The influence of dislocations on R-phase transformations in a NiTi shape memory alloy
Authors:
Himanshu Vashishtha,
David M. Collins
Abstract:
The ability to control the stress-induced phase transformation of the shape memory alloy, NiTi, is an important technological challenge that must be understood for their wide application in devices that can exploit their reversible strain properties. This study elucidates the direct relationship between dislocation density and the \textit{R}-phase transformation, including its formation temperatur…
▽ More
The ability to control the stress-induced phase transformation of the shape memory alloy, NiTi, is an important technological challenge that must be understood for their wide application in devices that can exploit their reversible strain properties. This study elucidates the direct relationship between dislocation density and the \textit{R}-phase transformation, including its formation temperature from interrupted annealing of rolled NiTi samples. Deformation is shown to determine the enthalpy change required for the B2$\rightarrow$\textit{R}-phase transformation, with associated transformation temperatures being modifiable via dislocation density and recovery processes. Recovery is shown to be rapid, highly heterogeneous and sensitive to crystal orientation. Grains with a $\langle100\rangle$ direction close to the macroscopic rolling direction recover more rapidly than $\langle110\rangle$ and $\langle111\rangle$ orientated grains. Considered to be governed by processing induced residual stresses and resultant crystallographic dependent annihilation/slip pathways, there are opportunities to tune B2$\rightarrow$\textit{R}-phase transformation on either a grain-averaged or an orientation dependant per-grain basis.
△ Less
Submitted 18 June, 2024;
originally announced June 2024.
-
A micromechanical study of heat treatment induced hardening in α-brass
Authors:
Jonathan Birch,
Emily Jenkins,
Anastasia Vrettou,
Mohammed Said,
Himanshu Vashishtha,
Thomas Connolley,
Jeff Brooks,
David M. Collins
Abstract:
The mechanisms that govern a previously unexplained hardening effect of a single phase Cu-30wt%Zn α-brass after heating have been investigated. After cold-work, the alloy possesses an increased yield strength and hardening rate only when heat treated to temperatures close to 220{^\circ}C, and is otherwise softer. Crystallographic texture and microstructure, explored using electron backscatter diff…
▽ More
The mechanisms that govern a previously unexplained hardening effect of a single phase Cu-30wt%Zn α-brass after heating have been investigated. After cold-work, the alloy possesses an increased yield strength and hardening rate only when heat treated to temperatures close to 220{^\circ}C, and is otherwise softer. Crystallographic texture and microstructure, explored using electron backscatter diffraction (EBSD), describe the deformation heterogeneity including twin development, as a function of heat treatment. When heated, an increased area fraction of deformation twins is observed, with dimensions reaching a critical size that maximises the resistance to dislocation slip in the parent grains. The effect is shown to dominate over other alloy characteristics including short range order, giving serrated yielding during tensile testing which is mostly eliminated after heating. In-situ X-ray diffraction during tensile testing corroborates these findings; dislocation-related line broadening and lattice strain development between as worked and heated α-brass is directly related to the interaction between the dislocations and the population of deformation twins. The experiments unambiguously disprove that other thermally-induced microstructure features contribute to thermal hardening. Specifically, the presence of recrystallised grains or second phases do not play a role. As these heat treatments match annealing conditions subjected to α-brass during deformation-related manufacturing processes, the results here are considered critical to understand, predict and exploit, where appropriate, any beneficial process-induced structural behaviour.
△ Less
Submitted 14 June, 2024;
originally announced June 2024.
