Do** of large amount tetravalent Ge ions into Fe2O3 structure and experimental results on modified structural, optical and electronic properties
Authors:
Divya Sherin G T,
R. N Bhowmik
Abstract:
We report the do** high concentration of tetravalent Ge4+ ions (5 mol % for x = 0.05 to 30 mol % for x = 0.30) at the Fe3+ sites of Fe2-xGexO3 system by chemical coprecipitation route. The charge state of Fe and Ge ions has been modified into lower values, in addition to their normal +3 and +4 states, to stabilize the rhombohedral phase of hematite (α-Fe2O3) structure. X-ray photoelectron spectr…
▽ More
We report the do** high concentration of tetravalent Ge4+ ions (5 mol % for x = 0.05 to 30 mol % for x = 0.30) at the Fe3+ sites of Fe2-xGexO3 system by chemical coprecipitation route. The charge state of Fe and Ge ions has been modified into lower values, in addition to their normal +3 and +4 states, to stabilize the rhombohedral phase of hematite (α-Fe2O3) structure. X-ray photoelectron spectra and optical band gap measurements indicated a combination of ionic and covalence character of metal-oxygen bonds as an effect of Ge do** in hematite structure. The Ge doped hematite samples have exhibited wide band gap semiconductor properties with band gap 4.50-4.70 eV and remarkably enhanced electrical conductivity (σ ~ 10-4 S/m) in comparison to α-Fe2O3 (10-11 S/m). The thermo-conductivity measurements using warming and cooling modes showed a highly irreversible feature in the semiconductor regime at higher temperatures. Some of the samples indicated metal-like state at lower temperature, in addition to semiconductor state. Our experimental results confirmed the strategy of enhancing electrical conductivity by do** tetravalent ions in hematite structure. It has been understood that combination of ionic and covalence character of the metal-oxygen bonds has played an important role in modifying the semiconductor properties in Ge doped Fe2O3 system.
△ Less
Submitted 7 September, 2023;
originally announced September 2023.
-
Bulk superconductivity and non-trivial band topology analysis of Pb2Pd
Authors:
M. M. Sharma,
N. K. Karn,
Poonam Rani,
R. N. Bhowmik,
V. P. S. Awana
Abstract:
A perfect topological superconductor can be realized by the simultaneous existence of bulk superconductivity along with topological non-trivial surface states. In this article, we report single crystal growth of superconducting binary compound Pb2Pd. The crystal is well characterized through X-Ray Diffraction (XRD), Selected Area electron diffraction (SAED), Transmission Electron Microscopy (TEM),…
▽ More
A perfect topological superconductor can be realized by the simultaneous existence of bulk superconductivity along with topological non-trivial surface states. In this article, we report single crystal growth of superconducting binary compound Pb2Pd. The crystal is well characterized through X-Ray Diffraction (XRD), Selected Area electron diffraction (SAED), Transmission Electron Microscopy (TEM), Field emission Scanning electron Microscopy (FESEM) and X-Ray Photoelectron spectroscopy (XPS). The bulk superconducting nature of the studied crystal is determined through AC susceptibility and magneto-heat capacity measurements. The specific heat jump at superconducting transition suggests Pb2Pd to be a moderately coupled s-wave superconductor. The topological non-trivial character of Pb2Pd is evidenced through bulk electronic band structure and Z2 invariants, which are calculated under the protocols of Density Functional Theory (DFT). This is the first report on topological invariant of Pb2Pd, showing Pb2Pd to possess non-trivial topological band structure
△ Less
Submitted 28 June, 2022; v1 submitted 14 December, 2021;
originally announced December 2021.
-
Probing low temperature non-equilibrium magnetic state in Co$_{2.75}$Fe$_{0.25}$O$_{4+δ}$ spinel oxide using dc magnetization, ac susceptibility and neutron diffraction experiments
Authors:
R. N. Bhowmik,
Amit Kumar,
A. K. Sinha,
S. M. Yusuf
Abstract:
The low temperature lattice structure and magnetic properties of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite have been investigated using experimental results from synchrotron x-ray diffraction (SXRD), dc magnetization, ac susceptibility, neutron diffraction and neutron depolarization techniques. The samples have been prepared by chemical co-precipitation of the Fe and Co nitrates solution in high alkalin…
▽ More
The low temperature lattice structure and magnetic properties of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite have been investigated using experimental results from synchrotron x-ray diffraction (SXRD), dc magnetization, ac susceptibility, neutron diffraction and neutron depolarization techniques. The samples have been prepared by chemical co-precipitation of the Fe and Co nitrates solution in high alkaline medium and subsequent thermal annealing of the precipitates in the temperature range of 200- 900 $^\circ$C. Rietveld refinement of the SXRD patterns at room temperature indicated two-phased cubic spinel structure for the samples annealed at temperatures 200-600 $^\circ$C. The samples annealed at temperatures 700 $^\circ$C and 900 $^\circ$C (CF90) have been best fitted with single phased lattice structure. Refinement of the neutron diffraction patterns in the temperature range of 5-300 K confirmed antiferromagnetic (AFM) Co$_3$O$_4$ and ferrimagnetic (FIM) Co$_{2.75}$Fe$_{0.25}$O$_4$ phases for the sample annealed at 600 $^\circ$C and single FIM phase of Co$_{2.75}$Fe$_{0.25}$O$_4$ for the CF90 sample. Magnetic measurements have shown a non-equilibrium magnetic structure, consisting of the high temperature FIM phase and low temperature AFM phase. The magnetic phases are sensitive to magnetic fields, where high temperature phase is suppressed at higher magnetic fields by enhancing the low temperature AFM phase, irrespective of annealing temperature of the samples.
