
▽ More
Structural as well as magnetization studies have been carried out on graphite samples irradiated by neutrons over 50 years in the CIRUS research reactor at Trombay. Neutron diffraction studies reveal that the defects in irradiated graphite samples are not well annealed and remain significant up to high temperatures much greater than 653 K where the Wigner energy is completely released. We infer that the remnant defects may be intralayer Frenkel defects, which do not store large energy, unlike the interlayer Frenkel defects that store the Wigner energy. Magnetization studies on the irradiated graphite show ferromagnetic behavior even at 300 K and a large additional paramagnetic contribution at 5 K. Ab-initio calculations based on the spin-polarized density-functional theory show that the magnetism in defected graphite is essentially confined on to a single 2-coordinated carbon atom that is located around a vacancy in the hexagonal layer.
△ Less
Submitted 10 August, 2020;
originally announced August 2020.
-
Defect topology and annihilation by cooperative cascading movement of atoms in highly neutron irradiated graphite
Authors:
Ranjan Mittal,
Mayanak K. Gupta,
Sanjay K. Mishra,
Sourabh Wajhal,
Himanshu K. Poswal,
Baltej Singh,
Anil Bhimrao Shinde,
Poluri Siva Rama Krishna,
Peram Delli Babu,
Ratikant Mishra,
Pulya Umamaheswara Sastry,
Rakesh Ranjan,
Samrath Lal Chaplot
Abstract:
Graphite has been used as neutron moderator or reflector in many nuclear reactors. The irradiation of graphite in a nuclear reactor results in a complex population of defects. Heating of the irradiated graphite at high temperatures results in annihilation of the defects with release of an unusually large energy, called the Wigner energy. From various experiments on highly irradiated graphite sampl…
▽ More
Graphite has been used as neutron moderator or reflector in many nuclear reactors. The irradiation of graphite in a nuclear reactor results in a complex population of defects. Heating of the irradiated graphite at high temperatures results in annihilation of the defects with release of an unusually large energy, called the Wigner energy. From various experiments on highly irradiated graphite samples from CIRUS reactor at Trombay and ab-initio simulations, we have for the first time identified various 2-, 3- and 4-coordinated topological structures in defected graphite, and provided microscopic mechanism of defect annihilation on heating and release of the Wigner energy. The annihilation process involves cascading cooperative movement of atoms in two steps involving an intermediate structure. Our work provides new insights in understanding of the defect topologies and annihilation in graphite which is of considerable importance to wider areas of graphitic materials including graphene and carbon nanotubes.
△ Less
Submitted 14 February, 2020;
originally announced February 2020.
-
Revised crystal structure and electronic properties of high dielectric Ba(Fe$_{1/2}$Nb$_{1/2}$)O$_{3}$ ceramics
Authors:
Rajyavardhan Ray,
A. K. Himanshu,
Golak K. Mandal,
Uday Kumar,
S. N. Jha,
N Patra,
D. Bhattacharya,
A. B. Shinde,
Manuel Richter,
P. S. R. Krishna
Abstract:
Ba(Fe$_{1/2}$Nb$_{1/2}$)O$_3$ (BFN) ceramics are considered to be promising for technological applications owing to their high dielectric constant over a wide range of temperatures. However, there exists considerable discrepancy over the structural details. We address this discrepancy through a combined x-ray diffraction at room temperature and neutron powder diffraction measurements in the range…
▽ More
Ba(Fe$_{1/2}$Nb$_{1/2}$)O$_3$ (BFN) ceramics are considered to be promising for technological applications owing to their high dielectric constant over a wide range of temperatures. However, there exists considerable discrepancy over the structural details. We address this discrepancy through a combined x-ray diffraction at room temperature and neutron powder diffraction measurements in the range from 5K up to room temperature, supplemented by a comparative analysis of the earlier reported structures. Our study reveals a cubic structure with space group Pm$\bar{3}$m at all measured temperatures. Further, the x-ray near edge structure and the extended x-ray absorption fine structure studies on the local environment of the Fe ions is consistent with the cubic symmetry. An appropriate value of $U$ for DFT+$U$ calculations is obtained by comparison with x-ray absorption spectroscopy, which agrees well with the earlier reported electronic properties.
