Coexistence of superconductivity and charge-density wave in the quasi-one-dimensional material HfTe3
Authors:
Saleem J. Denholme,
Akinori Yukawa,
Kohei Tsumura,
Masanori Nagao,
Ryuji Tamura,
Satoshi Watauchi,
Isao Tanaka,
Hideaki Takayanagi,
Nobuaki Miyakawa
Abstract:
We present the first experimental evidence for metallicity, superconductivity (SC) and the co-existence of charge density waves (CDW) in the quasi-one-dimensional material HfTe3. The existence of such phenomena is a typical characteristic of the transition metal chalcogenides however, without the application of hydrostatic pressure/chemical do**, it is rare for a material to exhibit the co-exist…
▽ More
We present the first experimental evidence for metallicity, superconductivity (SC) and the co-existence of charge density waves (CDW) in the quasi-one-dimensional material HfTe3. The existence of such phenomena is a typical characteristic of the transition metal chalcogenides however, without the application of hydrostatic pressure/chemical do**, it is rare for a material to exhibit the co-existence of both states. Materials such as HfTe3 can therefore provide us with a unique insight into the relationship between these multiple ordered states. By improving on the original synthesis conditions, we have successfully synthesised single phase HfTe3 and confirmed the resultant structure by performing Rietveld refinement. Using low temperature resistivity measurements, we provide the first experimental evidence of SC at ~1.4 K as well as a resistive anomaly indicative of a CDW formation at ~82 K. By the application of hydrostatic-pressure, the resistivity anomaly shifts to higher temperature. The results show that HfTe3 is a promising new material to help study the relationship between SC and CDW.
△ Less
Submitted 28 November, 2017;
originally announced November 2017.
-
Pressure-Induced Superconductivity in BiS2-based EuFBiS2
Authors:
Kouji Suzuki,
Masashi Tanaka,
Saleem James Denholme,
Masaya Fujioka,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
We measured the electrical resistivity of a BiS2-based compound EuFBiS2 under high pressure. Polycrystalline EuFBiS2 shows insulator-metal transition and pressure-induced superconductivity above 0.7 GPa. The superconducting transition temperature increases with increasing applied pressure and shows the maximum value around 8.6 K at 1.8 GPa.
We measured the electrical resistivity of a BiS2-based compound EuFBiS2 under high pressure. Polycrystalline EuFBiS2 shows insulator-metal transition and pressure-induced superconductivity above 0.7 GPa. The superconducting transition temperature increases with increasing applied pressure and shows the maximum value around 8.6 K at 1.8 GPa.
△ Less
Submitted 29 October, 2015; v1 submitted 29 May, 2015;
originally announced May 2015.
-
Origin of the Higher-$T_\rm{c}$ Phase in the K$_x$Fe$_{2-y}$Se$_2$ System
Authors:
Masashi Tanaka,
Yusuke Yanagisawa,
Masaya Fujioka,
Saleem J. Denholme,
Shiro Funahashi,
Yoshitaka Matsushita,
Nobuo Ishizawa,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
Single crystals of K$_x$Fe$_{2-y}$Se$_2$ are prepared by quenching at various temperatures. The crystals obtained at higher quenching temperatures have a surface morphology with mesh-like texture. They show a sharp superconducting transition at $T_\rm{c}$ ~32 K with a large shielding volume fraction. On the other hand, the crystals prepared without quenching show an onset superconducting transitio…
▽ More
Single crystals of K$_x$Fe$_{2-y}$Se$_2$ are prepared by quenching at various temperatures. The crystals obtained at higher quenching temperatures have a surface morphology with mesh-like texture. They show a sharp superconducting transition at $T_\rm{c}$ ~32 K with a large shielding volume fraction. On the other hand, the crystals prepared without quenching show an onset superconducting transition at ~44 K and a zero resistivity around ~33 K, and they possess island-like regions on the surface with a larger amount of Fe incorporation. In-situ high-temperature single crystal X-ray diffraction measurements tell us the Fe-vacancy ordered phase is generated at a temperature region around 270 °C via iron diffusion. The creation of this Fe-vacancy ordered phase may become a driving force of the growth of the higher $T_\rm{c}$ phase. The superconductivity at ~44 K is attributed to a metallic phase with no Fe-vacancy.