-
Microscale stress-geometry interactions in an additively manufactured NiTi cardiovascular stent: A synchrotron dual imaging tomography and diffraction study
Authors:
Himanshu Vashishtha,
Parastoo Jamshidi,
Anastasia Vrettou,
Anna Kareer,
Michael Goode,
Hans Deyhle,
Andrew James,
Sharif Ahmad,
Christina Reinhard,
Moataz M. Attallah,
David M. Collins
Abstract:
This study explores cardiovascular stents fabricated using laser powder bed fusion (LPBF); an emerging method to offer patient-specific customisable parts. Here, the shape memory alloy NiTi, in a near equiatomic composition, was investigated to deconvolve the material response from macroscopic component effects. Specifically, stress-geometry interactions were revealed, in-situ, for a minaturised c…
▽ More
This study explores cardiovascular stents fabricated using laser powder bed fusion (LPBF); an emerging method to offer patient-specific customisable parts. Here, the shape memory alloy NiTi, in a near equiatomic composition, was investigated to deconvolve the material response from macroscopic component effects. Specifically, stress-geometry interactions were revealed, in-situ, for a minaturised cardiovascular stent subjected to an externally applied cylindrical stress whilst acquiring synchrotron X-ray imaging and diffraction data. The approach enabled the collection of spatially resolved micromechanical deformation data; the formation of stress-induced martensite and R-phase was evident, occurring in locations near junctions between stent ligaments where stress concentrations exist. In the as-fabricated condition, hardness maps were obtained through nanoindentation, demonstrating that the localised deformation and deformation patterning is further controlled by porosity and microstructural heterogeneity. Electron backscatter diffraction (EBSD) supported these observations, showing a finer grain structure near stent junctions with higher associated lattice curvature. These features, combined with stress concentrations when loaded will initiate localised phase transformations. If the stent was subjected to repeated loading, representing in-vivo conditions, these regions would be susceptible to cyclic damage through transformation memory loss, leading to premature component failure. This study highlights the challenges that must be addressed for the post-processing treatment of LABF-processed stents for healthcare-related applications.
△ Less
Submitted 12 December, 2023;
originally announced December 2023.
-
Grain-level effects on in-situ deformation-induced phase transformations in a complex-phase steel using 3DXRD and EBSD
Authors:
James A. D. Ball,
Claire Davis,
Carl Slater,
Himanshu Vashishtha,
Mohammed Said,
Louis Hébrard,
Florian Steinhilber,
Jonathan P. Wright,
Thomas Connolley,
Stefan Michalik,
David M. Collins
Abstract:
A novel complex-phase steel alloy is conceived with a deliberately unstable austenite, $γ$, phase that enables the deformation-induced martensitic transformations (DIMT) to be explored at low levels of plastic strain. The DIMT was thus explored, in-situ and non-destructively, using both far-field Three-Dimensional X-Ray Diffraction (3DXRD) and Electron Back-Scatter Diffraction (EBSD). Substantial…
▽ More
A novel complex-phase steel alloy is conceived with a deliberately unstable austenite, $γ$, phase that enables the deformation-induced martensitic transformations (DIMT) to be explored at low levels of plastic strain. The DIMT was thus explored, in-situ and non-destructively, using both far-field Three-Dimensional X-Ray Diffraction (3DXRD) and Electron Back-Scatter Diffraction (EBSD). Substantial $α'$ martensite formation was observed under 10% applied strain with EBSD, and many $\varepsilon$ grain formation events were captured with 3DXRD, indicative of the indirect transformation of martensite via the reaction $γ\rightarrow \varepsilon \rightarrow α'$. Using $\varepsilon$ grain formation as a direct measurement of $γ$ grain stability, the influence of several microstructural properties, such as grain size, orientation and neighbourhood configuration, on $γ$ stability have been identified. Larger $γ$ grains were found to be less stable than smaller grains. Any $γ$ grains oriented with {100} parallel to the loading direction preferentially transformed with lower stresses. Parent $\varepsilon$-forming $γ$ grains possessed a neighbourhood with increased ferritic/martensitic volume fraction. This finding shows, unambiguously, that $α$/$α'$ promotes $\varepsilon$ formation in neighbouring grains. The minimum strain work criterion model for $\varepsilon$ variant prediction was also evaluated, which worked well for most grains. However, $\varepsilon$-forming grains with a lower stress were less well predicted by the model, indicating crystal-level behaviour must be considered for accurate $\varepsilon$ formation. The findings from this work are considered key for the future design of alloys where the deformation response can be controlled by tailoring microstructure and local or macroscopic crystal orientations.
△ Less
Submitted 7 November, 2023; v1 submitted 6 November, 2023;
originally announced November 2023.
