Coupling liquid electrochemical TEM and mass-spectrometry to investigate electrochemical reactions occurring in a Na-ion battery anode
Authors:
Kevyn Gallegos Moncayo,
Nicolas Folastre,
Milan Toledo,
Hélène Tonnoir,
François Rabuel,
Grégory Gachot,
Da Huo,
Arnaud Demortière
Abstract:
In this study, we propose a novel approach for investigating the formation of solid electrolyte interphase (SEI) in Na-ion batteries (NIB) through the coupling of in situ liquid electrochemical transmission electron microscopy (ec-TEM) and gas-chromatography mass-spectrometry (GC/MS). To optimize this coupling, we conducted experiments on the sodiation of hard carbon materials (HC) using two diffe…
▽ More
In this study, we propose a novel approach for investigating the formation of solid electrolyte interphase (SEI) in Na-ion batteries (NIB) through the coupling of in situ liquid electrochemical transmission electron microscopy (ec-TEM) and gas-chromatography mass-spectrometry (GC/MS). To optimize this coupling, we conducted experiments on the sodiation of hard carbon materials (HC) using two different setups: in situ ec-TEM holder (operating in an "anode free" configuration, referred to as $μ$-battery) and ex-situ setup (Swagelok battery configuration). In the in situ TEM experiments, we intentionally degraded the electrolyte (NP30) using cyclic voltammetry (CV) and analyzed the recovered liquid product using GC/MS, while the solid product ($μ$-chip) was analyzed using TEM techniques in a post-mortem analysis. The ex-situ experiments served as a reference to observe and detect the insertion of Na+ ions in the HC, SEI size (389 nm), SEI composition (P, Na, F, and O), and Na plating. Furthermore, the TEM analysis revealed a cyclability limitation in our in situ TEM system. This issue appears to be caused by the deposition of Na in the form of a "foam" structure, resulting from the gas release during the reaction of Na with DMC/EC electrolyte. The foam structure, subsequently transforms into a second SEI, is electrochemically inactive and reduce the cyclability of the battery. Overall, our results demonstrate the powerful synergy achieved by coupling in situ ec-TEM and GC/MS techniques, which provides a deeper understanding of the dynamics and behavior of SEI. Consequently, this knowledge contributes to the advancement of the new generation of NIB.
△ Less
Submitted 9 August, 2023;
originally announced August 2023.
Binder-free CNT cathodes for Li-O$_2$ batteries with more than one life
Authors:
Zeliang Su,
Israel Temprano,
Nicolas Folastre,
Victor Vanpeene,
Julie Villanova,
Gregory Gachot,
Elena Shevchenko,
Clare P. Grey,
Alejandro A. Franco,
Arnaud Demortiere
Abstract:
Li-O$_2$ batteries (LOB) performance degradation ultimately occurs through the accumulation of discharge products and irreversible clogging of the porous electrode during the cycling. Electrode binder degradation in the presence of reduced oxygen species can result in additional coating of the conductive surface, exacerbating capacity fading. Herein, we establish a facile method to fabricate free-…
▽ More
Li-O$_2$ batteries (LOB) performance degradation ultimately occurs through the accumulation of discharge products and irreversible clogging of the porous electrode during the cycling. Electrode binder degradation in the presence of reduced oxygen species can result in additional coating of the conductive surface, exacerbating capacity fading. Herein, we establish a facile method to fabricate free-standing, binder-free electrodes for LOBs in which multi-wall carbon nanotubes (MWCNT) form cross-linked networks exhibiting high porosity, conductivity, and flexibility. These electrodes demonstrate high reproducibility upon cycling in LOBs. After cell death, efficient and inexpensive methods to wash away the accumulated discharge products are demonstrated, as reconditioning method. The second life usage of these electrodes is validated, without noticeable loss of performance. These findings aim to assist in the development of greener high energy density batteries while reducing manufacturing and recycling costs.
△ Less
Submitted 15 February, 2023;
originally announced February 2023.