Enhanced magnetism and suppressed magnetoelastic coupling induced by electron do** in Ca$_{1-x}$Y$_{x}$MnReO$_6$
Authors:
A. S. Cavichini,
M. T. Orlando,
M. C. A. Fantini,
R. Tartaglia,
C. W. Galdino,
F. Damay,
F. Porcher,
E. Granado
Abstract:
The Ca$_2$MnReO$_6$ double perovskite is a spin-orbit-assisted Mott insulator with exotic magnetic properties, including a largely non-collinear Mn$^{2+}$ spin arrangement and nearly orthogonal coupling between such spins and the much smaller Re $5d$ magnetic moments. Here, the electron-doped compound Ca$_{1.7}$Y$_{0.3}$MnReO$_6$ is investigated. Neutron and X-ray powder diffraction confirm that n…
▽ More
The Ca$_2$MnReO$_6$ double perovskite is a spin-orbit-assisted Mott insulator with exotic magnetic properties, including a largely non-collinear Mn$^{2+}$ spin arrangement and nearly orthogonal coupling between such spins and the much smaller Re $5d$ magnetic moments. Here, the electron-doped compound Ca$_{1.7}$Y$_{0.3}$MnReO$_6$ is investigated. Neutron and X-ray powder diffraction confirm that nearly full chemical order is maintained at the Mn and Re sites under the Y substitution at the Ca site. X-ray absorption measurements and an analysis of the Mn-O/Re-O bond distances show that the Mn oxidation state remains stable at +2 whereas Re is reduced upon do**. The electron do** increases the magnetic ordering temperature from $T_c = 121$ to $150$ K and also enhances significantly the ferromagnetic component of the Mn spins at the expense of the antiferromagnetic component at the base temperature ($T=3$ K). The lattice parameter anomalies at $T_c$ observed in the parent compound are suppressed by the electron do**. The possible reasons for the enhanced magnetism and the suppressed magnetoelastic coupling in Ca$_{1.7}$Y$_{0.3}$MnReO$_6$ are discussed.
△ Less
Submitted 16 February, 2022;
originally announced February 2022.
-
Crystal structure, cobalt and iron speciation and oxygen non-stoichiometry of La0.6Sr0.4Co1-yFeyO3-d nanorods for IT-SOFC cathodes
Authors:
Augusto E. Mejía Gómez,
Joaquín Sacanell,
Cristián Huck-Iriart,
Cinthia Ramos,
Analía L. Soldati,
Santiago J. A. Figueroa,
Manfredo H. Tabacniks,
Márcia C. A. Fantini,
Aldo F. Craievich,
Diego G. Lamas
Abstract:
Single-phased La0.6Sr0.4Co1-yFeyO3-d (y = 0.2, 0.5, 0.8) nanorods exhibiting the rhombohedral perovskite-type phase were synthesized by a pore-wetting technique. We studied their chemical composition, crystal and electronic structures, morphology and hyperfine properties as a function of the Co/Fe content of the samples. Our results demonstrate that Co cations exhibit a slightly lower oxidation st…
▽ More
Single-phased La0.6Sr0.4Co1-yFeyO3-d (y = 0.2, 0.5, 0.8) nanorods exhibiting the rhombohedral perovskite-type phase were synthesized by a pore-wetting technique. We studied their chemical composition, crystal and electronic structures, morphology and hyperfine properties as a function of the Co/Fe content of the samples. Our results demonstrate that Co cations exhibit a slightly lower oxidation state than Fe ones, resulting in a higher oxygen non-stoichiometry d for Co-rich samples. In addition, the values of d determined in this work for nanostructured samples are much higher than those reported in the literature for bulk materials. This can be attributed to the high degree of defects in nanomaterials and is probably one important factor in the high electrochemical performance for the oxygen reduction reaction of nanostructured La0.6Sr0.4Co1-yFeyO3-d IT-SOFC cathodes, which have been reported in a previous work. Keywords: electrode materials; nanostructured materials; X-ray diffraction; NEXAFS; Mössbauer spectroscopy
△ Less
Submitted 3 December, 2019;
originally announced December 2019.
-
Structural studies of mesoporous ZrO$_{2}$-CeO$_{2}$ and ZrO$_{2}$-CeO$_{2}$/SiO$_{2}$ mixed oxides for catalytical applications
Authors:
R. Bacani,
T. S. Martins,
D. G. Lamas,
M. C. A. Fantini
Abstract:
In this work the synthesis of ZrO$_{2}$-CeO$_{2}$ and ZrO$_{2}$-CeO$_{2}$/SiO$_{2}$ were developed, based on the process to form ordered mesoporous materials such as SBA-15 silica. The triblock copolymer Pluronic P-123 was used as template, aiming to obtain crystalline single phase walls and larger specific surface area, for future applications in catalysis. SAXS and XRD results showed a relations…
▽ More
In this work the synthesis of ZrO$_{2}$-CeO$_{2}$ and ZrO$_{2}$-CeO$_{2}$/SiO$_{2}$ were developed, based on the process to form ordered mesoporous materials such as SBA-15 silica. The triblock copolymer Pluronic P-123 was used as template, aiming to obtain crystalline single phase walls and larger specific surface area, for future applications in catalysis. SAXS and XRD results showed a relationship between ordered pores and the material crystallization. 90% of CeO$_{2}$ leaded to single phase homogeneous ceria-zirconia solid solution of cubic fluorite structure (Fm$\bar{3}$m). The SiO$_{2}$ addition improved structural and textural properties as well as the reduction behavior at lower temperatures, investigated by XANES measurements under H$_{2}$ atmosphere.
△ Less
Submitted 12 January, 2016; v1 submitted 6 March, 2015;
originally announced March 2015.