△ Less
Submitted 25 February, 2016; v1 submitted 16 April, 2015;
originally announced April 2015.
-
Electrochemical deposition of FeSe on RABiTS tapes
Authors:
Satoshi Demura,
Masashi Tanaka,
Aichi Yamashita,
Saleem J. Denholme,
Hiroyuki Okazaki,
Masaya Fujioka,
Takahide Yamaguchi,
Hiroyuki Takeya,
Kazumasa Iida,
Bernhard Holzapfel,
Hideaki Sakata,
Yoshihiko Takano
Abstract:
FeSe film is successfully fabricated onto Rolling Assisted Biaxially Textured Substrate (RABiTS) tapes by an electrochemical deposition technique. The deposited FeSe films tend to become high crystallinity with a decrease in the applied voltage to -1.0 V, and the compositional ratio of Fe to Se approaches 1:1. The sample deposited at -1.0 V shows a superconducting transition approximately 8.0 K in…
▽ More
FeSe film is successfully fabricated onto Rolling Assisted Biaxially Textured Substrate (RABiTS) tapes by an electrochemical deposition technique. The deposited FeSe films tend to become high crystallinity with a decrease in the applied voltage to -1.0 V, and the compositional ratio of Fe to Se approaches 1:1. The sample deposited at -1.0 V shows a superconducting transition approximately 8.0 K in the magnetic susceptibility.
△ Less
Submitted 3 December, 2015; v1 submitted 29 December, 2014;
originally announced December 2014.
-
Site Selectivity on Chalcogen Atoms in Superconducting La(O,F)BiSSe
Authors:
Masashi Tanaka,
Takuma Yamaki,
Yoshitaka Matsushita,
Masaya Fujioka,
Saleem J. Denholme,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
Single crystals of La(O,F)BiSSe were successfully grown by a CsCl flux method. Single crystal X-ray structural analysis revealed that the crystal structure is isostructural with BiS$_2$- or BiSe$_2$-based compounds with space group $P4/nmm$ (lattice parameters $a$ = 4.1110(2) Å, $c$ = 13.6010(7) Å). However, the S atoms are selectively occupied at the apical site of the Bi-SSe pyramids in the supe…
▽ More
Single crystals of La(O,F)BiSSe were successfully grown by a CsCl flux method. Single crystal X-ray structural analysis revealed that the crystal structure is isostructural with BiS$_2$- or BiSe$_2$-based compounds with space group $P4/nmm$ (lattice parameters $a$ = 4.1110(2) Å, $c$ = 13.6010(7) Å). However, the S atoms are selectively occupied at the apical site of the Bi-SSe pyramids in the superconducting layer. The single crystals show a superconducting transition at 4.2 K in the magnetic susceptibility and resistivity measurement. The superconducting anisotropic parameter is determined to be 34 from its upper critical magnetic field. The anisotropy is in the same range with that of other members of the La(O,F)BiCh$_2$ ($Ch$ = S, Se) family under ambient pressure.
△ Less
Submitted 12 March, 2015; v1 submitted 29 December, 2014;
originally announced December 2014.
-
Pressure-dependent magnetization and magnetoresistivity studies on the tetragonal FeS (mackinawite): revealing its intrinsic metallic character
Authors:
S. J. Denholme,
H. Okazaki,
S. Demura,
K. Deguchi,
M. Fujioka,
T. Yamaguchi,
H. Takeya,
M. ElMassalami,
H. Fujiwara,
T. Wakita,
T. Yokoya,
Y. Takano
Abstract:
The transport and magnetic properties of the tetragonal Fe$_{1+δ}$S were investigated using magnetoresistivity and magnetization within 2$\leq T\leq $300 K, $H\leq$70 kOe and $P\leq$ 3.0 GPa. In addition, room-temperature X-ray diffraction and photoelectron spectroscopy were also applied. In contrast to previously reported nonmetallic character, Fe$_{1+δ}$S is intrinsically metallic but due to a p…
▽ More
The transport and magnetic properties of the tetragonal Fe$_{1+δ}$S were investigated using magnetoresistivity and magnetization within 2$\leq T\leq $300 K, $H\leq$70 kOe and $P\leq$ 3.0 GPa. In addition, room-temperature X-ray diffraction and photoelectron spectroscopy were also applied. In contrast to previously reported nonmetallic character, Fe$_{1+δ}$S is intrinsically metallic but due to a presence of a weak localization such metallic character is not exhibited below room temperature. An applied pressure reduces strongly this additional resistive contribution and as such enhances the temperature range of the metallic character which, for $\sim$3 GPa, is evident down to 75 K. The absence of superconductivity as well as the mechanism behind the weak localization will be discussed.
