High-throughput assessment of the microstructural stability of segregation-engineered nanocrystalline Al-Ni-Y alloys
Authors:
W. Streit Cunningham,
Jungho Shin,
Tianjiao Lei,
Timothy J Rupert,
Daniel S. Gianola
Abstract:
Segregation engineering has emerged as a promising pathway towards designing thermally stable nanocrystalline alloys with enhanced mechanical properties. However, the compositional and processing space for solute stabilized microstructures is vast, thus the application of high-throughput techniques to accelerate optimal material development is increasingly attractive. In this work, combinatorial s…
▽ More
Segregation engineering has emerged as a promising pathway towards designing thermally stable nanocrystalline alloys with enhanced mechanical properties. However, the compositional and processing space for solute stabilized microstructures is vast, thus the application of high-throughput techniques to accelerate optimal material development is increasingly attractive. In this work, combinatorial synthesis is combined with high-throughput characterization techniques to explore microstructural transitions through annealing of a nanocrystalline ternary Al-base alloy containing a transition metal (TM=Ni) and rare earth dopant (RE=Y). A down-selected optimal composition with the highest thermal stability is annealed through in situ transmission electron microscopy, revealing that the removal of the RE species is correlated to a reduction in the microstructural stability at high temperatures as a result of variations in intermetallic phase formation. Results demonstrate the benefits of co-segregation for enhancing mechanical hardness and delaying the onset of microstructural instability.
△ Less
Submitted 30 August, 2023;
originally announced August 2023.
-
Strengthening from dislocation restructuring and local climb at platelet linear complexions in Al-Cu alloys
Authors:
Pulkit Garg,
Daniel S. Gianola,
Timothy J. Rupert
Abstract:
Stress-driven segregation at dislocations can lead to structural transitions between different linear complexion states. In this work, we examine how platelet array linear complexions influence dislocation motion and quantify the associated strengthening effect in Al-Cu alloys using atomistic simulations. The presence of platelet complexions leads to faceting of the dislocations, with nanoscale se…
▽ More
Stress-driven segregation at dislocations can lead to structural transitions between different linear complexion states. In this work, we examine how platelet array linear complexions influence dislocation motion and quantify the associated strengthening effect in Al-Cu alloys using atomistic simulations. The presence of platelet complexions leads to faceting of the dislocations, with nanoscale segments climbing upwards along the platelet growth direction, resulting in a complex non-planar configuration that restricts subsequent dislocation motion. Upon deformation, the leading partial dislocation must climb down from the platelet complexions first, followed by a similar sequence at the trailing partial dislocation, in order to overcome the precipitates and commence plastic slip. The dislocation depinning mechanism of linear complexions is strikingly different from traditional precipitation-strengthened alloys, where dislocations overcome obstacles by either shearing through or loo** around obstacles. The critical shear stress required to unpin dislocations from platelet complexions is found to be inversely proportional to precipitate spacing, which includes not just the open space (as observed in Orowan bowing) but also the region along the platelet particle where climb occurs. Thus, platelet linear complexions provide a new way to modify dislocation structure directly and improve the mechanical properties of metal alloys.
△ Less
Submitted 9 April, 2024; v1 submitted 30 August, 2023;
originally announced August 2023.
-
Dislocation breakaway from nanoparticle array linear complexions: Plasticity mechanisms and strength scaling laws
Authors:
Divya Singh,
Daniel S. Gianola,
Timothy J. Rupert
Abstract:
Linear complexions are stable defect states, where the stress field associated with a dislocation induces a local phase transformation that remains restricted to nanoscale dimensions. As these complexions are born at the defects which control plasticity in metals, it is crucial to understand their impact on subsequent mechanical properties. In this work, atomistic modeling is used to understand ho…
▽ More
Linear complexions are stable defect states, where the stress field associated with a dislocation induces a local phase transformation that remains restricted to nanoscale dimensions. As these complexions are born at the defects which control plasticity in metals, it is crucial to understand their impact on subsequent mechanical properties. In this work, atomistic modeling is used to understand how dislocation mechanics are altered by the presence of nanoparticle array linear complexions in a Ni-Al alloy. Molecular dynamics simulations are used to identify the critical shear stress needed to drive dislocation breakaway, first for nanoparticle arrays formed by Monte Carlo/molecular dynamics methods to represent realistic configurations and subsequently for simplified models that allow the effects of particle spacing and size to be varied in a controlled manner. A combined bowing and progressive unpinning mechanism is uncovered, leading to the demonstration of a new strength scaling law that differs in keys ways from classical Orowan bowing.
