Anomalous thermal expansion in one-dimensional transition-metal cyanides: Behavior of the trimetallic cyanide Cu$_{1/3}$Ag$_{1/3}$Au$_{1/3}$CN
Authors:
Stella d'Ambrumenil,
Mohamed Zbiri,
Simon J. Hibble,
Ann M. Chippindale,
Dean S. Keeble,
Camille Wright,
Nicholas H. Rees
Abstract:
The structural dynamics of a 1D mixed-metal cyanide, Cu$_{1/3}$Ag$_{1/3}$Au$_{1/3}$CN, with intriguing thermal properties is explored. All the current known related compounds with straight-chain structures, such as CuCN, AgCN, AuCN and M$_x$M'$_{1-x}$CN (M, M' = Cu, Ag, Au), exhibit 1D negative thermal expansion (NTE) along the chains and positive thermal expansion (PTE) perpendicular to them. Cu…
▽ More
The structural dynamics of a 1D mixed-metal cyanide, Cu$_{1/3}$Ag$_{1/3}$Au$_{1/3}$CN, with intriguing thermal properties is explored. All the current known related compounds with straight-chain structures, such as CuCN, AgCN, AuCN and M$_x$M'$_{1-x}$CN (M, M' = Cu, Ag, Au), exhibit 1D negative thermal expansion (NTE) along the chains and positive thermal expansion (PTE) perpendicular to them. Cu$_{1/3}$Ag$_{1/3}$Au$_{1/3}$CN exhibits similar PTE perpendicular to the chains, however PTE, rather than NTE, is also observed along the chains. In order to understand the origin of this unexpected behavior, inelastic neutron scattering (INS) measurements were carried out, underpinned by DFT calculations. Synchrotron-based PDF analysis and 13C SSNMR measurements were also performed to build an input structural model for the lattice dynamical study. The results indicate that transverse motions of the metal ions are responsible for the PTE perpendicular to the chains, as is the case for the related group 11 cyanides. However NTE along the chain due to the tension effect of these transverse motions is not observed. For this system, DFT-based phonon calculations predict small PTE along the chain due to low-energy chain-slip** modes induced by a bond-rotation effect on the weak metallophilic bonds. However the observed PTE is greater than that predicted with the straight-chain model. Small bends in the chain to accommodate truly co-planar metals provide an alternative explanation for thermal behavior. These would mitigate the tension effect induced by the transverse motions of the metals and, as temperature increases and the chains move further apart, a straightening could occur resulting in the observed PTE. This hypothesis is further supported by unusual evolution in the phonon spectra, which suggest small changes in local symmetry with temperature.
△ Less
Submitted 20 November, 2019; v1 submitted 1 October, 2019;
originally announced October 2019.
-
Lattice dynamics and negative thermal expansion in the framework compound ZnNi(CN)$_4$ with two-dimensional and three-dimensional local environments
Authors:
Stella d'Ambrumenil,
Mohamed Zbiri,
Ann M. Chippindale,
Simon J. Hibble,
Elena Marelli,
Alex C. Hannon
Abstract:
ZnNi(CN)$_4$ is a 3D framework material consisting of two interpenetrating PtS-type networks in which tetrahedral [ZnN$_4$] units are linked by square-planar [NiC$_4$] units. Both the parent compounds, cubic Zn(CN)$_2$ and layered Ni(CN)$_2$, are known to exhibit 3D and 2D negative thermal expansion (NTE), respectively. Temperature-dependent inelastic neutron scattering measurements were performed…
▽ More
ZnNi(CN)$_4$ is a 3D framework material consisting of two interpenetrating PtS-type networks in which tetrahedral [ZnN$_4$] units are linked by square-planar [NiC$_4$] units. Both the parent compounds, cubic Zn(CN)$_2$ and layered Ni(CN)$_2$, are known to exhibit 3D and 2D negative thermal expansion (NTE), respectively. Temperature-dependent inelastic neutron scattering measurements were performed on a powdered sample of ZnNi(CN)$_4$ to probe phonon dynamics. The measurements were underpinned by ab initio lattice dynamical calculations. Good agreement was found between the measured and calculated generalized phonon density-of-states, validating our theoretical model and indicating that it is a good representation of the dynamics of the structural units. The calculated linear thermal expansion coefficients are $α_a$=-21.2 $\times$ 10$^{-6}$ K$^{-1}$ and $α_c$=+14.6$\times$10$^{-6}$K$^{-1}$, leading to an overall volume expansion coefficient $α_V$ of -26.95$\times$10$^{-6}$K$^{-1}$, pointing towards pronounced NTE behavior. Analysis of the derived mode-Grüneisen parameters shows that optic modes around 12 and 40 meV make a significant contribution to NTE. These modes involve localized rotational motions of the [NiC$_4$] and/or [ZnN$_4$] rigid units, echoing what has previously been observed in Zn(CN)$_2$ and Ni(CN)$_2$. However, in ZnNi(CN)$_4$, modes below 10 meV have the most negative Grüneisen parameters. Analysis of their eigenvectors reveals that a large transverse motion of the Ni atom in the direction perpendicular to its square-planar environment induces a distortion of the units. This mode is a consequence of the Ni atom being constrained only in 2D within a 3D framework. Hence, although rigid-unit modes account for some of the NTE-driving phonons, the added d-o-f compared with Zn(CN)$_2$ results in modes with twisting motions, capable of inducing greater NTE.
