A new class of carbon stabilized austenitic steels resistant to hydrogen embrittlement
Authors:
Heena Khanchandani,
Stefan Zeiler,
Lucas Strobel,
Mathias Goeken,
Peter Felfer
Abstract:
High strength steels are susceptible to H-induced failure, which is typically caused by the presence of diffusible H in the microstructure. The diffusivity of H in austenitic steels with fcc crystal structure is slow. The austenitic steels are hence preferred for applications in the hydrogen-containing atmospheres. However, the fcc structure of austenitic steels is often stabilized by the addition…
▽ More
High strength steels are susceptible to H-induced failure, which is typically caused by the presence of diffusible H in the microstructure. The diffusivity of H in austenitic steels with fcc crystal structure is slow. The austenitic steels are hence preferred for applications in the hydrogen-containing atmospheres. However, the fcc structure of austenitic steels is often stabilized by the addition of Ni, Mn or N, which are relatively expensive alloying elements to use. Austenite can kinetically also be stabilized by using C. Here, we present an approach applied to a commercial cold work tool steel, where we use C to fully stabilize the fcc phase. This results in a microstructure consisting of only austenite and an M7C3 carbide. An exposure to H by cathodic hydrogen charging exhibited no significant influence on the strength and ductility of the C stabilized austenitic steel. While this material is only a prototype based on an existing alloy of different purpose, it shows the potential for low-cost H-resistant steels based on C stabilized austenite.
△ Less
Submitted 27 September, 2023; v1 submitted 24 May, 2023;
originally announced May 2023.
-
A new method for microscale cyclic crack growth characterization from notched microcantilevers and application to single crystalline tungsten and a metallic glass
Authors:
S. Gabel,
B. Merle,
E. Bitzek,
M. Göken
Abstract:
The lifetime of most metals is limited by cyclic loads, ending in fatigue failure. The progressive growth of cracks ends up in catastrophic failure. An advanced method is presented for the determination of cyclic crack growth on the microscale using a nanoindenter, which allows the characterization of > 10,000 loading cycles. It uses focused ion beam fabricated notched microcantilevers. The method…
▽ More
The lifetime of most metals is limited by cyclic loads, ending in fatigue failure. The progressive growth of cracks ends up in catastrophic failure. An advanced method is presented for the determination of cyclic crack growth on the microscale using a nanoindenter, which allows the characterization of > 10,000 loading cycles. It uses focused ion beam fabricated notched microcantilevers. The method has been validated by cyclic bending metallic glass and tungsten microcantilevers. The experiments reveal a stable crack growth during the lifetime of both samples. The metallic glass shows less plasticity due to the absence of dislocations, but shows shearing caused by the deformation. The crack growth rates determined in the tests follow Paris' power law relationship. The results are reliable, reproducible and comparable with macroscopic setups. Due to the flexibility of the method, it is suitable for the characterization of specific microstructural features, like single phases, grain boundaries or different grain orientations.
△ Less
Submitted 2 August, 2022;
originally announced August 2022.
-
Structural reorientation and compaction of porous MoS2 coatings during wear testing
Authors:
Sebastian Krauß,
Armin Seynstahl,
Stephan Tremmel,
Bernd Meyer,
Erik Bitzek,
Mathias Göken,
Tadahiro Yokosawa,
Benjamin Apeleo Zubiri,
Erdmann Spiecker,
Benoit Merle
Abstract:
Industrial upscaling frequently results in a different coating microstructure than the laboratory prototypes presented in the literature. Here, we investigate the wear behavior of physical vapor deposited (PVD) MoS2 coatings: A dense, nanocrystalline MoS2 coating, and a porous, prismatic-textured MoS2 coating. Transmission electron microscopy (TEM) investigations before and after wear testing evid…
▽ More
Industrial upscaling frequently results in a different coating microstructure than the laboratory prototypes presented in the literature. Here, we investigate the wear behavior of physical vapor deposited (PVD) MoS2 coatings: A dense, nanocrystalline MoS2 coating, and a porous, prismatic-textured MoS2 coating. Transmission electron microscopy (TEM) investigations before and after wear testing evidence a crystallographic reorientation towards a basal texture in both samples. A basal texture is usually desirable due to its low-friction properties. This favorable reorientation is associated to a tribological compaction of the porous specimens. Following running-in, sliding under high contact pressure ultimately leads to a wear rate as small as for an ideal grown bulk MoS2 single crystal grown by chemical vapor deposition (CVD). This suggests that the imperfections of industrial grade MoS2 coatings can be remediated by a suitable pretreatment.
