Sub-100 nm Skyrmions at Zero Magnetic Field in Ir/Fe/Co/Pt Nanostructures
Authors:
Pin Ho,
Anthony K. C. Tan,
S. Goolaup,
A. L. Gonzalez Oyarce,
M. Raju,
L. S. Huang,
Anjan Soumyanarayanan,
C. Panagopoulos
Abstract:
Magnetic skyrmions are chiral spin structures that have recently been observed at room temperature (RT) in multilayer thin films. Their topological stability should enable high scalability in confined geometries - a sought-after attribute for device applications. While umpteen theoretical predictions have been made regarding the phenomenology of sub-100 nm skyrmions confined in dots, in practice t…
▽ More
Magnetic skyrmions are chiral spin structures that have recently been observed at room temperature (RT) in multilayer thin films. Their topological stability should enable high scalability in confined geometries - a sought-after attribute for device applications. While umpteen theoretical predictions have been made regarding the phenomenology of sub-100 nm skyrmions confined in dots, in practice their formation in the absence of an external magnetic field and evolution with confinement remain to be established. Here we demonstrate the confinement-induced stabilization of sub-100 nm RT skyrmions at zero field (ZF) in Ir/Fe(x)/Co(y)/Pt nanodots over a wide range of magnetic and geometric parameters. The ZF skyrmion size can be as small as ~50 nm, and varies by a factor of 4 with dot size and magnetic parameters. Crucially, skyrmions with varying thermodynamic stability exhibit markedly different confinement phenomenologies. These results establish a comprehensive foundation for skyrmion phenomenology in nanostructures, and provide immediate directions for exploiting their properties in nanoscale devices.
△ Less
Submitted 14 September, 2017;
originally announced September 2017.
Origin of the two-dimensional electron gas at LaAlO3/SrTiO3 interfaces: The role of oxygen vacancies and electronic reconstruction
Authors:
Z. Q. Liu,
C. J. Li,
W. M. Lü,
X. H. Huang,
Z. Huang,
S. W. Zeng,
X. P. Qiu,
L. S. Huang,
A. Annadi,
J. S. Chen,
J. M. D. Coey,
T. Venkatesan,
Ariando
Abstract:
The relative importance of atomic defects and electron transfer in explaining conductivity at the crystalline LaAlO3/SrTiO3 interface has been a topic of debate. Metallic interfaces with similar electronic properties produced by amorphous oxide overlayers on SrTiO3 have called in question the original polarization catastrophe model. We resolve the issue by a comprehensive comparison of (100)-orien…
▽ More
The relative importance of atomic defects and electron transfer in explaining conductivity at the crystalline LaAlO3/SrTiO3 interface has been a topic of debate. Metallic interfaces with similar electronic properties produced by amorphous oxide overlayers on SrTiO3 have called in question the original polarization catastrophe model. We resolve the issue by a comprehensive comparison of (100)-oriented SrTiO3 substrates with crystalline and amorphous overlayers of LaAlO3 of different thicknesses prepared under different oxygen pressures. For both types of overlayers, there is a critical thickness for the appearance of conductivity, but its value is always 4 unit cells (around 1.6 nm) for the oxygen-annealed crystalline case, whereas in the amorphous case, the critical thickness could be varied in the range 0.5 to 6 nm according to the deposition conditions. Subsequent ion milling of the overlayer restores the insulating state for the oxygen-annealed crystalline heterostructures but not for the amorphous ones. Oxygen post-annealing removes the oxygen vacancies, and the interfaces become insulating in the amorphous case. However, the interfaces with a crystalline overlayer remain conducting with reduced carrier density. These results demonstrate that oxygen vacancies are the dominant source of mobile carriers when the LaAlO3 overlayer is amorphous, while both oxygen vacancies and polarization catastrophe contribute to the interface conductivity in unannealed crystalline LaAlO3/SrTiO3 heterostructures, and the polarization catastrophe alone accounts for the conductivity in oxygen-annealed crystalline LaAlO3/SrTiO3 heterostructures. Furthermore, we find that the crystallinity of the LaAlO3 layer is crucial for the polarization catastrophe mechanism in the case of crystalline LaAlO3 overlayers.
△ Less
Submitted 30 May, 2013; v1 submitted 22 May, 2013;
originally announced May 2013.