Mechanisms of Elevated Temperature Galling in Hardfacings
Authors:
Samuel R. Rogers,
David Stewart,
Paul Taplin,
David Dye
Abstract:
The galling mechanism of Tristelle 5183, an Fe-based hardfacing alloy, was investigated at elevated temperature. The test was performed using a bespoke galling rig. Adhesive transfer and galling were found to occur, as a result of shear at the adhesion boundary and the activation of an internal shear plane within one of the tribosurfaces. During deformation, carbides were observed to have fracture…
▽ More
The galling mechanism of Tristelle 5183, an Fe-based hardfacing alloy, was investigated at elevated temperature. The test was performed using a bespoke galling rig. Adhesive transfer and galling were found to occur, as a result of shear at the adhesion boundary and the activation of an internal shear plane within one of the tribosurfaces. During deformation, carbides were observed to have fractured, as a result of the shear train they were exposed to and their lack of ductility. In the case of niobium carbides, their fracture resulted in the formation of voids, which were found to coalesce and led to cracking and adhesive transfer. A tribologically affected zone (TAZ) was found to form, which contained nanocrystalline austenite, as a result of the shear exerted within 30μm of the adhesion boundaries. The galling of Tristelle 5183 initiated from the formation of an adhesive boundary, followed by sub-surface shear in only one tribosurface, Following further sub-surface shear, an internal shear plane is activated. internal shear and shear at the adhesion boundary continues until fracture occur, resulting in adhesive transfer.
△ Less
Submitted 12 March, 2024;
originally announced March 2024.
-
Slip intermittency and dwell fatigue in titanium alloys: a discrete dislocation plasticity analysis
Authors:
Yilun Xu,
Felicity Worsnop,
David Dye,
Fionn P. E. Dunne
Abstract:
Slip intermittency and stress oscillations in titanium alloy Ti-7Al-O that were observed using in-situ far-field high energy X-ray diffraction microscopy (ff-HEDM) are investigated using a discrete dislocation plasticity (DDP) model. The mechanistic foundation of slip intermittency and stress oscillations are shown to be dislocation escape from obstacles during stress holds, governed by a thermal…
▽ More
Slip intermittency and stress oscillations in titanium alloy Ti-7Al-O that were observed using in-situ far-field high energy X-ray diffraction microscopy (ff-HEDM) are investigated using a discrete dislocation plasticity (DDP) model. The mechanistic foundation of slip intermittency and stress oscillations are shown to be dislocation escape from obstacles during stress holds, governed by a thermal activation constitutive law. The stress drop events due to <a>-basal slip are larger in magnitude than those along <a>-prism, which is a consequence of their differing rate sensitivities, previously found from micropillar testing. It is suggested that interstitial oxygen suppresses stress oscillations by inhibiting the thermal activation process. Understanding of these mechanisms is of benefit to the design and safety assessment of jet engine titanium alloys subjected to dwell fatigue.
△ Less
Submitted 11 July, 2023;
originally announced July 2023.
-
Carbon in solution and the Charpy impact performance of medium Mn steels
Authors:
TWK Kwok,
FF Worsnop,
JO Douglas,
D Dye
Abstract:
Carbon is a well known austenite stabiliser and can be used to alter the stacking fault energy and stability against martensitic transformation in medium Mn steels, producing a range of deformation mechanisms such as the Transformation Induced Plasticity (TRIP) or combined Twinning and Transformation Induced Plasticity (TWIP $+$ TRIP) effects. However, the effect of C beyond quasi-static tensile b…
▽ More
Carbon is a well known austenite stabiliser and can be used to alter the stacking fault energy and stability against martensitic transformation in medium Mn steels, producing a range of deformation mechanisms such as the Transformation Induced Plasticity (TRIP) or combined Twinning and Transformation Induced Plasticity (TWIP $+$ TRIP) effects. However, the effect of C beyond quasi-static tensile behaviour is less well known. Therefore, two medium Mn steels with 0.2 wt\% and 0.5 wt\% C were designed to produce similar austenite fractions and stability and therefore tensile behaviour. These were processed to form lamellar and mixed equiaxed $+$ lamellar microstructures. The low C steel had a corrected Charpy impact energy (KV\textsubscript{10}) of 320 J cm\textsuperscript{-2} compared to 66 J cm\textsuperscript{-2} in the high C steel despite both having a ductility of over 35\%. Interface segregation, e.g. of tramp elements, was investigated as a potential cause and none was found. Only a small amount of Mn rejection from partitioning was observed at the interface. The fracture surfaces were investigated and the TRIP effect was found to occur more readily in the Low C Charpy specimen. Therefore it is concluded that the use of C to promote TWIP$+$TRIP behaviour should be avoided in alloy design but the Charpy impact performance can be understood purely in terms of C in solution.
△ Less
Submitted 3 January, 2023;
originally announced January 2023.
-
Crystallographic ordering of Al and Sn in α-Ti
Authors:
Felicity F. Worsnop,
Susannah L. M. Lea,
Jan Ilavsky,
David Rugg,
David Dye
Abstract:
Increasing attention is being paid to $α$$_2$ Ti$_3$(Al,Sn) precipitation from the $α$ phase of titanium alloys owing to its effect on slip band formation, localisation and the implications for fatigue performance in jet engine titanium. However, the early stages of $α$$_2$ precipitation have historically been difficult to observe in TEM, neutron diffraction or atom probe analysis. Here, small ang…
▽ More
Increasing attention is being paid to $α$$_2$ Ti$_3$(Al,Sn) precipitation from the $α$ phase of titanium alloys owing to its effect on slip band formation, localisation and the implications for fatigue performance in jet engine titanium. However, the early stages of $α$$_2$ precipitation have historically been difficult to observe in TEM, neutron diffraction or atom probe analysis. Here, small angle X-ray scattering is used to reexamine the phase boundary in binary Ti-Al and Ti-Sn alloys with around 500 ppmw O. It is found that the phase boundaries in the literature are approximately correct, at 6.2 wt.% Al and 16.9 wt.% Sn, and that this favours the use of Al as a solid solution strengthener over Sn for ambient temperature applications. However, once O content and phase partitioning in $α$+$β$ alloys are taken into account, this implies that Al$_{eq}$ limits for future alloy design of critical rotating parts should be lowered substantially.
△ Less
Submitted 21 November, 2022; v1 submitted 12 October, 2022;
originally announced October 2022.
