Investigating Cathode Electrolyte Interphase Formation in NMC 811 Primary Particles Through Advanced 4D-STEM ACOM Analysis
Authors:
Kevyn Gallegos-Moncayo,
Justine Jean,
Nicolas Folastre,
Arash Jamali,
Arnaud Demortière
Abstract:
The study focuses on NMC811, a promising material for high-capacity batteries, and investigates the challenges associated with its use, specifically the formation of the Cathode Electrolyte Interphase (CEI) layer due to chemical reactions. This layer is a consequence of the position of the LUMO energy level of NMC811 that is close to the HOMO level of liquid electrolyte, resulting in electrolyte o…
▽ More
The study focuses on NMC811, a promising material for high-capacity batteries, and investigates the challenges associated with its use, specifically the formation of the Cathode Electrolyte Interphase (CEI) layer due to chemical reactions. This layer is a consequence of the position of the LUMO energy level of NMC811 that is close to the HOMO level of liquid electrolyte, resulting in electrolyte oxidation and cathode surface alterations during charging. A stable CEI layer can mitigate further degradation by reducing the interaction between the reactive cathode material and the electrolyte. Our research analyzed the CEI layer on NMC811 using advanced techniques such as 4D-STEM ACOM and STEM- EDX, focusing on the effects of different charging voltages (4.3 V and 4.5 V). The findings revealed varying degrees of degradation and the formation of a fluorine-rich layer on the secondary particles. Detailed analysis showed the composition of this layer differed based on the voltage: only LiF at 4.5 V and a combination of LiF and LiOH at 4.3 V. Despite LiF's known stability as a CEI protective layer, our observations indicate it does not effectively prevent degradation in NMC811. The study concludes that impurities and unwanted chemical reactions leading to suboptimal CEI formation are inevitable. Therefore, future efforts should focus on develo** protective strategies for NMC811, such as the use of specific additives or coatings.
△ Less
Submitted 20 December, 2023;
originally announced December 2023.
-
Coupling liquid electrochemical TEM and mass-spectrometry to investigate electrochemical reactions occurring in a Na-ion battery anode
Authors:
Kevyn Gallegos Moncayo,
Nicolas Folastre,
Milan Toledo,
Hélène Tonnoir,
François Rabuel,
Grégory Gachot,
Da Huo,
Arnaud Demortière
Abstract:
In this study, we propose a novel approach for investigating the formation of solid electrolyte interphase (SEI) in Na-ion batteries (NIB) through the coupling of in situ liquid electrochemical transmission electron microscopy (ec-TEM) and gas-chromatography mass-spectrometry (GC/MS). To optimize this coupling, we conducted experiments on the sodiation of hard carbon materials (HC) using two diffe…
▽ More
In this study, we propose a novel approach for investigating the formation of solid electrolyte interphase (SEI) in Na-ion batteries (NIB) through the coupling of in situ liquid electrochemical transmission electron microscopy (ec-TEM) and gas-chromatography mass-spectrometry (GC/MS). To optimize this coupling, we conducted experiments on the sodiation of hard carbon materials (HC) using two different setups: in situ ec-TEM holder (operating in an "anode free" configuration, referred to as $μ$-battery) and ex-situ setup (Swagelok battery configuration). In the in situ TEM experiments, we intentionally degraded the electrolyte (NP30) using cyclic voltammetry (CV) and analyzed the recovered liquid product using GC/MS, while the solid product ($μ$-chip) was analyzed using TEM techniques in a post-mortem analysis. The ex-situ experiments served as a reference to observe and detect the insertion of Na+ ions in the HC, SEI size (389 nm), SEI composition (P, Na, F, and O), and Na plating. Furthermore, the TEM analysis revealed a cyclability limitation in our in situ TEM system. This issue appears to be caused by the deposition of Na in the form of a "foam" structure, resulting from the gas release during the reaction of Na with DMC/EC electrolyte. The foam structure, subsequently transforms into a second SEI, is electrochemically inactive and reduce the cyclability of the battery. Overall, our results demonstrate the powerful synergy achieved by coupling in situ ec-TEM and GC/MS techniques, which provides a deeper understanding of the dynamics and behavior of SEI. Consequently, this knowledge contributes to the advancement of the new generation of NIB.