△ Less
Submitted 16 December, 2021; v1 submitted 1 July, 2019;
originally announced July 2019.
-
The X-ray photoemission and Co K -Edge X-ray absorption of Ba2CoWO6
Authors:
Dhiraj Jha,
A. K. Himanshu,
Bijay K Singh,
Dinesh Shukla,
Uday Kuma,
Ravi Kumar,
Kaustava Bhattacharyya,
A. B. Shinde,
P. S. R. Krishna,
Alo Dutta,
T. P. Sinha,
Rajyavardhan Ray
Abstract:
The structural, electronic and optical properties of cubic double perovskite BaCoWO6 have been studied. Neutron powder diffraction data is collected on this sample from 6K to 300K. The crystal structure is face centered cubic, space group being Fm3m (No. 225). We did not find evidence for long range magnetic ordering in this system in this temperature range. The band-gap is estimated using Uv-vis…
▽ More
The structural, electronic and optical properties of cubic double perovskite BaCoWO6 have been studied. Neutron powder diffraction data is collected on this sample from 6K to 300K. The crystal structure is face centered cubic, space group being Fm3m (No. 225). We did not find evidence for long range magnetic ordering in this system in this temperature range. The band-gap is estimated using Uv-vis spectroscopy. The Co-K edge X-ray absorption (XAFS) spectra of Ba2CoWO6 was analysed together with those Co-foil, which was used as reference compounds. X-ray photoemission spectroscopy (XPS), X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) studies give the insight of the electronic and structural information on the Co local environment for Ba2CoWO6.
△ Less
Submitted 4 July, 2019; v1 submitted 30 June, 2019;
originally announced July 2019.
-
Evidence for existence of Functional Monoclinic Phase in Sodium Niobate based Solid Solution by Powder Neutron Diffraction
Authors:
S. K. Mishra,
Mrinal Jauhari,
R. Mittal,
P. S. R. Krishna,
V. R. Reddy,
S. L. Chaplot
Abstract:
We have carried out systematic temperature-dependent neutron diffraction measurements in conjunction with dielectric spectroscopy from 6 to 300 K for sodium niobate based compounds (1-x) NaNbO3 -xBaTiO3 (NNBTx). The dielectric constant is measured both as a function of temperature and frequency. It shows an anomaly at different temperatures in cooling and heating cycles and exhibits a large therma…
▽ More
We have carried out systematic temperature-dependent neutron diffraction measurements in conjunction with dielectric spectroscopy from 6 to 300 K for sodium niobate based compounds (1-x) NaNbO3 -xBaTiO3 (NNBTx). The dielectric constant is measured both as a function of temperature and frequency. It shows an anomaly at different temperatures in cooling and heating cycles and exhibits a large thermal hysteresis of 150 K for the composition x=0.03. The dielectric constant is found to be dispersive in nature and suggests a relaxor ferroelectric behavior. In order to explore structural changes as a function of temperature, we analyzed the powder neutron diffraction data for the composition x=0.03 and 0.05, respectively. Drastic changes are observed in the powder profiles near 30.6°, 32.1° and 34.6° in the diffraction pattern below 200 K during cooling and above 190 K in heating cycles, respectively.The disappearance of superlattice reflection and splitting in main perovskite peaks provide a signature for structural phase transition. We observed stabilization of a monoclinic phase (Cc) at low temperature. This monoclinic phase is believed to provide a flexible polarization rotation and considered to be directly linked to the high performance piezoelectricity in materials. The thermal hysteresis for composition x=0.03 is larger than x=0.05. This suggests that addition of BaTiO3 in NaNbO3 suppresses the thermal hysteresis. It is also observed that the structural phase transition temperature decreases on increasing dopant concentration.
△ Less
Submitted 20 April, 2018;
originally announced April 2018.