-
The mechanism of twin thickening and the elastic strain state of TWIP steel nanotwins
Authors:
T W J Kwok,
T P McAuliffe,
A K Ackerman,
B H Savitzky,
M Danaie,
C Ophus,
D Dye
Abstract:
A Twinning Induced Plasticity (TWIP) steel with a nominal composition of Fe-16.4Mn-0.9C-0.5Si-0.05Nb-0.05V was deformed to an engineering strain of 6\%. The strain around the deformation twins were mapped using the 4D-STEM technique. Strain map** showed a large average elastic strain of approximately 6\% in the directions parallel and perpendicular to the twinning direction. However, the large a…
▽ More
A Twinning Induced Plasticity (TWIP) steel with a nominal composition of Fe-16.4Mn-0.9C-0.5Si-0.05Nb-0.05V was deformed to an engineering strain of 6\%. The strain around the deformation twins were mapped using the 4D-STEM technique. Strain map** showed a large average elastic strain of approximately 6\% in the directions parallel and perpendicular to the twinning direction. However, the large average strain comprised of several hot spots of even larger strains of up to 12\%. These hot spots could be attributed to a high density of sessile Frank dislocations on the twin boundary and correspond to shear stresses of 1--1.5 GPa. The strain and therefore stress fields are significantly larger than other materials known to twin and are speculated to be responsible for the early thickness saturation of TWIP steel nanotwins. The ability to keep twins extremely thin helps improve grain fragmentation, \textit{i.e.} the dynamic Hall-Petch effect, and underpins the large elongations and strain hardening rates in TWIP steels.
△ Less
Submitted 30 September, 2022;
originally announced September 2022.
-
Adhesive Transfer operates during Galling
Authors:
Samuel R Rogers,
Jaimie Daure,
Philip Shipway,
David Stewart,
David Dye
Abstract:
In order to reduce cobalt within the primary circuit of pressurised water reactors (PWRs), wear-resistant steels are being researched and developed. In particular interest is the understanding of galling mechanisms, an adhesive wear mechanism which is particularly prevalent in PWR valves. Here we show that large shear stresses and adhesive transfer occur during galling by exploiting the 2 wt per c…
▽ More
In order to reduce cobalt within the primary circuit of pressurised water reactors (PWRs), wear-resistant steels are being researched and developed. In particular interest is the understanding of galling mechanisms, an adhesive wear mechanism which is particularly prevalent in PWR valves. Here we show that large shear stresses and adhesive transfer occur during galling by exploiting the 2 wt per cent manganese difference between 304L and 316L stainless steels, even at relatively low compressive stresses of 50 MPa. Through these findings, the galling mechanisms of stainless steels can be better understood, which may help with the development of galling resistant stainless steels.
△ Less
Submitted 3 October, 2022; v1 submitted 27 May, 2022;
originally announced May 2022.
-
The relative contributions of TWIP and TRIP to strength in fine grained medium-Mn steels
Authors:
T W J Kwok,
P Gong,
R Rose,
D Dye
Abstract:
A medium Mn steel of composition Fe-4.8Mn-2.8Al-1.5Si-0.51C (wt.\%) was processed to obtain two different microstructures representing two different approaches in the hot rolling mill, resulting in equiaxed vs. a mixed equiaxed and lamellar microstructures. Both were found to exhibit a simultaneous TWIP$+$TRIP plasticity enhancing mechanism where deformation twins and $α'$-martensite formed indepe…
▽ More
A medium Mn steel of composition Fe-4.8Mn-2.8Al-1.5Si-0.51C (wt.\%) was processed to obtain two different microstructures representing two different approaches in the hot rolling mill, resulting in equiaxed vs. a mixed equiaxed and lamellar microstructures. Both were found to exhibit a simultaneous TWIP$+$TRIP plasticity enhancing mechanism where deformation twins and $α'$-martensite formed independently of twinning with strain. Interrupted tensile tests were conducted in order to investigate the differences in deformation structures between the two microstructures. A constitutive model was used to find that, surprisingly, twinning contributed relatively little to the strength of the alloy, chiefly due to the fine initial slip lengths that then gave rise to relatively little opportunity for work hardening by grain subdivision. Nevertheless, with lower high-cost alloying additions than equivalent Dual Phase steels (2-3 wt\% Mn) and greater ductility, medium-Mn TWIP$+$TRIP steels still represent an attractive area for future development.
△ Less
Submitted 19 August, 2022; v1 submitted 11 April, 2022;
originally announced April 2022.
-
The influence of alloying on slip intermittency and the implications for dwell fatigue in titanium
Authors:
Felicity F. Worsnop,
Rachel E. Lim,
Joel V. Bernier,
Darren C. Pagan,
Yilun Xu,
Thomas P. McAuliffe,
David Rugg,
David Dye
Abstract:
Dwell fatigue, the reduction in fatigue life experienced by titanium alloys due to holds at stresses as low as 60% of yield, has been implicated in several uncontained jet engine failures. Dislocation slip has long been observed to be an intermittent, scale-bridging phenomenon, similar to that seen in earthquakes but at the nanoscale, leading to the speculation that large stress bursts might promo…
▽ More
Dwell fatigue, the reduction in fatigue life experienced by titanium alloys due to holds at stresses as low as 60% of yield, has been implicated in several uncontained jet engine failures. Dislocation slip has long been observed to be an intermittent, scale-bridging phenomenon, similar to that seen in earthquakes but at the nanoscale, leading to the speculation that large stress bursts might promote the initial opening of a crack. Here we observe such stress bursts at the scale of individual grains in situ, using high energy X-ray diffraction microscopy in Ti-7Al-O alloys. This shows that the detrimental effect of precipitation of ordered Ti_3Al is to increase the magnitude of rare pri<a> and bas<a> slip bursts associated with slip localisation. In contrast, the addition of trace O interstitials is beneficial, reducing the magnitude of bas<a> slip bursts and increasing the homogeneity between basal and prismatic <a> slip. This is further evidence that the formation of long paths for easy basal plane slip localisation should be avoided when engineering titanium alloys against dwell fatigue.
△ Less
Submitted 1 August, 2022; v1 submitted 28 March, 2022;
originally announced March 2022.
-
The role of \b{eta} pockets resulting from Fe impurities in hydride formation in titanium
Authors:
Qing Tan,
Zhiran Yan,
Huijun Wang,
David Dye,
Stoichko Antonov,
Baptiste Gault
Abstract:
The corrosion potential of commercially pure titanium in NaCl solutions is dramatically affected by trace Fe additions, which cause the appearance of submicron pockets of \b{eta} phase at grain boundary triple points. Furthermore, the low solubility of hydrogen in hexagonal close-packed α-Ti makes titanium alloys prone to subsequent hydride-associated failures due to stress corrosion cracking. We…
▽ More
The corrosion potential of commercially pure titanium in NaCl solutions is dramatically affected by trace Fe additions, which cause the appearance of submicron pockets of \b{eta} phase at grain boundary triple points. Furthermore, the low solubility of hydrogen in hexagonal close-packed α-Ti makes titanium alloys prone to subsequent hydride-associated failures due to stress corrosion cracking. We analyzed α-α and α-\b{eta} sections of the abutting grain boundary of a \b{eta} pocket in a Grade 2 CP-Ti, and the α-\b{eta} phase boundary. Fe and H partition to \b{eta} and segregate at the grain boundary, but no segregation is seen at the α-\b{eta} phase boundary. In contrast, a significant Ni (>1 at%) accumulation is observed at the α-\b{eta} phase boundary. We propose that the \b{eta}-pockets act as hydrogen traps and facilitate the nucleation and growth of hydrides along grain boundaries in CP-Ti.
△ Less
Submitted 5 January, 2022;
originally announced January 2022.