△ Less
Submitted 10 October, 2023; v1 submitted 29 August, 2023;
originally announced August 2023.
-
Binary nanocrystalline alloys with strong glass forming interfacial regions: Complexion stability, segregation competition, and diffusion pathways
Authors:
Tianjiao Lei,
Esther C. Hessong,
Daniel S. Gianola,
Timothy J. Rupert
Abstract:
Stabilization of grain structure is important for nanocrystalline alloys, and grain boundary segregation is a common approach to restrict coarsening. Do** can alter grain boundary structure, with high temperature states such as amorphous complexions being particularly promising for stabilization. Dopant enrichment at grain boundaries may also result in precipitate formation, giving rise to dopan…
▽ More
Stabilization of grain structure is important for nanocrystalline alloys, and grain boundary segregation is a common approach to restrict coarsening. Do** can alter grain boundary structure, with high temperature states such as amorphous complexions being particularly promising for stabilization. Dopant enrichment at grain boundaries may also result in precipitate formation, giving rise to dopant partitioning between these two types of features. The present study elucidates the effect of dopant choice on the retention of amorphous complexions and the stabilization of grain size due to various forms of interfacial segregation in three binary nanocrystalline Al-rich systems, Al-Mg, Al-Ni, and Al-Y as investigated in detail using transmission electron microscopy. Amorphous complexions were retained in Al-Y even for very slow cooling conditions, suggesting that Y is the most efficient complexion stabilizer. Moreover, this system exhibited the highest number density of nanorod precipitates, reinforcing a recently observed correlation between amorphous complexions and grain boundary precipitation events. The dopant concentration at the grain boundaries in Al-Y is lower than in the other two systems, although enrichment compared to the matrix is similar, while secondary segregation to nanorod precipitate edges is much stronger in Al-Y than in Al-Mg and Al-Ni. Y is generally observed to be an efficient do** additive, as it stabilizes amorphous features and nanorod precipitates, and leaves very few atoms trapped in the matrix. As a result, all grains in Al-Y remained nanosized whereas abnormal grain growth occurred in the Al-Mg and Al-Ni alloys. The present study demonstrates nanocrystalline stability via simple alloy formulations and fewer dopant elements, which further encourage the usage of bulk nanostructured materials.
△ Less
Submitted 14 September, 2023; v1 submitted 12 June, 2023;
originally announced June 2023.
-
Inducing Skyrmion Flop Transitions in Co$_8$Zn$_8$Mn$_4$ at Room Temperature
Authors:
Simon A. Meynell,
Yolita M. Eggeler,
Joshua D. Bocarsly,
Daniil A. Kitchaev,
Bailey E. Rhodes,
Tresa M. Pollock,
Stephen D. Wilson,
Anton Van der Ven,
Ram Seshadri,
Marc De Graef,
Ania Bleszynski Jayich,
Daniel S. Gianola
Abstract:
Magnetic skyrmions are topologically-protected spin textures that manifest in certain non-centrosymmetric ferromagnets under the right conditions of temperature and field. In thin film skyrmion hosts, demagnetization effects combined with geometric confinement can result in two distinct types of spin textures: those with their axis of symmetry in the plane of the film (IP) and those with their axi…
▽ More
Magnetic skyrmions are topologically-protected spin textures that manifest in certain non-centrosymmetric ferromagnets under the right conditions of temperature and field. In thin film skyrmion hosts, demagnetization effects combined with geometric confinement can result in two distinct types of spin textures: those with their axis of symmetry in the plane of the film (IP) and those with their axis pointing out-of-plane (OOP). Here we present Lorentz transmission electron microscopy evidence in conjunction with numerical modeling showing a flop transition between IP and OOP skyrmions in Co$_8$Zn$_8$Mn$_4$ at room temperature. We show that this skyrmion flop transition is controllable via the angle of the external field relative to the film normal and we illustrate how this transition depends on thickness. Finally, we propose a skyrmion-writing device that utilizes the details of this transition.
△ Less
Submitted 1 December, 2022;
originally announced December 2022.