-
Nonmonotonic particle-size-dependence of magnetoelectric coupling in strained nanosized particles of BiFeO$_3$
Authors:
Sudipta Goswami,
Dipten Bhattacharya,
Chandan K. Ghosh,
Barnali Ghosh,
S. D. Kaushik,
V. Siruguri,
P. S. R. Krishna
Abstract:
Using high resolution powder x-ray and neutron diffraction experiments, we determined the off-centered displacement of the ions within a unit cell and magnetoelectric coupling in nanoscale BiFeO$_3$ ($\approx$20-200 nm). We found that both the off-centered displacement of the ions and magnetoelectric coupling exhibit nonmonotonic variation with particle size. They increase as the particle size red…
▽ More
Using high resolution powder x-ray and neutron diffraction experiments, we determined the off-centered displacement of the ions within a unit cell and magnetoelectric coupling in nanoscale BiFeO$_3$ ($\approx$20-200 nm). We found that both the off-centered displacement of the ions and magnetoelectric coupling exhibit nonmonotonic variation with particle size. They increase as the particle size reduces from bulk and reach maximum around 30 nm. With further decrease in particle size, they decrease precipitously. The magnetoelectric coupling is determined by the anomaly in off-centering of ions around the magnetic transition temperature ($T_N$). The ions, in fact, exhibit large anomalous displacement around the $T_N$ which is analyzed using group theoretical approach. It underlies the nonmonotonic particle-size-dependence of off-centre displacement of ions and magnetoelectric coupling. The nonmonotonic variation of magnetoelectric coupling with particle size is further verified by direct electrical measurement of remanent ferroelectric hysteresis loops at room temperature under zero and $\sim$20 kOe magnetic field. Competition between enhanced lattice strain and compressive pressure appears to be causing the nonmonotonic particle-size-dependence of off-centre displacement while coupling between piezo and magnetostriction leads to nonmonotonicity in the variation of magnetoelectric coupling.
△ Less
Submitted 22 March, 2018;
originally announced March 2018.
-
High Temperature Phase Stability in Li0.12Na0.88NbO3: A Combined powder X-Ray and Neutron Diffraction Study
Authors:
S. K. Mishra,
P. S. R. Krishna,
A. B. Shinde,
V. B. Jayakrishnan,
R. Mittal,
P. U. Sastry,
S. L. Chaplot
Abstract:
Lithium doped sodium niobate is an ecofriendly piezoelectric material that exhibits a variety of structural phase transitions with composition and temperature. We have investigated the phase stabilities of an important composition Li0.12Na0.88NbO3 (LNN12) using a combination of powder x-ray and neutron diffraction techniques in the temperature range 300 - 1100 K. Detailed Rietveld analyses of ther…
▽ More
Lithium doped sodium niobate is an ecofriendly piezoelectric material that exhibits a variety of structural phase transitions with composition and temperature. We have investigated the phase stabilities of an important composition Li0.12Na0.88NbO3 (LNN12) using a combination of powder x-ray and neutron diffraction techniques in the temperature range 300 - 1100 K. Detailed Rietveld analyses of thermo-diffractograms show a variety of structural phase transitions ranging from non-polar antiferrodistortive to ferroelectric in nature. In the temperature range of 525 K to 675 K, unambiguous experimental evidence is shown for phase coexistence of orthorhombic paraelectric O1 phase (space group Cmcm) and orthorhombic ferroelectric O2 phase (space group Pmc21). The bp primitive lattice parameter of the ferroelectric orthorhombic phase (O2 phase) decreases, while the ap and cp primitive lattice parameters show normal increase with increase in temperature. Above 675 K, in the O1 phase, all lattice parameters come close to each other and increase continuously with increase of temperature, and around 925 K, ap parameter approaches bp parameter and thus the sample undergoes an orthorhombic to tetragonal phase transition. Further as temperature increases, the cp lattice parameter decreases, and finally approaches to ap parameter, and the sample transform into the cubic phase. The continuous change in the lattice parameters reveals that the successive phase transformations from orthorhombic O1 to high temperature tetragonal phase and finally to the cubic phase are not of a strong first order type in nature. We argue that application of chemical pressure as a result of Li substitution in NaNbO3 matrix, favours the freezing of zone centre phonons over the zone boundary phonons that are known to freeze in pure NaNbO3 as function of temperature.