-
Tailoring the Deformation Behaviour of a Medium Mn Steel through Isothermal Intercritical Annealing
Authors:
X. Xu,
T. W. J. Kwok,
P. Gong,
D. Dye
Abstract:
A novel concept of varying the strain hardening rate of a medium Mn steel with 8 wt\% Mn by varying the duration of the intercritical anneal after hot rolling was explored. It was found that the stability of the austenite phase showed an inverse square root relationship with intercritical annealing duration and that the maximum strain hardening rate showed a linear relationship with austenite stab…
▽ More
A novel concept of varying the strain hardening rate of a medium Mn steel with 8 wt\% Mn by varying the duration of the intercritical anneal after hot rolling was explored. It was found that the stability of the austenite phase showed an inverse square root relationship with intercritical annealing duration and that the maximum strain hardening rate showed a linear relationship with austenite stability. The change in austenite stability was attributed to continuous Mn enrichment with increasing intercritical annealling duration. Twinned martensite was also found to be the most likely product of the martensitic transformation during deformation.
△ Less
Submitted 4 April, 2022; v1 submitted 22 December, 2021;
originally announced December 2021.
-
Strengthening $κ$-carbide steels using residual dislocation content
Authors:
T. W. J. Kwok,
K. M. Rahman,
V. A. Vorontsov,
D. Dye
Abstract:
A steel with nominal composition Fe-28Mn-8Al-1.0C in mass percent was hot rolled at two temperatures, 1100 \degree C and 850 \degree C and subsequently aged at 550 \degree C for 24 h. The lower temperature rolling resulted in a yield strength increment of 299 MPa while still retaining an elongation to failure of over 30\%. The large improvement in strength was attributed to an increase in residual…
▽ More
A steel with nominal composition Fe-28Mn-8Al-1.0C in mass percent was hot rolled at two temperatures, 1100 \degree C and 850 \degree C and subsequently aged at 550 \degree C for 24 h. The lower temperature rolling resulted in a yield strength increment of 299 MPa while still retaining an elongation to failure of over 30\%. The large improvement in strength was attributed to an increase in residual dislocation density which was retained even after the ageing heat treatment. A homogeneous precipitation of $κ$-carbides in both samples also showed that the high residual dislocation density did not adversely affect precipitation kinetics. These findings demonstrate that the tensile properties of this class of steel can yet be improved by optimising hot rolling process parameters.
△ Less
Submitted 2 December, 2021;
originally announced December 2021.
-
Precipitate dissolution during deformation induced twin thickening in a CoNi-base superalloy subject to creep
Authors:
Vassili Vorontsov,
Thomas McAuliffe,
Mark C. Hardy,
David Dye,
Ioannis Bantounas
Abstract:
The tensile creep performance of a polycrystalline Co/Ni-base superalloy with a multimodal gamma prime distribution has been examined at 800C and 300MPa. The rupture life of the alloy is comparable to that of RR1000 tested under similar conditions. Microstructural examination of the alloy after testing revealed the presence of continuous gamma prime precipitates and M23C6 carbides along the grain…
▽ More
The tensile creep performance of a polycrystalline Co/Ni-base superalloy with a multimodal gamma prime distribution has been examined at 800C and 300MPa. The rupture life of the alloy is comparable to that of RR1000 tested under similar conditions. Microstructural examination of the alloy after testing revealed the presence of continuous gamma prime precipitates and M23C6 carbides along the grain boundaries. Intragranularly, coarsening of the secondary gamma prime precipitates occurred at the expense of the fine tertiary gamma prime. Long planar deformation bands, free of gamma prime, were also observed to traverse individual grains ending in steps at the grain boundaries. Examination of the deformation bands confirmed that they were microtwins. Long sections of the microtwins examined were depleted of gamma prime stabilising elements across their entire width, suggesting that certain alloy compositions are susceptible to precipitate dissolution during twin thickening. A mechanism for the dissolution of the precipitates is suggested based on the Kolbe reordering mechanism.
△ Less
Submitted 24 November, 2021;
originally announced November 2021.
-
A scale up study on chemical segregation and the effects on tensile properties in two medium Mn steel castings
Authors:
T. W. J. Kwok,
C. Slater,
X. Xu,
C. Davis,
D. Dye
Abstract:
Two ingots weighing 400 g and 5 kg with nominal compositions of Fe-8Mn-4Al-2Si-0.5C-0.07V-0.05Sn were produced to investigate the effect of processing variables on microstructure development. The larger casting has a cooling rate more representative of commercial production and provides an understanding of the potential challenges arising from casting-related segregation during efforts to scale up…
▽ More
Two ingots weighing 400 g and 5 kg with nominal compositions of Fe-8Mn-4Al-2Si-0.5C-0.07V-0.05Sn were produced to investigate the effect of processing variables on microstructure development. The larger casting has a cooling rate more representative of commercial production and provides an understanding of the potential challenges arising from casting-related segregation during efforts to scale up medium Mn steels, whilst the smaller casting has a high cooling rate and different segregation pattern. Sections from both ingots were homogenised at 1250 \degree C for various times to study the degree of chemical homogeneity and $δ$-ferrite dissolution. Within 2 h, the Mn segregation range (max $-$ min) decreased from 8.0 to 1.7 wt\% in the 400 g ingot and from 6.2 to 1.5 wt\% in the 5 kg ingot. Some $δ$-ferrite also remained untransformed after 2 h in both ingots but with the 5 kg ingot showing nearly three times more than the 400 g ingot. Micress modelling was carried out and good agreement was seen between predicted and measured segregation levels and distribution. After thermomechanical processing, it was found that the coarse untransformed $δ$-ferrite in the 5 kg ingot turned into coarse $δ$-ferrite stringers in the finished product, resulting in a slight decrease in yield strength. Nevertheless, rolled strips from both ingots showed $>$900 MPa yield strength, $>$1100 MPa tensile strength and $>$40\% elongation with $<$10\% difference in strength and no change in ductility when compared to a fully homogenised sample.
△ Less
Submitted 25 October, 2021;
originally announced October 2021.
-
Microstructure evolution and tensile behaviour of a cold rolled 8 wt\% Mn medium manganese steel
Authors:
Thomas WJ Kwok,
Peng Gong,
Xin Xu,
John Nutter,
W Mark Rainforth,
David Dye
Abstract:
A novel medium manganese steel named Novalloy with composition Fe-8.3Mn-3.8Al-1.8Si-0.5C-0.06V-0.05Sn was developed and thermomechanically processed through hot rolling and intercritical annealing. The steel possessed a yield strength of 1 GPa, tensile strength of 1.13 GPa and ductility of 41\%. In order to study the effect of cold rolling after intercritical annealing on subsequent tensile proper…
▽ More
A novel medium manganese steel named Novalloy with composition Fe-8.3Mn-3.8Al-1.8Si-0.5C-0.06V-0.05Sn was developed and thermomechanically processed through hot rolling and intercritical annealing. The steel possessed a yield strength of 1 GPa, tensile strength of 1.13 GPa and ductility of 41\%. In order to study the effect of cold rolling after intercritical annealing on subsequent tensile properties, the steel was further cold rolled up to 20\% reduction. After cold rolling, it was observed that the strain hardening rate increased continuously with increasing cold rolling reduction but without a significant drop in ductility during subsequent tensile tests. The microstructural evolution with cold rolling reduction was analysed to understand the mechanisms behind this enhanced TRIP effect. It was found that cold rolling activated additional twinning systems which provided a large number of potent nucleation sites for strain induced martensite to form during subsequent tensile tests.
