A micromechanical study of heat treatment induced hardening in α-brass
Authors:
Jonathan Birch,
Emily Jenkins,
Anastasia Vrettou,
Mohammed Said,
Himanshu Vashishtha,
Thomas Connolley,
Jeff Brooks,
David M. Collins
Abstract:
The mechanisms that govern a previously unexplained hardening effect of a single phase Cu-30wt%Zn α-brass after heating have been investigated. After cold-work, the alloy possesses an increased yield strength and hardening rate only when heat treated to temperatures close to 220{^\circ}C, and is otherwise softer. Crystallographic texture and microstructure, explored using electron backscatter diff…
▽ More
The mechanisms that govern a previously unexplained hardening effect of a single phase Cu-30wt%Zn α-brass after heating have been investigated. After cold-work, the alloy possesses an increased yield strength and hardening rate only when heat treated to temperatures close to 220{^\circ}C, and is otherwise softer. Crystallographic texture and microstructure, explored using electron backscatter diffraction (EBSD), describe the deformation heterogeneity including twin development, as a function of heat treatment. When heated, an increased area fraction of deformation twins is observed, with dimensions reaching a critical size that maximises the resistance to dislocation slip in the parent grains. The effect is shown to dominate over other alloy characteristics including short range order, giving serrated yielding during tensile testing which is mostly eliminated after heating. In-situ X-ray diffraction during tensile testing corroborates these findings; dislocation-related line broadening and lattice strain development between as worked and heated α-brass is directly related to the interaction between the dislocations and the population of deformation twins. The experiments unambiguously disprove that other thermally-induced microstructure features contribute to thermal hardening. Specifically, the presence of recrystallised grains or second phases do not play a role. As these heat treatments match annealing conditions subjected to α-brass during deformation-related manufacturing processes, the results here are considered critical to understand, predict and exploit, where appropriate, any beneficial process-induced structural behaviour.
△ Less
Submitted 14 June, 2024;
originally announced June 2024.
-
Grain-level effects on in-situ deformation-induced phase transformations in a complex-phase steel using 3DXRD and EBSD
Authors:
James A. D. Ball,
Claire Davis,
Carl Slater,
Himanshu Vashishtha,
Mohammed Said,
Louis Hébrard,
Florian Steinhilber,
Jonathan P. Wright,
Thomas Connolley,
Stefan Michalik,
David M. Collins
Abstract:
A novel complex-phase steel alloy is conceived with a deliberately unstable austenite, $γ$, phase that enables the deformation-induced martensitic transformations (DIMT) to be explored at low levels of plastic strain. The DIMT was thus explored, in-situ and non-destructively, using both far-field Three-Dimensional X-Ray Diffraction (3DXRD) and Electron Back-Scatter Diffraction (EBSD). Substantial…
▽ More
A novel complex-phase steel alloy is conceived with a deliberately unstable austenite, $γ$, phase that enables the deformation-induced martensitic transformations (DIMT) to be explored at low levels of plastic strain. The DIMT was thus explored, in-situ and non-destructively, using both far-field Three-Dimensional X-Ray Diffraction (3DXRD) and Electron Back-Scatter Diffraction (EBSD). Substantial $α'$ martensite formation was observed under 10% applied strain with EBSD, and many $\varepsilon$ grain formation events were captured with 3DXRD, indicative of the indirect transformation of martensite via the reaction $γ\rightarrow \varepsilon \rightarrow α'$. Using $\varepsilon$ grain formation as a direct measurement of $γ$ grain stability, the influence of several microstructural properties, such as grain size, orientation and neighbourhood configuration, on $γ$ stability have been identified. Larger $γ$ grains were found to be less stable than smaller grains. Any $γ$ grains oriented with {100} parallel to the loading direction preferentially transformed with lower stresses. Parent $\varepsilon$-forming $γ$ grains possessed a neighbourhood with increased ferritic/martensitic volume fraction. This finding shows, unambiguously, that $α$/$α'$ promotes $\varepsilon$ formation in neighbouring grains. The minimum strain work criterion model for $\varepsilon$ variant prediction was also evaluated, which worked well for most grains. However, $\varepsilon$-forming grains with a lower stress were less well predicted by the model, indicating crystal-level behaviour must be considered for accurate $\varepsilon$ formation. The findings from this work are considered key for the future design of alloys where the deformation response can be controlled by tailoring microstructure and local or macroscopic crystal orientations.
△ Less
Submitted 7 November, 2023; v1 submitted 6 November, 2023;
originally announced November 2023.