△ Less
Submitted 10 October, 2014;
originally announced October 2014.
-
Pressure-induced phase transition for single crystalline LaO0.5F0.5BiSe2
Authors:
Masaya Fujioka,
Masashi Tanaka,
Saleem J. Denholme,
Takuma Yamaki,
Hiroyuki Takeya,
Takahide Yamaguchi,
Yoshihiko Takano
Abstract:
We have demonstrated a pressure-induced phase transition from a low-Tc phase to a high-Tc phase in a single crystal of the superconductor LaO0.5F0.5BiSe2. The high-Tc phase appears at 2.16 GPa and the maximum superconducting transition temperature (Tc) is observed at 6.7 K under 2.44 GPa. Although the anisotropy (γ) for the low-Tc phase is estimated to be 20, it is reduced by around half (9.3) in…
▽ More
We have demonstrated a pressure-induced phase transition from a low-Tc phase to a high-Tc phase in a single crystal of the superconductor LaO0.5F0.5BiSe2. The high-Tc phase appears at 2.16 GPa and the maximum superconducting transition temperature (Tc) is observed at 6.7 K under 2.44 GPa. Although the anisotropy (γ) for the low-Tc phase is estimated to be 20, it is reduced by around half (9.3) in the high-Tc phase. This tendency is the same for the BiS2 system. The Tc of LaO0.5F0.5BiSe2 has continued to increase up to the maximum pressure of this study (2.44 GPa). Therefore applied further pressure has the potential to induce a much higher Tc in this system.
△ Less
Submitted 1 August, 2014;
originally announced August 2014.
-
Superconductivity in FeTe{1-x}S_x induced by electrochemical reaction using ionic liquid solution
Authors:
Aichi Yamashita,
Satoshi Demura,
Masashi Tanaka,
Keita Deguchi,
Takuma Yamaki,
Hiroshi Hara,
Kouji Suzuki,
Yunchao Zhang,
Saleem J. Denholme,
Hiroyuki Okazaki,
Masaya Fujioka,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
Superconductivity in FeTe0.8S0.2 is successfully induced by an electrochemical reaction using an ionic liquid solution. A clear correlation between the Fe concentration in the solution and the manifestation of superconductivity was confirmed, suggesting that superconductivity was induced by the deintercalation of excess iron.
Superconductivity in FeTe0.8S0.2 is successfully induced by an electrochemical reaction using an ionic liquid solution. A clear correlation between the Fe concentration in the solution and the manifestation of superconductivity was confirmed, suggesting that superconductivity was induced by the deintercalation of excess iron.
△ Less
Submitted 18 July, 2014;
originally announced July 2014.
-
High-Tc Phase of PrO0.5F0.5BiS2 single crystal induced by uniaxial pressure
Authors:
Masaya Fujioka,
Masanori Nagao,
Saleem J. Denholme,
Masashi Tanaka,
Hiroyuki Takeya,
Takahide Yamaguchi,
Yoshihiko Takano
Abstract:
We demonstrated a pressure-induced phase transition from a low-Tc phase (3.5 K) to a high-Tc phase (8.7 K) in single crystalline PrO0.5F0.5BiS2. The high-Tc phase is easily observed even at 0.7 GPa by uniaxial pressure obtained from a geometric effect of a single crystal with an extremely-thin thickness. For this phase transition, superconducting anisotropy and the coherence length along the c axi…
▽ More
We demonstrated a pressure-induced phase transition from a low-Tc phase (3.5 K) to a high-Tc phase (8.7 K) in single crystalline PrO0.5F0.5BiS2. The high-Tc phase is easily observed even at 0.7 GPa by uniaxial pressure obtained from a geometric effect of a single crystal with an extremely-thin thickness. For this phase transition, superconducting anisotropy and the coherence length along the c axis change from γ = 20 to 9.3 and from ξc = 0.56 to 0.71 nm respectively. It is suggested that a shrinkage in the c lattice constant by applied uniaxial pressure enhances the three dimensionality in the superconducting state.
