Impact of medium temperature heat treatment on flux trap** sensitivity in SRF cavities
Authors:
Pashupati Dhakal,
Bashu Dev Khanal,
Eric Lechner,
Gianluigi Ciovati
Abstract:
The effect of mid-T heat treatment on flux trap** sensitivity was measured on several 1.3 GHz single cell cavities subjected to vacuum annealing at temperature of 150 - 400 $^\circ$C for a duration of 3 hours. The cavity was cooldown with residual magnetic field $\sim$0 and $\sim$20 mG in the Dewar with cooldown condition of full flux trap**. The quality factor as a function of accelerating gr…
▽ More
The effect of mid-T heat treatment on flux trap** sensitivity was measured on several 1.3 GHz single cell cavities subjected to vacuum annealing at temperature of 150 - 400 $^\circ$C for a duration of 3 hours. The cavity was cooldown with residual magnetic field $\sim$0 and $\sim$20 mG in the Dewar with cooldown condition of full flux trap**. The quality factor as a function of accelerating gradient was measured. The results show the correlation between the treatment temperature, quality factor, and sensitivity to flux trap**. Sensitivity increases with increasing heat treatment temperatures within the range of (200 - 325 $^\circ$C/3h). Moreover, variations in the effective penetration depth of the magnetic field and the density of quasi-particles can occur, influencing alterations in the cavity's electromagnetic response and resonance frequency.
△ Less
Submitted 16 May, 2024;
originally announced May 2024.
-
Field, frequency and temperature dependence of the surface resistance of nitrogen diffused niobium superconducting radio frequency cavities
Authors:
P. Dhakal,
B. D. Khanal,
A. Gurevich,
G. Ciovati
Abstract:
We report the RF performance of several single-cell superconducting radio-frequency cavities subjected to low temperature heat treatment in nitrogen environment. The cavities were treated at temperature 120 - 165 $^{\circ}$C for an extended period of time (24 - 48 hours) either in high vacuum or in a low partial pressure of ultra-pure nitrogen. The improvement in $Q_0$ with a Q-rise was observed w…
▽ More
We report the RF performance of several single-cell superconducting radio-frequency cavities subjected to low temperature heat treatment in nitrogen environment. The cavities were treated at temperature 120 - 165 $^{\circ}$C for an extended period of time (24 - 48 hours) either in high vacuum or in a low partial pressure of ultra-pure nitrogen. The improvement in $Q_0$ with a Q-rise was observed when nitrogen gas was injected at $\sim$300 $^{\circ} $C during the cavity cooldown from 800 $^{\circ}$C and held at 165 $^{\circ}$C, without any degradation in accelerating gradient over the baseline performance. The treatment was applied to several elliptical cavities with frequency ranging from 0.75 GHz to 3.0 GHz, showing an improved quality factor as a result of low temperature nitrogen treatments. The Q-rise feature is similar to that achieved by nitrogen alloying Nb cavities at higher temperature, followed by material removal by electropolishing. The surface modification was confirmed by the change in electronic mean free path and tuned with the temperature and duration of heat treatment. The decrease of the temperature-dependent surface resistance with increasing RF field, resulting in a Q-rise, becomes stronger with increasing frequency and decreasing temperature. The data suggest a crossover frequency of $\sim 0.95$~GHz above which the Q-rise phenomenon occurs at 2~K. Some of these results can be explained qualitatively with an existing model of intrinsic field-dependence of the surface resistance with both equilibrium and nonequilibrium quasiparticle distribution functions. The change in the Q-slope below 0.95 GHz may result from masking contribution of trapped magnetic flux to the residual surface resistance.
△ Less
Submitted 16 May, 2024; v1 submitted 27 February, 2024;
originally announced February 2024.