△ Less
Submitted 8 July, 2020;
originally announced July 2020.
-
Tuning of structural phase, magnetic spin order and electrical conductivity in mechanical alloyed material of alpha-Fe2O3 and alpha-Cr2O3 oxides
Authors:
R. N. Bhowmik,
K. Venkata Siva,
V. R. Reddy,
A. K. Sinha
Abstract:
Alpha-Fe2O3 and alpha-Cr2O3 has been mechanical alloyed to prepare Fe1-xCrxO3 oxides for x = 0.2-0.8. Synchrotron X-ray diffraction and Raman spectra have shown inhomogeneous structure of α-Fe2O3 and α-Cr2O3 phases in as-alloyed samples. The as-alloyed samples have shown soft ferromagnetic properties with signature of two Morin transitions. The heat treatment of as-alloyed samples has homogenized…
▽ More
Alpha-Fe2O3 and alpha-Cr2O3 has been mechanical alloyed to prepare Fe1-xCrxO3 oxides for x = 0.2-0.8. Synchrotron X-ray diffraction and Raman spectra have shown inhomogeneous structure of α-Fe2O3 and α-Cr2O3 phases in as-alloyed samples. The as-alloyed samples have shown soft ferromagnetic properties with signature of two Morin transitions. The heat treatment of as-alloyed samples has homogenized structure and successfully incorporated the Cr atoms into the lattice sites of Fe atoms in α-Fe2O3. The magnetic and electrical properties have been modified in the heat treated samples. For example, canted antiferromagnetic order has been appeared as an effect of heat treatment, irrespective of the Cr content in Fe1-xCrxO3. The magnetic field induced spin flop transition has been observed at a critical magnetic field that depends on Cr content in the system. The Mössbauer spectrum at room temperature has been fitted with two sextets. The variation of Mössbauer parameters suggest a distribution of magnetic spin order between Fe and Cr ions in the rhombohedral structure of Fe1-xCrxO3. The electrical conductivity, derived from current-voltage characteristics of the heat treated samples, has been enhanced by increasing Cr content in alpha-Fe2O3 structure. The experimental results have been explained based on the theoretical models available in literature.
△ Less
Submitted 8 January, 2020;
originally announced January 2020.
-
High temperature thermal cycling effect on the irreversible responses of lattice structure, magnetic properties and electrical conductivity in Co$_{2.75}$Fe$_{0.25}$O$_{4+δ}$ spinel oxide
Authors:
R. N. Bhowmik,
P. D. Babu,
A. K. Sinhac,
Abhay Bhisikar
Abstract:
We report high temperature synchrotron X-ray diffraction (SXRD), dc magnetization and current-voltage (I-V) characteristics for the samples of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite. The material was prepared by chemical reaction of the Fe and Co nitrate solutions at pH = 11 and subsequent annealing at temperatures 200 0C, 500 0C and 900 0C. The measurements were performed by cycling the temperature…
▽ More
We report high temperature synchrotron X-ray diffraction (SXRD), dc magnetization and current-voltage (I-V) characteristics for the samples of Co$_{2.75}$Fe$_{0.25}$O$_4$ ferrite. The material was prepared by chemical reaction of the Fe and Co nitrate solutions at pH = 11 and subsequent annealing at temperatures 200 0C, 500 0C and 900 0C. The measurements were performed by cycling the temperature from 300 K to high temperature (warming mode) and return back to 300 K (cooling mode). The SXRD patterns indicated a fine bi-phased cubic spinel structure in the highly Co rich spinel oxide. Magnetization curves showed intrinsic ferrimagnetic features and defect induced additional ferromagnetic phase at higher temperatures. Electrical conductivity showed thermal hysteresis loop between warming and cooling modes of temperature variation. The samples exhibited new information on the irreversibility phenomena of lattice structure, magnetization and electrical conductivity on cycling the measurement temperatures.
△ Less
Submitted 15 April, 2020; v1 submitted 8 January, 2020;
originally announced January 2020.
-
Non-equilibrium spin dynamics in the temperature and magnetic field dependence of magnetization curves of ferrimagnetic Co$_{1.75}$Fe$_{1.25}$O$_4$ and its composite with BaTiO$_3$
Authors:
R. N. Bhowmik,
R. Ranganathan
Abstract:
A comparative study of the non-equilibrium magnetic phenomena (magnetic blocking, memory, exchange bias and aging effect) has been presented for ferrimagnetic Co$_{1.75}$Fe$_{1.25}$O$_4$ (CFO) and its composite with non-magnetic BaTiO$_3$ (BTO). Synchrotron X-Ray diffraction patterns have confirmed coexistence of CFO and BTO structures in composite, but magnetic spin dynamics have been remarkably…
▽ More
A comparative study of the non-equilibrium magnetic phenomena (magnetic blocking, memory, exchange bias and aging effect) has been presented for ferrimagnetic Co$_{1.75}$Fe$_{1.25}$O$_4$ (CFO) and its composite with non-magnetic BaTiO$_3$ (BTO). Synchrotron X-Ray diffraction patterns have confirmed coexistence of CFO and BTO structures in composite, but magnetic spin dynamics have been remarkably modified. The blocking phenomenon of ferrimagnetic domains below the room temperature has been studied by different modes of (zero field cooled and field cooled) magnetic measurements in collaboration with magnetic fields ON and OFF modes and time dependent magnetization. The applications of unconventional protocols during time dependent magnetization measurement at different stages of the temperature and field dependence of the magnetization curves have been useful to reveal the non-equilibrium dynamics of magnetic spin order. The applying of off-field relaxation experiments has made possible to tune the magnetic state and coercivity of the systems. The role of interfacial coupling between magnetic and non-magnetic particles has been understood on different magnetic phenomena (meta-stable magnetic state, exchange bias and memory effect) by comparing the experimental results of Co$_{1.75}$Fe$_{1.25}$O$_4$ spinel oxide and its composite with BaTiO$_3$ particles.
