Structure and physical properties of superconducting compounds Y(La)-Ba(Sr)-Cu-O
Authors:
B. I. Verkin,
B. B. Banduryan,
A. S. Barylnik,
A. G. Batrak,
N. L. Bobrov,
I. S. Braude,
Yu. L. Gal'chinetskaya,
A. L. Gaiduk,
A. M. Gurevich,
V. V. Demirskii,
V. I. Dotsenko,
V. I. Eropkin,
S. V. Zherlitsyn,
A. P. Isakina,
I. F. Kislyak,
V. A. Konovodchenko,
F. F. Lavrent'ev,
L. S. Litinskaya,
V. A. Mikheev,
V. I. Momot,
V. D. Natsik,
I. N. Nechiporenko,
A. S. Panfilov,
Yu. A. Pokhil,
A. I. Prokhvatilov
, et al. (13 additional authors not shown)
Abstract:
The structure and physical properties of superconducting compounds Y(La)-Ba(Sr)-Cu-O are studied, the compounds being prepared by the method of cryogenic dispersion of a charge consisting of premix oxides and carbonates. Electrical conductivity and critical current density of the superconductors are measured over a wide temperature range of 10~$mK$ to 300~$K$. Degradation of the superconductor cri…
▽ More
The structure and physical properties of superconducting compounds Y(La)-Ba(Sr)-Cu-O are studied, the compounds being prepared by the method of cryogenic dispersion of a charge consisting of premix oxides and carbonates. Electrical conductivity and critical current density of the superconductors are measured over a wide temperature range of 10~$mK$ to 300~$K$. Degradation of the superconductor critical parameters in time and structural characteristics, magnetic susceptibility, heat capacity and acoustic properties are studied, and current-voltage characteristics are determined.
△ Less
Submitted 25 March, 2017;
originally announced March 2017.
-
Effect of γ-irradiation on superconductivity in polycrystalline YBa_{2}Cu_{3}O_{7-δ}
Authors:
B. I. Belevtsev,
I. V. Volchok,
N. V. Dalakova,
V. I. Dotsenko,
L. G. Ivanchenko,
A. V. Kuznichenko,
I. I. Logvinov
Abstract:
A bulk polycrystalline sample of YBa_{2}Cu_{3}O_{7-δ} (δ\approx 0.1) has been irradiated by γ-rays with ^{60}Co source. Non-monotonic behavior of T_c (defined as the temperature at which normal resistance is halved) with increasing irradiation dose Φ(up to about 220 MR) is observed: T_c decreases at low doses (Φ\leq 50 MR) from initial value (\approx 93 K) by about 2 K and then rises, forming mi…
▽ More
A bulk polycrystalline sample of YBa_{2}Cu_{3}O_{7-δ} (δ\approx 0.1) has been irradiated by γ-rays with ^{60}Co source. Non-monotonic behavior of T_c (defined as the temperature at which normal resistance is halved) with increasing irradiation dose Φ(up to about 220 MR) is observed: T_c decreases at low doses (Φ\leq 50 MR) from initial value (\approx 93 K) by about 2 K and then rises, forming minimum. At highest doses (Φ\geq 120 MR) T_c goes down again. The temperature width, δT_c, of resistive transition increases rather sharp with dose below 75 MR and somewhat drops at higher dose. We believe that this effect is revealed for the first time at γ-irradiation of high-T_c superconductor. The cross section for the displacement of lattice atoms in YBCO by γ-rays due to the Compton process were calculated, and possible dpa values were estimated. The results obtained are discussed taking into account that the sample is granular superconductor and, hence, the observed variations of superconducting properties should be connected primarily with the influence of γ-rays on intergrain Josephson coupling.
△ Less
Submitted 21 July, 2000;
originally announced July 2000.
-
Effect of γ-irradiation on superconducting transition temperature and resistive transition in polycrystalline YBa_{2}Cu_{3}O_(7-δ)
Authors:
B. I. Belevtsev,
I. V. Volchok,
N. V. Dalakova,
V. I. Dotsenko,
L. G. Ivanchenko,
A. V. Kuznichenko,
I. I. Logvinov
Abstract:
A bulk polycrystalline sample of YBa_(2)Cu_(3)O_(7-δ) (δ\approx 0.1) has been irradiated by γ-rays with ^{60}Co source. Non-monotonic behavior of T_{c} with increasing irradiation dose Φ(up to 220 MR) is observed: T_{c} decreases at low doses (Φ< 50 MR) from initial value (\approx 93 K) by about 2 K and then rises, forming a minimum. At higher doses (Φ> 120 MR) T_{c} goes down again. The tempera…
▽ More
A bulk polycrystalline sample of YBa_(2)Cu_(3)O_(7-δ) (δ\approx 0.1) has been irradiated by γ-rays with ^{60}Co source. Non-monotonic behavior of T_{c} with increasing irradiation dose Φ(up to 220 MR) is observed: T_{c} decreases at low doses (Φ< 50 MR) from initial value (\approx 93 K) by about 2 K and then rises, forming a minimum. At higher doses (Φ> 120 MR) T_{c} goes down again. The temperature width of resistive transition increases rather sharply with dose below 75 MR and drops somewhat at higher dose. The results observed are discussed, taking into account the granular structure of sample studied and the influence of γ-rays on intergrain Josephson coupling.
△ Less
Submitted 11 March, 2000;
originally announced March 2000.