△ Less
Submitted 9 August, 2023;
originally announced August 2023.
-
Combining X-ray Nano-CT and XANES Techniques for 3D Operando Monitoring of Lithiation Spatial Composition evolution in NMC Electrode
Authors:
Tuan-Tu Nguyen,
Jiahui Xu,
Zeliang Su,
Vincent De Andrade,
Alejandro A. Franco,
Bruno Delobel,
Charles Delacourt,
Arnaud Demortière
Abstract:
In this study, we present a well-defined methodology for conducting Operando X-ray absorption near-edge structure spectroscopy (XANES) in conjunction with transmission X-ray nano computed tomography (TXM-nanoCT) experiments on the LiNi$_{0.5}$Mn$_{0.3}$Co$_{0.2}$O$_2$ (NMC) cathode electrode. To minimize radiation-induced damage to the sample during charge and discharge cycles and to gain a compre…
▽ More
In this study, we present a well-defined methodology for conducting Operando X-ray absorption near-edge structure spectroscopy (XANES) in conjunction with transmission X-ray nano computed tomography (TXM-nanoCT) experiments on the LiNi$_{0.5}$Mn$_{0.3}$Co$_{0.2}$O$_2$ (NMC) cathode electrode. To minimize radiation-induced damage to the sample during charge and discharge cycles and to gain a comprehensive 3D perspective of the (de)lithiation process of the active material, we propose a novel approach that relies on employing only three energy levels, strategically positioned at pre-edge, edge, and post-edge. By adopting this technique, we successfully track the various (de)lithiation states within the three-dimensional space during partial cycling. Furthermore, we are able to extract the nanoscale lithium distribution within individual secondary particles. Our observations reveal the formation of a core-shell structure during lithiation and we also identify that not all surface areas of the particles exhibit activity during the process. Notably, lithium intercalation exhibits a distinct preference, leading to non-uniform lithiation degrees across different electrode locations. The proposed methodology is not limited to the NMC cathode electrode but can be extended to study realistic dedicated electrodes with high active material (AM) density, facilitating exploration and quantification of heterogeneities and inhomogeneous lithiation within such electrodes. This multi-scale insight into the (de)lithiation process and lithiation heterogeneities within the electrodes is expected to provide valuable knowledge for optimizing electrode design and ultimately enhancing electrode performance in the context of material science and battery materials research.
△ Less
Submitted 9 August, 2023; v1 submitted 17 July, 2023;
originally announced July 2023.
-
Computational Model for Predicting Particle Fracture During Electrode Calendering
Authors:
Jiahui Xu,
Brayan Paredes-Goyes,
Zeliang Su,
Mario Scheel,
Timm Weitkamp,
Arnaud Demortiere,
Alejandro A. Franco
Abstract:
In the context of calling for low carbon emissions, lithium-ion batteries (LIBs) have been widely concerned as a power source for electric vehicles, so the fundamental science behind their manufacturing has attracted much attention in recent years. Calendering is an important step of the LIB electrode manufacturing process, and the changes it brings to the electrode microstructure and mechanical p…
▽ More
In the context of calling for low carbon emissions, lithium-ion batteries (LIBs) have been widely concerned as a power source for electric vehicles, so the fundamental science behind their manufacturing has attracted much attention in recent years. Calendering is an important step of the LIB electrode manufacturing process, and the changes it brings to the electrode microstructure and mechanical properties are worth studying. In this work, we reported the observed cracking of active material (AM) particles due to calendering pressure under ex situ nano-X-ray tomography experiments. We developed a 3D-resolved discrete element method (DEM) model with bonded connections to physically mimic the calendering process using real AM particle shapes derived from the tomography experiments. The DEM model can well predict the change of the morphology of the dry electrode under pressure, and the changes of the applied pressure and porosity are consistent with the experimental values. At the same time, the model is able to simulate the secondary AM particles cracking by the fracture of the bond under force. Our model is the first of its kind being able to predict the fracture of the secondary particles along the calendering process. This work provides a tool for guidance in the manufacturing of optimized LIB electrodes.