△ Less
Submitted 5 May, 2015;
originally announced May 2015.
-
Evidence for anomalous structural behavior in CaFe2As2
Authors:
S. K. Mishra,
R. Mittal,
P. S. R. Krishna,
P. U. Sastry,
S. L. Chaplot,
P. D. Babu,
S. Matsuishi,
H. Hosono
Abstract:
The structural properties of the CaFe2As2 have been investigated by x-ray and neutron powder diffraction techniques as a function of temperature. Unambiguous experimental evidence is shown for coexistence of tetragonal and orthorhombic phases below 170 K in contrast to existing literature. Detailed Rietveld analyses of thermo-diffractograms show that the sample does not transform completely in to…
▽ More
The structural properties of the CaFe2As2 have been investigated by x-ray and neutron powder diffraction techniques as a function of temperature. Unambiguous experimental evidence is shown for coexistence of tetragonal and orthorhombic phases below 170 K in contrast to existing literature. Detailed Rietveld analyses of thermo-diffractograms show that the sample does not transform completely in to the orthorhombic phase at the lowest temperature even though it is the majority phase. We have found that the unit cell volume of the orthorhombic phase is higher compared to that of the tetragonal phase for all the temperatures. X-ray data on CaFe2As2 shows anomalous (at) lattice parameter contraction with increasing temperature and phase co-existence behavior below 170 K unlike other members of the 122 family of compounds like SrFe2As2 and EuFe2As2. Temperature dependent magnetization of polycrystalline CaFe2As2 sample show weak anomalies below 170 K. This behavior of the polycrystalline sample is in contrast to that of a single crystal reported earlier.
△ Less
Submitted 26 November, 2013; v1 submitted 2 April, 2013;
originally announced April 2013.
-
Origin of Large Dielectric Constant with Large Remnant Polarization and Evidence of Magnetoelectric Coupling in Multiferroic La modified BiFeO3-PbTiO3 Solid Solution
Authors:
Anupinder Singh,
Ratnamala Chatterjee,
S. K. Mishra,
P. S. R. Krishna,
S. L. Chaplot
Abstract:
The presence of superlattice reflections and detailed analyses of the powder neutron and x-ray diffraction data reveal that La rich (BF$_{0.50}$-LF$_{0.50}$)$_{0.50}$-(PT)$_{0.50}$ (BF-LF-PT) has ferroelectric rhombohedral crystal structure with space group \textit{$R3c$} at ambient conditions. The temperature dependence of lattice parameters, tilt angle, calculated polarization $(P_{s})$, volum…
▽ More
The presence of superlattice reflections and detailed analyses of the powder neutron and x-ray diffraction data reveal that La rich (BF$_{0.50}$-LF$_{0.50}$)$_{0.50}$-(PT)$_{0.50}$ (BF-LF-PT) has ferroelectric rhombohedral crystal structure with space group \textit{$R3c$} at ambient conditions. The temperature dependence of lattice parameters, tilt angle, calculated polarization $(P_{s})$, volume, and integrated intensity of superlattice and magnetic reflections show an anomaly around 170 K. Impedance spectroscopy, dielectric and ac conductivity measurements were performed in temperature range $473K \leq T \leq 573K$ to probe the origin of large remnant polarization and frequency dependent broad transitions with large dielectric constant near $T_c^{FE}$. Results of impedance spectroscopy measurements clearly show contributions of both grain and grain boundaries throughout the frequency range ($10^{3}$ Hz$\leq f\leq 10^{7} $ Hz). It could be concluded that the grain boundaries are more resistive and capacitive as compared to the grains, resulting in inhomogeneities in the sample causing broad frequency dependent dielectric anomalies. Enhancement in dielectric constant and remnant polarization values are possibly due to space charge polarization caused by piling of charges at the interface of grains and grain boundaries. The imaginary parts of dielectric constant ($ε^{\prime\prime}$) Vs frequency data were fitted using Maxwell-Wagner model at $T_c^{FE}(\sim 523$K) and model fits very well with the data up to $10^{5}$ Hz. Magnetodielectric measurements prove that the sample starts exhibiting magnetoelectric coupling at $\sim 170$ K, which is also validated by neutron diffraction data.