△ Less
Submitted 29 July, 2021; v1 submitted 19 March, 2021;
originally announced March 2021.
-
Social Media Study of Public Opinions on Potential COVID-19 Vaccines: Informing Dissent, Disparities, and Dissemination
Authors:
Hanjia Lyu,
Junda Wang,
Wei Wu,
Viet Duong,
Xiyang Zhang,
Timothy D. Dye,
Jiebo Luo
Abstract:
The current development of vaccines for SARS-CoV-2 is unprecedented. Little is known, however, about the nuanced public opinions on the vaccines on social media. We adopt a human-guided machine learning framework using more than six million tweets from almost two million unique Twitter users to capture public opinions on the potential vaccines for SARS-CoV-2, classifying them into three groups: pr…
▽ More
The current development of vaccines for SARS-CoV-2 is unprecedented. Little is known, however, about the nuanced public opinions on the vaccines on social media. We adopt a human-guided machine learning framework using more than six million tweets from almost two million unique Twitter users to capture public opinions on the potential vaccines for SARS-CoV-2, classifying them into three groups: pro-vaccine, vaccine-hesitant, and anti-vaccine. We aggregate opinions at the state and country levels, and find that the major changes in the percentages of different opinion groups roughly correspond to the major pandemic-related events. Interestingly, the percentage of the pro-vaccine group is lower in the Southeast part of the United States. Using multinomial logistic regression, we compare demographics, social capital, income, religious status, political affiliations, geo-locations, sentiment of personal pandemic experience and non-pandemic experience, and county-level pandemic severity perception of these three groups to investigate the scope and causes of public opinions on vaccines. We find that socioeconomically disadvantaged groups are more likely to hold polarized opinions on potential COVID-19 vaccines. People who have the worst personal pandemic experience are more likely to hold the anti-vaccine opinion. Next, by conducting counterfactual analyses, we find that the U.S. public is most concerned about the safety, effectiveness, and political issues regarding potential vaccines for COVID-19, and improving personal pandemic experience increases the vaccine acceptance level. We believe this is the first large-scale social media-based study to analyze public opinions on potential COVID-19 vaccines that can inform more effective vaccine distribution policies and strategies.
△ Less
Submitted 9 August, 2021; v1 submitted 3 December, 2020;
originally announced December 2020.
-
Mechanisms of Ti3Al precipitation in hcp alpha-Ti
Authors:
Felicity F. Dear,
Paraskevas Kontis,
Baptiste Gault,
Jan Ilavsky,
David Rugg,
David Dye
Abstract:
Nucleation and growth of Ti$_3$Al \textalpha{}$_2$ ordered domains in \textalpha{}-Ti--Al--X alloys were characterised using a combination of transmission electron microscopy, atom probe tomography and small angle X-ray scattering. Model alloys based on Ti--7Al~(wt.\%) and containing O, V and Mo were aged at \SI{550}{\celsius} for times up to \SI{120}{\day} and the resulting precipitate dispersion…
▽ More
Nucleation and growth of Ti$_3$Al \textalpha{}$_2$ ordered domains in \textalpha{}-Ti--Al--X alloys were characterised using a combination of transmission electron microscopy, atom probe tomography and small angle X-ray scattering. Model alloys based on Ti--7Al~(wt.\%) and containing O, V and Mo were aged at \SI{550}{\celsius} for times up to \SI{120}{\day} and the resulting precipitate dispersions were observed at intermediate points. Precipitates grew to around \SI{30}{\nano\metre} in size, with a volume fraction of 6--10\% depending on tertiary solutes. Interstitial O was found to increase the equilibrium volume fraction of \textalpha{}$_2$, while V and Mo showed relatively little influence. Addition of any of the solutes in this study, but most prominently Mo, was found to increase nucleation density and decrease precipitate size and possibly coarsening rate. Coarsening can be described by the Lifshitz-Slyozov-Wagner model, suggesting a matrix diffusion-controlled coarsening mechanism (rather than control by interfacial coherency). Solutionising temperature was found to affect nucleation number density with an activation energy of $E_{\mathrm{f}} = 1.5\pm{}0.4$~eV, supporting the hypothesis that vacancy concentration affects \textalpha{}$_2$ nucleation. The observation that all solutes increase nucleation number density is also consistent with a vacancy-controlled nucleation mechanism.
△ Less
Submitted 18 March, 2021; v1 submitted 26 October, 2020;
originally announced October 2020.
-
AgCl-induced hot salt stress corrosion cracking in a titanium alloy
Authors:
Yitong Shi,
Sudha Joseph,
Edward A. Saunders,
Rebecca S. Sandala,
Adrian Walker,
Trevor C. Lindley,
David Dye
Abstract:
The mechanism of AgCl-induced stress corrosion cracking of Ti-6246 was examined at \SI{500}{\mega\pascal} and \SI{380}{\celsius} for \SI{24}{\hour} exposures. SEM and STEM-EDX examination of a FIB-sectioned blister and crack showed that metallic Ag was formed and migrated along the crack. TEM analysis also revealed the presence of \ce{SnO2} and \ce{Al2O3} corrosion products mixed into \ce{TiO2}. T…
▽ More
The mechanism of AgCl-induced stress corrosion cracking of Ti-6246 was examined at \SI{500}{\mega\pascal} and \SI{380}{\celsius} for \SI{24}{\hour} exposures. SEM and STEM-EDX examination of a FIB-sectioned blister and crack showed that metallic Ag was formed and migrated along the crack. TEM analysis also revealed the presence of \ce{SnO2} and \ce{Al2O3} corrosion products mixed into \ce{TiO2}. The fracture surface has a transgranular nature with a brittle appearance in the primary $α$ phase. Long, straight and non-interacting dislocations were observed in a cleavage-fractured primary $α$ grain, with basal and pyramidal traces. This is consistent with a dislocation emission view of the the cracking mechanism.
△ Less
Submitted 19 March, 2021; v1 submitted 26 October, 2020;
originally announced October 2020.
