Impact of cation redox chemistry on continuous hydrothermal synthesis of 2D-Ni(Co/Fe) hydroxides
Authors:
Massimo Rosa,
Debora Marani,
Giovanni Perin,
Søren Bredmose Simonsen,
Philipp Zielke,
Antonella Glisenti,
Ragnar Kiebach,
Andreas Lesch,
Vincenzo Esposito
Abstract:
Continuous hydrothermal flow synthesis (CHFS) is a facile, upscalable and cost-efficient synthetic method enabling the nanostructuring of advanced functional materials in steady conditions, i.e. not in batch synthesis. In this paper, we use CHFS to crystallize NiCo- and NiFe-hydroxides in water solution with 2D nanofeatures. By tuning the synthetic parameters, we disclose the key role of the catio…
▽ More
Continuous hydrothermal flow synthesis (CHFS) is a facile, upscalable and cost-efficient synthetic method enabling the nanostructuring of advanced functional materials in steady conditions, i.e. not in batch synthesis. In this paper, we use CHFS to crystallize NiCo- and NiFe-hydroxides in water solution with 2D nanofeatures. By tuning the synthetic parameters, we disclose the key role of the cation redox chemistry in the transition between two competitive phases: from 2D-nanoplatelets of brucite to layered double hydroxides (LDH). For controlling the precipitation of different Ni, Fe, Co-hydroxide phases, we propose the combined use of an oxidizing (H2O2) and a complexing (NH3) agent. At temperatures as low as 80 °C, the presence of H2O2 and a low concentration of NH3 favour the Ni2+/Co3+ over Ni2+/Co2+ oxidation states, shifting the product structure from brucite phase (temperatures > 80 °C) to LDH. Conversely, for the NiFe-hydroxides the transition from LDH (temperatures < 80 °C) to brucite phase (temperatures > 80 °C) is controlled by the reaction temperature only. Due to the high stability of Fe3+, the synthesis of NiFe products by CHFS does not require oxidizing and complexing agents, resulting in a robust process for large-scale production.
△ Less
Submitted 11 October, 2019;
originally announced October 2019.
Gd0.2Ce0.8O1.9/Y0.16Zr0.84O1.92 nanocomposite thin films for low temperature ionic conductivity
Authors:
Giovanni Perin,
Christophe Gadea,
Massimo Rosa,
Simone Sanna,
Yu Xu,
Ragnar Kiebach,
Antonella Glisenti,
Vincenzo Esposito
Abstract:
Gd0.2Ce0.8O1.9/Y0.16Zr0.84O1.92 (GDC/YSZ) nanocomposite is synthesized by a novel hybrid chemical route, where colloidal crystalline GDC nanoparticles from continuous hydrothermal synthesis are dispersed into a metalorganic YSZ matrix precursor. The result is a mixture of metal oxides in which GDC nanoparticles are finely distributed in a continuous metalorganic polymeric matrix to be crystallized…
▽ More
Gd0.2Ce0.8O1.9/Y0.16Zr0.84O1.92 (GDC/YSZ) nanocomposite is synthesized by a novel hybrid chemical route, where colloidal crystalline GDC nanoparticles from continuous hydrothermal synthesis are dispersed into a metalorganic YSZ matrix precursor. The result is a mixture of metal oxides in which GDC nanoparticles are finely distributed in a continuous metalorganic polymeric matrix to be crystallized after calcination. The GDC nanoparticles reduce the temperature necessary to obtain crystalline YSZ, which is already formed at 400 °C. The nanocomposite reveals structural stability up to 800 °C when treated in both air and reducing atmosphere, showing the onset of diffusion below 1000 °C. The diffusional processes are largely dependent on the nanometric grain size, with Zr4+ diffusing abruptly towards GDC in air at 1000 °C and GDC/YSZ interdiffusion being hindered in reducing environment despite the onset temperature of 900 °C. The nanocomposite precursor is an inkjet-printable reactive water-based material, suitable for the deposition of thin films with a thickness below 100 nm after calcination at 750 °C. The crystal structure of the film reveals no interaction between GDC and YSZ but a microstrain (0.3% tensile strain for YSZ). The thin film microstructure shows a compact layer with 94% density. The nanocomposite shows high oxygen ionic conductivity at low temperatures (> 5 * 10-3 S cm-1 at 500 °C), low activation energy (0.55 eV), and dominant oxygen ionic conductivity even in reducing conditions (pO2 < 10-25 atm). We show that these properties arise from the large interface between the components of the composite, due to the embedding of the GDC nanoparticles in the YSZ matrix, while ZrO-CeO intermixing can be avoided and no n-type conductivity is observed even at low oxygen activities and high temperatures.
△ Less
Submitted 15 April, 2019;
originally announced April 2019.