-
Registration between DCT and EBSD datasets for multiphase microstructures
Authors:
James A. D. Ball,
Jette Oddershede,
Claire Davis,
Carl Slater,
Mohammed Said,
Himanshu Vashishtha,
Stefan Michalik,
David M. Collins
Abstract:
The ability to characterise the three-dimensional microstructure of multiphase materials is essential for understanding the interaction between phases and associated materials properties. Here, laboratory-based diffraction-contrast tomography (DCT), a recently-established materials characterization technique that can determine grain phases, morphologies, positions and orientations in a voxel-based…
▽ More
The ability to characterise the three-dimensional microstructure of multiphase materials is essential for understanding the interaction between phases and associated materials properties. Here, laboratory-based diffraction-contrast tomography (DCT), a recently-established materials characterization technique that can determine grain phases, morphologies, positions and orientations in a voxel-based reconstruction method, was used to map part of a dual-phase steel alloy sample. To assess the resulting microstructures that were produced by the DCT technique, an EBSD map was collected within the same sample volume. To identify the 2D slice of the 3D DCT reconstruction that best corresponded to the EBSD map, a novel registration technique based solely on grain-averaged orientations was developed -- this registration technique requires very little a priori knowledge of dataset alignment and can be extended to other techniques that only recover grain-averaged orientation data such as far-field 3D X-ray diffraction microscopy. Once the corresponding 2D slice was identified in the DCT dataset, comparisons of phase balance, grain size, shape and texture were performed between DCT and EBSD techniques. More complicated aspects of the microstructural morphology such as grain boundary shape and grains less than a critical size were poorly reproduced by the DCT reconstruction, primarily due to the difference in resolutions of the technique compared with EBSD. However, lab-based DCT is shown to accurately determine the centre-of-mass position, orientation, and size of the large grains for each phase present, austenite and martensitic ferrite. The results reveals a complex ferrite grain network of similar crystal orientations that are absent from the EBSD dataset. Such detail demonstrates that lab-based DCT, as a technique, shows great promise in the field of multi-phase material characterization.
△ Less
Submitted 29 June, 2023;
originally announced June 2023.
-
High Resolution 3D Strain and Orientation Map** within a Grain of a Directed Energy Deposition Laser Additively Manufactured Superalloy
Authors:
Y. Chen,
Y. T. Tang,
D. M. Collins,
S. J. Clark,
W. Ludwig,
R. Rodriguez-Lamas,
C. Detlefs,
R. C. Reed,
P. D. Lee,
P. J. Withers,
C. Yildirim
Abstract:
The industrialization of Laser Additive Manufacturing (LAM) is challenged by the undesirable microstructures and high residual stresses originating from the fast and complex solidification process. Non-destructive assessment of the mechanical performance controlling deformation patterning is therefore critical. Here, we use Dark Field X-ray Microscopy (DFXM) to non-destructively map the 3D intragr…
▽ More
The industrialization of Laser Additive Manufacturing (LAM) is challenged by the undesirable microstructures and high residual stresses originating from the fast and complex solidification process. Non-destructive assessment of the mechanical performance controlling deformation patterning is therefore critical. Here, we use Dark Field X-ray Microscopy (DFXM) to non-destructively map the 3D intragranular orientation and strain variations throughout a surface breaking grain within a directed energy deposition nickel superalloy. DFXM results reveal a highly heterogenous 3D microstructure in terms of the local orientation and lattice strain. The grain comprises $\approx$ 5$μ$m-sized cells with alternating strain states, as high as 5 $\times 10^{-3}$, and orientation differences <0.5° . The DFXM results are compared to Electron Backscatter Diffraction measurements of the same grain from its cut-off surface. We discuss the microstructure developments during LAM, rationalising the development of the deformation patterning from the extreme thermal gradients during processing and the susceptibility for solute segregation.
△ Less
Submitted 8 March, 2023;
originally announced March 2023.