-
A cracking oxygen story: a new view of stress corrosion cracking in titanium alloys
Authors:
Sudha Joseph,
Paraskevas Kontis,
Yanhong Chang,
Yitong Shi,
Dierk Raabe,
Baptiste Gault,
David Dye
Abstract:
Titanium alloys can suffer from halide-associated stress corrosion cracking at elevated temperatures e.g., in jet engines, where chlorides and Ti-oxide promote the cracking of water vapour in the gas stream, depositing embrittling species at the crack tip. Here we report, using isotopically-labelled experiments, that crack tips in an industrial Ti-6Al-2Sn-4Zr-6Mo alloy are strongly enriched (>5 at…
▽ More
Titanium alloys can suffer from halide-associated stress corrosion cracking at elevated temperatures e.g., in jet engines, where chlorides and Ti-oxide promote the cracking of water vapour in the gas stream, depositing embrittling species at the crack tip. Here we report, using isotopically-labelled experiments, that crack tips in an industrial Ti-6Al-2Sn-4Zr-6Mo alloy are strongly enriched (>5 at.%) in oxygen from the water vapour, far greater than the amounts (0.25 at.%) required to embrittle the material. Surprisingly, relatively little hydrogen (deuterium) is measured, despite careful preparation and analysis. Therefore, we suggest that a combined effect of O and H leads to cracking, with O playing a vital role, since it is well-known to cause embrittlement of the alloy. In contrast it appears that in alpha+beta Ti alloys, it may be that H may drain away into the bulk owing to its high solubility in beta-Ti, rather than being retained in the stress field of the crack tip. Therefore, whilst hydrides may form on the fracture surface, hydrogen ingress might not be the only plausible mechanism of embrittlement of the underlying matrix. This possibility challenges decades of understanding of stress-corrosion cracking as being related solely to the hydrogen enhanced localised plasticity (HELP) mechanism, which explains why H-doped Ti alloys are embrittled. This would change the perspective on stress corrosion embrittlement away from a focus purely on hydrogen to also consider the ingress of O originating from the water vapour, insights critical for designing corrosion resistant materials.
△ Less
Submitted 23 November, 2021; v1 submitted 22 September, 2020;
originally announced September 2020.
-
Quantitative precipitate classification and grain boundary property control in Co/Ni-base superalloys
Authors:
Thomas P McAuliffe,
Ioannis Bantounas,
Lucy R Reynolds,
Alex Foden,
Mark Hardy,
T Ben Britton,
David Dye
Abstract:
A correlative approach is employed to simultaneously assess structure and chemistry of (carbide and boride) precipitates in a set of novel Co/Ni-base superalloys. Structure is derived from electron backscatter diffraction (EBSD) with pattern template matching, and chemistry obtained with energy dispersive X-ray spectroscopy (EDS). It is found that the principal carbide in these alloys is Mo and W…
▽ More
A correlative approach is employed to simultaneously assess structure and chemistry of (carbide and boride) precipitates in a set of novel Co/Ni-base superalloys. Structure is derived from electron backscatter diffraction (EBSD) with pattern template matching, and chemistry obtained with energy dispersive X-ray spectroscopy (EDS). It is found that the principal carbide in these alloys is Mo and W rich with the M6C structure. An M2B boride, also exhibiting Mo and W segregation is observed at B levels above approximately 0.085 at.%. These phases are challenging to distinguish in an SEM with chemical information (EDS or backscatter Z-contrast) alone, without the structural information provided by EBSD. Only correlative chemical and structural fingerprinting is necessary and sufficient to fully define a phase. The identified phases are dissimilar to those predicted using ThermoCalc. We additionally perform an assessment of the grain boundary serratability in these alloys, and observe that significant amplitude is only obtained in the absence of pinning intergranular precipitates.
△ Less
Submitted 2 September, 2020;
originally announced September 2020.
-
Fatigue cracking in gamma titanium aluminide
Authors:
Claire F Trant,
Trevor C Lindley,
Nigel Martin,
Mark Dixon,
David Dye
Abstract:
Cast and HIP'ed \textgamma-TiAl 4522XD is being developed for use in jet engine low pressure turbine blades, where temperature variations occur through the flight cycle. The effects of temperature variations on fatigue cracking were therefore examined in this study. It was found that fatigue crack growth rates were higher at 750C than 400C, but that $ΔK_\mathrm{th}$ was also higher. Temperature ex…
▽ More
Cast and HIP'ed \textgamma-TiAl 4522XD is being developed for use in jet engine low pressure turbine blades, where temperature variations occur through the flight cycle. The effects of temperature variations on fatigue cracking were therefore examined in this study. It was found that fatigue crack growth rates were higher at 750C than 400C, but that $ΔK_\mathrm{th}$ was also higher. Temperature excursions between 400 and 750C during fatigue crack growth resulted in retardation of the crack growth rate, both on heating and cooling. It was also found that for notches $0.6$~mm in length and smaller, initiation from the microstructure could instead be observed at stresses similar to the material failure stress; a microstructural initiation site exists. A change from trans- to mixed trans-, inter- and intra-lamellar cracking could be observed where the estimated size of the crack tip plastic zone exceeded the colony size.
△ Less
Submitted 27 August, 2020; v1 submitted 9 July, 2020;
originally announced July 2020.
-
Spherical-angular dark field imaging and sensitive microstructural phase clustering with unsupervised machine learning
Authors:
Thomas P McAuliffe,
David Dye,
T Ben Britton
Abstract:
Electron backscatter diffraction is a widely used technique for nano- to micro-scale analysis of crystal structure and orientation. Backscatter patterns produced by an alloy solid solution matrix and its ordered superlattice exhibit only extremely subtle differences, due to the inelastic scattering that precedes coherent diffraction. We show that unsupervised machine learning (with PCA, NMF, and a…
▽ More
Electron backscatter diffraction is a widely used technique for nano- to micro-scale analysis of crystal structure and orientation. Backscatter patterns produced by an alloy solid solution matrix and its ordered superlattice exhibit only extremely subtle differences, due to the inelastic scattering that precedes coherent diffraction. We show that unsupervised machine learning (with PCA, NMF, and an autoencoder neural network) is well suited to fine feature extraction and superlattice/matrix classification. Remap** cluster average patterns onto the diffraction sphere lets us compare Kikuchi band profiles to dynamical simulations, confirm the superlattice stoichiometry, and facilitate virtual imaging with a spherical solid angle aperture. This pipeline now enables unparalleled map** of exquisite crystallographic detail from a wide range of materials within the scanning electron microscope.
△ Less
Submitted 12 October, 2020; v1 submitted 21 May, 2020;
originally announced May 2020.
-
4D-STEM elastic stress state characterisation of a TWIP steel nanotwin
Authors:
T P McAuliffe,
A K Ackerman,
B H Savitzky,
T W J Kwok,
M Danaie,
C Ophus,
D Dye
Abstract:
We measure the stress state in and around a deformation nanotwin in a twinning-induced plasticity (TWIP) steel. Using four-dimensional scanning transmission electron microscopy (4D-STEM), we measure the elastic strain field in a 68.2-by-83.1 nm area of interest with a scan step of 0.36 nm and a diffraction limit resolution of 0.73 nm. The stress field in and surrounding the twin matches the form e…
▽ More
We measure the stress state in and around a deformation nanotwin in a twinning-induced plasticity (TWIP) steel. Using four-dimensional scanning transmission electron microscopy (4D-STEM), we measure the elastic strain field in a 68.2-by-83.1 nm area of interest with a scan step of 0.36 nm and a diffraction limit resolution of 0.73 nm. The stress field in and surrounding the twin matches the form expected from analytical theory and is on the order of 15 GPa, close to the theoretical strength of the material. We infer that the measured back-stress limits twin thickening, providing a rationale for why TWIP steel twins remain thin during deformation, continuously dividing grains to give substantial work hardening. Our results support modern mechanistic understanding of the influence of twinning on crack propagation and embrittlement in TWIP steels.