△ Less
Submitted 19 July, 2014; v1 submitted 15 June, 2014;
originally announced June 2014.
-
First single crystal growth and structural analysis of superconducting layered bismuth oxyselenide; La(O,F)BiSe2
Authors:
Masashi Tanaka,
Masanori Nagao,
Yoshitaka Matsushita,
Masaya Fujioka,
Saleem J. Denholme,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
Single crystal of La(O,F)BiSe2 was successfully grown for the first time by the CsCl flux method. Single crystal X-ray structural analysis clearly showed that La(O,F)BiSe2 crystalizes with space group P4/nmm (lattice parameters a = 4.1408(2) Å, c = 14.1096(6) Å). The structure is composed of alternating BiSe2 and LaO layers. Magnetic susceptibility and resistivity measurements showed the supercond…
▽ More
Single crystal of La(O,F)BiSe2 was successfully grown for the first time by the CsCl flux method. Single crystal X-ray structural analysis clearly showed that La(O,F)BiSe2 crystalizes with space group P4/nmm (lattice parameters a = 4.1408(2) Å, c = 14.1096(6) Å). The structure is composed of alternating BiSe2 and LaO layers. Magnetic susceptibility and resistivity measurements showed the superconducting transition at 3.6 K, which is higher than that of as-grown La(O,F)BiS2. The structural analysis implies that La(O,F)BiSe2 is potential superconductor having higher Tc under high pressure.
△ Less
Submitted 3 June, 2014;
originally announced June 2014.
-
Superconductivity in FeTe0.8S0.2 induced by battery-like reaction
Authors:
Aichi Yamashita,
Satoshi Demura,
Masashi Tanaka,
Keita Deguchi,
Takuma Yamaki,
Hiroshi Hara,
Kouji Suzuki,
Yunchao Zhang,
Saleem James Denholme,
Hiroyuki Okazaki,
Masaya Fujioka,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
Superconductivity is successfully induced by utilizing a battery-like reaction found in a typical Li-ion battery. Excess Fe in FeTe0.8S0.2 is electrochemically de-intercalated by applying a voltage in a citric acid solution. The superconducting properties improve with an increase in the applied voltage up to 1.5 V. This result suggests that an electrochemical reaction can be used as a novel method…
▽ More
Superconductivity is successfully induced by utilizing a battery-like reaction found in a typical Li-ion battery. Excess Fe in FeTe0.8S0.2 is electrochemically de-intercalated by applying a voltage in a citric acid solution. The superconducting properties improve with an increase in the applied voltage up to 1.5 V. This result suggests that an electrochemical reaction can be used as a novel method to develop new superconducting materials.
△ Less
Submitted 14 May, 2014;
originally announced May 2014.
-
The effect of exceptionally high fluorine do** on the anisotropy of single crystalline SmFeAsO1-xFx
Authors:
Masaya Fujioka,
Saleem J. Denholme,
Masashi Tanaka,
Hiroyuki Takeya,
Takahide Yamaguchi,
Yoshihiko Takano
Abstract:
We succeeded in growing single crystalline SmFeAsO1-xFx with exceptionally high fluorine concentration by using a CsCl flux method. Comparing to conventional flux methods, this method can introduce about double the amount of fluorine into the oxygen site. The obtained single crystal shows the highest superconducting transition temperature (Tc = 57.5 K) in single crystalline iron pnictides. In addi…
▽ More
We succeeded in growing single crystalline SmFeAsO1-xFx with exceptionally high fluorine concentration by using a CsCl flux method. Comparing to conventional flux methods, this method can introduce about double the amount of fluorine into the oxygen site. The obtained single crystal shows the highest superconducting transition temperature (Tc = 57.5 K) in single crystalline iron pnictides. In addition, the residual resistivity ratio (RRR) is almost three times as large as that of previously reported single crystals. This suggests that our single crystals are suitable for investigation of the intrinsic superconducting properties since they have few defects and impurities. Using both the Werthamer-Helfand-Hohenberg model and the effective mass model, we demonstrated that a higher fluorine concentration suppresses the anisotropic superconductivity of SmFeAsO1-xFx.