-
Per-grain and neighbourhood stress interactions during deformation of a ferritic steel obtained using three-dimensional X-ray diffraction
Authors:
James A. D. Ball,
Anna Kareer,
Oxana V. Magdysyuk,
Stefan Michalik,
Thomas Connolley,
David M. Collins
Abstract:
Three-dimensional X-ray diffraction (3DXRD) has been used to measure, in-situ, the evolution of $\sim 1800$ grains in a single phase low carbon ferritic steel sample during uniaxial deformation. The distribution of initial residual grain stresses in the material was observed to prevail as plasticity builds, though became less pronounced, and therefore less influential as strain increased. The init…
▽ More
Three-dimensional X-ray diffraction (3DXRD) has been used to measure, in-situ, the evolution of $\sim 1800$ grains in a single phase low carbon ferritic steel sample during uniaxial deformation. The distribution of initial residual grain stresses in the material was observed to prevail as plasticity builds, though became less pronounced, and therefore less influential as strain increased. The initial Schmid factor of a grain was found to be strongly correlated to the intergranular stress change and the range of stresses that are permissible; a grain well aligned for easy slip is more likely to exhibit a range of stresses than those orientated poorly for dislocation motion. The orientation path of a grain, however, is not only dependent on its initial orientation, but hypothesised to be influenced by its stress state and the stress state of its grain environment. A grain neighbourhood effect is observed: the Schmid factor of serial adjoining grains influences the stress state of a grain of interest, whereas parallel neighbours are much less influential. This phenomenon is strongest at low plastic strains only, with the effect diminishing as plasticity builds. The influence of initial residual stresses becomes less evident, and grains rotate to eliminate any orientation dependent load shedding. The ability of the BCC ferrite to exhaust such neighbourhood interactions, which would otherwise be detrimental in crystal structures with lower symmetric and fewer slip systems, is considered key to the high ductility possessed by these materials.
△ Less
Submitted 21 February, 2023;
originally announced February 2023.
-
Macroscopic analysis of time dependent plasticity in Ti alloys
Authors:
Yi Xiong,
Phani S. Karamched,
Chi-Toan Nguyen,
David M. Collins,
Christopher M. Magazzeni,
Edmund Tarleton,
Angus J. Wilkinson
Abstract:
Component failure due to cold dwell fatigue of titanium and its alloys is a long-standing problem which has significant safety and economic implications to the aviation industry. This can be addressed by understanding the governing mechanisms of time dependent plasticity behaviour of Ti at low temperatures. Here, stress relaxation tests were performed at four different temperatures on three major…
▽ More
Component failure due to cold dwell fatigue of titanium and its alloys is a long-standing problem which has significant safety and economic implications to the aviation industry. This can be addressed by understanding the governing mechanisms of time dependent plasticity behaviour of Ti at low temperatures. Here, stress relaxation tests were performed at four different temperatures on three major alloy systems: commercially pure titanium (two alloys with different oxygen content), Ti-6Al-4V (two microstructures with differing beta phase fractions) and Ti-6Al-2Sn-4Zr-xMo (two alloys with different Mo content x= 2 or 6, and portion of beta phase). Key parameters controlling the time dependent plasticity were determined as a function of temperature. Both activation volume and energy were found to increase with temperature in all six alloys. It was found that the dwell fatigue effect is more significant by oxygen alloying but is suppressed by the addition of Mo. The presence of the beta phase did not strongly affect the dwell fatigue, however, it was suppressed at high temperature due to the low strain rate and strain rate sensitivity.
△ Less
Submitted 12 April, 2022;
originally announced April 2022.
-
Implementing and evaluating far-field 3D X-ray diffraction at the I12 JEEP beamline, Diamond Light Source
Authors:
James A. D. Ball,
Anna Kareer,
Oxana V. Magdysyuk,
Stefan Michalik,
Anastasia Vrettou,
Neal Parkes,
Thomas Connolley,
David M. Collins
Abstract:
Three-dimensional X-ray diffraction (3DXRD) is shown to be feasible at the I12 Joint Engineering, Environmental and Processing (JEEP) beamline of Diamond Light Source. As a demonstration, a microstructually simple low-carbon ferritic steel was studied in a highly textured and annealed state. A processing pipeline suited to this beamline was created, using software already established in the 3DXRD…
▽ More
Three-dimensional X-ray diffraction (3DXRD) is shown to be feasible at the I12 Joint Engineering, Environmental and Processing (JEEP) beamline of Diamond Light Source. As a demonstration, a microstructually simple low-carbon ferritic steel was studied in a highly textured and annealed state. A processing pipeline suited to this beamline was created, using software already established in the 3DXRD user community, enabling grain centre-of-mass positions, orientations and strain tensor elements to be determined. Orientations, with texture measurements independently validated from electron backscatter diffraction (EBSD) data, possessed a $\sim 0.1^\circ$ uncertainty, comparable with other 3DXRD instruments. The spatial resolution was limited by the far-field detector pixel size; the average of the grain centre of mass position errors was determined as $\pm \sim 80 μ$m. An average per-grain error of $\sim 1 \times 10^{-3}$ for the elastic strains was also measured; this could be reduced in future experiments by improving sample preparation, data collection and analysis techniques. Application of 3DXRD onto I12 shows great potential, where its implementation is highly desirable due the flexible, open architecture of the beamline. User-owned or designed sample environments can be used, thus 3DXRD could be applied to previously unexplored scientific areas.