△ Less
Submitted 3 June, 2023;
originally announced June 2023.
-
Adaptative Diffraction Image Registration for 4D-STEM to optimize ACOM Pattern Matching
Authors:
Nicolas Folastre,
Junhao Cao,
Gozde Oney,
Sunkyu Park,
Arash Jamali,
Christian Masquelier,
Laurence Croguennec,
Muriel Veron,
Edgar F. Rauch,
Arnaud Demortière
Abstract:
The technique known as 4D-STEM has recently emerged as a powerful tool for the local characterization of crystalline structures in materials, such as cathode materials for Li-ion batteries or perovskite materials for photovoltaics. However, the use of new detectors optimized for electron diffraction patterns and other advanced techniques requires constant adaptation of methodologies to address the…
▽ More
The technique known as 4D-STEM has recently emerged as a powerful tool for the local characterization of crystalline structures in materials, such as cathode materials for Li-ion batteries or perovskite materials for photovoltaics. However, the use of new detectors optimized for electron diffraction patterns and other advanced techniques requires constant adaptation of methodologies to address the challenges associated with crystalline materials. In this study, we present a novel image processing method to improve pattern matching in the determination of crystalline orientations and phases. Our approach uses sub-pixelar adaptative image processing to register and reconstruct electron diffraction signals in large 4D-STEM datasets. By using adaptive prominence and linear filters such as mean and gaussian blur, we are able to improve the quality of the diffraction pattern registration. The resulting data compression rate of 103 is well-suited for the era of big data and provides a significant enhancement in the performance of the entire ACOM data processing method. Our approach is evaluated using dedicated metrics, which demonstrate a high improvement in phase recognition. Our results demonstrate that this data preparation method not only enhances the quality of the resulting image but also boosts the confidence level in the analysis of the outcomes related to determining crystal orientation and phase. Additionally, it mitigates the impact of user bias that may occur during the application of the method through the manipulation of parameters.
△ Less
Submitted 3 May, 2023;
originally announced May 2023.
-
Binder-free CNT cathodes for Li-O$_2$ batteries with more than one life
Authors:
Zeliang Su,
Israel Temprano,
Nicolas Folastre,
Victor Vanpeene,
Julie Villanova,
Gregory Gachot,
Elena Shevchenko,
Clare P. Grey,
Alejandro A. Franco,
Arnaud Demortiere
Abstract:
Li-O$_2$ batteries (LOB) performance degradation ultimately occurs through the accumulation of discharge products and irreversible clogging of the porous electrode during the cycling. Electrode binder degradation in the presence of reduced oxygen species can result in additional coating of the conductive surface, exacerbating capacity fading. Herein, we establish a facile method to fabricate free-…
▽ More
Li-O$_2$ batteries (LOB) performance degradation ultimately occurs through the accumulation of discharge products and irreversible clogging of the porous electrode during the cycling. Electrode binder degradation in the presence of reduced oxygen species can result in additional coating of the conductive surface, exacerbating capacity fading. Herein, we establish a facile method to fabricate free-standing, binder-free electrodes for LOBs in which multi-wall carbon nanotubes (MWCNT) form cross-linked networks exhibiting high porosity, conductivity, and flexibility. These electrodes demonstrate high reproducibility upon cycling in LOBs. After cell death, efficient and inexpensive methods to wash away the accumulated discharge products are demonstrated, as reconditioning method. The second life usage of these electrodes is validated, without noticeable loss of performance. These findings aim to assist in the development of greener high energy density batteries while reducing manufacturing and recycling costs.
△ Less
Submitted 15 February, 2023;
originally announced February 2023.