-
Linear complexions directly modify dislocation motion in face-centered cubic alloys
Authors:
Divya Singh,
Vladyslav Turlo,
Daniel S. Gianola,
Timothy J. Rupert
Abstract:
Linear complexions are defect phases that form in the presence of dislocations and thus are promising for the direct control of plasticity. In this study, atomistic simulations are used to model the effect of linear complexions on dislocation-based mechanisms for plasticity, demonstrating unique behaviors that differ from classical dislocation glide mechanisms. Linear complexions impart higher res…
▽ More
Linear complexions are defect phases that form in the presence of dislocations and thus are promising for the direct control of plasticity. In this study, atomistic simulations are used to model the effect of linear complexions on dislocation-based mechanisms for plasticity, demonstrating unique behaviors that differ from classical dislocation glide mechanisms. Linear complexions impart higher resistance to the initiation and continuation of dislocation motion when compared to solid solution strengthening in all of the face-centered cubic alloys investigated here, with the exact strengthening level determined by the linear complexion type. Stacking fault linear complexions impart the most pronounced strengthening effect, as the dislocation core is delocalized, and initiation of plastic flow requires a dislocation nucleation event. The nanoparticle and platelet array linear complexions impart strengthening by acting as pinning sites for the dislocations, where the dislocations unpin one at a time through bowing mechanisms. For the nanoparticle arrays, this event occurs even though the obstacles do not cross the slip plane and instead only interact through modification of the dislocation's stress field. The bowing modes observed in the current work appear similar to traditional Orowan bowing around classical precipitates but differ in a number of important ways depending on the complexion type. As a whole, this study demonstrates that linear complexions are a unique tool for microstructure engineering that can allow for the creation of alloys with new plastic deformation mechanisms and extreme strength.
△ Less
Submitted 21 March, 2023; v1 submitted 8 November, 2022;
originally announced November 2022.
-
Intermetallic particle heterogeneity controls shear localization in high-strength nanostructured Al alloys
Authors:
Tianjiao Lei,
Esther C. Hessong,
Jungho Shin,
Daniel S. Gianola,
Timothy J. Rupert
Abstract:
The mechanical behavior of two nanocrystalline Al alloys, Al-Mg-Y and Al-Fe-Y, is investigated with in-situ micropillar compression testing. Both alloys were strengthened by a hierarchical microstructure including grain boundary segregation, nanometer-thick amorphous complexions, carbide nanorod precipitates with sizes of a few nanometers, and submicron-scale intermetallic particles. The maximum y…
▽ More
The mechanical behavior of two nanocrystalline Al alloys, Al-Mg-Y and Al-Fe-Y, is investigated with in-situ micropillar compression testing. Both alloys were strengthened by a hierarchical microstructure including grain boundary segregation, nanometer-thick amorphous complexions, carbide nanorod precipitates with sizes of a few nanometers, and submicron-scale intermetallic particles. The maximum yield strength of the Al-Mg-Y system is measured to be 950 MPa, exceeding that of the Al-Fe-Y system (680 MPa), primarily due to a combination of more carbide nanorods and more amorphous complexions. Both alloys exhibited yield strengths much higher than those of commercial Al alloys, and therefore have great potential for structural applications. However, some micropillar specimens were observed to plastically soften through shear banding. Post-mortem investigation revealed that intermetallic-free deformation pathways of a few micrometers in length were responsible for this failure. Further characterization showed significant grain growth within the shear band. The coarsened grains maintained the same orientation with each other, pointing to grain boundary mechanisms for plastic flow, specifically grain rotation and/or grain boundary migration. The presence of intermetallic particles makes it difficult for both matrix and intermetallic grains to rotate into the same orientation due to the different lattice parameters and slip systems. Therefore, we are able to conclude that a uniform distribution of intermetallic particles with an average spacing less than the percolation length of shear localization can effectively prevent the maturation of shear bands, offering a design strategy for high-strength nanocrystalline Al alloys with both high strength and stable plastic flow.
△ Less
Submitted 30 July, 2022; v1 submitted 19 May, 2022;
originally announced May 2022.