-
Temperature, RF Field, and Frequency Dependence Performance Evaluation of Superconducting Niobium Half-Wave Cavity
Authors:
N. K. Raut,
B. D. Khanal,
J. K. Tiskumara,
S. De Silva,
P. Dhakal,
G. Ciovati1,
J. R. Delayen
Abstract:
Recent advancement in superconducting radio frequency cavity processing techniques, with diffusion of impurities within the RF penetration depth, resulted in high quality factor with increase in quality factor with increasing accelerating gradient. The increase in quality factor is the result of a decrease in the surface resistance as a result of nonmagnetic impurities do** and change in electro…
▽ More
Recent advancement in superconducting radio frequency cavity processing techniques, with diffusion of impurities within the RF penetration depth, resulted in high quality factor with increase in quality factor with increasing accelerating gradient. The increase in quality factor is the result of a decrease in the surface resistance as a result of nonmagnetic impurities do** and change in electronic density of states. The fundamental understanding of the dependence of surface resistance on frequency and surface preparation is still an active area of research. Here, we present the result of RF measurements of the TEM modes in a coaxial half wave niobium cavity resonating at frequencies between 0.3-1.3 GHz. The temperature dependence of the surface resistance was measured between 4.2 K and 1.6 K. The field dependence of the surface resistance was measured at 2.0 K. The baseline measurements were made after standard surface preparation by buffered chemical polishing.
△ Less
Submitted 18 August, 2023;
originally announced August 2023.
-
Quench Detection in a Superconducting Radio Frequency Cavity with Combine Temperature and Magnetic Field Map**
Authors:
B. D. Khanal,
P. Dhakal,
G. Ciovati
Abstract:
Local dissipation of RF power in superconducting radio frequency cavities create so called hot spots, primary precursors of cavity quench driven by either thermal or magnetic instability. These hot spots are detected by a temperature map** system, and a large increase in temperature on the outer surface is detected during cavity quench events. Here, we have used combined magnetic and temperature…
▽ More
Local dissipation of RF power in superconducting radio frequency cavities create so called hot spots, primary precursors of cavity quench driven by either thermal or magnetic instability. These hot spots are detected by a temperature map** system, and a large increase in temperature on the outer surface is detected during cavity quench events. Here, we have used combined magnetic and temperature map** systems using anisotropic magnetoresistance (AMR) sensors and carbon resisters to locate the hot spots and areas with high trapped flux on a 3.0 GHz single-cell Nb cavity during the RF tests at 2.0 K. The quench location and hot spots were detected near the equator when the residual magnetic field in the Dewar is kept < 1 mG. The hot spots and quench locations moved when the magnetic field is trapped locally, as detected by T-map** system. No significant dynamics of trapped flux is detected by AMR sensors, however, change in magnetic flux during cavity quench is detected by a flux gate magnetometer, close to the quench location. The result provides the direct evidence of hot spots and quench events due to localized trapped vortices.
△ Less
Submitted 16 August, 2023;
originally announced August 2023.
-
Evaluation of flux expulsion and flux trap** sensitivity of srf cavities fabricated from cold work Nb sheet with successive heat treatment
Authors:
B. D. Khanal,
P. Dhakal
Abstract:
The main source of RF losses leading to lower quality factor of superconducting radio-frequency cavities is due to the residual magnetic flux trapped during cool-down. The loss due to flux trap** is more pronounced for cavities subjected to impurities do**. The flux trap** and its sensitivity to rf losses are related to several intrinsic and extrinsic phenomena. To elucidate the effect of re…
▽ More
The main source of RF losses leading to lower quality factor of superconducting radio-frequency cavities is due to the residual magnetic flux trapped during cool-down. The loss due to flux trap** is more pronounced for cavities subjected to impurities do**. The flux trap** and its sensitivity to rf losses are related to several intrinsic and extrinsic phenomena. To elucidate the effect of re-crystallization by high temperature heat treatment on the flux trap** sensitivity, we have fabricated two 1.3 GHz single cell cavities from cold-worked Nb sheets and compared with cavities made from standard fine-grain Nb. Flux expulsion ratio and flux trap** sensitivity were measured after successive high temperature heat treatments. The cavity made from cold worked Nb showed better flux expulsion after 800 C/3h heat treatments and similar behavior when heat treated with additional 900 C/3h and 1000 C/3h. In this contribution, we present the summary of flux expulsion, trap** sensitivity, and RF results.
△ Less
Submitted 16 August, 2023;
originally announced August 2023.