△ Less
Submitted 20 October, 2020; v1 submitted 8 April, 2020;
originally announced April 2020.
-
The Interaction of Galling and Oxidation in 316L Stainless Steel
Authors:
Samuel R. Rogers,
David Bowden,
Rahul Unnikrishnan,
Fabio Scenini,
Michael Preuss,
David Stewart,
Daniele Dini,
David Dye
Abstract:
The galling behaviour of 316L stainless steel was investigated in both the unoxidised and oxidised states, after exposure in simulated PWR water for 850 hours. Galling testing was performed according to ASTM G196 in ambient conditions. 316L was found to gall by the wedge growth and flow mechanism in both conditions. This resulted in folds ahead of the prow and adhesive junction, forming a heavily…
▽ More
The galling behaviour of 316L stainless steel was investigated in both the unoxidised and oxidised states, after exposure in simulated PWR water for 850 hours. Galling testing was performed according to ASTM G196 in ambient conditions. 316L was found to gall by the wedge growth and flow mechanism in both conditions. This resulted in folds ahead of the prow and adhesive junction, forming a heavily sheared multilayered prow. The galling trough was seen to have failed through successive shear failure during wedge flow. Immediately beneath the surface a highly sheared nanocrystalline layer was seen, termed the tribologically affected zone (TAZ). It was observed that strain-induced martensite formed within the TAZ. Galling damage was quantified using Rt (maximum height - maximum depth) and galling area (the proportion of the sample which is considered galled), and it was shown that both damage measures decreased significantly on the oxidised samples. At an applied normal stress of 4.2 MPa the galled area was 14 % vs. 1.2 % and the Rt was 780 um vs. 26 um for the unoxidised and oxidised sample respectively. This trend was present at higher applied normal stresses, although less prominent. This difference in galling behaviour is likely to be a result of a reduction in adhesion in the case of the oxidised surface.
△ Less
Submitted 11 December, 2019;
originally announced December 2019.
-
Design of a High Strength, High Ductility 12 wt% Mn Medium Manganese Steel With Hierarchical Deformation Behaviour
Authors:
T W J Kwok,
K M Rahman,
X Xu,
I Bantounas,
J F Kelleher,
S Daswari,
T Alam,
R Banerjee,
D Dye
Abstract:
A novel medium Mn steel of composition Fe-12Mn-4.8Al-2Si-0.32C-0.3V was manufactured with 1.09 GPa yield strength, 1.26 GPa tensile strength and 54% elongation. The thermomechanical process route was designed to be industrially translatable and consists of hot and then warm rolling before a 30 min intercritical anneal. The resulting microstructure comprised of coarse elongated austenite grains in…
▽ More
A novel medium Mn steel of composition Fe-12Mn-4.8Al-2Si-0.32C-0.3V was manufactured with 1.09 GPa yield strength, 1.26 GPa tensile strength and 54% elongation. The thermomechanical process route was designed to be industrially translatable and consists of hot and then warm rolling before a 30 min intercritical anneal. The resulting microstructure comprised of coarse elongated austenite grains in the rolling direction surrounded by necklace layers of fine austenite and ferrite grains. The tensile behaviour was investigated by in-situ neutron diffraction and the evolution of microstructure studied with Electron Backscattered Diffraction (EBSD). It was found that the coarse austenite grains contributed to the first stage of strain hardening by transforming into martensite and the fine austenite necklace grains contributed to the second stage of strain hardening by a mixture of twinning and transformation induced plasticity (TWIP and TRIP) mechanisms. This hierarchical deformation behaviour contributed to the exceptional ductility of this steel.
△ Less
Submitted 21 April, 2020; v1 submitted 20 August, 2019;
originally announced August 2019.
-
Advancing characterisation with statistics from correlative electron diffraction and X-ray spectroscopy, in the scanning electron microscope
Authors:
T. P. McAuliffe,
A. Foden,
C. Bilsland,
D. Daskalaki-Mountanou,
D. Dye,
T. B. Britton
Abstract:
The routine and unique determination of minor phases in microstructures is critical to materials science. In metallurgy alone, applications include alloy and process development and the understanding of degradation in service. We develop a correlative method, exploring superalloy microstructures which are examined in the scanning electron microscope (SEM) using simultaneous energy dispersive X-ray…
▽ More
The routine and unique determination of minor phases in microstructures is critical to materials science. In metallurgy alone, applications include alloy and process development and the understanding of degradation in service. We develop a correlative method, exploring superalloy microstructures which are examined in the scanning electron microscope (SEM) using simultaneous energy dispersive X-ray spectroscopy (EDS) and electron backscatter diffraction (EBSD). This is performed at an appropriate length scale for characterisation of carbide phases' shape, size, location, and distribution. EDS and EBSD data are generated using two different physical processes, but each provide a signature of the material interacting with the incoming electron beam. Recent advances in post-processing, driven by "big data" approaches, include use of principal component analysis (PCA). Components are subsequently characterised to assign labels to a mapped region. To provide physically meaningful signals, the principal components may be rotated to control the distribution of variance. In this work, we develop this method further through a weighted PCA approach. We use the EDS and EBSD signals concurrently, thereby labelling each region using both EDS (chemistry) and EBSD (crystal structure) information. This provides a new method of amplifying signal-to-noise for very small phases in mapped regions, especially where the EDS or EBSD signal is not unique enough alone for classification.
△ Less
Submitted 14 January, 2020; v1 submitted 12 August, 2019;
originally announced August 2019.
-
Could face-centered cubic titanium in cold-rolled commercially-pure titanium only be a Ti-hydride?
Authors:
Yanhong Chang,
Siyuan Zhang,
Christian H. Liebscher,
David Dye,
Dirk Ponge,
Christina Scheu,
Gerhard Dehm,
Dierk Raabe,
Baptiste Gault,
Wenjun Lu
Abstract:
A face-centered cubic (FCC) phase in electro-polished specimens for transmission electron microscopy of commercially pure titanium has sometimes been reported. Here, a combination of atom-probe tomography, scanning transmission electron microscopy and low-loss electron energy loss spectroscopy is employed to study both the crystal structural and chemical composition of this FCC phase. Our results…
▽ More
A face-centered cubic (FCC) phase in electro-polished specimens for transmission electron microscopy of commercially pure titanium has sometimes been reported. Here, a combination of atom-probe tomography, scanning transmission electron microscopy and low-loss electron energy loss spectroscopy is employed to study both the crystal structural and chemical composition of this FCC phase. Our results prove that the FCC phase is actually a TiHx (x>1) hydride, and not a new allotrope of Ti, in agreement with previous reports. The formation of the hydride is discussed.
△ Less
Submitted 23 October, 2019; v1 submitted 2 July, 2019;
originally announced July 2019.