△ Less
Submitted 9 July, 2014; v1 submitted 22 January, 2014;
originally announced January 2014.
-
Coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2
Authors:
Satoshi Demura,
Keita Deguchi,
Yoshikazu Mizuguchi,
Kazuki Sato,
Ryouta Honjyo,
Aichi Yamashita,
Takuma Yamaki,
Hiroshi Hara,
Tohru Watanabe,
Saleem J. Denholme,
Masaya Fujioka,
Hiroyuki Okazaki,
Toshinori Ozaki,
Osuke Miura,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
We show the observation of the coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2(x = 0 - 1.0) prepared by annealing under high-pressure. In CeO1-xFxBiS2 system, both superconductivity and two types of ferromagnetism with respective magnetic transition temperatures of 4.5 K and 7.5 K are induced upon systematic F substitution. This fact suggests that carriers generated by the…
▽ More
We show the observation of the coexistence of bulk superconductivity and ferromagnetism in CeO1-xFxBiS2(x = 0 - 1.0) prepared by annealing under high-pressure. In CeO1-xFxBiS2 system, both superconductivity and two types of ferromagnetism with respective magnetic transition temperatures of 4.5 K and 7.5 K are induced upon systematic F substitution. This fact suggests that carriers generated by the substitution of O by F are supplied to not only the BiS2 superconducting layers but also the CeO blocking layers. Furthermore, the highest superconducting transition temperature is observed when the ferromagnetism is also enhanced, which implies that superconductivity and ferromagnetism are linked to each other in the CeO1-xFxBiS2 system.
△ Less
Submitted 18 November, 2013;
originally announced November 2013.
-
Sulfur annealing effect for superconductivity in iron chalcogenide compounds
Authors:
K. Deguchi,
A. Yamashita,
T. Yamaki,
H. Hara,
S. Demura,
S. J. Denholme,
M. Fujioka,
H. Okazaki,
H. Takeya,
T. Yamaguchi,
Y. Takano
Abstract:
We discovered a novel annealing method for Fe-chalcogenide superconductors. It was found that sulfur annealing deintercalated excess Fe via formation of FeS2. Due to its specifics, sulfur annealing is applicable when preparing Fe-chalcogenide-based wires or cables.
We discovered a novel annealing method for Fe-chalcogenide superconductors. It was found that sulfur annealing deintercalated excess Fe via formation of FeS2. Due to its specifics, sulfur annealing is applicable when preparing Fe-chalcogenide-based wires or cables.
△ Less
Submitted 26 August, 2013;
originally announced August 2013.
-
Phase diagram and superconductivity at 58.1 K in α-FeAs free SmFeAsO1-xFx
Authors:
Masaya Fujioka,
Saleem James Denholme,
Toshinori Ozaki,
Hiroyuki Okazaki,
Keita Deguchi,
Satoshi Demura,
Hiroshi Hara,
Tohru Watanabe,
Hiroyuki Takeya,
Takahide Yamaguchi,
Hiroaki Kumakura,
Yoshihiko Takano
Abstract:
The Phase diagram of SmFeAsO1-xFx in terms of x is exhibited in this study. SmFeAsO1-xFx from x = 0 to x = 0.3 were prepared by low temperature sintering with slow cooling. The low temperature sintering suppresses the formation of the amorphous FeAs, which is inevitably produced as an impurity by using high temperature sintering. Moreover, slow cooling is effective to obtain the high fluorine conc…
▽ More
The Phase diagram of SmFeAsO1-xFx in terms of x is exhibited in this study. SmFeAsO1-xFx from x = 0 to x = 0.3 were prepared by low temperature sintering with slow cooling. The low temperature sintering suppresses the formation of the amorphous FeAs, which is inevitably produced as an impurity by using high temperature sintering. Moreover, slow cooling is effective to obtain the high fluorine concentration. The compositional change from feedstock composition is quite small after this synthesis. We can reproducibly observe a record superconducting transition for an iron based superconductor at 58.1 K. This achievement of a high superconducting transition is due to the success in a large amount of fluorine substitution. A shrinking of the a lattice parameter caused by fluorine substitution is observed and the substitutional rate of fluorine changes at x =0.16.
