Multifilamentary character of anticorrelated capacitive and resistive switching in memristive structures based on (CoFeB)x(LiNbO3)100-x nanocomposite
Authors:
M. N. Martyshov,
A. V. Emelyanov,
V. A. Demin,
K. E. Nikiruy,
A. A. Minnekhanov,
S. N. Nikolaev,
A. N. Taldenkov,
A. V. Ovcharov,
M. Yu. Presnyakov,
A. V. Sitnikov,
A. L. Vasiliev,
P. A. Forsh,
A. B. Granovskiy,
P. K. Kashkarov,
M. V. Kovalchuk,
V. V. Rylkov
Abstract:
Resistive and capacitive switching in capacitor metal/nanocomposite/metal (M/NC/M) structures based on (CoFeB)x(LiNbO3)100-x NC fabricated by ion-beam sputtering with metal content x $\approx$ 8-20 at. % is studied. The peculiarity of the structure synthesis was the use of increased oxygen content ($\approx$ 2*10^-5 Torr) at the initial stage of the NC growth. The NC films, along with metal nanogr…
▽ More
Resistive and capacitive switching in capacitor metal/nanocomposite/metal (M/NC/M) structures based on (CoFeB)x(LiNbO3)100-x NC fabricated by ion-beam sputtering with metal content x $\approx$ 8-20 at. % is studied. The peculiarity of the structure synthesis was the use of increased oxygen content ($\approx$ 2*10^-5 Torr) at the initial stage of the NC growth. The NC films, along with metal nanogranules of 3-6 nm in size, contained a large number of dispersed Co (Fe) atoms (up to ~10^22 cm^-3). Measurements were performed both in DC and AC (frequency range 5-13 MHz) regimes. When switching structures from high-resistance (Roff) to low-resistance (Ron) state, the effect of a strong increase in their capacity was found, which reaches 8 times at x $\approx$ 15 at. % and the resistance ratio Roff/Ron $\approx$ 40. The effect is explained by the synergetic combination of the multifilamentary character of resistive switching (RS) and structural features of the samples associated, in particular, with the formation of high-resistance and strongly polarizable LiNbO3 layer near the bottom electrode of the structures. The proposed model is confirmed by investigations of RS of two-layer nanoscale M/NC/LiNbO3/M structures as well as by studies of the magnetization of M/NC/M structures in the pristine state and after RS.
△ Less