△ Less
Submitted 8 February, 2010;
originally announced February 2010.
-
A growth walk model for estimating the canonical partition function of Interacting Self Avoiding Walk
Authors:
S. L. Narasimhan,
P. S. R. Krishna,
M. Ponmurugan,
K. P. N. Murthy
Abstract:
We have explained in detail why the canonical partition function of Interacting Self Avoiding Walk (ISAW), is exactly equivalent to the configurational average of the weights associated with growth walks, such as the Interacting Growth Walk (IGW), if the average is taken over the entire genealogical tree of the walk. In this context, we have shown that it is not always possible to factor the the…
▽ More
We have explained in detail why the canonical partition function of Interacting Self Avoiding Walk (ISAW), is exactly equivalent to the configurational average of the weights associated with growth walks, such as the Interacting Growth Walk (IGW), if the average is taken over the entire genealogical tree of the walk. In this context, we have shown that it is not always possible to factor the the density of states out of the canonical partition function if the local growth rule is temperature-dependent. We have presented Monte Carlo results for IGWs on a diamond lattice in order to demonstrate that the actual set of IGW configurations available for study is temperature-dependent even though the weighted averages lead to the expected thermodynamic behavior of Interacting Self Avoiding Walk (ISAW).
△ Less
Submitted 21 August, 2007; v1 submitted 1 June, 2007;
originally announced June 2007.
-
Competing antiferroelectric and ferroelectric interactions in NaNbO3 : Neutron diffraction and theoretical studies
Authors:
S. K. Mishra,
N. Choudhury,
S. L. Chaplot,
P. S. R. Krishna,
R. Mittal
Abstract:
Neutron diffraction studies using powder samples have been used to understand the complex sequence of low temperature phase transitions of NaNbO3 in the temperature range from 12 K-350 K. Detailed Rietveld analysis of the diffraction data reveal that the antiferroelectric to ferroelectric phase transition occurs on cooling around 73 K while the reverse ferroelectric to antiferroelectric transiti…
▽ More
Neutron diffraction studies using powder samples have been used to understand the complex sequence of low temperature phase transitions of NaNbO3 in the temperature range from 12 K-350 K. Detailed Rietveld analysis of the diffraction data reveal that the antiferroelectric to ferroelectric phase transition occurs on cooling around 73 K while the reverse ferroelectric to antiferroelectric transition occurs on heating at 245 K. However, the former transformation is not complete till down to 12 K and there is unambiguous evidence for the presence of the ferroelectric R3c phase coexisting with an antiferroelectic phase (Pbcm) over a wide range of temperatures. The coexisting phases and reported anomalous smearing of the dielectric response akin to dipole glasses and relaxors observed in the same temperature range are consistent with competing ferroelectric and antiferroelectric interactions in NaNbO3. We have carried out theoretical lattice dynamical calculations which reveal that the free energies of the antiferroelectric Pbcm and ferroelectric R3c phases are nearly identical over a wide range of temperature. The small energy difference between the two phases is of interest as it explains the observed coexistence of these phases over a wide range of temperature. The computed double well depths and energy barriers from paraelectric Pm m to antiferroelectric Pbcm and ferroelectric R3c phases in NaNbO3 are also quite similar, although the ferroelectric R3c phase has a slightly lower energy.
△ Less
Submitted 14 March, 2007;
originally announced March 2007.