-
Growth and structural transitions of core-shell nanorods in nanocrystalline Al-Ni-Y
Authors:
Tianjiao Lei,
Mingjie Xu,
Jungho Shin,
Daniel S. Gianola,
Timothy J. Rupert
Abstract:
Unique nanorod precipitates with a core-shell structure are found to nucleate from the grain boundaries of a bulk nanocrystalline Al-Ni-Y alloy fabricated via powder consolidation, contributing significantly to stabilization and strengthening. The local structure, chemistry, and evolution of these features during annealing is reported here. In the as-consolidated state, the nanorods can be either…
▽ More
Unique nanorod precipitates with a core-shell structure are found to nucleate from the grain boundaries of a bulk nanocrystalline Al-Ni-Y alloy fabricated via powder consolidation, contributing significantly to stabilization and strengthening. The local structure, chemistry, and evolution of these features during annealing is reported here. In the as-consolidated state, the nanorods can be either structurally ordered or disordered, yet a consistent chemical patterning is found where the core is primarily Al plus C while the shell is enriched with Y. As annealing time increases, more nanorods transform to an ordered structure as they coarsen while the core composition remains unchanged. In contrast, the shell chemistry transitions from Y-rich to Ni-rich with longer annealing treatments, most likely due to the different diffusivities of Y and Ni in Al. Moreover, a spatial and chemical correlation between the nanorods and amorphous complexions is observed, suggesting that these complexions serve as preferential nucleation sites.
△ Less
Submitted 4 January, 2022; v1 submitted 24 November, 2021;
originally announced November 2021.
-
Bulk nanocrystalline Al alloys with hierarchical reinforcement structures via grain boundary segregation and complexion formation
Authors:
Tianjiao Lei,
Jungho Shin,
Daniel S. Gianola,
Timothy J. Rupert
Abstract:
Grain size engineering, particularly reducing grain size into the nanocrystalline regime, offers a promising pathway to further improve the strength-to-weight ratio of Al alloys. Unfortunately, the fabrication of nanocrystalline metals often requires non-equilibrium processing routes, which typically limit the specimen size and require large energy budgets. In this study, multiple dopant atoms in…
▽ More
Grain size engineering, particularly reducing grain size into the nanocrystalline regime, offers a promising pathway to further improve the strength-to-weight ratio of Al alloys. Unfortunately, the fabrication of nanocrystalline metals often requires non-equilibrium processing routes, which typically limit the specimen size and require large energy budgets. In this study, multiple dopant atoms in ternary Al alloys are deliberately selected to enable segregation to the grain boundary region and promote the formation of amorphous complexions. Three different fully dense bulk nanocrystalline Al alloys (Al-Mg-Y, Al-Fe-Y, and Al-Ni-Y) with small grain sizes were successfully fabricated using a simple powder metallurgy approach, with full densification connected directly to the onset of amorphous complexion formation. All the compositions demonstrate densities above 99% with grain sizes of <60 nm following consolidation via hot pressing at 585 oC. The very fine grain structure results in excellent mechanical properties, with nanoindentation hardness values in the range of 2.2-2.8 GPa. Detailed microstructural characterization verifies the segregation of all dopant species to grain boundaries as well as the formation of amorphous complexions, which suggests their influential role in aiding effective consolidation and endowing thermal stability in the alloys. Moreover, nanorods with a core-shell structure are also observed at the grain boundaries, which likely contribute to the stabilization of the grain structure and high strength. Finally, intermetallic particles with a sizes of hundreds of nanometers form. As a whole, the results presented here demonstrate a general alloy design strategy of segregation and boundary evolution pathway that enables the fabrication of multiple nanocrystalline Al alloys with hierarchical microstructures and improved performance.
△ Less
Submitted 5 October, 2021; v1 submitted 5 September, 2021;
originally announced September 2021.
-
Electron Backscattered Diffraction using a New Monolithic Direct Detector: High Resolution and Fast Acquisition
Authors:
Fulin Wang,
McLean P. Echlin,
Aidan A. Taylor,
Jungho Shin,
Benjamin Bammes,
Barnaby D. A. Levin,
Marc De Graef,
Tresa M. Pollock,
Daniel S. Gianola
Abstract:
A monolithic active pixel sensor based direct detector that is optimized for the primary beam energies in scanning electron microscopes is implemented for electron back-scattered diffraction (EBSD) applications. The high detection efficiency of the detector and its large array of pixels allow sensitive and accurate detection of Kikuchi bands arising from primary electron beam excitation energies o…
▽ More
A monolithic active pixel sensor based direct detector that is optimized for the primary beam energies in scanning electron microscopes is implemented for electron back-scattered diffraction (EBSD) applications. The high detection efficiency of the detector and its large array of pixels allow sensitive and accurate detection of Kikuchi bands arising from primary electron beam excitation energies of 4 keV to 28 keV, with the optimal contrast occurring in the range of 8-16 keV. The diffraction pattern acquisition speed is substantially improved via a sparse sampling mode, resulting from the acquisition of a reduced number of pixels on the detector. Standard inpainting algorithms are implemented to effectively estimate the information in the skipped regions in the acquired diffraction pattern. For EBSD map**, a speed as high as 5988 scan points per second is demonstrated, with a tolerable fraction of indexed points and accuracy. The collective capabilities spanning from high angular resolution EBSD pattern to high speed pattern acquisition are achieved on the same detector, facilitating simultaneous detection modalities that enable a multitude of advanced EBSD applications, including lattice strain map**, structural refinement, low-dose characterization, 3D-EBSD and dynamic in situ EBSD.