-
Per-grain and neighbourhood stress interactions during deformation of a ferritic steel obtained using three-dimensional X-ray diffraction
Authors:
James A. D. Ball,
Anna Kareer,
Oxana V. Magdysyuk,
Stefan Michalik,
Thomas Connolley,
David M. Collins
Abstract:
Three-dimensional X-ray diffraction (3DXRD) has been used to measure, in-situ, the evolution of $\sim 1800$ grains in a single phase low carbon ferritic steel sample during uniaxial deformation. The distribution of initial residual grain stresses in the material was observed to prevail as plasticity builds, though became less pronounced, and therefore less influential as strain increased. The init…
▽ More
Three-dimensional X-ray diffraction (3DXRD) has been used to measure, in-situ, the evolution of $\sim 1800$ grains in a single phase low carbon ferritic steel sample during uniaxial deformation. The distribution of initial residual grain stresses in the material was observed to prevail as plasticity builds, though became less pronounced, and therefore less influential as strain increased. The initial Schmid factor of a grain was found to be strongly correlated to the intergranular stress change and the range of stresses that are permissible; a grain well aligned for easy slip is more likely to exhibit a range of stresses than those orientated poorly for dislocation motion. The orientation path of a grain, however, is not only dependent on its initial orientation, but hypothesised to be influenced by its stress state and the stress state of its grain environment. A grain neighbourhood effect is observed: the Schmid factor of serial adjoining grains influences the stress state of a grain of interest, whereas parallel neighbours are much less influential. This phenomenon is strongest at low plastic strains only, with the effect diminishing as plasticity builds. The influence of initial residual stresses becomes less evident, and grains rotate to eliminate any orientation dependent load shedding. The ability of the BCC ferrite to exhaust such neighbourhood interactions, which would otherwise be detrimental in crystal structures with lower symmetric and fewer slip systems, is considered key to the high ductility possessed by these materials.
△ Less
Submitted 21 February, 2023;
originally announced February 2023.
-
Implementing and evaluating far-field 3D X-ray diffraction at the I12 JEEP beamline, Diamond Light Source
Authors:
James A. D. Ball,
Anna Kareer,
Oxana V. Magdysyuk,
Stefan Michalik,
Anastasia Vrettou,
Neal Parkes,
Thomas Connolley,
David M. Collins
Abstract:
Three-dimensional X-ray diffraction (3DXRD) is shown to be feasible at the I12 Joint Engineering, Environmental and Processing (JEEP) beamline of Diamond Light Source. As a demonstration, a microstructually simple low-carbon ferritic steel was studied in a highly textured and annealed state. A processing pipeline suited to this beamline was created, using software already established in the 3DXRD…
▽ More
Three-dimensional X-ray diffraction (3DXRD) is shown to be feasible at the I12 Joint Engineering, Environmental and Processing (JEEP) beamline of Diamond Light Source. As a demonstration, a microstructually simple low-carbon ferritic steel was studied in a highly textured and annealed state. A processing pipeline suited to this beamline was created, using software already established in the 3DXRD user community, enabling grain centre-of-mass positions, orientations and strain tensor elements to be determined. Orientations, with texture measurements independently validated from electron backscatter diffraction (EBSD) data, possessed a $\sim 0.1^\circ$ uncertainty, comparable with other 3DXRD instruments. The spatial resolution was limited by the far-field detector pixel size; the average of the grain centre of mass position errors was determined as $\pm \sim 80 μ$m. An average per-grain error of $\sim 1 \times 10^{-3}$ for the elastic strains was also measured; this could be reduced in future experiments by improving sample preparation, data collection and analysis techniques. Application of 3DXRD onto I12 shows great potential, where its implementation is highly desirable due the flexible, open architecture of the beamline. User-owned or designed sample environments can be used, thus 3DXRD could be applied to previously unexplored scientific areas.
△ Less
Submitted 20 February, 2023; v1 submitted 12 November, 2021;
originally announced November 2021.
