Impact of a ferromagnetic insulating barrier in magnetic tunnel junctions
Authors:
M. Abbasi Eskandari,
S. Ghotb,
P. Fournier
Abstract:
We investigate spin-dependent conductance across a magnetic tunnel junction (MTJ) including a ferromagnetic insulating barrier. The MTJ consists of two half-metallic ferromagnetic La2/3Sr1/3MnO3 (LSMO) manganites as electrodes and La2NiMnO6 (LNMO) double perovskite as a ferromagnetic insulating barrier. The resistance of the junction is strongly dependent not only on the orientation of the magneti…
▽ More
We investigate spin-dependent conductance across a magnetic tunnel junction (MTJ) including a ferromagnetic insulating barrier. The MTJ consists of two half-metallic ferromagnetic La2/3Sr1/3MnO3 (LSMO) manganites as electrodes and La2NiMnO6 (LNMO) double perovskite as a ferromagnetic insulating barrier. The resistance of the junction is strongly dependent not only on the orientation of the magnetic moments in LSMO electrodes, but also on the direction of the magnetization of the LNMO barrier with respect to that of LSMO. The ratio of tunnel magnetoresistance reaches a maximum value of 24% at 10 K, and it decreases with temperature until it completely disappears above the critical temperature of LNMO at 280 K. The tunneling process is described using a mechanism which involves both empty and filled eg states of the LNMO barrier acting as a spin-filter. A magnetic insulating barrier is an interesting path for achieving room temperature magnetoresistance in oxide-based heterostructures.
△ Less
Submitted 8 December, 2022;
originally announced December 2022.
-
Tunable magnetocaloric effect and enhanced refrigerant capacity in composite-like oxide heterostructures
Authors:
Mohammad Abbasi Eskandari,
Seyedeh Sara Ghotb,
Mohamed balli,
Patrick Fournier
Abstract:
We report a detailed study of the magnetocaloric effect in heterostructures of La2NiMnO6 and La2/3Sr1/3MnO3. The shape, width and magnitude of the temperature dependence of the magnetic entropy change ($ΔS_{m}$) for these multilayer samples can be tuned and controlled by changing their layout. A large $ΔS_{m}$ over a wide temperature range which goes beyond room temperature is observed in all samp…
▽ More
We report a detailed study of the magnetocaloric effect in heterostructures of La2NiMnO6 and La2/3Sr1/3MnO3. The shape, width and magnitude of the temperature dependence of the magnetic entropy change ($ΔS_{m}$) for these multilayer samples can be tuned and controlled by changing their layout. A large $ΔS_{m}$ over a wide temperature range which goes beyond room temperature is observed in all samples. We observe a temperature-independent table-top-like $ΔS_{m}$ over a temperature range as large as 100 K in the trilayer samples. La2NiMnO6 double perovskite with multiple magnetic phase transitions is the key to tuning and sha** the temperature dependence of the magnetic entropy changes to suit the requirements of several cooling cycles.
△ Less
Submitted 4 November, 2022;
originally announced November 2022.
-
Magnetic do** effects on the superconductivity of Y1-xMxBa2Cu3O7-d (M = Fe, Co, Ni)
Authors:
Hamideh Shakeripour,
Seyed Sajjad Hosseini,
Seyedeh Sara Ghotb,
Behnaz Hadi-Sichani,
Sepideh Pourasad
Abstract:
The discovery of superconductivity in copper oxide compounds has attracted considerable attention over the past three decades. The high transition temperature in these compounds, exhibiting proximity to an antiferromagnetic order in their phase diagrams, remains one of the main areas of research. The present study attempts to introduce Fe, Co and Ni magnetic impurities into the superconducting Y-1…
▽ More
The discovery of superconductivity in copper oxide compounds has attracted considerable attention over the past three decades. The high transition temperature in these compounds, exhibiting proximity to an antiferromagnetic order in their phase diagrams, remains one of the main areas of research. The present study attempts to introduce Fe, Co and Ni magnetic impurities into the superconducting Y-123 with the aim of exploring the transition temperature behavior. The solid-state synthesis is exploited to prepare fully oxygenated Y1-xMxBa2Cu3O7 (M = Co, Fe, Ni) samples with low levels of do** (0< x < 0.03). Systematic measurements are then employed to assess the synthesized samples using AC magnetic susceptibility, electrical resistivity and X-ray diffraction. The measurements revealed an increase in Tc as a result of magnetic substitution for Y. However, the study of non-magnetic do**s on the fully oxygenated Y1-xM'xBa2Cu3O7 (M' = Ca, Sr) samples showed a decrease in Tc. Quantitative XRD analysis further suggested that the internal pressure could have minor effects on the increase in Tc. The normal state resistivity vs temperature showed a linear profile, confirming that the samples are at an optimal do** of the carrier concentration.
△ Less
Submitted 22 January, 2021;
originally announced January 2021.