Hop** magnetoresistance in ion irradiated monolayer graphene
Authors:
I. Shlimak,
E. Zion,
A. V. Butenko,
L. Wolfson,
V. Richter,
Yu. Kaganovskii,
A. Sharoni,
A. Haran,
D. Naveh,
E. Kogan,
M. Kaveh
Abstract:
Magnetoresistance (MR) of ion irradiated monolayer graphene samples with variable-range hop** (VRH) mechanism of conductivity was measured at temperatures down to $T = 1.8$ K in magnetic fields up to $B = 8$ T. It was observed that in perpendicular magnetic fields, hop** resistivity $R$ decreases, which corresponds to negative MR (NMR), while parallel magnetic field results in positive MR (PMR…
▽ More
Magnetoresistance (MR) of ion irradiated monolayer graphene samples with variable-range hop** (VRH) mechanism of conductivity was measured at temperatures down to $T = 1.8$ K in magnetic fields up to $B = 8$ T. It was observed that in perpendicular magnetic fields, hop** resistivity $R$ decreases, which corresponds to negative MR (NMR), while parallel magnetic field results in positive MR (PMR) at low temperatures. NMR is explained on the basis of the "orbital" model in which perpendicular magnetic field suppresses the destructive interference of many paths through the intermediate sites in the total probability of the long-distance tunneling in the VRH regime. At low fields, a quadratic dependence ($|ΔR/R|\sim B^2$) of NMR is observed, while at $B > B^*$, the quadratic dependence is replaced by the linear one. It was found that all NMR curves for different samples and different temperatures could be merged into common dependence when plotted as a function of $B/B^*$. It is shown that $B^*\sim T^{1/2}$ in agreement with predictions of the "orbital" model. The obtained values of $B^*$ allowed also to estimate the localization radius $ξ$ of charge carriers for samples with different degree of disorder. PMR in parallel magnetic fields is explained by suppression of hop** transitions via double occupied states due to alignment of electron spins.
△ Less
Submitted 23 October, 2015; v1 submitted 6 July, 2015;
originally announced July 2015.
-
Localization of charge carriers in monolayer graphene gradually disordered by ion irradiation
Authors:
E. Zion,
A. Haran,
A. V. Butenko,
L. Wolfson,
Yu. Kaganovskii,
T. Havdala,
A. Sharoni,
D. Naveh,
V. Richter,
M. Kaveh,
E. Kogan,
I. Shlimak
Abstract:
Gradual localization of charge carriers was studied in a series of micro-size samples of monolayer graphene fabricated on the common large scale film and irradiated by different doses of C$^+$ ions with energy 35 keV. Measurements of the temperature dependence of conductivity and magnetoresistance in fields up to 4 T showed that at low disorder, the samples are in the regime of weak localization a…
▽ More
Gradual localization of charge carriers was studied in a series of micro-size samples of monolayer graphene fabricated on the common large scale film and irradiated by different doses of C$^+$ ions with energy 35 keV. Measurements of the temperature dependence of conductivity and magnetoresistance in fields up to 4 T showed that at low disorder, the samples are in the regime of weak localization and antilocalization. Further increase of disorder leads to strong localization regime, when conductivity is described by the variable-range-hop** (VRH) mechanism. A crossover from the Mott regime to the Efros-Shklovskii regime of VRH is observed with decreasing temperature. Theoretical analysis of conductivity in both regimes showed a remarkably good agreement with experimental data.
△ Less
Submitted 14 May, 2015; v1 submitted 19 January, 2015;
originally announced January 2015.
-
Raman scattering and electrical resistance of highly disordered graphene
Authors:
I. Shlimak,
A. Haran,
E. Zion,
T. Havdala,
Yu. Kaganovskii,
A. V. Butenko,
L. Wolfson,
V. Richter,
D. Naveh,
A. Sharoni,
E. Kogan,
M. Kaveh
Abstract:
Raman scattering (RS) spectra and current-voltage characteristics at room temperature were measured in six series of small samples fabricated by means of electron-beam lithography on the surface of a large size (5x5 mm) industrial monolayer graphene film. Samples were irradiated by different doses of C${}^+$ ion beam up to $10^{15}$ cm${}^{-2}$. It was observed that at the utmost degree of disorde…
▽ More
Raman scattering (RS) spectra and current-voltage characteristics at room temperature were measured in six series of small samples fabricated by means of electron-beam lithography on the surface of a large size (5x5 mm) industrial monolayer graphene film. Samples were irradiated by different doses of C${}^+$ ion beam up to $10^{15}$ cm${}^{-2}$. It was observed that at the utmost degree of disorder, the Raman spectra lines disappear which is accompanied by the exponential increase of resistance and change in the current-voltage characteristics.These effects are explained by suggestion that highly disordered graphene film ceases to be a continuous and splits into separate fragments. The relationship between structure (intensity of RS lines) and sample resistance is defined. It is shown that the maximal resistance of the continuous film is of order of reciprocal value of the minimal graphene conductivity $πh/4e^2\approx 20$ kOhm.
△ Less
Submitted 2 January, 2015; v1 submitted 13 October, 2014;
originally announced October 2014.