-
Correlative Synchrotron X-ray Imaging and Diffraction of Directed Energy Deposition Additive Manufacturing
Authors:
Yunhui Chen,
Samuel J. Clark,
David M. Collins,
Sebastian Marussi,
Simon A. Hunt,
Danielle M. Fenech,
Thomas Connolley,
Robert C. Atwood,
Oxana V. Magdysyuk,
Gavin J. Baxter,
Martyn A. Jones,
Chu Lun Alex Leung,
Peter D. Lee
Abstract:
The governing mechanistic behaviour of Directed Energy Deposition Additive Manufacturing (DED-AM) is revealed by a combined in situ and operando synchrotron X-ray imaging and diffraction study of a nickel-base superalloy, IN718. Using a unique process replicator, real-space phase-contrast imaging enables quantification of the melt-pool boundary and flow dynamics during solidification. This imaging…
▽ More
The governing mechanistic behaviour of Directed Energy Deposition Additive Manufacturing (DED-AM) is revealed by a combined in situ and operando synchrotron X-ray imaging and diffraction study of a nickel-base superalloy, IN718. Using a unique process replicator, real-space phase-contrast imaging enables quantification of the melt-pool boundary and flow dynamics during solidification. This imaging knowledge informed precise diffraction measurements of temporally resolved microstructural phases during transformation and stress development with a spatial resolution of 100 $μ$m. The diffraction quantified thermal gradient enabled a dendritic solidification microstructure to be predicted and coupled to the stress orientation and magnitude. The fast cooling rate entirely suppressed the formation of secondary phases or recrystallisation in the solid-state. Upon solidification, the stresses rapidly increase to the yield strength during cooling. This insight, combined with IN718 $'$s large solidification range suggests that the accumulated plasticity exhausts the alloy$'$s ductility, causing liquation cracking. This study has revealed additional fundamental mechanisms governing the formation of highly non-equilibrium microstructures during DED-AM.
△ Less
Submitted 16 September, 2020;
originally announced September 2020.
-
In situ and Operando X-ray Imaging of Directed Energy Deposition Additive Manufacturing
Authors:
Yunhui Chen,
Samuel J. Clark,
Lorna Sinclair,
Chu Lun Alex Leung,
Sebastian Marussi,
Thomas Connolley,
Oxana V. Magdysyuk,
Robert C. Atwood,
Gavin J. Baxter,
Martyn A. Jones,
David G. McCartney,
Iain Todd,
Peter D. Lee
Abstract:
The mechanical performance of Directed Energy Deposition Additive Manufactured (DED-AM) components can be highly material dependent. Through in situ and operando synchrotron X-ray imaging we capture the underlying phenomena controlling build quality of stainless steel (SS316) and titanium alloy (Ti6242 or Ti-6Al-2Sn-4Zr-2Mo). We reveal three mechanisms influencing the build efficiency of titanium…
▽ More
The mechanical performance of Directed Energy Deposition Additive Manufactured (DED-AM) components can be highly material dependent. Through in situ and operando synchrotron X-ray imaging we capture the underlying phenomena controlling build quality of stainless steel (SS316) and titanium alloy (Ti6242 or Ti-6Al-2Sn-4Zr-2Mo). We reveal three mechanisms influencing the build efficiency of titanium alloys compared to stainless steel: blown powder sintering; reduced melt-pool wetting due to the sinter; and pore pushing in the melt-pool. The former two directly increase lack of fusion porosity, while the later causes end of track porosity. Each phenomenon influences the melt-pool characteristics, wetting of the substrate and hence build efficacy and undesirable microstructural feature formation. We demonstrate that porosity is related to powder characteristics, pool flow, and solidification front morphology. Our results clarify DED-AM process dynamics, illustrating why each alloy builds differently, facilitating the wider application of additive manufacturing to new materials.
△ Less
Submitted 16 June, 2020;
originally announced June 2020.
-
3D Characterisation of the Fe-rich intermetallic phases in Al-5%Cu alloys by synchrotron X-ray microtomography and skeletonisation
Authors:
Y. Zhao,
W. Du,
B. Koe,
T. Connolley,
S. Irvine,
P. K. Allan,
C. M. Schlepütz,
W. Zhang,
F. Wang,
D. G. Eskin,
J. Mi
Abstract:
Synchrotron X-ray microtomography and skeletonisation method were used to study the true 3D network structures and morphologies of the Fe-rich intermetallic phases in Al-5.0%Cu-0.6%Mn alloys with 0.5% and 1.0% Fe. It was found that, the Fe-phases in the 1.0%Fe alloy have node lengths of 5-25m; while those in the 0.5%Fe alloy are of 3-17 m. The Fe-phases in the 1.0%Fe alloy also developed sharper m…
▽ More
Synchrotron X-ray microtomography and skeletonisation method were used to study the true 3D network structures and morphologies of the Fe-rich intermetallic phases in Al-5.0%Cu-0.6%Mn alloys with 0.5% and 1.0% Fe. It was found that, the Fe-phases in the 1.0%Fe alloy have node lengths of 5-25m; while those in the 0.5%Fe alloy are of 3-17 m. The Fe-phases in the 1.0%Fe alloy also developed sharper mean curvature with wider distribution than those in the 0.5%Fe alloy. Combining SEM studies of the deeply-etched samples, the true 3D structures of 4 different type Fe-phases in both alloys are also revealed and demonstrated.
△ Less
Submitted 11 December, 2017;
originally announced December 2017.