Small anisotropy of the lower critical field and $s_\pm$-wave two-gap feature in single crystal LiFeAs
Authors:
Yoo Jang Song,
** Soo Ghim,
Jae Hyun Yoon,
Kyu Joon Lee,
Myung Hwa Jung,
Hyo-Seok Ji,
Ji Hoon Shim,
Yong Seung Kwon
Abstract:
The in- and out-of-plane lower critical fields and magnetic penetration depths for LiFeAs were examined. The anisotropy ratio $γ_{H_{c1}}(0)$ is smaller than the expected theoretical value, and increased slightly with increasing temperature from 0.6$T_c$ to $T_c$. This small degree of anisotropy was numerically confirmed by considering electron correlation effect. The temperature dependence of the…
▽ More
The in- and out-of-plane lower critical fields and magnetic penetration depths for LiFeAs were examined. The anisotropy ratio $γ_{H_{c1}}(0)$ is smaller than the expected theoretical value, and increased slightly with increasing temperature from 0.6$T_c$ to $T_c$. This small degree of anisotropy was numerically confirmed by considering electron correlation effect. The temperature dependence of the penetration depths followed a power law($\sim$$T^n$) below 0.3$T_c$, with $n$$>$3.5 for both $λ_{ab}$ and $λ_c$. Based on theoretical studies of iron-based superconductors, these results suggest that the superconductivity of LiFeAs can be represented by an extended $s_\pm$-wave due to weak impurity scattering effect. And the magnitudes of the two gaps were also evaluted by fitting the superfluid density for both the in- and out-of-plane to the two-gap model. The estimated values for the two gaps are consistent with the results of angle resolved photoemission spectroscopy and specific heat experiments.
△ Less
Submitted 13 April, 2011; v1 submitted 28 July, 2010;
originally announced July 2010.
Synthesis, anisotropy, and superconducting properties of LiFeAs single crystal
Authors:
Yoo Jang Song,
** Soo Ghim,
Byeong Hun Min,
Yong Seung Kwon,
Myung Hwa Jung,
Jong-Soo Rhyee
Abstract:
A LiFeAs single crystal with $T_c^{onset}$$\sim$19.7 K was grown successfully in a sealed tungsten crucible using the Bridgeman method. The electrical resistivity experiments revealed a ratio of room temperature to residual resistivity (RRR) of approximately 46 and 18 for the in-plane and out-of plane directions. The estimated anisotropic resistivity, $γ_ρ$=$ρ_c$ / $ρ_{ab}$, was approximately 3.…
▽ More
A LiFeAs single crystal with $T_c^{onset}$$\sim$19.7 K was grown successfully in a sealed tungsten crucible using the Bridgeman method. The electrical resistivity experiments revealed a ratio of room temperature to residual resistivity (RRR) of approximately 46 and 18 for the in-plane and out-of plane directions. The estimated anisotropic resistivity, $γ_ρ$=$ρ_c$ / $ρ_{ab}$, was approximately 3.3 at $T_c^{onset}$. The upper critical fields had large $H_{c2} ^{\shortparallel ab}$ and $H_{c2}^{\shortparallel c}$ values of 83.4 T and 72.5 T, respectively, and an anisotropy ratio is $γ_H$=$H_{c2}^{\shortparallel ab}$ / $H_{c2} ^{\shortparallel c}$$\sim$1.15. The high upper critical field value and small anisotropy highlight the potential use of LiFeAs in a variety of applications. The calculated critical current density $(J_c)$ from the $M$-$H$ loop is approximately 10$^3$ A/cm$^2$
△ Less
Submitted 10 February, 2010;
originally announced February 2010.