△ Less
Submitted 7 July, 2020; v1 submitted 8 January, 2020;
originally announced January 2020.
-
Physical properties of RIr3 (R = Gd, Tb, Ho) compounds with coexisting polymorphic phases
Authors:
Binita Mondal,
Shovan Dan,
Sudipta Mondal,
R. N. Bhowmik,
R. Ranganathan,
Chandan Mazumdar
Abstract:
The binary compounds GdIr3, TbIr3 and HoIr3 are synthesized successfully and found to form in macroscopic co-existence of two polymorphic phases: C15b and AuCu3-type. The dc magnetization and heat capacity studies confirm that C15b phase orders ferromagnetically, whereas the AuCu3 phase remains paramagnetic down to 2 K. The frequency dependent ac-susceptibility data, time dependent magnetic relaxa…
▽ More
The binary compounds GdIr3, TbIr3 and HoIr3 are synthesized successfully and found to form in macroscopic co-existence of two polymorphic phases: C15b and AuCu3-type. The dc magnetization and heat capacity studies confirm that C15b phase orders ferromagnetically, whereas the AuCu3 phase remains paramagnetic down to 2 K. The frequency dependent ac-susceptibility data, time dependent magnetic relaxation behavior and magnetic memory effect studies suggest that TbIr3 and HoIr3 are cannonical spin-glass system, but no glassy feature could be found in GdIr3. The critical behavior of all the three compounds has been investigated from the magnetization and heat capacity measurements around the transition temperature (TC). The critical exponents alpha, beta, gamma and delta have been estimated using different techniques such as Arrott-Noaks plot, Kouvel-Fisher plot, critical isotherm as well as analysis of specific heat data and study of magnetocaloric effect. The critical analysis study identifies the type of universal magnetic class in which the three compounds belong.
△ Less
Submitted 9 April, 2019;
originally announced April 2019.
-
Low temperature ferromagnetic properties, magnetic field induced spin order and random spin freezing effect in Ni1.5Fe1.5O4 ferrite; prepared at different pH values and annealing temperatures
Authors:
R. N. Bhowmik,
K. S. Aneeshkumar
Abstract:
We present the low temperature magnetic properties in Ni1.5Fe1.5O4 ferrite as the function of pH at which the material was prepared by chemical route and post annealing temperature. The material is a ferri or ferromagnet, but showed magnetic blocking and random spin freezing process on lowering the measurement temperature down to 5 K. The sample prepared at pH =12 and annealed at 800 ^C showed a s…
▽ More
We present the low temperature magnetic properties in Ni1.5Fe1.5O4 ferrite as the function of pH at which the material was prepared by chemical route and post annealing temperature. The material is a ferri or ferromagnet, but showed magnetic blocking and random spin freezing process on lowering the measurement temperature down to 5 K. The sample prepared at pH =12 and annealed at 800 ^C showed a sharp magnetization peak at 105 K, the superparamagnetic blocking temperature of the particles. The magnetization peak remained incomplete within measurement temperature up to 350 K for rest of the samples, although peak temperature was brought down by increasing applied dc field. The fitting of temperature dependence of coercivity data according to Kneller law suggested random orientation of ferromagnetic particles. The fitting of saturation magnetization according to Bloch law provided the exponent that largely deviated from 1.5, a typical value for long ranged ferromagnet. An abrupt increase of saturation magnetization below 50 K suggested the active role of frozen surface spins in low temperature magnetic properties. AC susceptibility data elucidated the low temperature spin freezing dynamics and exhibited the characters of cluster spin glass in the samples depending on pH value and annealing temperature.
△ Less
Submitted 17 December, 2017;
originally announced December 2017.
-
Non-equilibrium character of resistive switching and negative differential resistance in Ga-doped Cr2O3 system
Authors:
R. N. Bhowmik,
K. Venkata Siva
Abstract:
We have synthesized Ga-doped Cr2O3 system with compositions Cr1.45Ga0.55O3 and Cr1.17Ga0.83O3 by chemical co-precipitation route and post annealing at 800^C. The samples have been stabilized in rhombohedral crystal structure with space group R3C. The present work focuses on the study of non-linear current-voltage (I-V) characteristics of the samples, which exhibited many interesting electronic pro…
▽ More
We have synthesized Ga-doped Cr2O3 system with compositions Cr1.45Ga0.55O3 and Cr1.17Ga0.83O3 by chemical co-precipitation route and post annealing at 800^C. The samples have been stabilized in rhombohedral crystal structure with space group R3C. The present work focuses on the study of non-linear current-voltage (I-V) characteristics of the samples, which exhibited many interesting electronic properties, e.g., I-V loop, resistive switching, bi-stable electronic states, and negative differential resistance. The non-equilibrium character of the I-V characteristics has been studied by measurement of bias voltage cycling up to 20 times and current relaxation with time at set bias voltage. The charge conduction process in the samples has been understood by analysing I-V curves using different phenomenological models based on electrode-limited and bulk-limited charge conduction mechanisms proposed for metal electrode-metal oxide-metal electrode (M-MO-M) junctions. It is understood that competitions between injection of charge carriers from metal electrode to metal oxide, charge flow through the material (trap**/de-trap** and recombination of charge carriers at the defect sites), space charge formation at the junctions of electrodes and metal oxides, and ejection of electrons from metal oxide to metal electrode control the non-equilibrium I-V characteristics in the present samples.
