Processing and mechanical properties of novel biodegradable poly-lactic acid/Zn 3D printed scaffolds for application in tissue regeneration
Authors:
C. Pascual-González,
J. de la Vega,
C. Thompson,
J. P. Fernández-Blázquez,
D. Herráez-Molinero,
N. Biurrun,
I. Lizarralde,
J. Sánchez del Río,
C. González,
J. LLorca
Abstract:
The feasibility to manufacture scaffolds of poly-lactic acid reinforced with Zn particles by fused filament fabrication is demonstrated for the first time. Filaments of 2.85 mm in diameter of PLA reinforced with different weight fractions of $μ$m-sized Zn - 1 wt. \% Mg alloy particles (in the range 3.5 to 17.5 wt. \%) were manufactured by a double extrusion in method in which standard extrusion is…
▽ More
The feasibility to manufacture scaffolds of poly-lactic acid reinforced with Zn particles by fused filament fabrication is demonstrated for the first time. Filaments of 2.85 mm in diameter of PLA reinforced with different weight fractions of $μ$m-sized Zn - 1 wt. \% Mg alloy particles (in the range 3.5 to 17.5 wt. \%) were manufactured by a double extrusion in method in which standard extrusion is followed by a precision extrusion in a filament-maker machine. Filaments with constant diameter, negligible porosity and a homogeneous reinforcement distribution were obtained for Zn weight fractions of up to 10.5\%. It was found that the presence of Zn particles led to limited changes in the physico-chemical properties of the PLA that did not affect the window temperature for 3D printing nor the melt flow index. Thus, porous scaffolds could be manufactured by fused filament fabrication at 190\textdegree C with poly-lactic acid/Zn composites containing 3.5 and 7 wt. \% of Zn and at 170\textdegree C when the Zn content was 10.5 wt. \% with excellent dimensional accuracy and mechanical properties.
△ Less
Submitted 4 August, 2023;
originally announced August 2023.
-
Fractal carbon nanotube fibers with mesoporous crystalline structure
Authors:
H. Yue,
V. Reguero,
E. Senokos,
A. Monreal-Bernal,
B. Mas,
J. P. Fernández-Blázquez,
R. Marcilla,
J. J. Vilatela
Abstract:
Macroscopic fibres of carbon nanotubes are hierarchical structures combining long building blocks preferentially oriented along the fibre axis and a large porosity arising from the imperfect packing of bundles. Synchrotron small-angle X-ray scattering SAXS measurements show that such structure is a surface fractal with fractal dimension (Ds) of 2.5 for MWCNT fibres and 2.8 for SWCNT fibres. N2 ads…
▽ More
Macroscopic fibres of carbon nanotubes are hierarchical structures combining long building blocks preferentially oriented along the fibre axis and a large porosity arising from the imperfect packing of bundles. Synchrotron small-angle X-ray scattering SAXS measurements show that such structure is a surface fractal with fractal dimension (Ds) of 2.5 for MWCNT fibres and 2.8 for SWCNT fibres. N2 adsorption measurements give similar values of 2.54 and 2.50, respectively. The fractal dimension and deviation from Porods law are related to density fluctuations associated with the wide distribution of separations between CNTs. These fluctuations are also evident as diffuse wide-angle X-ray scattering (WAXS) from CNTs at distances above turbostratic separation. The structure of CNT fibres produced at different draw ratios is compared in terms of degree of orientation and characteristic lengths parallel and perpendicular to the fibre. Drawing not only increases alignment but also the fraction of graphitic planes forming coherent domains capable of taking part in stress transfer by shear; thus increasing both tensile modulus and strength. The invariant-normalized intensity of the (002) equatorial reflection thus takes the form of a degree of crystallinity closely related to tensile properties.
△ Less
Submitted 11 February, 2019;
originally announced February 2019.
-
Threading Through Macrocycles Enhances the Performance of Carbon Nanotubes as Polymer Fillers
Authors:
A. López-Moreno,
B. Nieto-Ortega,
M. Moffa,
A. de Juan,
M. Mar Bernal,
J. P. Fernández-Blázquez,
J. J. Vilatela,
D. Pisignano,
E. M. Pérez
Abstract:
In this work we study the reinforcement of polymers by mechanically interlocked derivatives of single-walled carbon nanotubes (SWNTs). We compare the mechanical properties of fibers made of polymers and of composites with pristine single-walled carbon nanotubes (SWNTs), mechanically interlocked derivatives of SWNTs (MINTs) and the corresponding supramolecular models. Improvements of both Young's m…
▽ More
In this work we study the reinforcement of polymers by mechanically interlocked derivatives of single-walled carbon nanotubes (SWNTs). We compare the mechanical properties of fibers made of polymers and of composites with pristine single-walled carbon nanotubes (SWNTs), mechanically interlocked derivatives of SWNTs (MINTs) and the corresponding supramolecular models. Improvements of both Young's modulus and tensile strength of up to 200 % were observed for the polystyrene-MINTs samples with an optimized loading of just 0.01 wt.%, while the supramolecular models with identical chemical composition and loading showed negligible or even detrimental influence. This behavior is found for three different types of SWNTs and two types of macrocycles. Molecular dynamics simulations show that the polymer adopts an elongated conformation parallel to the SWNT when interacting with MINT fillers, irrespective of the macrocycle chemical nature, whereas a more globular structure is taken upon facing with either pristine SWNTs or supramolecular models. The MINT composite architecture thus leads to a more efficient exploitation of the axial properties of the SWNTs and of the polymer chain at the interface, in agreement with experimental results. Our findings demonstrate that the mechanical bond imparts distinctive advantageous properties to SWNT derivatives as polymer fillers.
△ Less
Submitted 2 August, 2016;
originally announced August 2016.