△ Less
Submitted 20 February, 2023; v1 submitted 12 November, 2021;
originally announced November 2021.
-
Weighted ellipse fitting routine for spotty or incomplete Debye-Scherrer rings on a 2D detector
Authors:
Phani S. Karamched,
Yi Xiong,
Chi-Toan Nguyen,
David M. Collins,
Christopher M. Magazzeni,
Angus J. Wilkinson
Abstract:
We introduce a weighted ellipse fitting routine to measure Debye Scherrer rings acquired on 2D area detectors and demonstrate its use in strain determination. The method is relatively robust against incomplete rings due to low number of grains in the diffraction volume (spotty rings), or strong texture (intensity depletion in some azimuths). The method works by applying an annular mask around each…
▽ More
We introduce a weighted ellipse fitting routine to measure Debye Scherrer rings acquired on 2D area detectors and demonstrate its use in strain determination. The method is relatively robust against incomplete rings due to low number of grains in the diffraction volume (spotty rings), or strong texture (intensity depletion in some azimuths). The method works by applying an annular mask around each diffraction ring and fitting an ellipse, using all pixel positions and their diffracted intensity as weights in the minimisation. We compare this method to the more popular cake integration method, and show that the weighted ellipse method works when the cake integration method fails or works poorly. The lattice strain sensitivity from spotty diffraction rings is in the order or 2E-5 or better. The algorithm has been made available for public use and works with 2D diffraction patterns acquired in a laboratory scale XRD equipment, TEM or a synchrotron.
△ Less
Submitted 11 October, 2021;
originally announced October 2021.
-
An in-situ synchrotron diffraction study of stress relaxation in titanium: Effect of temperature and oxygen on cold dwell fatigue
Authors:
Yi Xiong,
Phani S. Karamched,
Chi-Toan Nguyen,
David M. Collins,
Nicolo Grilli,
Christopher M. Magazzeni,
Edmund Tarleton,
Angus J. Wilkinson
Abstract:
There is a long-standing technological problem in which a stress dwell during cyclic loading at room temperature in Ti causes a significant fatigue life reduction. It is thought that localised time dependent plasticity in soft grains favourably oriented for easy plastic slip leads to load shedding and an increase in stress within a neighbouring hard grain poorly oriented for easy slip. Quantifying…
▽ More
There is a long-standing technological problem in which a stress dwell during cyclic loading at room temperature in Ti causes a significant fatigue life reduction. It is thought that localised time dependent plasticity in soft grains favourably oriented for easy plastic slip leads to load shedding and an increase in stress within a neighbouring hard grain poorly oriented for easy slip. Quantifying this time dependent plasticity process is key to understand the complex cold dwell fatigue problem. Knowing the effect of operating temperature and oxygen content on cold dwell fatigue will be beneficial for future alloy design to address this problem. In this work, synchrotron X-ray diffraction during stress relaxation experiments was used to characterise the time dependent plastic behaviour of two commercially pure titanium samples (grade 1 and grade 4) with different oxygen content at 4 different temperatures (room temperature, 75C, 145C and 250C). Lattice strains were measured by tracking the diffraction peak shift from multiple crystallographic plane families (21 diffraction rings) as a function of their orientation with respect to the loading direction. Critical resolved shear stress, activation energy and activation volume were established for both prismatic and basal slip as a function of temperature and oxygen content by fitting a crystal plasticity finite element model to the lattice strain relaxation responses measured along the loading axis for five strong reflections. Higher strain rate sensitivity was found to lead to higher plasticity during cold dwell.
