Bridging Fidelities to Predict Nanoindentation Tip Radii Using Interpretable Deep Learning Models
Authors:
Claus O. W. Trost,
Stanislav Zak,
Sebastian Schaffer,
Christian Saringer,
Lukas Exl,
Megan J. Cordill
Abstract:
As the need for miniaturized structural and functional materials has increased,the need for precise materials characterizaton has also expanded. Nanoindentation is a popular method that can be used to measure material mechanical behavior which enables high-throughput experiments and, in some cases, can also provide images of the indented area through scanning. Both indenting and scanning can cause…
▽ More
As the need for miniaturized structural and functional materials has increased,the need for precise materials characterizaton has also expanded. Nanoindentation is a popular method that can be used to measure material mechanical behavior which enables high-throughput experiments and, in some cases, can also provide images of the indented area through scanning. Both indenting and scanning can cause tip wear that can influence the measurements. Therefore, precise characterization of tip radii is needed to improve data evaluation. A data fusion method is introduced which uses finite element simulations and experimental data to estimate the tip radius in situ in a meaningful way using an interpretable multi-fidelity deep learning approach. By interpreting the machine learning models, it is shown that the approaches are able to accurately capture physical indentation phenomena.
△ Less
Submitted 1 July, 2022;
originally announced July 2022.
-
Estimation of the in-situ elastic constants of wood pulp fibers in freely dried paper via AFM experiments
Authors:
Caterina Czibula,
August Brandberg,
Megan J. Cordill,
Aleksandar Matković,
Oleksandr Glushko,
Chiara Czibula,
Artem Kulachenko,
Christian Teichert,
Ulrich Hirn
Abstract:
Atomic force microscopy-based nanoindentation (AFM-NI) enables characterization of the basic mechanical properties of wood pulp fibers in conditions representative of the state inside a paper sheet. Determination of the mechanical properties under different loads is critical for the success of increasingly advanced computational models to understand, predict and improve the behavior of paper and p…
▽ More
Atomic force microscopy-based nanoindentation (AFM-NI) enables characterization of the basic mechanical properties of wood pulp fibers in conditions representative of the state inside a paper sheet. Determination of the mechanical properties under different loads is critical for the success of increasingly advanced computational models to understand, predict and improve the behavior of paper and paperboard. Here, AFM-NI was used to indent fibers transverse to and along the longitudinal axis of the fiber. Indentation moduli and hardness were obtained for relative humidity from 25 % to 75 %. The hardness and the indentation modulus exhibit moisture dependency, decreasing by 75 % and 50 %, respectively, over the range tested. The determined indentation moduli were combined with previous work to estimate the longitudinal and transverse elastic modulus of the fiber wall. Due to the relatively low indentation moduli, the elastic constants are also low compared to values obtained via single fiber testing.
△ Less
Submitted 5 December, 2020;
originally announced December 2020.
-
A new approach to evaluate the elastic modulus of metallic foils
Authors:
C. O. W. Trost,
S. Wurster,
C. Freitag,
A. Steinberger,
M. J. Cordill
Abstract:
The accurate determination of the elastic properties is non-trivial for metallic foils. The measured elastic modulus is often described in literature as significantly smaller than the respective modulus of the bulk counterparts. This paper describes a straight forward way to minimize the influence of the measurement on the calculated values using a standard tensile testing device combined with a l…
▽ More
The accurate determination of the elastic properties is non-trivial for metallic foils. The measured elastic modulus is often described in literature as significantly smaller than the respective modulus of the bulk counterparts. This paper describes a straight forward way to minimize the influence of the measurement on the calculated values using a standard tensile testing device combined with a laser speckle extensometer and advanced data evaluation. The elasticmodulus obtained with a monotonic tensile procedure is compared to values obtained frommultiple loading unloading cycles in the elastic regime. The latter were found to lead to more reproducible and reasonable values with significantly smaller standard deviations. To enable interpretation of the modulus values electron backscatter diffraction and X ray diffraction were used to emphasize the effects of texture and microstructure. Two different electrodeposited copper foilswere characterized since copper iswidely used in many industrial applications.
△ Less
Submitted 29 September, 2020;
originally announced September 2020.