-
Coil-Globule transition of a single short polymer chain - an exact enumeration study
Authors:
M. Ponmurugan,
S. L. Narasimhan,
P. S. R. Krishna,
K. P. N. Murthy
Abstract:
We present an exact enumeration study of short SAWs in two as well as three dimensions that addresses the question, `what is the shortest walk for which the existence of all the three phases - coil, globule and the {\it theta} - could be demonstrated'. Even though we could easily demonstrate the coil and the globule phases from Free Energy considerations, we could demonstrate the existence of a…
▽ More
We present an exact enumeration study of short SAWs in two as well as three dimensions that addresses the question, `what is the shortest walk for which the existence of all the three phases - coil, globule and the {\it theta} - could be demonstrated'. Even though we could easily demonstrate the coil and the globule phases from Free Energy considerations, we could demonstrate the existence of a {\it theta} phase only by using a scaling form for the distribution of gyration radius. That even such short walks have a scaling behavior is an unexpected result of this work.
△ Less
Submitted 2 January, 2007;
originally announced January 2007.
-
A formalism for studying long-range correlations in many-alphabets sequences
Authors:
S. L. Narasimhan,
Joseph A. Nathan,
P. S. R. Krishna,
K. P. N. Murthy
Abstract:
We formulate a mean-field-like theory of long-range correlated $L$-alphabets sequences, which are actually systems with $(L-1)$ independent parameters. Depending on the values of these parameters, the variance on the average number of any given symbol in the sequence shows a linear or a superlinear dependence on the total length of the sequence. We present exact solution to the four-alphabets an…
▽ More
We formulate a mean-field-like theory of long-range correlated $L$-alphabets sequences, which are actually systems with $(L-1)$ independent parameters. Depending on the values of these parameters, the variance on the average number of any given symbol in the sequence shows a linear or a superlinear dependence on the total length of the sequence. We present exact solution to the four-alphabets and three-alphabets sequences. We also demonstrate that a map** of the given sequence into a smaller alphabets sequence (namely, a {\it coarse-graining} process) does not necessarily imply that long-range correlations found in the latter would correspond to those of the former.
△ Less
Submitted 13 September, 2005; v1 submitted 2 September, 2004;
originally announced September 2004.
-
Structural and Magnetic Studies on La2-xDyxCa2xBa2Cu4+2xOz Type Superconducting Oxides
Authors:
S. Rayaprol,
Darshan C. Kundaliya,
C. M. Thaker,
D. G. Kuberkar,
Keka R. Chakraborty,
P. S. R. Krishna,
M. Ramanadham
Abstract:
The La-2125 type La2-xDyxCa2xBa2Cu4+2xOz (0.1 < x < 0.5; LDBO) compounds have been synthesized and studied for their structural and superconducting properties by room temperature neutron diffraction, high field dc magnetization, four-probe resistivity and iodometric double titration. The Rietveld analysis of the neutron diffraction data reveals tetragonal structure for all the samples, which cry…
▽ More
The La-2125 type La2-xDyxCa2xBa2Cu4+2xOz (0.1 < x < 0.5; LDBO) compounds have been synthesized and studied for their structural and superconducting properties by room temperature neutron diffraction, high field dc magnetization, four-probe resistivity and iodometric double titration. The Rietveld analysis of the neutron diffraction data reveals tetragonal structure for all the samples, which crystallizes into La-123 type tetragonal structure in P4/mmm space group. Iodometric double titrations were performed to determine the oxygen content values and calculate mobile charge carrier (holes) density. The superconducting transition temperatures (Tc) increases from ~ 20 K for x = 0.1 to a maximum of 75 K for x = 0.5. Flux pinning force (Fp) and critical current density (Jc), calculated from the low temperature hysteresis loops, also increases with increasing dopant concentration. The paper presents the studies on structure and superconducting properties of all LDBO compounds in light of the role of calcium in inducing superconductivity in the tetragonal non-superconducting oxide.
△ Less
Submitted 14 August, 2004;
originally announced August 2004.