△ Less
Submitted 26 August, 2020;
originally announced August 2020.
-
Flexible Conductive Composites with Programmed Electrical Anisotropy Using Acoustophoresis
Authors:
Drew S. Melchert,
Rachel R. Collino,
Tyler R. Ray,
Neil Dolinski,
Leanne Friedrich,
Matthew R. Begley,
Daniel S. Gianola
Abstract:
3D printing mechanically flexible composite materials with high electrical conductivity is currently hindered by the need to use high loading of conductive filler, which severely limits flexibility. Here, microstructural patterning of composite materials via acoustophoresis imparts these materials with high conductivity and flexibility simultaneously, filling a technology gap in the field. Acousto…
▽ More
3D printing mechanically flexible composite materials with high electrical conductivity is currently hindered by the need to use high loading of conductive filler, which severely limits flexibility. Here, microstructural patterning of composite materials via acoustophoresis imparts these materials with high conductivity and flexibility simultaneously, filling a technology gap in the field. Acoustophoresis patterns filler particles into highly efficient percolated networks which utilize up to 97\% of the particles in the composite, whereas the inefficient stochastic networks of conventional dispersed-fiber composites utilize $<5$\%. These patterned materials have conductivity an order of magnitude higher than conventional composites made with the same ink, reaching 48\% the conductivity of bulk silver within the assembled silver-particle networks (at 2.6v\% loading). They also have low particle loading so that they're flexible, withstanding $>$500 bending cycles without losses in conductivity and changing conductivity only $5$\% within cycles on average (for 2.6v\% composites). In contrast, conventional unpatterned composites with the same conductivity require such high loading that they're prohibitively brittle. Finally, modulating the shape of the applied acoustic fields allows control over the anisotropy of the conductive networks and produces materials which are either 2-D conductive, 1-D conductive, or insulating, all using the same nozzle and ink.
△ Less
Submitted 11 July, 2019; v1 submitted 21 February, 2019;
originally announced February 2019.
-
New techniques for imaging and identifying defects in electron microscopy
Authors:
Daniel S. Gianola,
T. Ben Britton,
Stefan Zaefferer
Abstract:
Defects in crystalline materials control the properties of materials, and their characterization focuses our strategies to optimize performance. Electron microscopy has served as the backbone of our understanding of defect structure and their interactions owing to beneficial spatial resolution and contrast mechanisms that enable direct imaging of defects. These defects reside in complex microstruc…
▽ More
Defects in crystalline materials control the properties of materials, and their characterization focuses our strategies to optimize performance. Electron microscopy has served as the backbone of our understanding of defect structure and their interactions owing to beneficial spatial resolution and contrast mechanisms that enable direct imaging of defects. These defects reside in complex microstructures and chemical environments, demanding a combination of experimental approaches for full defect characterization. In this article, we describe recent progress and trends in methods for examining defects using scanning electron microscopy platforms, where several emerging approaches offer attractive benefits, for instance in correlative microscopy across length scales and in situ studies of defect dynamics.
△ Less
Submitted 16 March, 2019; v1 submitted 19 February, 2019;
originally announced February 2019.
