Spatially controlled fabrication of single NV centers in IIa HPHT diamond
Authors:
S. D. Trofimov,
S. A. Tarelkin,
S. V. Bolshedvorskii,
V. S. Bormashov,
S. Yu. Troshchiev,
A. V. Golovanov,
N. V. Luparev,
D. D. Prikhodko,
K. N. Boldyrev,
S. A. Terentiev,
A. V. Akimov,
N. I. Kargin,
N. S. Kukin,
A. S. Gusev,
A. A. Shemukhin,
Yu. V. Balakshin,
S. G. Buga,
V. D. Blank
Abstract:
Single NV centers in HPHT IIa diamond are fabricated by helium implantation through lithographic masks. The concentrations of created NV centers in different growth sectors of HPHT are compared quantitatively. It is shown that the purest {001} growth sector (GS) of HPHT diamond allows to create groups of single NV centers in predetermined locations. The {001} GS HPHT diamond is thus considered a g…
▽ More
Single NV centers in HPHT IIa diamond are fabricated by helium implantation through lithographic masks. The concentrations of created NV centers in different growth sectors of HPHT are compared quantitatively. It is shown that the purest {001} growth sector (GS) of HPHT diamond allows to create groups of single NV centers in predetermined locations. The {001} GS HPHT diamond is thus considered a good material for applications that involve single NV centers.
△ Less
Submitted 4 December, 2019; v1 submitted 27 November, 2019;
originally announced November 2019.
-
Nanotwinning in boron subphosphide B12P2
Authors:
Boris A. Kulnitskiy,
Igor A. Perezhogin,
Vladimir D. Blank,
Vladimir A. Mukhanov,
Vladimir L. Solozhenko
Abstract:
Microstructure of boron subphosphide B12P2 produced by self-propagated high-temperature synthesis has been studied by high-resolution transmission electron microscopy. Two systems of twins have been found i.e. conventional twins on the (0003)h plane and nanotwins resulting from duplication of the rhombohedral unit cell of B12P2 along one of the basic vectors.
Microstructure of boron subphosphide B12P2 produced by self-propagated high-temperature synthesis has been studied by high-resolution transmission electron microscopy. Two systems of twins have been found i.e. conventional twins on the (0003)h plane and nanotwins resulting from duplication of the rhombohedral unit cell of B12P2 along one of the basic vectors.
△ Less
Submitted 6 February, 2019;
originally announced February 2019.
-
All-diamond optical assemblies for a beam-multiplexing X-ray monochromator at the Linac Coherent Light Source
Authors:
S. Stoupin,
S. A. Terentyev,
V. D. Blank,
Yu. V. Shvyd'ko,
K. Goetze,
L. Assoufid,
S. N. Polyakov,
M. S. Kuznetsov,
N. V. Kornilov,
J. Katsoudas,
R. Alonso-Mori,
M. Chollet,
Y. Feng,
J. M. Glownia,
H. Lemke,
A. Robert,
S. Song,
M. Sikorski,
D. Zhu
Abstract:
A double-crystal diamond (111) monochromator recently implemented at the Linac Coherent Light Source (LCLS) enables splitting of the primary X-ray beam into a pink (transmitted) and a monochromatic (reflected) branch. The first monochromator crystal with a thickness of 100 um provides sufficient X-ray transmittance to enable simultaneous operation of two beamlines. Here we report on the design, fa…
▽ More
A double-crystal diamond (111) monochromator recently implemented at the Linac Coherent Light Source (LCLS) enables splitting of the primary X-ray beam into a pink (transmitted) and a monochromatic (reflected) branch. The first monochromator crystal with a thickness of 100 um provides sufficient X-ray transmittance to enable simultaneous operation of two beamlines. Here we report on the design, fabrication, and X-ray characterization of the first and second (300-um-thick) crystals utilized in the monochromator and the optical assemblies holding these crystals. Each crystal plate has a region of about 5 X 2 mm2 with low defect concentration, sufficient for use in X-ray optics at the LCLS. The optical assemblies holding the crystals were designed to provide mounting on a rigid substrate and to minimize mounting-induced crystal strain. The induced strain was evaluated using double-crystal X-ray topography and was found to be small over the 5 X 2 mm2 working regions of the crystals.
△ Less
Submitted 23 January, 2014;
originally announced January 2014.
-
Bulk Nanocrystalline Thermoelectrics Based on Bi-Sb-Te Solid Solution
Authors:
L. P. Bulat.,
D. A. Pshenai-Severin,
V. V. Karatayev,
V. B. Osvenskii,
Yu. N. Parkhomenko,
V. Lavrentev,
A. Sorokin,
V. D. Blank,
G. I. Pivovarov,
V. T. Bublik,
N. Yu. Tabachkova
Abstract:
A nanopowder from p-Bi-Sb-Te with particles ~ 10 nm were fabricated by the ball milling using different technological modes. Cold and hot pressing at different conditions and also SPS process were used for consolidation of the powder into a bulk nanostructure and nanocomposites. The main factors allowing slowing-down of the growth of nanograins as a result of recrystallization are the reduction of…
▽ More
A nanopowder from p-Bi-Sb-Te with particles ~ 10 nm were fabricated by the ball milling using different technological modes. Cold and hot pressing at different conditions and also SPS process were used for consolidation of the powder into a bulk nanostructure and nanocomposites. The main factors allowing slowing-down of the growth of nanograins as a result of recrystallization are the reduction of the temperature and of the duration of the pressing, the increase of the pressure, as well as addition of small value additives (like MoS2, thermally expanded graphite or fullerenes). It was reached the thermoelectric figure of merit ZT=1.22 (at 360 K) in the bulk nanostructure Bi0,4Sb1,6Te3 fabricated by SPS method. Some mechanisms of the improvement of the thermoelectric efficiency in bulk nanocrystalline semiconductors based on BixSb2-xTe3 are studied theoretically. The reduction of nanograin size can lead to improvement of the thermoelectric figure of merit. The theoretical dependence of the electric and heat conductivities and the thermoelectric power as the function of nanograins size in BixSb2-xTe3 bulk nanostructure are quite accurately correlates with the experimental data.
△ Less
Submitted 14 March, 2012;
originally announced March 2012.
-
Behaviour of muonium in synthetic diamond
Authors:
T. N. Mamedov,
V. D. Blank,
V. N. Gorelkin,
K. I. Gritsaj,
M. S. Kuznetsov,
S. A. Nosukhin,
V. G. Ralchenko,
A. V. Stoykov,
R. Scheuermann,
S. A. Terentiev
Abstract:
The probabilities of finding the muon in various states in synthetic single crystal and polycrystalline diamond were studied. In the IIa-type single-crystal sample at 150 K the contributions of the diamagnetic muon, `normal', and `anomalous' muonium were observed to be 1.5 %, 57 % and 8.1 %, respectively. The missing fraction of muon polarization was 33.4 %, which is approximately two times smalle…
▽ More
The probabilities of finding the muon in various states in synthetic single crystal and polycrystalline diamond were studied. In the IIa-type single-crystal sample at 150 K the contributions of the diamagnetic muon, `normal', and `anomalous' muonium were observed to be 1.5 %, 57 % and 8.1 %, respectively. The missing fraction of muon polarization was 33.4 %, which is approximately two times smaller than in the Ia-type natural diamond, and two or three times greater than in the IIa- and IIb-type natural diamonds. The muon spin relaxation rates at the `normal' and `anomalous' muonium states in the synthetic and natural samples of IIa- and IIb-type are similar.
△ Less
Submitted 25 May, 2011; v1 submitted 21 May, 2010;
originally announced May 2010.