-
The Impact of Inter-grain Phases on the Ionic Conductivity of LAGP Solid Electrolyte Prepared by Spark Plasma Sintering
Authors:
Sorina Cretu,
David G. Bradley,
Omer Ulas Kudu,
Li Patrick Wen Feng,
Linh Lan Nguyen,
Tuan Tu Nguyen,
Arash Jamali,
Jean-Noel Chotard,
Vincent Seznec,
John V. Hanna,
Arnaud Demortière,
Martial Duchamp
Abstract:
Li1.5Al0.5Ge1.5(PO4)3 (LAGP) is a promising oxide solid electrolyte for all-solid-state batteries due to its excellent air stability, wide electrochemical stability window and cost-effective precursor materials. However, further improvement in their ionic conductivity performance is hindered by the presence of inter-grain phases leading to a major obstacle to the advanced design of oxide based sol…
▽ More
Li1.5Al0.5Ge1.5(PO4)3 (LAGP) is a promising oxide solid electrolyte for all-solid-state batteries due to its excellent air stability, wide electrochemical stability window and cost-effective precursor materials. However, further improvement in their ionic conductivity performance is hindered by the presence of inter-grain phases leading to a major obstacle to the advanced design of oxide based solid-state electrolytes. This study establishes and quantifies the influence of inter-grain phases, their 3D morphology, and formed compositions on the overall ion conductivity properties of LAGP pellets fabricated under different Spark plasma sintering conditions. Based on complementary techniques, such as PEIS, XRD, 3D FIB-SEM tomography and solid-state MAS NMR coupled with DFT modelling, a deep insight into the inter-grain phase microstructures is obtained revealing that the inter-grain region is comprised of Li4P2O7 and a disordered Li9Al3(P2O7)3(PO4)2 phase. We demonstrate that optimal ionic conductivity for the LAGP system is achieved for the 680 °C SPS preparation when the disordered Li9Al3(P2O7)3(PO4)2 phase dominates the inter-grain region composition with reduced contributions from the highly ordered Li4P2O7 phases.
△ Less
Submitted 11 November, 2022;
originally announced November 2022.
-
Morphological Evolution of NMC Secondary Particles Through in situ electrochemical FIB/SEM experiment
Authors:
François Cadiou,
Tuan-Tu Nguyen,
Martin Bettge,
Zeliang Su,
Jonathan Ando,
Vincent De Andrade,
Dean Miller,
Arnaud Demortière
Abstract:
Microstructural evolution of NMC secondary particles during the battery operation drives the electrochemical performance and impacts the Li-ion battery lifetime. In this work, we develop an in situ methodology using the FIB/SEM instrument to cycle single secondary particles of NMC active materials while following the modifications of their 3D morphology. Two types of secondary particles, i.e. low…
▽ More
Microstructural evolution of NMC secondary particles during the battery operation drives the electrochemical performance and impacts the Li-ion battery lifetime. In this work, we develop an in situ methodology using the FIB/SEM instrument to cycle single secondary particles of NMC active materials while following the modifications of their 3D morphology. Two types of secondary particles, i.e. low and high gradient NMC, were studied alongside morphological investigations in both pristine state and different number of cycles. The quantification of initial inner porosity and cracking evolution upon electrochemical cycling reveals a clear divergence depending on the type of gradient particles. An unexpected enhancement of the discharge capacity is observed during the first cycles concurrently to the appearance of inner cracks. At the first stages, impedance spectroscopy shows a charge transfer resistance reduction that suggests a widening of the crack network connected to the surface, which leads to an increase of contact area between liquid electrolyte and NMC particle. 3D microstructure of individual secondary particles after in situ cycles were investigated using FIB/SEM and nano-XCT. The results suggest a strong impact of the initial porosity shape on the degradation rate.
△ Less
Submitted 1 August, 2022;
originally announced August 2022.