△ Less
Submitted 2 November, 2017;
originally announced November 2017.
-
Electric field controlled magnetic exchange bias and magnetic state switching at room temperature in Ga doped α-Fe2O3 oxide
Authors:
R. N. Bhowmik,
Abdul Gaffar Lone
Abstract:
We have developed a new magnetoelectric material based on Ga doped α-Fe2O3 in rhombohedral phase. The material is a canted ferromagnet at room temperature and showing magneto-electric properties. The experimental results of electric field controlled magnetic state provided a direct evidence of room temperature magnetoelectric coupling in Ga doped α-Fe2O3 system. Interestingly, (un-doped) α-Fe2O3 s…
▽ More
We have developed a new magnetoelectric material based on Ga doped α-Fe2O3 in rhombohedral phase. The material is a canted ferromagnet at room temperature and showing magneto-electric properties. The experimental results of electric field controlled magnetic state provided a direct evidence of room temperature magnetoelectric coupling in Ga doped α-Fe2O3 system. Interestingly, (un-doped) α-Fe2O3 system does not exhibit any electric field controlled magnetic exchange bias shift, but Ga doped α-Fe2O3 system has shown an extremely high electric field induced magnetic exchange bias shift up to the value of 1120 Oe (positive). On the other hand, in a first time, we report the electric field controlled magnetic state switching both in α-Fe2O3 and in Ga doped α-Fe2O3 systems. The switching of magnetic state is highly sensitive to ON and OFF modes, as well as to the change of polarity of applied electric voltage during in-field magnetic relaxation experiments. The switching of magnetic state to upper level for positive electric field and to down level for negative electric field indicates that electric and magnetic orders are coupled in the Ga doped hematite system. Such material is of increasing demand in today for multifunctional applications in next generation magnetic sensor, switching, non-volatile memory and spintronic devices.
△ Less
Submitted 13 July, 2017;
originally announced July 2017.
-
Effect of annealing temperatures on the electrical conductivity and dielectric properties of Ni1.5Fe1.5O4 spinel ferrite prepared by chemical reaction at different pH values
Authors:
K. S. Aneesh Kumar,
R. N. Bhowmik
Abstract:
The electrical conductivity and dielectric properties of Ni1.5Fe1.5O4 ferrite has been controlled by varying the annealing temperature of the chemical routed samples. The frequency activated conductivity obeyed Jonschers power law and universal scaling suggested semiconductor nature. An unusual metal like state has been revealed in the measurement temperature scale in between two semiconductor sta…
▽ More
The electrical conductivity and dielectric properties of Ni1.5Fe1.5O4 ferrite has been controlled by varying the annealing temperature of the chemical routed samples. The frequency activated conductivity obeyed Jonschers power law and universal scaling suggested semiconductor nature. An unusual metal like state has been revealed in the measurement temperature scale in between two semiconductor states with different activation energy. The metal like state has been affected by thermal annealing of the material. The analysis of electrical impedance and modulus spectra has confirmed non-Debye dielectric relaxation with contributions from grains and grain boundaries. The dielectric relaxation process is thermally activated in terms of measurement temperature and annealing temperature of the samples. The hole hop** process, due to presence of Ni3+ ions in the present Ni rich ferrite, played a significant role in determining the thermal activated conduction mechanism. This work has successfully applied the technique of a combined variation of annealing temperature and pH value during chemical reaction for tuning electrical parameters in a wide range; for example dc limit of conductivity 10power(-4) -10power(-12) S/cm, and unusually high activation energy 0.17-1.36 eV.
△ Less
Submitted 24 November, 2017; v1 submitted 8 April, 2017;
originally announced April 2017.
-
Evidence of room temperature magnetoelectric properties in α-Fe1.6Ga0.4O3 oxide by magnetic field controlled electric properties and electric field controlled magnetism
Authors:
R. N. Bhowmik,
Abdul Gaffar Lone
Abstract:
We have stabilized the α-Fe1.6Ga0.4O3 (Ga doped α-Fe2O3) system in rhombohedral structure. The system has shown magnetically canted ferromagnetic state and ferroelectric properties at room temperature. In first time, we confirm the existence of magneto-electric coupling and multiferro-electric properties at room temperature in the Ga doped α-Fe2O3 system based on the experimental observation of ma…
▽ More
We have stabilized the α-Fe1.6Ga0.4O3 (Ga doped α-Fe2O3) system in rhombohedral structure. The system has shown magnetically canted ferromagnetic state and ferroelectric properties at room temperature. In first time, we confirm the existence of magneto-electric coupling and multiferro-electric properties at room temperature in the Ga doped α-Fe2O3 system based on the experimental observation of magnetic field controlled electric polarization and electric field controlled magnetization. The α-Fe2O3 system does not exhibit electric field controlled magnetic exchange bias effect, where as Ga doped α-Fe2O3 showed exchange bias shift up to the value of 370 Oe. We have recorded the response of current-voltage characteristics and in-field magnetic relaxation of the system under the simultaneous application of magnetic and electric fields. The magnetization of the system is found highly sensitive to the ON and OFF modes, as well as change of the polarity of external electric field. The system is a new addition in the list of non-traditional magneto-electrics/multi-ferroelectrics so far reported in literature. Such novel materials, where magnetization and electric polarization can be controlled by simultaneous application of magnetic and electric fields, is in the increasing demand for potential applications in the field of next generation magnetic sensor, switching, non-volatile memory and spintronic devices.
