Intermixing of Fe and Cu on the atomic scale by high-pressure torsion as revealed by DC- and AC-SQUID susceptometry and atom probe tomography
Authors:
Martin Stückler,
Heinz Krenn,
Philipp Kürnsteiner,
Baptiste Gault,
Frédéric De Geuser,
Lukas Weissitsch,
Stefan Wurster,
Reinhard Pippan,
Andrea Bachmaier
Abstract:
The capability of high-pressure torsion on the preparation of supersaturated solid solutions, consisting of Cu-14Fe (wt.%), is studied. From microstructural investigations a steady state is obtained with nanocrystalline grains. The as-deformed state is analyzed with atom probe tomography, revealing an enhanced solubility and the presence of Fe-rich particles. The DC-hysteresis loop shows suppresse…
▽ More
The capability of high-pressure torsion on the preparation of supersaturated solid solutions, consisting of Cu-14Fe (wt.%), is studied. From microstructural investigations a steady state is obtained with nanocrystalline grains. The as-deformed state is analyzed with atom probe tomography, revealing an enhanced solubility and the presence of Fe-rich particles. The DC-hysteresis loop shows suppressed long range interactions in the as-deformed state and evolves towards a typical bulk hysteresis loop when annealed at 500°C. AC-susceptometry measurements of the as-deformed state reveal the presence of a superparamagnetic blocking peak, as well as a magnetic frustrated phase, whereas the transition of the latter follows the Almeida-Thouless line, coinciding with the microstructural investigations by atom probe tomography. AC-susceptometry shows that the frustrated state vanishes for annealing at 250°C.
△ Less
Submitted 7 September, 2020;
originally announced September 2020.
-
Nanoscale Investigation of Microcracks and Grain Boundary Wetting in Press Hardened Galvanized 20MnB8 Steel
Authors:
M. Arndt,
P. Kürnsteiner,
T. Truglas,
J. Duchoslav,
K. Hingerl,
D. Stifter,
C. Commenda,
J. Haslmayr,
S. Kolnberger,
J. Faderl,
H. Groiss
Abstract:
Grain boundary wetting as a preliminary stage for zinc induced grain boundary weakening and embrittlement in a Zn coated press hardened 20MnB8 steel was analyzed by means of electron backscatter diffraction, Auger electron spectroscopy, energy dispersive X-ray analysis, atom probe tomography and transmission electron microscopy on the nanometer scale. Microcracks at prior austenite grain boundarie…
▽ More
Grain boundary wetting as a preliminary stage for zinc induced grain boundary weakening and embrittlement in a Zn coated press hardened 20MnB8 steel was analyzed by means of electron backscatter diffraction, Auger electron spectroscopy, energy dispersive X-ray analysis, atom probe tomography and transmission electron microscopy on the nanometer scale. Microcracks at prior austenite grain boundaries were observed and structures that developed after microcrack formation were identified. Zn/Fe intermetallic phases with grain sizes smaller than 100 nm in diameter are present at the crack surfaces and at the wedge-shaped crack tips. In order to get a complete picture, including the microstructure before cracking, an undeformed, electrolytically coated reference sample which underwent the same heat treatment as the press hardened material was investigated. Here, Zn, in the order of one atomic layer or less, could be found along prior austenite grain boundaries several micrometers away from the actual Zn/Fe phases in the coating. Such a grain boundary weakening by Zn wetting of prior austenitic grain boundaries during austenitization and/or hot forming is a necessary condition for microcrack formation.
△ Less
Submitted 28 December, 2021; v1 submitted 2 July, 2020;
originally announced July 2020.
-
Characterizing solute hydrogen and hydrides in pure and alloyed titanium at the atomic scale
Authors:
Yanhong Chang,
Andrew J. Breen,
Zahra Tarzimoghadam,
Philipp Kürnsteiner,
Hazel Gardner,
Abigail Ackerman,
Anna Radecka,
Paul A. J. Bagot,
Wenjun Lu,
Tong Li,
Eric A. Jägle,
Michael Herbig,
Leigh T. Stephenson,
Michael P. Moody,
David Rugg,
David Dye,
Dirk Ponge,
Dierk Raabe,
Baptiste Gault
Abstract:
Ti has a high affinity for hydrogen and is a typical hydride formers. Ti-hydride are brittle phases which probably cause premature failure of Ti-alloys. Here, we used atom probe tomography and electron microscopy to investigate the hydrogen distribution in a set of specimens of commercially pure Ti, model and commercial Ti-alloys. Although likely partly introduced during specimen preparation with…
▽ More
Ti has a high affinity for hydrogen and is a typical hydride formers. Ti-hydride are brittle phases which probably cause premature failure of Ti-alloys. Here, we used atom probe tomography and electron microscopy to investigate the hydrogen distribution in a set of specimens of commercially pure Ti, model and commercial Ti-alloys. Although likely partly introduced during specimen preparation with the focused-ion beam, we show formation of Ti-hydrides along α grain boundaries and α/\b{eta} phase boundaries in commercial pure Ti and α+\b{eta} binary model alloys. No hydrides are observed in the α phase in alloys with Al addition or quenched-in Mo supersaturation.
△ Less
Submitted 11 March, 2018;
originally announced March 2018.