-
Lithium Ion Battery Electrode Manufacturing Model Accounting for 3D Realistic Shapes of Active Material Particles
Authors:
Jiahui Xu,
Alain C. Ngandjong,
Chaoyue Liu,
Franco M. Zanotto,
Oier Arcelus,
Arnaud Demortiere,
Alejandro A. Franco
Abstract:
The demand for lithium ion batteries (LIBs) on the market has gradually risen, with production increasing every year. To meet industrial needs, the development of digital twins designed to optimize LIB manufacturing processes is essential. Here, by using LiNi0.33Co0.33Mn0.33O2 (NMC111) material as an example, we introduce the realistic particles shapes of the active material obtained from X-ray mi…
▽ More
The demand for lithium ion batteries (LIBs) on the market has gradually risen, with production increasing every year. To meet industrial needs, the development of digital twins designed to optimize LIB manufacturing processes is essential. Here, by using LiNi0.33Co0.33Mn0.33O2 (NMC111) material as an example, we introduce the realistic particles shapes of the active material obtained from X-ray micro-computed tomography into a Coarse-Grained Molecular Dynamic physical model to simulate the slurry and its drying, and into a Discrete Element Method model able to simulate the calendering of the resulting electrode. This model enables to link the manufacturing parameters with the microstructure of the electrodes and to better observe the effect of the former on the heterogeneity of the electrodes. The results of the simulations allow us, among others, to observe the alteration of the electrode heterogeneity during the manufacturing process and the slight deformation of the secondary particles of active material.
△ Less
Submitted 8 June, 2022;
originally announced June 2022.
-
Adorym: A multi-platform generic x-ray image reconstruction framework based on automatic differentiation
Authors:
Ming Du,
Saugat Kandel,
Jun**g Deng,
Xiao**g Huang,
Arnaud Demortiere,
Tuan Tu Nguyen,
Remi Tucoulou,
Vincent De Andrade,
Qiaoling **,
Chris Jacobsen
Abstract:
We describe and demonstrate an optimization-based x-ray image reconstruction framework called Adorym. Our framework provides a generic forward model, allowing one code framework to be used for a wide range of imaging methods ranging from near-field holography to and fly-scan ptychographic tomography. By using automatic differentiation for optimization, Adorym has the flexibility to refine experime…
▽ More
We describe and demonstrate an optimization-based x-ray image reconstruction framework called Adorym. Our framework provides a generic forward model, allowing one code framework to be used for a wide range of imaging methods ranging from near-field holography to and fly-scan ptychographic tomography. By using automatic differentiation for optimization, Adorym has the flexibility to refine experimental parameters including probe positions, multiple hologram alignment, and object tilts. It is written with strong support for parallel processing, allowing large datasets to be processed on high-performance computing systems. We demonstrate its use on several experimental datasets to show improved image quality through parameter refinement.
△ Less
Submitted 22 December, 2020;
originally announced December 2020.
-
Low-threshold stimulated emission using colloidal quantum wells
Authors:
Chunxing She,
Igor Fedin,
Dmitriy S. Dolzhnikov,
Arnaud Demortière,
Richard D. Schaller,
Matthew Pelton,
Dmitri V. Talapin
Abstract:
Semiconductor nanocrystals can be synthesized using inexpensive, scalable, solution-based techniques, and their utility as tunable light emitters has been demonstrated in various applications, including biolabeling and light-emitting devices. By contrast, the use of colloidal nanocrystals for optical amplification and lasing has been limited by the high input power densities that have been require…
▽ More
Semiconductor nanocrystals can be synthesized using inexpensive, scalable, solution-based techniques, and their utility as tunable light emitters has been demonstrated in various applications, including biolabeling and light-emitting devices. By contrast, the use of colloidal nanocrystals for optical amplification and lasing has been limited by the high input power densities that have been required. In this work, we show that colloidal nanoplatelets (NPLs) produce amplified spontaneous emission (ASE) with pump-fluence thresholds as low 6 uJ/cm2 and gain as high as 600 cm-1, both a 4-fold improvement over the best reported values for colloidal nanocrystals; in addition, gain saturation occurs at pump fluences two orders of magnitude higher than the ASE threshold. We attribute this exceptional performance to large optical cross-sections, slow Auger recombination rates, and the narrow emission linewidth of the NPL ensemble. The NPLs bring the advantages of quantum wells as an optical gain medium to a colloidal system, opening up the possibility of producing high-efficiency, solution-processed lasers.
△ Less
Submitted 11 December, 2013;
originally announced December 2013.