△ Less
Submitted 19 December, 2016;
originally announced December 2016.
-
Do** of Ga in antiferromagnetic semiconductor alpha-Cr2O3oxide and its effects on modified magnetic and electronic properties
Authors:
R. N. Bhowmik,
K. Venkata Siva,
R. Ranganathan,
Chandan Mazumdar
Abstract:
The samples of Ga doped Cr2O3 oxide have been prepared using chemical co-precipitation route. X-ray diffraction pattern and Raman spectra have confirmed rhombohedral crystal structure with space group R3-C. Magnetic measurement has indicated the dilution of antiferromagnetic (AFM) spin order in Ga doped alpha-Cr2O3 system oxide, where the AFM transition temperature of bulk alpha-Cr2O3 oxide at abo…
▽ More
The samples of Ga doped Cr2O3 oxide have been prepared using chemical co-precipitation route. X-ray diffraction pattern and Raman spectra have confirmed rhombohedral crystal structure with space group R3-C. Magnetic measurement has indicated the dilution of antiferromagnetic (AFM) spin order in Ga doped alpha-Cr2O3 system oxide, where the AFM transition temperature of bulk alpha-Cr2O3 oxide at about 320 K has been suppressed and ferrimagnetic behavior is observed from the analysis of the temperature dependence of magnetization data below 350 K. Apart from Ga do** effect, the spin freezing (50 K-70 K) and superparamagnetic behavior of the surface spins at lower temperatures, typically below 50 K, have been exhibited due to nano-sized grains of the samples. All the samples showed non-linear current-voltage (I-V) characteristics. However, I-V characteristics of the Ga doped samples are remarkably different from alpha-Cr2O3 sample. The I-V curves of Ga doped samples have exhibited many unique electronic properties, e.g., bi-stable (low resistance- LR and high resistance-HR) electronic states and negative differential resistance (NDR). Optical absorption spectra revealed three electronic transitions in the samples associated with band gap energy at about 2.67-2.81 eV, 1.91-2.11 eV, 1.28-1.35 eV, respectively.
△ Less
Submitted 26 October, 2016;
originally announced October 2016.
-
Observation of plastoferrite character and semiconductor to metal transition in soft ferromagnetic Li0.5Mn0.5Fe2O4ferrite
Authors:
R. N. Bhowmik
Abstract:
We prepared Li0.5Mn0.5Fe2O4 ferrite through chemical reaction in highly acidic solution and subsequent sintering of chemical routed powder at temperatures > 800 0C. Surface morphology showed plastoferrite character for sintering temperature > 1000 0C. Mechanical softening of metal-oxygen bonds at higher measurement temperatures stimulated delocalization of charge carriers, which were strongly loca…
▽ More
We prepared Li0.5Mn0.5Fe2O4 ferrite through chemical reaction in highly acidic solution and subsequent sintering of chemical routed powder at temperatures > 800 0C. Surface morphology showed plastoferrite character for sintering temperature > 1000 0C. Mechanical softening of metal-oxygen bonds at higher measurement temperatures stimulated delocalization of charge carriers, which were strongly localized in A and B sites of the spinel structure at lower temperatures. The charge delocalization process has activated semiconductor to metallic transition in ac conductivity curves, obeyed by Jonscher power law and Drude equation, respectively. Metallic state is also confirmed by the frequency dependence of dielectric constant curves.
△ Less
Submitted 18 September, 2013;
originally announced September 2013.
-
Low temperature ferromagnetism, surface paramagnetism and exchange bias effect in nano-grained alpha-Fe1.4Ga0.6O3 oxide
Authors:
R. N. Bhowmik,
N. Naresh,
B. Ghosh,
S. Banerjee
Abstract:
The compound alpha-Fe1.4Ga0.6O3 has been prepared by mechanical alloying of alpha-Fe2O3 and Ga2O3 and subsequent heating of the mechanical alloyed samples in vacuum condition. Magnetic ordering of alpha-Fe2O3 has been modified by substitution of non-magnetic Ga atoms. The ferromagnetism in alpha-Fe1.4Ga0.6O3 is more soft and enhanced in comparison to alpha-Fe2O3. Mössbauer spectroscopy also confir…
▽ More
The compound alpha-Fe1.4Ga0.6O3 has been prepared by mechanical alloying of alpha-Fe2O3 and Ga2O3 and subsequent heating of the mechanical alloyed samples in vacuum condition. Magnetic ordering of alpha-Fe2O3 has been modified by substitution of non-magnetic Ga atoms. The ferromagnetism in alpha-Fe1.4Ga0.6O3 is more soft and enhanced in comparison to alpha-Fe2O3. Mössbauer spectroscopy also confirmed enhanced ferromagnetic order in alpha-Fe1.4Ga0.6O3. The room temperature soft ferromagnetism by Ga substitution is interesting for designing alpha-Fe2O3 based unconventional ferromagnet, which is a great challenge to the materials scientists. The alpha-Fe1.4Ga0.6O3 samples also exhibited features of exchange bias, low temperature surface paramagnetism, and suppression of Morin transition. These features have been affected up to certain extent by the nano-sized grains of the samples.