-
The role of dwell hold on the dislocation mechanisms of fatigue in a near alpha titanium alloy
Authors:
Sudha Joseph,
Kavitha Joseph,
Trevor C Lindley,
David Dye
Abstract:
The dislocation structures appearing in highly mis-oriented soft/hard grain pairs in near-alpha titanium alloy Ti6242Si were examined with and without the application of load holds (dwell) during fatigue. Dislocation pile-up in a soft grain resulted in internal stresses in an adjacent hard grain which could be relaxed by dislocation multiplication at localized Frank-Read sources, a process assiste…
▽ More
The dislocation structures appearing in highly mis-oriented soft/hard grain pairs in near-alpha titanium alloy Ti6242Si were examined with and without the application of load holds (dwell) during fatigue. Dislocation pile-up in a soft grain resulted in internal stresses in an adjacent hard grain which could be relaxed by dislocation multiplication at localized Frank-Read sources, a process assisted by the provision of a relaxation time during a load hold. The rate of this process is suggested to be controlled by <c+a> pyramidal cross-slip and <a> basal junction formation. A high density of <a> prism pile-ups is observed by dual slip, together with the nucleation of edge dislocations in the soft grain of a highly mis-oriented grain pair, increasing the possibility of cracking. The stress concentration developed by such pile-ups is found to be higher in dwell fatigue (single-ended pile-ups) than in LCF (double ended). Analytical modelling shows that the maximum normal stress produced on the hard grain in dwell fatigue by this pile-up would be near-basal, ~2.5 degree to (0002). This provides support for the dominant hypothesis for the rationalisation of dwell fatigue crack nucleation in Ti alloys, which derives from the Stroh pile-up model, and elaboration of the underlying dislocation phenomena that result from load shedding and lead to basal faceting.
△ Less
Submitted 13 May, 2020; v1 submitted 28 May, 2019;
originally announced May 2019.
-
Rapid Electron Backscatter Diffraction Map**: Painting by Numbers
Authors:
Vivian S Tong,
Alexander J Knowles,
David Dye,
T Ben Britton
Abstract:
Microstructure characterisation has been greatly enhanced through the use of electron backscatter diffraction (EBSD), where rich maps are generated through analysis of the crystal phase and orientation in the scanning electron microscope (SEM). Conventional EBSD analysis involves raster scanning of the electron beam and the serial analysis of each diffraction pattern in turn. For grain shape, crys…
▽ More
Microstructure characterisation has been greatly enhanced through the use of electron backscatter diffraction (EBSD), where rich maps are generated through analysis of the crystal phase and orientation in the scanning electron microscope (SEM). Conventional EBSD analysis involves raster scanning of the electron beam and the serial analysis of each diffraction pattern in turn. For grain shape, crystallographic texture, and microstructure analysis this can be inefficient. In this work, we present Rapid EBSD, a data fusion approach combining forescatter electron (FSE) imaging with static sparse sampling of EBSD patterns. We segment the FSE image into regions of similar colour (i.e. phase and crystal orientation) and then collect representative EBSD data for each segmented region. This enables microstructural assessment to be performed at the spatial resolution of the (fast) FSE imaging whilst including orientation and phase information from EBSD analysis of representative points. We demonstrate the Rapid EBSD technique on samples of a cobalt based superalloy and a strained dual phase titanium alloy, comparing the results with conventional analysis. Rapid EBSD is advantageous for assessing grain size distributions in time-limited experiments.
△ Less
Submitted 13 November, 2018; v1 submitted 19 September, 2018;
originally announced September 2018.
-
The effect of pressure on hydrogen solubility in Zircaloy-4
Authors:
H. E. Weekes,
D. Dye,
J. E. Proctor,
D. S. Smith,
C. Simionescu,
T. J. Prior,
M. R. Wenman
Abstract:
The effect of pressure on the room temperature solubility of hydrogen in Zircaloy-4 was examined using synchrotron X-ray diffraction on small ground flake samples in a diamond anvil cell at pressures up to 20.9 GPa. Different combinations of hydrogen level/state in the sample and of pressure transmitting medium were examined; in all three cases examined, it could be concluded that pressure resulte…
▽ More
The effect of pressure on the room temperature solubility of hydrogen in Zircaloy-4 was examined using synchrotron X-ray diffraction on small ground flake samples in a diamond anvil cell at pressures up to 20.9 GPa. Different combinations of hydrogen level/state in the sample and of pressure transmitting medium were examined; in all three cases examined, it could be concluded that pressure resulted in the dissolution of d hydrides and that interstitial hydrogen retards the formation of w Zr. A pressure of around 9 GPa was required to halve the hydride fraction. These results imply that the effect of pressure is thermodynamically analogous to that of increasing temperature, but that the effect is small. The results are consistent with the volume per Zr atom of the a, d and w phases, with the bulk moduli of a and d, and with previous measurements of the hydrogen site molar volumes in the a and d phases. The results are interpreted in terms of their implication for our understanding of the driving forces for hydride precipitation at crack tips, which are in a region of hydrostatic tensile stress on the order of 1.5 GPa.
△ Less
Submitted 11 July, 2019; v1 submitted 25 June, 2018;
originally announced June 2018.
-
Dislocation interactions and crack nucleation in a fatigued near-alpha titanium alloy
Authors:
Sudha Joseph,
Trevor C Lindley,
David Dye
Abstract:
Dislocation interactions at the crack nucleation site were investigated in near-alpha titanium alloy Ti-6242Si subjected to low cycle fatigue. Cyclic plastic strain in the alloy resulted in dislocation pile-ups in the primary alpha grains, nucleated at the boundaries between the primary alpha and the two-phase regions. These two phase regions provided a barrier to slip transfer between primary alp…
▽ More
Dislocation interactions at the crack nucleation site were investigated in near-alpha titanium alloy Ti-6242Si subjected to low cycle fatigue. Cyclic plastic strain in the alloy resulted in dislocation pile-ups in the primary alpha grains, nucleated at the boundaries between the primary alpha and the two-phase regions. These two phase regions provided a barrier to slip transfer between primary alpha grains. We suggest that crack nucleation occurred near the basal plane of primary alpha grains by the subsurface double-ended pile-up mechanism first conceived by Tanaka and Mura. Superjogs on the basal <a> dislocations were observed near the crack nucleation location. The two phase regions showed direct transmission of a3 dislocations between secondary alpha plates, transmitted through the beta ligaments as a[010], which then decompose into (a/2)<111> dislocation networks in the beta. The beta ligaments themselves do not appear to form an especially impenetrable barrier to slip, in agreement with the micropillar and crystal plasticity investigations of Zhang et al.
△ Less
Submitted 17 June, 2018;
originally announced June 2018.
-
The Kinetics of Primary Alpha Plate Growth in Titanium Alloys
Authors:
Abigail K Ackerman,
Alexander J. Knowles,
Hazel M. Gardner,
Andre A N Nemeth,
Ioannis Bantounas,
Anna Radecka,
Michael P. Moody,
Paul A. J. Bagot,
Roger C. Reed,
David Rugg,
David Dye
Abstract:
The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is availab…
▽ More
The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is available to drive plate growth. In Ti-6246, the plate growth velocity was found to be around 0.32 um min-1 at 850 oC, which was in good agreement with the model prediction of 0.36 um min-1 . The solute field around the growing plates, and the plate thickness, was found to be quite variable, due to the intergrowth of plates and soft im**ement. This solute field was found to extend to up to 30 nm, and the interface concentration in the beta was found to be around 6.4 at.% Mo. It was found that increasing O content will have minimal effect on the plate lengths expected during continuous cooling; in contrast, Mo approximately doubles the plate lengths obtained for every 2 wt.% Mo reduction. Alloys using V as the beta stabiliser instead of Mo are expected to have much faster plate growth kinetics at nominally equivalent V contents. These findings will provide a useful tool for the integrated design of alloys and process routes to achieve tailored microstructures.