△ Less
Submitted 21 August, 2022; v1 submitted 21 February, 2022;
originally announced February 2022.
-
Creep properties and deformation mechanisms of single-crystalline $γ^\prime$-strengthened superalloys in dependence of the Co/Ni ratio
Authors:
Nicklas Volz,
Christopher H. Zenk,
Nicolas Karpstein,
Malte Lenz,
Erdmann Spiecker,
Mathias Göken,
Steffen Neumeier
Abstract:
Co-base superalloys are considered as promising high temperature materials besides the well-established Ni-base superalloys. However, Ni appears to be an indispensable alloying element also in Co-base superalloys. To address the influence of the base elements on the deformation behavior, high-temperature compressive creep experiments were performed on a single crystal alloy series that was designe…
▽ More
Co-base superalloys are considered as promising high temperature materials besides the well-established Ni-base superalloys. However, Ni appears to be an indispensable alloying element also in Co-base superalloys. To address the influence of the base elements on the deformation behavior, high-temperature compressive creep experiments were performed on a single crystal alloy series that was designed to exhibit a varying Co/Ni ratio and a constant Al, W and Cr content. Creep tests were performed at 900 °C and 250 MPa and the resulting microstructures and defect configurations were characterized via electron microscopy. The minimum creep rates differ by more than one order of magnitude with changing Co/Ni ratio. An intermediate CoNi-base alloy exhibits the overall highest creep strength. Several strengthening contributions like solid solution strengthening of the $γ$ phase, effective diffusion coefficients or stacking fault energies were quantified. Precipitate shearing mechanisms differ significantly when the base element content is varied. While the Ni-rich superalloys exhibit SISF and SESF shearing, the Co-rich alloys develop extended APBs when the $γ^\prime$ phase is cut. This is mainly attributed to a difference in planar fault energies, caused by a changing segregation behavior. As result, it is assumed that the shearing resistivity and the occurring deformation mechanisms in the $γ^\prime$ phase are crucial for the creep properties of the investigated alloy series.
△ Less
Submitted 14 September, 2021;
originally announced September 2021.
-
Understanding creep of a single-crystalline Co-Al-W-Ta superalloy by studying the deformation mechanism, segregation tendency and stacking fault energy
Authors:
Nicklas Volz,
Fei Xue,
Christopher H. Zenk,
Andreas Bezold,
Stefan Gabel,
Aparna P. A. Subramanyam,
Ralf Drautz,
Thomas Hammerschmidt,
Surendra K. Makineni,
Baptiste Gault,
Mathias Göken,
Steffen Neumeier
Abstract:
A systematic study of the compression creep properties of a single-crystalline Co-base superalloy (Co-9Al-7.5W-2Ta) was conducted at 950 °C, 975 °C and 1000 °C to reveal the influence of temperature and the resulting diffusion velocity of solutes like Al, W and Ta on the deformation mechanisms. Two creep rate minima are observed at all temperatures indicating that the deformation mechanisms causin…
▽ More
A systematic study of the compression creep properties of a single-crystalline Co-base superalloy (Co-9Al-7.5W-2Ta) was conducted at 950 °C, 975 °C and 1000 °C to reveal the influence of temperature and the resulting diffusion velocity of solutes like Al, W and Ta on the deformation mechanisms. Two creep rate minima are observed at all temperatures indicating that the deformation mechanisms causing these minima are quite similar. Atom-probe tomography analysis reveals elemental segregation to stacking faults, which had formed in the $γ\prime$ phase during creep. Density-functional-theory calculations indicate segregation of W and Ta to the stacking fault and an associated considerable reduction of the stacking fault energy. Since solutes diffuse faster at a higher temperature, segregation can take place more quickly. This results in a significantly faster softening of the alloy, since cutting of the $γ\prime$ precipitate phase by partial dislocations is facilitated through segregation already during the early stages of creep. This is confirmed by transmission electron microscopy analysis. Therefore, not only the smaller precipitate fraction at higher temperatures is responsible for the worse creep properties, but also faster diffusion-assisted shearing of the $γ\prime$ phase by partial dislocations. The understanding of these mechanisms will help in future alloy development by offering new design criteria.