△ Less
Submitted 19 November, 2020;
originally announced November 2020.
-
Correlative Synchrotron X-ray Imaging and Diffraction of Directed Energy Deposition Additive Manufacturing
Authors:
Yunhui Chen,
Samuel J. Clark,
David M. Collins,
Sebastian Marussi,
Simon A. Hunt,
Danielle M. Fenech,
Thomas Connolley,
Robert C. Atwood,
Oxana V. Magdysyuk,
Gavin J. Baxter,
Martyn A. Jones,
Chu Lun Alex Leung,
Peter D. Lee
Abstract:
The governing mechanistic behaviour of Directed Energy Deposition Additive Manufacturing (DED-AM) is revealed by a combined in situ and operando synchrotron X-ray imaging and diffraction study of a nickel-base superalloy, IN718. Using a unique process replicator, real-space phase-contrast imaging enables quantification of the melt-pool boundary and flow dynamics during solidification. This imaging…
▽ More
The governing mechanistic behaviour of Directed Energy Deposition Additive Manufacturing (DED-AM) is revealed by a combined in situ and operando synchrotron X-ray imaging and diffraction study of a nickel-base superalloy, IN718. Using a unique process replicator, real-space phase-contrast imaging enables quantification of the melt-pool boundary and flow dynamics during solidification. This imaging knowledge informed precise diffraction measurements of temporally resolved microstructural phases during transformation and stress development with a spatial resolution of 100 $μ$m. The diffraction quantified thermal gradient enabled a dendritic solidification microstructure to be predicted and coupled to the stress orientation and magnitude. The fast cooling rate entirely suppressed the formation of secondary phases or recrystallisation in the solid-state. Upon solidification, the stresses rapidly increase to the yield strength during cooling. This insight, combined with IN718 $'$s large solidification range suggests that the accumulated plasticity exhausts the alloy$'$s ductility, causing liquation cracking. This study has revealed additional fundamental mechanisms governing the formation of highly non-equilibrium microstructures during DED-AM.
△ Less
Submitted 16 September, 2020;
originally announced September 2020.
-
Ultra high-temperature deformation in a single crystal superalloy: Meso-scale process simulation and micro-mechanisms
Authors:
Yuanbo T. Tang,
Neil D'Souza,
Bryan Roebuck,
Phani Karamched,
Chinnapat Panwisawas,
David M. Collins
Abstract:
A mesoscale study of a single crystal nickel-base superalloy subjected to an industrially relevant process simulation has revealed the complex interplay between microstructural development and the micromechanical behaviour. As sample gauge volumes were smaller than the length scale of the highly cored structure of the parent material from which they were produced, their subtle composition differen…
▽ More
A mesoscale study of a single crystal nickel-base superalloy subjected to an industrially relevant process simulation has revealed the complex interplay between microstructural development and the micromechanical behaviour. As sample gauge volumes were smaller than the length scale of the highly cored structure of the parent material from which they were produced, their subtle composition differences gave rise to differing work hardening rates, influenced by varying secondary dendrite arm spacings, gamma-prime phase solvus temperatures and a topologically inverted gamma/gamma-prime microstructure. The gamma-prime precipitates possessed a characteristic `X' morphology, resulting from the simultaneously active solute transport mechanisms of thermally favoured octodendritic growth and N-type rafting, indicating creep-type mechanisms were prevalent. High resolution-electron backscatter diffraction (HR-EBSD) characterisation reveals deformation patterning that follows the gamma/gamma-prime microstructure, with high geometrically necessary dislocation density fields localised to the gamma/gamma-prime interfaces; Orowan loo** is evidently the mechanism that mediated plasticity. Examination of the residual elastic stresses indicated the `X' gamma-prime precipitate morphology had significantly enhanced the deformation heterogeneity, resulting in stress states within the gamma channels that favour slip, and that encourage further growth of gamma-prime precipitate protrusions. The combination of such localised plasticity and residual stresses are considered to be critical in the formation of the recrystallisation defect in subsequent post-casting homogenisation heat treatments.