△ Less
Submitted 16 July, 2013; v1 submitted 15 March, 2013;
originally announced March 2013.
-
α-FeAs-free SmFeAsO1-xFx by low temperature sintering with slow cooling
Authors:
Masaya Fujioka,
Saleem James Denholme,
Toshinori Ozaki,
Hiroyuki Okazaki,
Keita Deguchi,
Satoshi Demura,
Hiroshi Hara,
Tohru Watanabe,
Hiroyuki Takeya,
Takahide Yamaguchi,
Hiroaki Kumakura,
Yoshihiko Takano
Abstract:
We obtained amorphous-FeAs-free SmFeAsO1-xFx using a low temperature sintering with slow cooling. SmFeAsO1-xFx is sintered at 980 °C for 40 hours and cooled slowly down to 600 °C. The low temperature sintering suppresses the formation of amorphous FeAs, and the slow cooling introduces much fluorine into SmFeAsO1-xFx. The superconductivity of this sample appears at 57.8 K and the superconducting vo…
▽ More
We obtained amorphous-FeAs-free SmFeAsO1-xFx using a low temperature sintering with slow cooling. SmFeAsO1-xFx is sintered at 980 °C for 40 hours and cooled slowly down to 600 °C. The low temperature sintering suppresses the formation of amorphous FeAs, and the slow cooling introduces much fluorine into SmFeAsO1-xFx. The superconductivity of this sample appears at 57.8 K and the superconducting volume fraction reaches 96 %. To study the change of fluorine concentration during the cooling process, samples are quenched by water at 950 °C, 900 °C, 850 °C, 800 °C, 750 °C and 700 °C. It is found that fluorine is substituted not only at the maximum heating temperature but also during the cooling process. The low temperature sintering with slow cooling is very effective to obtain a homogeneous SmFeAsO1-xFx with high fluorine concentration.
△ Less
Submitted 7 August, 2013; v1 submitted 6 March, 2013;
originally announced March 2013.
-
Superconductivity in Fe1+dTe0.9Se0.1 induced by deintercalation of excess Fe using alcoholic beverage treatment
Authors:
K. Deguchi,
S. Demura,
H. Hara,
T. Watanabe,
S. J. Denholme,
M. Fujioka,
H. Okazaki,
T. Ozaki,
H. Takeya,
T. Yamaguchi,
Y. Takano
Abstract:
Superconductivity in polycrystalline Fe1+dTe0.9Se0.1 was enhanced by heating in alcoholic beverages. We found that part of the excess Fe was deintercalated from the interlayer sites by the treatment and the shielding volume fractions were increased with the reduction of excess Fe content in sample. This behavior is similar to the case of Fe1+dTe1-xSx. Thus the technique of alcoholic beverage treat…
▽ More
Superconductivity in polycrystalline Fe1+dTe0.9Se0.1 was enhanced by heating in alcoholic beverages. We found that part of the excess Fe was deintercalated from the interlayer sites by the treatment and the shielding volume fractions were increased with the reduction of excess Fe content in sample. This behavior is similar to the case of Fe1+dTe1-xSx. Thus the technique of alcoholic beverage treatment can be applied generally to the Fe-chalcogenide superconductors.
△ Less
Submitted 22 October, 2012;
originally announced October 2012.