△ Less
Submitted 22 January, 2019; v1 submitted 7 September, 2018;
originally announced September 2018.
-
New Insights into the Compressibility and High-Pressure Stability of Ni(CN)2 from Neutron Diffraction, Raman Spectroscopy and Inelastic Neutron Scattering
Authors:
S. K. Mishra,
R. Mittal,
M. Zbiri,
Rekha Rao,
Prabhatasree Goel,
S. J. Hibble,
A. M. Chippindale,
T. Hansen,
H. Schober,
S. L. Chaplot
Abstract:
The layered structure of tetragonal Ni(CN)2, consisting of square-planar Ni(CN)4 units linked in the a-b plane, with no true periodicity along the c-axis, is expected to show anisotropic compression on the application of pressure. High-pressure neutron diffraction (elastic) and inelastic neutron scattering experiments have been performed on polycrystalline Ni(CN)2 to investigate its compressibilit…
▽ More
The layered structure of tetragonal Ni(CN)2, consisting of square-planar Ni(CN)4 units linked in the a-b plane, with no true periodicity along the c-axis, is expected to show anisotropic compression on the application of pressure. High-pressure neutron diffraction (elastic) and inelastic neutron scattering experiments have been performed on polycrystalline Ni(CN)2 to investigate its compressibility and stability. The intralayer a lattice parameter does not show any appreciable variation with increase of pressure up to 2.7 kbar. Above this pressure value, a decrease in a is observed. The c lattice parameter decreases slowly up to 1 kbar, then decreases sharply up to 20 kbar. It does not show any significant variation with further pressure increase up to 50 kbar. The response of the lattice parameters to the applied pressure is strongly anisotropic as the interlayer spacing (along the c-axis) shows a significantly larger contraction than the a-b plane. The experimental pressure dependence of the volume data is fitted to a bulk modulus, B0, of 1050 (20) kbar over the pressure range 0-1 kbar, and to 154 (2) kbar in the range 1-50 kbar. The change in the slope of the lattice parameters at 1 kbar is also supported by high-pressure Raman measurements, which indicate a phase transition at 1 kbar. Probably arising from a change in the CN ordering within the Ni(CN)2 layers. Raman measurements, performed up to 200 kbar, highlight the possible existence of a second phase transition taking place at about 70 kbar. Our neutron inelastic scattering measurements of the pressure dependence of the phonon spectra performed up to 2.7 kbar, also support the occurrence of a phase transition at low pressure.
△ Less
Submitted 14 July, 2015; v1 submitted 8 September, 2014;
originally announced September 2014.
-
Relationship Between Phonons and Thermal Expansion in Zn(CN)2 and Ni(CN)2 from Inelastic Neutron Scattering and Ab-Initio Calculations
Authors:
R Mittal,
M. Zbiri,
H. Schober,
E Marelli,
S. J. Hibble,
A. M. Chippindale,
S. L Chaplot
Abstract:
Zn(CN)2 and Ni(CN)2 are known for exhibiting anomalous thermal expansion over a wide temperature range. The volume thermal expansion coefficient for the cubic, three dimensionally connected material, Zn(CN)2, is negative (αV = -51 x 10-6 K-1) while for Ni(CN)2, a tetragonal material, the thermal expansion coefficient is negative in the two dimensionally connected sheets (αa=-7 x 10-6 K-1), but the…
▽ More
Zn(CN)2 and Ni(CN)2 are known for exhibiting anomalous thermal expansion over a wide temperature range. The volume thermal expansion coefficient for the cubic, three dimensionally connected material, Zn(CN)2, is negative (αV = -51 x 10-6 K-1) while for Ni(CN)2, a tetragonal material, the thermal expansion coefficient is negative in the two dimensionally connected sheets (αa=-7 x 10-6 K-1), but the overall thermal expansion coefficient is positive (αV=48 x 10-6 K-1). We have measured the temperature dependence of phonon spectra in these compounds and analyzed them using ab-initio calculations. The spectra of the two compounds show large differences that cannot be explained by simple mass renormalization of the modes involving Zn (65.38 amu) and Ni (58.69 amu) atoms. This reflects the fact that the structure and bonding are quite different in the two compounds. The calculated pressure dependence of the phonon modes and of the thermal expansion coefficient, αV, are used to understand the anomalous behavior in these compounds. Our ab-initio calculations indicate that it is the low-energy rotational modes in Zn(CN)2, which are shifted to higher energies in Ni(CN)2, that are responsible for the large negative thermal expansion. The measured temperature dependence of the phonon spectra has been used to estimate the total anharmonicity of both compounds. For Zn(CN)2, the temperature- dependent measurements (total anharmonicity), along with our previously reported pressure dependence of the phonon spectra (quasiharmonic), is used to separate the explicit temperature effect at constant volume (intrinsic anharmonicity).
△ Less
Submitted 28 September, 2010;
originally announced September 2010.