Magnetism and magnetocaloric properties of Co$_{1-x}$Mn$_x$Cr$_2$O$_4$
Authors:
Joya A. Cooley,
Gregor Dairaghi,
Guy C. Moore,
Matthew K. Horton,
Emily C. Schueller,
Kristin A. Persson,
Ram Seshadri
Abstract:
Co$_{1-x}$Mn$_x$Cr$_2$O$_4$ crystallizes as a normal spinel in the cubic $Fd \overline{3}m$ space group, and the end members have been reported to display a region of collinear ferrimagnetism as well as a low-temperature spin-spiral state with variable coherence lengths from 3 nm to 10 nm in polycrystalline samples. Here, we present the synthesis of the entire solid solution, and data showing that…
▽ More
Co$_{1-x}$Mn$_x$Cr$_2$O$_4$ crystallizes as a normal spinel in the cubic $Fd \overline{3}m$ space group, and the end members have been reported to display a region of collinear ferrimagnetism as well as a low-temperature spin-spiral state with variable coherence lengths from 3 nm to 10 nm in polycrystalline samples. Here, we present the synthesis of the entire solid solution, and data showing that the ferrimagnetic ordering temperature as well as the spin-spiral lock-in temperature are tunable with the Co/Mn ratio. The peak magnetocaloric entropy change was determined to be $ΔS_M$ = -5.63 J kg$^{-1}$ K$^{-1}$ in an applied magnetic field change of $ΔH$ = 0 T to 5 T for the Mn end-member at the ferrimagnetic ordering temperature. Using density functional theory (DFT), we explore the shortcomings of the magnetic deformation proxy to identify trends in $ΔS_M$ across composition in this spinel system, and explore future extensions of theory to address these discrepancies.
△ Less
Submitted 28 September, 2023;
originally announced September 2023.