High chemical activity of a perovskite surface: reaction of CO with Sr$_3$Ru$_2$O$_7$
Authors:
Bernhard Stöger,
Marcel Hieckel,
Florian Mittendorfer,
Zhiming Wang,
David Fobes,
** Peng,
Zhiqiang Mao,
Michael Schmid,
Josef Redinger,
Ulrike Diebold
Abstract:
Adsorption of CO at the Sr$_3$Ru$_2$O$_7$(001) surface was studied with low-temperature scanning tunneling microscopy (STM) and density functional theory. In situ cleaved single crystals terminate in an almost perfect SrO surface. At 78 K, CO first populates impurities and then adsorbs above the apical surface O with a binding energy E$_\mathrm{ads}$=-0.7 eV. Above 100 K, this physisorbed CO repla…
▽ More
Adsorption of CO at the Sr$_3$Ru$_2$O$_7$(001) surface was studied with low-temperature scanning tunneling microscopy (STM) and density functional theory. In situ cleaved single crystals terminate in an almost perfect SrO surface. At 78 K, CO first populates impurities and then adsorbs above the apical surface O with a binding energy E$_\mathrm{ads}$=-0.7 eV. Above 100 K, this physisorbed CO replaces the surface O, forming a bent CO2 with the C end bound to the Ru underneath. The resulting metal carboxylate (Ru-COO) can be desorbed by STM manipulation. A low activation (0.2 eV) and high binding (-2.2 eV) energy confirm a strong reaction between CO and regular surface sites of Sr$_3$Ru$_2$O$_7$; likely, this reaction causes the "UHV aging effect" reported for this and other perovskite oxides.
△ Less
Submitted 12 April, 2018;
originally announced April 2018.
-
Point defects at cleaved Sr$_{n+1}$Ru$_n$O$_{3n+1}$(001) surfaces
Authors:
Bernhard Stöger,
Marcel Hieckel,
Florian Mittendorfer,
Zhiming Wang,
Michael Schmid,
Gareth S. Parkinson,
David Fobes,
** Peng,
John. E. Ortmann,
Andreas Limbeck,
Zhiqiang Mao,
Josef Redinger,
Ulrike Diebold
Abstract:
The (001) surfaces of cleaved Sr$_3$Ru$_2$O$_7$ and Sr$_2$RuO$_4$ samples were investigated using low-temperature scanning tunneling microscopy and density functional theory calculations. Intrinsic defects are not created during cleaving. This experimental observation is consistent with calculations, where the formation energy for a Sr and O vacancy, 4.19 eV and 3.81 eV, respectively, is significa…
▽ More
The (001) surfaces of cleaved Sr$_3$Ru$_2$O$_7$ and Sr$_2$RuO$_4$ samples were investigated using low-temperature scanning tunneling microscopy and density functional theory calculations. Intrinsic defects are not created during cleaving. This experimental observation is consistent with calculations, where the formation energy for a Sr and O vacancy, 4.19 eV and 3.81 eV, respectively, is significantly larger than that required to cleave the crystal, 1.11 eV/(1 $\times$ 1) unit cell. Surface oxygen vacancies can be created through electron bombardment, however, and their appearance is shown to vary strongly with the imaging conditions. Point defects observed on as-cleaved surfaces result from bulk impurities and adsorption from the residual gas.
△ Less
Submitted 12 April, 2018;
originally announced April 2018.
-
Transition from reconstruction towards thin film on the (110) surface of strontium titanate
Authors:
Z. Wang,
A. Loon,
A. Subramanian,
S. Gerhold,
E. McDermott,
J. A. Enterkin,
M. Hieckel,
B. C. Russell,
R. J. Green,
A. Moewes,
J. Guo,
P. Blaha,
M. R. Castell,
U. Diebold,
L. D. Marks
Abstract:
The surfaces of metal oxides often are reconstructed with a geometry and composition that is considerably different from a simple termination of the bulk. Such structures can also be viewed as ultrathin films, epitaxed on a substrate. Here, the reconstructions of the SrTiO3 (110) surface are studied combining scanning tunneling microscopy, transmission electron diffraction, and X-ray absorption sp…
▽ More
The surfaces of metal oxides often are reconstructed with a geometry and composition that is considerably different from a simple termination of the bulk. Such structures can also be viewed as ultrathin films, epitaxed on a substrate. Here, the reconstructions of the SrTiO3 (110) surface are studied combining scanning tunneling microscopy, transmission electron diffraction, and X-ray absorption spectroscopy, and analyzed with density functional theory calculations. While SrTiO3 (110) invariably terminates with an overlayer of titania, with increasing density its structure switches from nx1 and 2xn. At the same time the coordination of the Ti atoms changes from a network of corner-sharing tetrahedra to a double layer of edge-shared octahedra with bridging units of octahedrally coordinated strontium. This transition from the nx1 to 2xn reconstructions is a transition from a pseudomorphically stabilized tetrahedral network towards an octahedral titania thin film with stress-relief from octahedral strontia units at the surface.
△ Less
Submitted 10 February, 2016;
originally announced February 2016.