△ Less
Submitted 17 August, 2020;
originally announced August 2020.
-
Spinodal decomposition versus classical gamma-prime nucleation in a nickel-base superalloy powder: An in-situ neutron diffraction and atomic-scale analysis
Authors:
David M Collins,
Neil D'Souza,
Chinnapat Panwisawas,
Chrysanthi Papadaki,
Geoff D West,
Aleksander Kostka,
Paraskevas Kontis
Abstract:
Contemporary powder-based polycrystalline nickel-base superalloys inherit microstructures and properties that are heavily determined by the thermo-mechanical treatments during processing. Here, the influence of a thermal exposure alone to an alloy powder is studied to elucidate the controlling formation mechanisms of the strengthening precipitates using a combination of atom probe tomography and i…
▽ More
Contemporary powder-based polycrystalline nickel-base superalloys inherit microstructures and properties that are heavily determined by the thermo-mechanical treatments during processing. Here, the influence of a thermal exposure alone to an alloy powder is studied to elucidate the controlling formation mechanisms of the strengthening precipitates using a combination of atom probe tomography and in-situ neutron diffraction. The initial powder comprised a single-phase supersaturated gamma only; from this, the evolution of gamma-prime volume fraction and lattice misfit was assessed. The initial powder notably possessed elemental segregation of Cr and Co and elemental repulsion between Ni, Al and Ti with Cr; here proposed to be a precursor for subsequent gamma to gamma-prime phase transformations. Subsolvus heat treatments yielded a unimodal gamma-prime distribution, formed during heating, with evidence supporting its formation to be via spinodal decomposition. A supersolvus heat treatment led to the formation of this same gamma-prime population during heating, but dissolves as the temperature increases further. The gamma-prime then reprecipitates as a multimodal population during cooling, here forming by classical nucleation and growth. Atom probe characterisation provided intriguing precipitate characteristics, including clear differences in chemistry and microstructure, depending on whether the gamma-prime formed during heating or cooling.
△ Less
Submitted 17 October, 2020; v1 submitted 2 April, 2020;
originally announced April 2020.
-
Cold Creep of Titanium: Analysis of stress relaxation using synchrotron diffraction and crystal plasticity simulations
Authors:
Yi Xiong,
Phani Karamched,
Chi-Toan Nguyen,
David M Collins,
Christopher M Magazzeni,
Edmund Tarleton,
Angus J Wilkinson
Abstract:
There is a long standing technological problem in which a stress dwell during cyclic loading at room temperature in Ti causes a significant fatigue life reduction. It is thought that localised time dependent plasticity in soft grains oriented for easy plastic slip leads to load shedding and an increase in stress within a neighbouring hard grain poorly oriented for easy slip. Quantifying this time…
▽ More
There is a long standing technological problem in which a stress dwell during cyclic loading at room temperature in Ti causes a significant fatigue life reduction. It is thought that localised time dependent plasticity in soft grains oriented for easy plastic slip leads to load shedding and an increase in stress within a neighbouring hard grain poorly oriented for easy slip. Quantifying this time dependent plasticity process is key to successfully predicting the complex cold dwell fatigue problem. This work uses a novel approach of in situ synchrotron X-ray diffraction during stress relaxation tests, to quantify the time dependent plasticity. Measured lattice strains from multiple lattice families (21 diffraction rings) were compared with simulated lattice strains from crystal plasticity finite element (CPFE) simulations. The prism slip parameters were found to show stronger strain rate sensitivity compared to basal slip, and this has a significant effect on stress redistribution to hard grain orientations during cold creep.
△ Less
Submitted 24 August, 2020; v1 submitted 3 March, 2020;
originally announced March 2020.