△ Less
Submitted 24 April, 2013;
originally announced April 2013.
-
Room temperature ferromagnetism and giant permittivity in chemical routed Co1.5Fe1.5O4 ferrite particles and their composite with NaNO3
Authors:
R. N. Bhowmik,
P. Lokeswara Rao,
J. Udaya Bhanu
Abstract:
We report structural, magnetic and dielectric properties of Co1.5Fe1.5O4 nanoparticles and their composites with non-magnetic NaNO3. The samples were derived from metal nitrates solution at different pH values. The chemical routed sample was air heated at 200 0C and 500 0C. Heating of the material showed unusual decrease of crystallite size, but cubic spinel structure is seen in all samples. The s…
▽ More
We report structural, magnetic and dielectric properties of Co1.5Fe1.5O4 nanoparticles and their composites with non-magnetic NaNO3. The samples were derived from metal nitrates solution at different pH values. The chemical routed sample was air heated at 200 0C and 500 0C. Heating of the material showed unusual decrease of crystallite size, but cubic spinel structure is seen in all samples. The samples of Co1.5Fe1.5O4 showed substantially large room temperature ferromagnetic moment, electrical conductivity, dielectric constant, and low dielectric loss. The samples are soft ferromagnet and electrically highly polarized. The interfaces of grains and grain boundaries are actively participating to determine the magnetic and dielectric properties of the ferrite grains. The effects of interfacial contribution are better realized using the ferrite and NaNO3 composite samples. We have examined different scopes of modifying the magnetic and dielectric parameters using same material in pure and composite form.
△ Less
Submitted 10 March, 2012;
originally announced March 2012.
-
Ferromagnetism in lead graphite-pencils and magnetic composite with CoFe2O4 particles
Authors:
R. N. Bhowmik
Abstract:
This work has been initiated with a curiosity to investigate the elemental composition and magnetic response of different grades of lead pencils (6B, 2B, HB, 2H, 5H) that people use in daily life. Interestingly, experimental results landed with a great achievement of observing soft magnetism in lead pencils, indicating a wide scope of magnetic tuning for room temperature applications. A novel magn…
▽ More
This work has been initiated with a curiosity to investigate the elemental composition and magnetic response of different grades of lead pencils (6B, 2B, HB, 2H, 5H) that people use in daily life. Interestingly, experimental results landed with a great achievement of observing soft magnetism in lead pencils, indicating a wide scope of magnetic tuning for room temperature applications. A novel magnetic composite has been synthesized by mixing different concentration of CoFe2O4 (CF) nanoparticles in 5H and 6B pencils for studying the magnetic tailoring aspects using pencils. Our results showed different possibilities of controlling disorder induced ferromagnetic parameters and a simple approach of producing sufficiently high coercive magnetic composite using pencils.
△ Less
Submitted 8 July, 2011;
originally announced July 2011.
-
Synthesis and study of alpha-Fe1.4Ga0.6O3: An advanced Ferromagnetic Semiconductor
Authors:
N. Naresh,
R. N. Bhowmik
Abstract:
We report the synthesis of alpha-Fe1.4Ga0.6O3 compound and present its structural phase stability and interesting magnetic, dielectric and photo-absorption properties. In our work Ga doped alpha-Fe2O3 samples are well stabilized in alpha phase (rhombohedral crystal structure with space group R3C). Properties of the present composition of Ga doped alpha-Fe2O3 system are remarkably advanced in compa…
▽ More
We report the synthesis of alpha-Fe1.4Ga0.6O3 compound and present its structural phase stability and interesting magnetic, dielectric and photo-absorption properties. In our work Ga doped alpha-Fe2O3 samples are well stabilized in alpha phase (rhombohedral crystal structure with space group R3C). Properties of the present composition of Ga doped alpha-Fe2O3 system are remarkably advanced in comparison with recently most studied FeGaO3 composition. At room temperature the samples are typical soft ferromagnet, as well as direct band gap semiconductor. Dielectric study showed low dielectric loss in the samples with large enhancement of ac conductivity at higher frequencies. Optical absorption in the visible range has been enhanced by 4 to 5%. This composition has exhibited large scope of tailoring room temperature ferromagnetic moment and optical band gap by varying grain size and non-ambient (vacuum) heat treatment of the as prepared samples by mechanical alloying.
△ Less
Submitted 11 April, 2011;
originally announced April 2011.
-
Evidence of Ferrimagnetism in Ferromagnetic La0_{67}Ca0_{33}MnO_3 nanoparticle
Authors:
R. N. Bhowmik
Abstract:
The present report is dedicated to show that ferromagnetic La0.67Ca0.33MnO3 (LCMN) particles can be better described in the framework of ferrimagnetic model. To confirm the ferrimagnetic signature in ferromagnetic LCMN particles, the temperature dependence of the inverse of magnetic susceptibility in the paramagnetic state of the samples was taken as a tool of data analysis. The observed ferrima…
▽ More
The present report is dedicated to show that ferromagnetic La0.67Ca0.33MnO3 (LCMN) particles can be better described in the framework of ferrimagnetic model. To confirm the ferrimagnetic signature in ferromagnetic LCMN particles, the temperature dependence of the inverse of magnetic susceptibility in the paramagnetic state of the samples was taken as a tool of data analysis. The observed ferrimagnetism is understood as an effect of of the core-shell spin structure in LCMN particles.