-
Evolution of superconductivity in LaO1-xFxBiS2 prepared by high pressure technique
Authors:
K. Deguchi,
Y. Mizuguchi,
S. Demura,
H. Hara,
T. Watanabe,
S. J. Denholme,
M. Fujioka,
H. Okazaki,
T. Ozaki,
H. Takeya,
T. Yamaguchi,
O. Miura,
Y. Takano
Abstract:
Novel BiS2-based superconductors LaO1-xFxBiS2 prepared by the high pressure synthesis technique were systematically studied. It was found that the high pressure annealing strongly the lattice as compared to the LaO1-xFxBiS2 samples prepared by conventional solid state reaction at ambient pressure. Bulk superconductivity was observed within a wide F-concentration range of x = 0.2 ~ 0.7. On the basi…
▽ More
Novel BiS2-based superconductors LaO1-xFxBiS2 prepared by the high pressure synthesis technique were systematically studied. It was found that the high pressure annealing strongly the lattice as compared to the LaO1-xFxBiS2 samples prepared by conventional solid state reaction at ambient pressure. Bulk superconductivity was observed within a wide F-concentration range of x = 0.2 ~ 0.7. On the basis of those results, we have established a phase diagram of LaO1-xFxBiS2.
△ Less
Submitted 18 September, 2012;
originally announced September 2012.
-
Fermiological Interpretation of Superconductivity/Non-superconductivity of FeTe_{1-x}Se_{x} Thin Crystal Determined by Quantum Oscillation Measurement
Authors:
H. Okazaki,
T. Watanabe,
T. Yamaguchi,
K. Deguchi,
S. Demura,
S. J. Denholme,
T. Ozaki,
Y. Mizuguchi,
H. Takeya,
T. Oguchi,
Y. Takano
Abstract:
We have successfully observed quantum oscillation (QO) for FeTe_{1-x}Se_{x}. QO measurements were performed using non-superconducting and superconducting thin crystals of FeTe_{0.65}Se_{0.35} fabricated by the scotch-tape method. We show that the Fermi surfaces (FS) of the non-superconducting crystal are in good agreement with the rigid band shift model based on electron do** by excess Fe while…
▽ More
We have successfully observed quantum oscillation (QO) for FeTe_{1-x}Se_{x}. QO measurements were performed using non-superconducting and superconducting thin crystals of FeTe_{0.65}Se_{0.35} fabricated by the scotch-tape method. We show that the Fermi surfaces (FS) of the non-superconducting crystal are in good agreement with the rigid band shift model based on electron do** by excess Fe while that of the superconducting crystal is in good agreement with the calculated FS with no shift. From the FS comparison of both crystals, we demonstrate the change of the cross-sectional area of the FS, suggesting that the suppression of the FS nesting with the vector Q_{s} = (π, π) due to excess Fe results in the disappearance of the superconductivity.
△ Less
Submitted 27 July, 2012;
originally announced July 2012.
-
BiS2 - based superconductivity in F-substituted NdOBiS2
Authors:
Satoshi Demura,
Yoshikazu Mizuguchi,
Keita Deguchi,
Hiroyuki Okazaki,
Hiroshi Hara,
Tohru Watanabe,
Saleem James Denholme,
Masaya Fujioka,
Toshinori Ozaki,
Hiroshi Fujihisa,
Yoshito Gotoh,
Osuke Miura,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
We have successfully synthesized a new BiS2-based superconductor NdOBiS2 with F-do**. This compound is composed of superconducting BiS2 layers and blocking NdO layers, which indicates that the BiS2 layer is the one of the common superconducting layers like the CuO2 layer of cuprates or Fe-As layer of Fe-based superconductors. We can obtain NdO1-xFxBiS2 with bulk superconductivity by a solid-stat…
▽ More
We have successfully synthesized a new BiS2-based superconductor NdOBiS2 with F-do**. This compound is composed of superconducting BiS2 layers and blocking NdO layers, which indicates that the BiS2 layer is the one of the common superconducting layers like the CuO2 layer of cuprates or Fe-As layer of Fe-based superconductors. We can obtain NdO1-xFxBiS2 with bulk superconductivity by a solid-state reaction under ambient pressure. Therefore, NdO1-xFxBiS2 should be the suitable material to elucidate the mechanism of superconductivity in the BiS2-layer.
△ Less
Submitted 22 July, 2012;
originally announced July 2012.
