Low Temperature Ageing Behaviour of U-Nb $α''$ Phase Alloys
Authors:
JE Sutcliffe,
CP Jones,
JE Darnbrough,
KR Hallam,
RS Springell,
P Ryan,
T Cartwright,
TB Scott
Abstract:
Ageing mechanisms of the U-5\,\%wtNb system have been investigated on samples exposed to temperatures of 150$\,^{\circ}$C for up to 5000\,hours. A variety of surface and bulk analytic techniques have been used to investigate phase, chemical and crystallographic changes. Characterisation of microstructural evolution was carried out through secondary electron microscopy (SEM), energy dispersive x-ra…
▽ More
Ageing mechanisms of the U-5\,\%wtNb system have been investigated on samples exposed to temperatures of 150$\,^{\circ}$C for up to 5000\,hours. A variety of surface and bulk analytic techniques have been used to investigate phase, chemical and crystallographic changes. Characterisation of microstructural evolution was carried out through secondary electron microscopy (SEM), energy dispersive x-ray spectroscopy (EDS), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM) and x-ray diffraction (XRD). This investigation suggests crystallographic defects such as twinning furthers the martensitic tendencies with ageing. Resizing of the lattice and shuffling of atoms results in a small progression from the $α''$ towards the $α'$ phase.
△ Less
Submitted 15 March, 2018;
originally announced March 2018.
Low Temperature Ageing Behaviour of U-Nb $γ^{o}$ Phase Alloys
Authors:
JE Sutcliffe,
CP Jones,
JE Darnbrough,
KR Hallam,
RS Springell,
P Ryan,
T Cartwright,
TB Scott
Abstract:
Ageing mechanisms of the U-7\%wtNb alloy have been investigated on samples exposed to temperatures of 150$^{o}$C for up to 5000\,hours. A variety of surface and bulk analytic techniques have been used to investigate microstructural, chemical and crystallographic changes. Characterisation of the alloy's evolving behaviour was carried out through secondary electron microscopy, energy dispersive x-ra…
▽ More
Ageing mechanisms of the U-7\%wtNb alloy have been investigated on samples exposed to temperatures of 150$^{o}$C for up to 5000\,hours. A variety of surface and bulk analytic techniques have been used to investigate microstructural, chemical and crystallographic changes. Characterisation of the alloy's evolving behaviour was carried out through secondary electron microscopy, energy dispersive x-ray spectroscopy, electron backscatter diffraction, transmission electron microscopy and x-ray diffraction. Vickers hardness testing showed evidence of a strong thermal hardening relationship with ageing. The mechanism responsible for these changes is thought to be a stress-induced isothermal martensitic transformation; a displacive reaction, in which correlated shuffling of atoms creates a phase change from $γ^{o}$ to $α''$ without chemical species redistribution.
△ Less
Submitted 15 March, 2018;
originally announced March 2018.