-
Neutron Diffraction Studies on La2-xDyxCa2xBa2Cu4+2xOz Superconductors
Authors:
S. Rayaprol,
Rohini Parmar,
D. G. Kuberkar,
Keka R. Chakraborty,
P. S. R. Krishna,
M. Ramanadham
Abstract:
Structural studies on Dy-substituted La-2125 type superconductors have been carried out by neutron diffraction experiments at room temperature using a monochromatic neutron beam of wavelength lambda = 1.249 Angstroms. A series of samples with La2-xDyxCa2xBa2Cu4+2xOz stoichiometric composition, for x = 0.1 - 0.5, have been studied for their structural properties. A tetragonal Y-123 unit cell was…
▽ More
Structural studies on Dy-substituted La-2125 type superconductors have been carried out by neutron diffraction experiments at room temperature using a monochromatic neutron beam of wavelength lambda = 1.249 Angstroms. A series of samples with La2-xDyxCa2xBa2Cu4+2xOz stoichiometric composition, for x = 0.1 - 0.5, have been studied for their structural properties. A tetragonal Y-123 unit cell was taken as the starting model for the Rietveld analysis. All the samples fit into the starting model, exhibiting no structural transition taking place with increasing dopant concentration. The results of Rietveld analysis and structural properties are discussed in detail.
△ Less
Submitted 14 August, 2004;
originally announced August 2004.
-
Interacting Growth Walk - a model for hyperquenched homopolymer glass?
Authors:
S. L. Narasimhan,
P. S. R. Krishna,
A. K. Rajarajan,
K. P. N. Murthy
Abstract:
We show that the compact self avoiding walk configurations, kinetically generated by the recently introduced Interacting Growth Walk (IGW) model, can be considered as members of a canonical ensemble if they are assigned random values of energy. Such a map** is necessary for studying the thermodynamic behaviour of this system. We have presented the specific heat data for the IGW, obtained from…
▽ More
We show that the compact self avoiding walk configurations, kinetically generated by the recently introduced Interacting Growth Walk (IGW) model, can be considered as members of a canonical ensemble if they are assigned random values of energy. Such a map** is necessary for studying the thermodynamic behaviour of this system. We have presented the specific heat data for the IGW, obtained from extensive simulations on a square lattice; we observe a broad hump in the specific heat above the $θ$-point, contrary to expectation.
△ Less
Submitted 9 September, 2002;
originally announced September 2002.
-
Interacting Growth Walk on a honeycomb lattice
Authors:
S. L. Narasimhan,
P. S. R. Krishna,
M. Ramanadham,
K. P. N. Murthy,
V. Sridhar
Abstract:
The Interacting Growth Walk (IGW) is a kinetic algorithm proposed recently for generating long, compact, self avoiding walks. The growth process in IGW is tuned by the so called growth temperature $T' = 1/(k_B β')$. On a square lattice and at $T' = 0$, IGW is attrition free and hence grows indefinitely. In this paper we consider IGW on a honeycomb lattice. We take contact energy, see text, as…
▽ More
The Interacting Growth Walk (IGW) is a kinetic algorithm proposed recently for generating long, compact, self avoiding walks. The growth process in IGW is tuned by the so called growth temperature $T' = 1/(k_B β')$. On a square lattice and at $T' = 0$, IGW is attrition free and hence grows indefinitely. In this paper we consider IGW on a honeycomb lattice. We take contact energy, see text, as $ε=-|ε|=-1$. We show that IGW at $β' =\infty$ ($T'=0$) is identical to Interacting Self Avoiding Walk (ISAW) at $β=\ln 4$ ($k_B T = 1/\ln 4=0.7213$). Also IGW at $β' = 0$ ($T' = \infty$) corresponds to ISAW at $β= \ln 2$ ($k_B T= 1/ln 2 = 1.4427$). For other temperatures we need to introduce a statistical weight factor to a walk of the IGW ensemble to make correspondence with the ISAW ensemble.
△ Less
Submitted 15 January, 2002;
originally announced January 2002.