-
Electrodeposition as a new route to synthesize superconducting FeSe
Authors:
Satoshi Demura,
Hiroyuki Okazaki,
Toshinori Ozaki,
Hiroshi Hara,
Yasuna Kawasaki,
Keita Deguchi,
Tohru Watanabe,
Saleem James Denholme,
Yoshikazu Mizuguchi,
Takahide Yamaguchi,
Hiroyuki Takeya,
Yoshihiko Takano
Abstract:
We have successfully synthesized FeSe films by the electrochemical deposition in the electrolyte containing FeCl_{2}\cdot4H_{2}O, SeO_{2} and Na_{2}SO_{4}. The composition ratio of Fe and Se was controlled by the synthesis voltage and pH value. The FeSe film with the composition ratio of Fe : Se = 1 : 1 is fabricated at a voltage of -0.9 V and pH 2.1 in our electrochemical deposition. This sample…
▽ More
We have successfully synthesized FeSe films by the electrochemical deposition in the electrolyte containing FeCl_{2}\cdot4H_{2}O, SeO_{2} and Na_{2}SO_{4}. The composition ratio of Fe and Se was controlled by the synthesis voltage and pH value. The FeSe film with the composition ratio of Fe : Se = 1 : 1 is fabricated at a voltage of -0.9 V and pH 2.1 in our electrochemical deposition. This sample has a highly crystalline tetragonal FeSe structure and exhibits a superconducting transition at 8.1 K, comparable to FeSe synthesized by other methods.
△ Less
Submitted 29 May, 2012;
originally announced May 2012.
-
Evidence of Inhomogeneous Superconductivity in FeTe$_{1-x}$Se$_x$ Thin Film Using Scotch-Tape Method
Authors:
H. Okazaki,
T. Watanabe,
T. Yamaguchi,
Y. Kawasaki,
K. Deguchi,
S. Demura,
T. Ozaki,
S. J. Denholme,
Y. Mizuguchi,
H. Takeya,
Y. Takano
Abstract:
We have fabricated thin films of FeTe$_{1-x}$Se$_x$ using a scotch-tape method. The superconductivities of the thin films are different from each other although these films were fabricated from the same bulk sample. The result clearly presents the inhomogeneous superconductivity in FeTe$_{1-x}$Se$_x$. The difference comes from inhomogeneity due to the excess Fe concentration. The resistivity of a…
▽ More
We have fabricated thin films of FeTe$_{1-x}$Se$_x$ using a scotch-tape method. The superconductivities of the thin films are different from each other although these films were fabricated from the same bulk sample. The result clearly presents the inhomogeneous superconductivity in FeTe$_{1-x}$Se$_x$. The difference comes from inhomogeneity due to the excess Fe concentration. The resistivity of a thin film with low excess Fe shows good superconductivity with the sharp superconducting-transition width and more isotropic superconductivity.
△ Less
Submitted 13 May, 2012;
originally announced May 2012.
-
Clarification as to why alcoholic beverages have the ability to induce superconductivity in Fe_{1+d}Te_{1-x}S_x
Authors:
K. Deguchi,
D. Sato,
M. Sugimoto,
H. Hara,
Y. Kawasaki,
S. Demura,
T. Watanabe,
S. J. Denholme,
H. Okazaki,
T. Ozaki,
T. Yamaguchi,
H. Takeya,
T. Soga,
M. Tomita,
Y. Takano
Abstract:
To elucidate the mechanism as to why alcoholic beverages can induce superconductivity in Fe_{1+d}Te_{1-x}S_x samples, we performed component analysis and found that weak acid such as organic acid has the ability to induce superconductivity. Inductively-coupled plasma spectroscopy was performed on weak acid solutions post annealing. We found that the mechanism of inducement of superconductivity in…
▽ More
To elucidate the mechanism as to why alcoholic beverages can induce superconductivity in Fe_{1+d}Te_{1-x}S_x samples, we performed component analysis and found that weak acid such as organic acid has the ability to induce superconductivity. Inductively-coupled plasma spectroscopy was performed on weak acid solutions post annealing. We found that the mechanism of inducement of superconductivity in Fe_{1+d}Te_{1-x}S_x is the deintercalation of excess Fe from the interlayer sites.
△ Less
Submitted 1 April, 2012;
originally announced April 2012.