△ Less
Submitted 25 February, 2010; v1 submitted 24 February, 2010;
originally announced February 2010.
-
Reproducibility of room temperature ferromagnetism in Zn0.95Mn0.05O and its understanding
Authors:
R. N. Bhowmik,
Asok Poddar,
A. Saravanan
Abstract:
The present work reproduces the room temperature ferromagnetism by do** magnetic Mn atoms in diamagnetic ZnO. The ferromagnetic ordering is extended up to 640 K in mechanical milled Zn0.95Mn0.05O samples. The bulk and nanocrystalline samples are stabilized in hexagonal crystal structure with space group p63mc. The grain size and lattice strain of the samples, estimated from XRD spectrum using…
▽ More
The present work reproduces the room temperature ferromagnetism by do** magnetic Mn atoms in diamagnetic ZnO. The ferromagnetic ordering is extended up to 640 K in mechanical milled Zn0.95Mn0.05O samples. The bulk and nanocrystalline samples are stabilized in hexagonal crystal structure with space group p63mc. The grain size and lattice strain of the samples, estimated from XRD spectrum using Williamson-Hall plot, showed a significant variation with milling time. Surface structure (morphology, distribution of grains and elements) is observed to be reasonably good from SEM picture and EDX spectrum at room temperature. The ferromagnetic ordering in bulk, milled and alloyed samples is primarily due to the diffusion of Mn(2+) ions into the lattice sites of ZnO. The enhancement of magnetic moment and ferromagnetic ordering temperature with reducing the grain size is discussed in terms of the existing theoretical predictions and experimental works. The role of mechanical milling induced disorder for the enhancement of room temperature ferromagnetism in Zn0.95Mn0.05O (dilute magnetic semiconductor) is also highlighted.
△ Less
Submitted 10 March, 2009;
originally announced March 2009.
-
Disorder Effects in La substituted ferrimagnetic Ca2FeMoO6 double perovskite
Authors:
I. Panneer Muthuselvam,
Asok Poddar,
R. N. Bhowmik
Abstract:
Ca2-xLaxFeMoO6 double perovskite with La concentration x = 0 to 0.6 was synthesized using solid state sintering route. The standard techniques of XRD, SEM and EDX were applied to characterize the material. Crystal structure of the samples was stabilized in monoclinic phase with space group P2I/n and lattice expansion was indicated with the increase of x. The increase of La concentration graduall…
▽ More
Ca2-xLaxFeMoO6 double perovskite with La concentration x = 0 to 0.6 was synthesized using solid state sintering route. The standard techniques of XRD, SEM and EDX were applied to characterize the material. Crystal structure of the samples was stabilized in monoclinic phase with space group P2I/n and lattice expansion was indicated with the increase of x. The increase of La concentration gradually suppressed the coexisting minor secondary phase in the material and simultaneously, EDX results indicated the accommodation of more Mo atoms in the crystal structure. A significant modification in the surface morphology of the material was noted from adhesive type surface for x = 0 to brittle type surface with more grain boundary contributions for La doped samples. We understand a significant change in magnetic properties (appearance of cluster glass component, reduction of magnetic moment and indication of higher TC) and in electrical properties (reduction of metallic character) in terms of enhanced internal disorder in the material, introduced due to La do** in double perovskite structure.
△ Less
Submitted 15 November, 2008; v1 submitted 12 November, 2008;
originally announced November 2008.
-
Magnetic Response of NiFe2O4 nanoparticles in polymer matrix
Authors:
A. Poddar,
R. N. Bhowmik,
Amitabha De,
Pintu Sen
Abstract:
We report the magnetic properties of magnetic nano-composite, consisting of different quantity of NiFe2O4 nanoparticles in polymer matrix. The nanoparticles exhibited a typical magnetization blocking, which is sensitive on the variation of magnetic field, mode of zero field cooled/field cooled experiments and particle quantity in the matrix. The samples with lower particle quantity showed an upt…
▽ More
We report the magnetic properties of magnetic nano-composite, consisting of different quantity of NiFe2O4 nanoparticles in polymer matrix. The nanoparticles exhibited a typical magnetization blocking, which is sensitive on the variation of magnetic field, mode of zero field cooled/field cooled experiments and particle quantity in the matrix. The samples with lower particle quantity showed an upturn of magnetization down to 5 K, whereas the blocking of magnetization dominates at lower temperatures as the particle quantity increases in the polymer. We examine such magnetic behaviour in terms of the competitive magnetic ordering between core and surface spins of nanoparticles, taking into account the effect of inter-particle (dipole-dipole) interactions on nanoparticle magnetic dynamics.
△ Less
Submitted 12 November, 2008;
originally announced November 2008.