△ Less
Submitted 1 June, 2021; v1 submitted 31 May, 2021;
originally announced May 2021.
-
On the influence of Al-concentration on the fracture toughness of NiAl: microcantilever fracture tests and atomistic simulations
Authors:
Ralf Webler,
Polina N. Baranova,
Shivraj Karewar,
Steffen Neumeier,
Johannes J. Möller,
Hauke Springer,
Mathias Göken,
Erik Bitzek
Abstract:
The mechanical properties of the stoichiometric B2 $β$-phase of NiAl are well established, however the effect of off-stoichiometric composition on the fracture toughness has not yet been systematically studied over the entire composition range of 40-50% Al. Here we use microbending tests on notched cantilever beams FIB-milled from NiAl single crystals with an aluminized as well as an oxidation-ind…
▽ More
The mechanical properties of the stoichiometric B2 $β$-phase of NiAl are well established, however the effect of off-stoichiometric composition on the fracture toughness has not yet been systematically studied over the entire composition range of 40-50% Al. Here we use microbending tests on notched cantilever beams FIB-milled from NiAl single crystals with an aluminized as well as an oxidation-induced composition gradient to determine the influence of the Al concentration on the mechanical properties. The fracture toughness is maximal for the stoichiometric composition. It decreases with increasing Ni-content in the Ni-rich composition range, where plastic deformation is observed to accompany the fracture process. In contrast, no plasticity is observed in Al-rich NiAl, which shows a nearly concentration-independent, low fracture toughness. The theoretical fracture toughness according to Griffith, however, shows only a very weak composition dependence in both, the Ni- and Al-rich composition range. The differences in fracture toughness could furthermore not be explained solely based on the different hardening contributions of Ni-antisites in the Ni-rich and structural vacancies in the Al-rich crystals. Atomistic fracture simulations show that crack propagation in NiAl takes place by the nucleation and migration of kinks on the crack front. The low fracture toughness of Al-rich NiAl can thus be understood by the dual effect of structural vacancies as strong obstacles to dislocation motion and as source of crack front kinks.
△ Less
Submitted 29 December, 2019;
originally announced December 2019.
-
Low temperature deformation of MoSi$_2$ and the effect of Ta, Nb and Al as alloying elements
Authors:
Carolin Zenk,
James S. K. -L. Gibson,
Verena Maier-Kiener,
Steffen Neumeier,
Mathias Göken,
Sandra Korte-Kerzel
Abstract:
Molybdenum disilicide (MoSi$_2$) is a very promising material for high temperature structural applications due to its high melting point (2030 °C), low density, high thermal conductivity and good oxidation resistance. However, MoSi$_2$ has limited ductility below 900 °C due to its anisotropic plastic deformation behaviour and high critical resolved shear stresses on particular slip systems. Nanoin…
▽ More
Molybdenum disilicide (MoSi$_2$) is a very promising material for high temperature structural applications due to its high melting point (2030 °C), low density, high thermal conductivity and good oxidation resistance. However, MoSi$_2$ has limited ductility below 900 °C due to its anisotropic plastic deformation behaviour and high critical resolved shear stresses on particular slip systems. Nanoindentation of MoSi$_2$ microalloyed with aluminium, niobium or tantalum showed that all alloying elements cause a decrease in hardness. Analysis of surface slip lines indicated the activation of the additional {1 1 0}<1 1 1> slip system in microalloyed MoSi$_2$, which is not active below 300 °C in pure MoSi$_2$. This was confirmed by TEM dislocation analysis of the indentation plastic zone. Further micropillar compression experiments comparing pure MoSi$_2$ and the Ta-alloyed sample enabled the determination of the critical resolved shear stresses of individual slip systems even in the most brittle [0 0 1] crystal direction.
△ Less