Nucleation at the phase transition near 40~$^{\circ }$C in MnAs nanodisks
Authors:
B Jenichen,
Y Takagaki,
K H Ploog,
N Darowski,
R Feyerherm,
I Zizak
Abstract:
The phase transition near 40~$^{\circ }$C of both as-grown thin epitaxial MnAs films prepared by molecular beam epitaxy on GaAs(001) and nanometer-scale disks fabricated from the same films is studied. The disks are found to exhibit a pronounced hysteresis in the temperature curve of the phase composition. In contrast, supercooling and overheating take place far less in the samples of continuous l…
▽ More
The phase transition near 40~$^{\circ }$C of both as-grown thin epitaxial MnAs films prepared by molecular beam epitaxy on GaAs(001) and nanometer-scale disks fabricated from the same films is studied. The disks are found to exhibit a pronounced hysteresis in the temperature curve of the phase composition. In contrast, supercooling and overheating take place far less in the samples of continuous layers. These phenomena are explained in terms of the necessary formation of nuclei of the other phase in each of the disks independent from each other. The influence of the elastic strains in the disks is reduced considerably.
△ Less
Submitted 16 July, 2019;
originally announced July 2019.
-
Exchange bias in GeMn nanocolumns: the role of surface oxidation
Authors:
S. Tardif,
S. Cherifi,
M. Jamet,
T. Devillers,
A. Barski,
D. Schmitz,
N. Darowski,
P. Thakur,
J. C. Cezar,
N. B. Brookes,
R. Mattana,
J. Cibert
Abstract:
We report on the exchange biasing of self-assembled ferromagnetic GeMn nanocolumns by GeMn-oxide caps. The x-ray absorption spectroscopy analysis of this surface oxide shows a multiplet fine structure that is typical of the Mn2+ valence state in MnO. A magnetization hysteresis shift |HE|~100 Oe and a coercivity enhancement of about 70 Oe have been obtained upon cooling (300-5 K) in a magnetic fiel…
▽ More
We report on the exchange biasing of self-assembled ferromagnetic GeMn nanocolumns by GeMn-oxide caps. The x-ray absorption spectroscopy analysis of this surface oxide shows a multiplet fine structure that is typical of the Mn2+ valence state in MnO. A magnetization hysteresis shift |HE|~100 Oe and a coercivity enhancement of about 70 Oe have been obtained upon cooling (300-5 K) in a magnetic field as low as 0.25 T. This exchange bias is attributed to the interface coupling between the ferromagnetic nanocolumns and the antiferromagnetic MnO-like caps. The effect enhancement is achieved by depositing a MnO layer on the GeMn nanocolumns.
△ Less
Submitted 17 August, 2010;
originally announced August 2010.