-
Dislocation density distribution at slip band-grain boundary intersections
Authors:
Yi Guo,
David M. Collins,
Edmund Tarleton,
Felix Hofmann,
Angus J. Wilkinson,
T. Ben Britton
Abstract:
We study the mechanisms of slip transfer at a grain boundary, in titanium, using Differential Aperture X-ray Laue Micro-diffraction (DAXM). This 3D characterization tool enables measurement of the full (9-component) Nye lattice curvature tensor and calculation of the density of geometrically necessary dislocations (GNDs). We observe dislocation pile-ups at a grain boundary, as the neighbor grain p…
▽ More
We study the mechanisms of slip transfer at a grain boundary, in titanium, using Differential Aperture X-ray Laue Micro-diffraction (DAXM). This 3D characterization tool enables measurement of the full (9-component) Nye lattice curvature tensor and calculation of the density of geometrically necessary dislocations (GNDs). We observe dislocation pile-ups at a grain boundary, as the neighbor grain prohibits easy passage for dislocation transmission. This incompatibility results in local micro-plasticity within the slip** grain, near to where the slip planes intersect the grain boundary, and we observe bands of GNDs lying near the grain boundary. We observe that the distribution of GNDs can be significantly influenced by the formation of grain boundary ledges that serve as secondary dislocation sources. This observation highlights the non-continuum nature of polycrystal deformation and helps us understand the higher order complexity of grain boundary characteristics.
△ Less
Submitted 6 September, 2019; v1 submitted 2 September, 2019;
originally announced September 2019.
-
Warren-Averbach line broadening analysis from a time of flight neutron diffractometer
Authors:
David M. Collins,
Angus J. Wilkinson,
Richard I. Todd
Abstract:
The well known Warren-Averbach theory of diffraction line profile broadening is shown to be applicable to time of flight data obtained from a neutron spallation source. Without modification, the method is applied to two very different examples; a cold worked ferritic steel and a thermally stressed alumina-30% SiC composite. Values of root mean square strains averaged over a range of lengths for th…
▽ More
The well known Warren-Averbach theory of diffraction line profile broadening is shown to be applicable to time of flight data obtained from a neutron spallation source. Without modification, the method is applied to two very different examples; a cold worked ferritic steel and a thermally stressed alumina-30% SiC composite. Values of root mean square strains averaged over a range of lengths for the ferritic steel were used to estimate dislocation densities; values were found to be in good agreement with geometrically necessary dislocation densities independently measured from similarly orientated grains measured from electron backscatter diffraction analysis. An analytical model for the ceramic is described to validate the estimate of root mean square strain.
△ Less
Submitted 28 July, 2019;
originally announced July 2019.
-
Applications of Multivariate Statistical Methods and Simulation Libraries to Analysis of Electron Backscatter Diffraction and Transmission Kikuchi Diffraction Datasets
Authors:
Angus J Wilkinson,
David M Collins,
Yevhen Zayachuk,
Rajesh Korla,
Arantxa Vilalta-Clemente
Abstract:
Multivariate statistical methods are widely used throughout the sciences, including microscopy, however, their utilisation for analysis of electron backscatter diffraction (EBSD) data has not been adequately explored. The basic aim of most EBSD analysis is to segment the spatial domain to reveal and quantify the microstructure, and links this to knowledge of the crystallography (eg crystal phase,…
▽ More
Multivariate statistical methods are widely used throughout the sciences, including microscopy, however, their utilisation for analysis of electron backscatter diffraction (EBSD) data has not been adequately explored. The basic aim of most EBSD analysis is to segment the spatial domain to reveal and quantify the microstructure, and links this to knowledge of the crystallography (eg crystal phase, orientation) within each segmented region. Two analysis strategies have been explored; principal component analysis (PCA) and k-means clustering. The intensity at individual (binned) pixels on the detector were used as the variables defining the multidimensional space in which each pattern in the map generates a single discrete point. PCA analysis alone did not work well but rotating factors to the VARIMAX solution did. K-means clustering also successfully segmented the data but was computational more expensive. The characteristic patterns produced by either VARIMAX or k-means clustering enhance weak patterns, remove pattern overlap, and allow subtle effects from polarity to be distinguished. Combining multivariate statistical analysis (MSA) approaches with template matching to simulation libraries can significantly reduce computational demand as the number of patterns to be matched is drastically reduced. Both template matching and MSA approaches may augment existing analysis methods but will not replace them in the majority of applications.
△ Less
Submitted 16 September, 2018; v1 submitted 6 June, 2018;
originally announced June 2018.