△ Less
Submitted 31 July, 2019; v1 submitted 24 May, 2018;
originally announced May 2018.
-
Interface characteristics in an α+β titanium alloy
Authors:
Abigail K. Ackerman,
Vassili A. Vorontsov,
Ioannis Bantounas,
Yufeng Zheng,
Thomas McAuliffe,
William A. Clark,
Hamish L. Fraser,
David Rugg,
David Dye
Abstract:
The alpha/beta interface in Ti-6Al-2Sn-4Zr-6Mo (Ti-6246) is investigated via centre of symmetry analysis, both as-grown and after 10% cold work. Semi-coherent interface steps are observed at a spacing of 4.5 +/-1.13 atoms in the as-grown condition, in good agreement with theory prediction (4.37 atoms). Lattice accommodation is observed, with elongation along [-1 2 -1 0]alpha and contraction along…
▽ More
The alpha/beta interface in Ti-6Al-2Sn-4Zr-6Mo (Ti-6246) is investigated via centre of symmetry analysis, both as-grown and after 10% cold work. Semi-coherent interface steps are observed at a spacing of 4.5 +/-1.13 atoms in the as-grown condition, in good agreement with theory prediction (4.37 atoms). Lattice accommodation is observed, with elongation along [-1 2 -1 0]alpha and contraction along [1 0 -1 0]alpha . Deformed alpha exhibited larger, less coherent steps with slip bands lying in {110}beta. This indicates dislocation pile-up at the grain boundary, a precursor to globularisation, offering insight into the effect of deformation processing on the interface, which is important for titanium alloy processing route design.
△ Less
Submitted 18 December, 2019; v1 submitted 24 May, 2018;
originally announced May 2018.
-
Characterizing solute hydrogen and hydrides in pure and alloyed titanium at the atomic scale
Authors:
Yanhong Chang,
Andrew J. Breen,
Zahra Tarzimoghadam,
Philipp Kürnsteiner,
Hazel Gardner,
Abigail Ackerman,
Anna Radecka,
Paul A. J. Bagot,
Wenjun Lu,
Tong Li,
Eric A. Jägle,
Michael Herbig,
Leigh T. Stephenson,
Michael P. Moody,
David Rugg,
David Dye,
Dirk Ponge,
Dierk Raabe,
Baptiste Gault
Abstract:
Ti has a high affinity for hydrogen and is a typical hydride formers. Ti-hydride are brittle phases which probably cause premature failure of Ti-alloys. Here, we used atom probe tomography and electron microscopy to investigate the hydrogen distribution in a set of specimens of commercially pure Ti, model and commercial Ti-alloys. Although likely partly introduced during specimen preparation with…
▽ More
Ti has a high affinity for hydrogen and is a typical hydride formers. Ti-hydride are brittle phases which probably cause premature failure of Ti-alloys. Here, we used atom probe tomography and electron microscopy to investigate the hydrogen distribution in a set of specimens of commercially pure Ti, model and commercial Ti-alloys. Although likely partly introduced during specimen preparation with the focused-ion beam, we show formation of Ti-hydrides along α grain boundaries and α/\b{eta} phase boundaries in commercial pure Ti and α+\b{eta} binary model alloys. No hydrides are observed in the α phase in alloys with Al addition or quenched-in Mo supersaturation.
△ Less
Submitted 11 March, 2018;
originally announced March 2018.
-
The mechanisms of hot salt stress corrosion cracking in titanium alloy Ti-6Al-2Sn-4Zr-6Mo
Authors:
Sudha Joseph,
Trevor C Lindley,
David Dye,
Edward A Saunders
Abstract:
Hot salt stress corrosion cracking in Ti 6246 alloy has been investigated to elucidate the chemical mechanisms that occur. Cracking was found to initiate beneath salt particles in the presence of oxidation. The observed transgranular fracture was suspected to be due to hydrogen charging; XRD and high-resolution transmission electron microscopy detected the presence of hydrides that were precipitat…
▽ More
Hot salt stress corrosion cracking in Ti 6246 alloy has been investigated to elucidate the chemical mechanisms that occur. Cracking was found to initiate beneath salt particles in the presence of oxidation. The observed transgranular fracture was suspected to be due to hydrogen charging; XRD and high-resolution transmission electron microscopy detected the presence of hydrides that were precipitated on cooling. SEM-EDS showed oxygen enrichment near salt particles, alongside chlorine and sodium. Aluminium and zirconium were also involved in the oxidation reactions. The role of intermediate corrosion products such as Na2TiO3, Al2O3, ZrO2, TiCl2 and TiH are discussed.
△ Less
Submitted 16 February, 2018;
originally announced February 2018.
-
Using transmission Kikuchi diffraction to characterise α variants in an α + β titanium alloy
Authors:
Vivian Tong,
Sudha Joseph,
Abigail K. Ackerman,
David Dye,
T. Ben Britton
Abstract:
Two phase titanium alloys are important for high performance engineering components, such as aeroengine discs. The microstructures of these alloys are tailored during thermomechanical processing to precisely control phase factions, morphology and crystallographic orientations. In bimodal two phase (α + β) Ti-6Al-2Sn-4Zr-2Mo (Ti-6242) alloys there are often three microstructural lengthscales to con…
▽ More
Two phase titanium alloys are important for high performance engineering components, such as aeroengine discs. The microstructures of these alloys are tailored during thermomechanical processing to precisely control phase factions, morphology and crystallographic orientations. In bimodal two phase (α + β) Ti-6Al-2Sn-4Zr-2Mo (Ti-6242) alloys there are often three microstructural lengthscales to consider: large (~10 μm) equiaxed primary α; >200 nm thick plate α with a basketweave morphology; and very fine scaled (>50 nm plate thickness) secondary α that grows between the larger α plates surrounded by retained β. In this work, we utilise high spatial resolution transmission Kikuchi diffraction (TKD, also known as transmission based electron backscatter diffraction, t-EBSD) and scanning electron microscopy (SEM) based forward scattering electron imaging to resolve the structures and orientations of basketweave and secondary α in Ti-6242. We analyse the α variants formed within one prior β grain, and test whether existing theories of habit planes of the phase transformation are upheld. Our analysis is important in understanding both the thermomechanical processing strategy of new bimodal two-phase titanium alloys, as well the ultimate performance of these alloys in complex loading regimes such as dwell fatigue. Our paper champions the significant increase in spatial resolution afforded using transmission techniques, combined with the ease of SEM based analysis using conventional electron backscatter diffraction (EBSD) systems and forescatter detector (FSD) imaging, to study the nanostructure of real-world engineering alloys.
△ Less
Submitted 4 April, 2017; v1 submitted 11 January, 2017;
originally announced January 2017.