Tungsten boride shields in a spherical tokamak
Authors:
Colin G Windsor,
Jack O Astbury,
James Davidson,
Charles J R McFadzean,
J Guy Morgan,
Christopher Wilson,
Samuel A Humphry-Baker
Abstract:
The favourable properties of tungsten borides for shielding the central High Temperature Superconductor (HTS) core of a spherical tokamak fusion power plant are modelled using the MCNP code. The objectives are to minimize the power deposition into the cooled HTS core, and to keep HTS radiation damage to acceptable levels by limiting the neutron and gamma fluxes. The shield materials compared are W…
▽ More
The favourable properties of tungsten borides for shielding the central High Temperature Superconductor (HTS) core of a spherical tokamak fusion power plant are modelled using the MCNP code. The objectives are to minimize the power deposition into the cooled HTS core, and to keep HTS radiation damage to acceptable levels by limiting the neutron and gamma fluxes. The shield materials compared are W2B, WB, W2B5 and WB4 along with a reactively sintered boride B0.329C0.074Cr0.024Fe0.274W0.299, monolithic W and WC. Of all these W2B5 gave the most favourable results with a factor of ~10 or greater reduction in neutron flux and gamma energy deposition as compared to monolithic W. These results are compared with layered water-cooled shields, giving the result that the monolithic shields, with moderating boron, gave comparable neutron flux and power deposition, and (in the case of W2B5) even better performance. Good performance without water-coolant has advantages from a reactor safety perspective due to the risks associated with radio-activation of oxygen. 10B isotope concentrations between 0 and 100% are considered for the boride shields. The naturally occurring 20% fraction gave much lower energy depositions than the 0% fraction, but the improvement largely saturated beyond 40%. Thermophysical properties of the candidate materials are discussed, in particular the thermal strain. To our knowledge, the performance of W2B5 is unrivalled by other monolithic shielding materials. This is partly as its trigonal crystal structure gives it higher atomic density compared with other borides. It is also suggested that its high performance depends on it having just high enough 10B content to maintain a constant neutron energy spectrum across the shield.
△ Less
Submitted 14 April, 2021;
originally announced April 2021.
-
Creep deformation of WC hardmetals with iron-based binders
Authors:
Samuel A. Humphry-Baker,
Luc. J. M. Vandeperre
Abstract:
Iron is a candidate to replace cobalt in WC hardmetals, due to its lower cost and toxicity. A WC-FeCr hardmetal was compression tested at 900-1200 °C. Particular attention is paid to the steady-state creep rates and stress-exponents (n) during isostress treatments. Three regimes of stress dependence are observed. Two of these were previously reported for WC-Co: power law creep (n~3) at medium stre…
▽ More
Iron is a candidate to replace cobalt in WC hardmetals, due to its lower cost and toxicity. A WC-FeCr hardmetal was compression tested at 900-1200 °C. Particular attention is paid to the steady-state creep rates and stress-exponents (n) during isostress treatments. Three regimes of stress dependence are observed. Two of these were previously reported for WC-Co: power law creep (n~3) at medium stresses; and grain boundary sliding (n~1) at higher stresses, generally >100MPa. A previously unreported low stress (<10MPa) regime with an exponent of n~2 is also observed. By combining electron microscopy with X-ray diffraction texture measurements, the low stress regime is attributed to viscous flow of the binder, which is accommodated by diffusional creep in the WC skeleton. The mechanism may be applicable to other hardmetals. Compared to analogous WC-Co materials, WC-FeCr shows improved creep resistance below 1000 °C, which can be explained by its lower self-diffusivity, and a lower solubility for WC than Co. However, at temperatures corresponding to liquid eutectic formation (~1140 °C), its creep resistance becomes inferior. These results indicate FeCr may be a suitable replacement for Co provided the eutectic temperature is not exceeded.
△ Less
Submitted 31 August, 2020;
originally announced August 2020.
-
A high temperature W$_2$B cermet for compact neutron shielding
Authors:
Michail Athanasakis,
Eugene Ivanov,
Eduardo del Rio,
Samuel A. Humphry-Baker
Abstract:
We have developed a new material for neutron shielding applications where space is restricted. W$_2$B is an excellent attenuator of neutrons and gamma-rays, due to the combined gamma attenuation of W and neutron absorption of B. However, its low fracture toughness (~3.5 MPa$\cdot$m$^{0.5}$) and high melting point (2670 °C) prevent the fabrication of large fully-dense monolithic parts with adequate…
▽ More
We have developed a new material for neutron shielding applications where space is restricted. W$_2$B is an excellent attenuator of neutrons and gamma-rays, due to the combined gamma attenuation of W and neutron absorption of B. However, its low fracture toughness (~3.5 MPa$\cdot$m$^{0.5}$) and high melting point (2670 °C) prevent the fabrication of large fully-dense monolithic parts with adequate mechanical properties. Here we meet these challenges by combining W$_2$B with a minor fraction (43 vol.%) of metallic W. The material was produced by reaction sintering W and BN powders. The mechanical properties under flexural and compressive loading were determined up to 1900 °C. The presence of the ductile metallic W phase enabled a peak flexural strength of ~950 MPa at 1100 °C, which is a factor of 2-3 higher than typical monolithic transition-metal borides. Its ductile-brittle transition temperature of ~1000 °C is typical of W-based composites, which is surprising as the W phase was the minor constituent and did not appear to form a fully continuous network. Compression tests showed hardening below ~1500 °C and significant elongation of the phase domains, which suggest that by forging or rolling, further improvements in ductility may be possible.
△ Less
Submitted 10 December, 2019;
originally announced December 2019.