-
Protein folding simulations with Interacting Growth Walk model
Authors:
S. L. Narasimhan,
P. S. R. Krishna,
M. Ramanadham,
K. P. N. Murthy,
R. Chidambaram
Abstract:
We demonstrate that the recently proposed interacting growth walk (IGW) model, modified for generating self-avoiding heteropolymers, proves to be a simpler alternative to the other Monte Carlo methods available in the literature for obtaining minimum energy conformation of lattice proteins. In fact, this simple growth algorithm seems to be capable of quickly leading to low energy states for all…
▽ More
We demonstrate that the recently proposed interacting growth walk (IGW) model, modified for generating self-avoiding heteropolymers, proves to be a simpler alternative to the other Monte Carlo methods available in the literature for obtaining minimum energy conformation of lattice proteins. In fact, this simple growth algorithm seems to be capable of quickly leading to low energy states for all the three dimensional bench mark HP-sequences investigated.
△ Less
Submitted 3 January, 2002; v1 submitted 3 December, 2001;
originally announced December 2001.
-
Comment on "Peculiar Scaling of Self-Avoiding Walk Contacts"
Authors:
S. L. Narasimhan,
P. S. R. Krishna,
K. P. N. Murthy,
M. Ramanadham
Abstract:
We demonstrate that the recently proposed Interacting Growth Walk (cond-mat/0108097) does not have the contact-scaling behaviour of Self-Avoiding Walk (M. Baiesi, E. Orlandini and A. L. Stella, Phys. Rev. Lett. 87, 070602 (2001)) at finite temperatures.
We demonstrate that the recently proposed Interacting Growth Walk (cond-mat/0108097) does not have the contact-scaling behaviour of Self-Avoiding Walk (M. Baiesi, E. Orlandini and A. L. Stella, Phys. Rev. Lett. 87, 070602 (2001)) at finite temperatures.
△ Less
Submitted 19 October, 2001;
originally announced October 2001.
-
A new monte carlo algorithm for growing compact Self Avoiding Walks
Authors:
S. L. Narasimhan,
P. S. R. Krishna,
K. P. N. Murthy,
M. Ramanadham
Abstract:
We propose an algorithm based on local growth rules for kinetically generating self avoiding walk configurations at any given temperature. This algorithm, called the Interacting Growth Walk (IGW) algorithm, does not suffer from attrition on a square lattice at zero temperature, in contrast to the existing algorithms. More importantly, the IGW algorithm facilitates growing compact configurations…
▽ More
We propose an algorithm based on local growth rules for kinetically generating self avoiding walk configurations at any given temperature. This algorithm, called the Interacting Growth Walk (IGW) algorithm, does not suffer from attrition on a square lattice at zero temperature, in contrast to the existing algorithms. More importantly, the IGW algorithm facilitates growing compact configurations at lower temperatures - a feature that makes it attractive for studying a variety of processes such as the folding of proteins. We demonstrate that our algorithm correctly describes the collapse transition of a homopolymer in two dimensions.
△ Less
Submitted 27 August, 2001; v1 submitted 6 August, 2001;
originally announced August 2001.
-
Sticky Spheres, Entropy barriers and Non-equilibrium phase transitions
Authors:
S. L. Narasimhan,
P. S. R. Krishna,
K. P. N. Murthy
Abstract:
A sticky spheres model to describe slow dynamics of a non-equilibrium system is proposed. The dynamical slowing down is due to the presence of entropy barriers. We present an exact mean field analysis of the model and demonstrate that there is a non-equilibrium phase transition from an exponential cluster size distribution to a powerlaw.
A sticky spheres model to describe slow dynamics of a non-equilibrium system is proposed. The dynamical slowing down is due to the presence of entropy barriers. We present an exact mean field analysis of the model and demonstrate that there is a non-equilibrium phase transition from an exponential cluster size distribution to a powerlaw.
△ Less
Submitted 5 August, 2001; v1 submitted 22 January, 2001;
originally announced January 2001.