-
Crack initiation of printed lines predicted with digital image correlation
Authors:
C. Katsarelis,
O. Glushko,
C. Tonkin,
M. S. Kennedy,
M. J. Cordill
Abstract:
Printing of metallic films has been preferred for roll-to-roll processes over vacuum technologies due to faster processing times and lower processing costs. Films can be produced by depositing inks containing suspended metallic particles within a solvent and then heating the films to both remove the solvent and sinter the particles. The resulting printed structure, electrical and mechanical behavi…
▽ More
Printing of metallic films has been preferred for roll-to-roll processes over vacuum technologies due to faster processing times and lower processing costs. Films can be produced by depositing inks containing suspended metallic particles within a solvent and then heating the films to both remove the solvent and sinter the particles. The resulting printed structure, electrical and mechanical behavior of the printed films has been studied to better understand their electro-mechanical response to loading and eventual brittle fracture. This study evaluated the electro-mechanical behavior of 1.25 μm printed Ag films using in-situ resistance and in-situ imaging methods. Digital image correlation was utilized with confocal laser scanning microscope images to better visualize crack initiation during tensile straining. This technique showed that cracks initiated earlier in the thicker areas of the film (crests) than in lower areas (troughs) because of a higher density of printing defects and the increased thickness.
△ Less
Submitted 9 April, 2019;
originally announced July 2019.
-
Monotonic and cyclic mechanical reliability of metallization lines on polymer substrates
Authors:
Oleksandr Glushko,
Andreas Klug,
Emil J. W. List-Kratochvil,
Megan J. Cordill
Abstract:
Mechanical stability of Ag and Cu printed and evaporated metallization lines on polymer substrates is investigated by means of monotonic tensile and cyclic bending tests. It is shown that lines which demonstrate good performance during monotonic tests fail at lower strains during a cyclic bending tests. Evaporated lines with the grain size of several hundreds of nanometers have good ductility and…
▽ More
Mechanical stability of Ag and Cu printed and evaporated metallization lines on polymer substrates is investigated by means of monotonic tensile and cyclic bending tests. It is shown that lines which demonstrate good performance during monotonic tests fail at lower strains during a cyclic bending tests. Evaporated lines with the grain size of several hundreds of nanometers have good ductility and consequently good stability during monotonic loading but at the same time they fail at low strains during cyclic bending. Printed lines with nanocrystalline microstructure, in contrast, demonstrate more intensive cracking during monotonic loading but higher failure strains during cyclic bending. Apart from the grain size effect, the effect of film thickness on the saturation crack density after cyclic bending is also demonstrated. Thinner films have higher crack density in accordance with the shear lag model.
△ Less
Submitted 9 April, 2019;
originally announced April 2019.
-
Explicit relationship between electrical and topological degradation of polymer-supported metal films subjected to mechanical loading
Authors:
Oleksandr Glushko,
Philipp Kraker,
M. J. Cordill
Abstract:
For a comprehensive characterization of mechanical reliability of metallization layers on polymer substrates both electrical and mechanical degradation should be taken into account. Although it is evident that cracking of a conductive film should lead to electrical degradation, the quantitative relationship between the growth of electric resistance and parameters of the induced crack pattern has r…
▽ More
For a comprehensive characterization of mechanical reliability of metallization layers on polymer substrates both electrical and mechanical degradation should be taken into account. Although it is evident that cracking of a conductive film should lead to electrical degradation, the quantitative relationship between the growth of electric resistance and parameters of the induced crack pattern has remained thus far unexplored. With the help of finite element modelling we were able to find an explicit and concise expression which shows that electrical resistance grows with the fourth order of the crack length and second order of the areal crack density. The discovered relationship was verified by comparison with the experimental results of tensile testing of polymer-supported thin metal films. Presented model is independent of the length scale and can be applied to films with different thicknesses as long as Ohm's law is valid. It is demonstrated that linear crack density is an ambiguous parameter which does not properly capture the development of a crack pattern. For the unambiguous characterization of the intensity of a crack pattern a universal dimensionless factor is proposed. Presented results show that there is a wide range of possible crack patterns which do not lead to electrical failure of a conductive film that can be used for failure-free design of flexible electronic devices.
△ Less
Submitted 5 April, 2019;
originally announced April 2019.
-
The driving force governing room temperature grain coarsening in thin gold films
Authors:
Oleksandr Glushko,
Megan J. Cordill
Abstract:
Strong room-temperature grain coarsening in gold films on polyimide induced by cyclic uniaxial mechanical strain is demonstrated. Detailed electron backscatter diffraction analysis revealed that, in contrast to the predictions of shear-coupled grain boundary migration model, the grain coarsening is isotropic and coarsened grains do not exhibit any specific crystallographic orientations or misorien…
▽ More
Strong room-temperature grain coarsening in gold films on polyimide induced by cyclic uniaxial mechanical strain is demonstrated. Detailed electron backscatter diffraction analysis revealed that, in contrast to the predictions of shear-coupled grain boundary migration model, the grain coarsening is isotropic and coarsened grains do not exhibit any specific crystallographic orientations or misorientations to the neighboring grains. It is shown that a thermodynamic model where the driving force appears due to the difference in yield stresses between the grains with different sizes provides an adequate explanation of the experimental data.
△ Less
Submitted 5 April, 2019;
originally announced April 2019.