-
Robust Scaling of Strength and Elastic Constants and Universal Cooperativity in Disordered Colloidal Micropillars
Authors:
Daniel J. Strickland,
Yun-Ru Huang,
Daeyeon Lee,
Daniel S. Gianola
Abstract:
We study the uniaxial compressive behavior of disordered colloidal free-standing micropillars composed of a bidisperse mixture of 3 and 6 um polystyrene particles. Mechanical annealing of confined pillars enables variation of the packing fraction across the phase space of colloidal glasses. The measured normalized strengths and elastic moduli of the annealed freestanding micropillars span almost t…
▽ More
We study the uniaxial compressive behavior of disordered colloidal free-standing micropillars composed of a bidisperse mixture of 3 and 6 um polystyrene particles. Mechanical annealing of confined pillars enables variation of the packing fraction across the phase space of colloidal glasses. The measured normalized strengths and elastic moduli of the annealed freestanding micropillars span almost three orders-of-magnitude despite similar plastic morphology governed by shear banding. We measure a robust correlation between ultimate strengths and elastic constants that is invariant to relative humidity, implying a critical strain of $\sim$0.01 that is strikingly similar to that observed in metallic glasses (MGs) [W.L. Johnson, K. Samwer, Phys. Rev. Lett. 95, 195501, 2005] and suggestive of a universal mode of cooperative plastic deformation. We estimate the characteristic strain of the underlying cooperative plastic event by considering the energy necessary to create an Eshelby-like ellipsoidal inclusion in an elastic matrix. We find that the characteristic strain is similar to that found in experiments and simulations of other disordered solids with distinct bonding and particle sizes, suggesting a universal criterion for the elastic to plastic transition in glassy materials with the capacity for finite plastic flow.
△ Less
Submitted 21 August, 2014;
originally announced August 2014.
-
The causal meaning of genomic predictors and how it affects the construction and comparison of genome-enabled selection models
Authors:
Bruno Dourado Valente,
Gota Morota,
Guilherme Jordao Magalhaes Rosa,
Daniel Gianola,
Kent Weigel
Abstract:
The additive genetic effect is arguably the most important quantity inferred in animal and plant breeding analyses. The term effect indicates that it represents causal information, which is different from standard statistical concepts as regression coefficient and association. The process of inferring causal information is also different from standard statistical learning, as the former requires c…
▽ More
The additive genetic effect is arguably the most important quantity inferred in animal and plant breeding analyses. The term effect indicates that it represents causal information, which is different from standard statistical concepts as regression coefficient and association. The process of inferring causal information is also different from standard statistical learning, as the former requires causal (i.e. non-statistical) assumptions and involves extra complexities. Remarkably, the task of inferring genetic effects is largely seen as a standard regression/prediction problem, contradicting its label. This widely accepted analysis approach is by itself insufficient for causal learning, suggesting that causality is not the point for selection. Given this incongruence, it is important to verify if genomic predictors need to represent causal effects to be relevant for selection decisions, especially because applying regression studies to answer causal questions may lead to wrong conclusions. The answer to this question defines if genomic selection models should be constructed aiming maximum genomic predictive ability or aiming identifiability of genetic causal effects. Here, we demonstrate that selection relies on a causal effect from genotype to phenotype, and that genomic predictors are only useful for selection if they distinguish such effect from other sources of association. Conversely, genomic predictors capturing non-causal signals provide information that is less relevant for selection regardless of the resulting predictive ability. Focusing on covariate choice decision, simulated examples are used to show that predictive ability, which is the criterion normally used to compare models, may not indicate the quality of genomic predictors for selection. Additionally, we propose using alternative criteria to construct models aiming for the identification of the genetic causal effects.
△ Less
Submitted 7 December, 2013;
originally announced January 2014.
-
Extremely Low Drift in Amorphous Phase Change Nanowire Materials
Authors:
Mukut Mitra,
Yeonwoong Jung,
Daniel S. Gianola,
Ritesh Agarwal
Abstract:
Time-dependent drift of resistance and threshold voltage in phase change memory (PCM) devices is of concern as it leads to data loss. Electrical drift in amorphous chalcogenides has been argued to be either due to electronic or stress relaxation mechanisms. Here we show that drift in amorphized Ge2Sb2Te5 nanowires with exposed surfaces is extremely low in comparison to thin-film devices. However,…
▽ More
Time-dependent drift of resistance and threshold voltage in phase change memory (PCM) devices is of concern as it leads to data loss. Electrical drift in amorphous chalcogenides has been argued to be either due to electronic or stress relaxation mechanisms. Here we show that drift in amorphized Ge2Sb2Te5 nanowires with exposed surfaces is extremely low in comparison to thin-film devices. However, drift in stressed nanowires embedded under dielectric films is comparable to thin-films. Our results shows that drift in PCM is due to stress relaxation and will help in understanding and controlling drift in PCM devices.
△ Less
Submitted 10 April, 2010;
originally announced April 2010.