Microstructure and superconducting properties of hot isostatically pressed MgB2

Authors: T C Shields, K Kawano, D Holdom, J S Abell

Abstract: Bulk samples of MgB2 have been formed by hot isostatic pressing (HIP**) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have indicated the presence of small amounts of second phases within the material, namely MgO and B rich compositions, probably MgB4. Magnetisation measurements performe… ▽ More Bulk samples of MgB2 have been formed by hot isostatic pressing (HIP**) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have indicated the presence of small amounts of second phases within the material, namely MgO and B rich compositions, probably MgB4. Magnetisation measurements performed at 20K have revealed values of Jc=1.3 x 106A/cm2 at zero field, and 9.3 x 105A/cm2 at 1T. Magneto optical (MO) studies have shown direct evidence for the superconducting homogeneity and strong intergranular current flow in the material. △ Less

Submitted 16 July, 2001; v1 submitted 2 July, 2001; originally announced July 2001.

Comments: 3 pages, 6 figures, text updated, new references included and discussed. Submitted to Superconductor Science and Technology

Journal ref: Superconductor Science and Technology 15(2002)202