-
Structural phase stability and Magnetism in Co2FeO4 spinel oxide
Authors:
I. Panneer Muthuselvam,
R. N. Bhowmik
Abstract:
We report a correlation between structural phase stability and magnetic properties of Co2FeO4 spinel oxide. We employed mechanical alloying and subsequent annealing to obtain the desired samples. The particle size of the samples changes from 25 nm to 45 nm. The structural phase separation of samples, except sample annealed at 9000C, into Co rich and Fe rich spinel phase has been examined from XR…
▽ More
We report a correlation between structural phase stability and magnetic properties of Co2FeO4 spinel oxide. We employed mechanical alloying and subsequent annealing to obtain the desired samples. The particle size of the samples changes from 25 nm to 45 nm. The structural phase separation of samples, except sample annealed at 9000C, into Co rich and Fe rich spinel phase has been examined from XRD spectrum, SEM picture, along with EDAX spectrum, and magnetic measurements. The present study indicated the ferrimagnetic character of Co2FeO4, irrespective of structural phase stability. The observation of mixed ferrimagnetic phases, associated with two Curie temperatures at TC1 and TC2 (>TC1), respectively, provides the additional support of the splitting of single cubic spinel phase in Co2FeO4 spinel oxide.
△ Less
Submitted 2 October, 2008;
originally announced October 2008.
-
Magnetic Modulation in Mechanical Alloyed Cr1.4fe0.6o3 Oxide
Authors:
R. N. Bhowmik,
Nrisimha Murty. M,
Sekhar Srinadhu. E
Abstract:
We have synthesized Cr1.4Fe0.6O3 compound through mechanical alloying of Cr2O3 and Fe2O3 powders and subsequent thermal annealing. The XRD spectrum, SEM picture and microanalysis of EDAX spectrum have been used to understand the structural evolution in the alloyed compound. The alloyed samples are matching to rhombohedral structure with R3C space group. The observation of a modulated magnetic or…
▽ More
We have synthesized Cr1.4Fe0.6O3 compound through mechanical alloying of Cr2O3 and Fe2O3 powders and subsequent thermal annealing. The XRD spectrum, SEM picture and microanalysis of EDAX spectrum have been used to understand the structural evolution in the alloyed compound. The alloyed samples are matching to rhombohedral structure with R3C space group. The observation of a modulated magnetic order confirmed a systematic diffusion of Fe atoms into the Cr sites of lattice structure. A field induced magnetic behaviour is seen in the field dependence of magnetization data of the annealed samples. The behaviour is significantly different from the mechanical alloyed samples. The experimental results provided the indications of considering the present material as a potential candidate for opto-electronic applications.
△ Less
Submitted 2 October, 2008;
originally announced October 2008.
-
Lattice disorder and Ferromagnetism in La0.67Ca0.33MnO3 nanoparticle
Authors:
R. N. Bhowmik,
Asok Poddar,
R. Ranganathan,
Chandan Majumdar
Abstract:
We study the ferromagnetism of La0.67Ca0.33MnO3 in bulk polycrystalline, nanocrystalline and amorphous phase. The structural change from crystalline phase to amorphous phase exhibited a systematic decrease of TC(paramagnetic to ferromagnetic transition temperature) and spontaneous magnetization (MS). The experimental results suggested few more features, e.g., appearance of large magnetic irrever…
▽ More
We study the ferromagnetism of La0.67Ca0.33MnO3 in bulk polycrystalline, nanocrystalline and amorphous phase. The structural change from crystalline phase to amorphous phase exhibited a systematic decrease of TC(paramagnetic to ferromagnetic transition temperature) and spontaneous magnetization (MS). The experimental results suggested few more features, e.g., appearance of large magnetic irreversibility in the temperature dependence of magnetization, lack of magnetic saturation at high magnetic field, blocking of magnetization below TB, and enhancement of coercivity. In addition, the magnetic phase transition near to TC has changed from first order character in bulk sample to second order character in nanocrystalline and amorphous samples. We understand the observed magnetic features as the effects of decreasing particle size and increasing magnetic (spin- lattice) disorder. We noted that magnetic dynamics of amorphous samples is distinctly different from the nanocrystalline samples. The ferromagnetism of amorphous samples are comparable with the properties of reported amorphous ferromagnetic nanoparticles. We also demonstrate the effect of disorder shell in controlling the dynamics of ferromagnetic cores.
△ Less
Submitted 1 October, 2008;
originally announced October 2008.
-
Unconventional relaxation in antiferromagnetic CoRh$_2$O$_4$ nanoparticles
Authors:
R. N. Bhowmik,
R. Ranganathan
Abstract:
Magnetic relaxation in antiferromagnetic CoRh$_2$O$_4$ nanoparticles is investigated at 2 K by cooling the sample from a temperature (70 K) well above the antiferromagnetic ordering temperature at 27 K, following zero field cooled (ZFC) and field cooled (FC) process. In ZFC process, the sample at 2 K is subsequently followed by magnetic field on and off sequences, whereas in FC process the cooli…
▽ More
Magnetic relaxation in antiferromagnetic CoRh$_2$O$_4$ nanoparticles is investigated at 2 K by cooling the sample from a temperature (70 K) well above the antiferromagnetic ordering temperature at 27 K, following zero field cooled (ZFC) and field cooled (FC) process. In ZFC process, the sample at 2 K is subsequently followed by magnetic field on and off sequences, whereas in FC process the cooling field is made off during measurement of remanent magnetization as a function of time. The experiments suggest an unconventional relaxation behaviour in the system, as an effect of increasing surface exchange anisotropy with decreasing the size of antiferromagnetic nanoparticles.
△ Less
Submitted 16 October, 2006;
originally announced October 2006.
-
Lattice expansion and non-collinear to collinear ferrimagnetic order in MnCr$_2$O$_4$ nanoparticle
Authors:
R. N. Bhowmik,
R. Ranganathan,
R. Nagarajan
Abstract:
We report magnetic behaviour of MnCr$_2$O$_4$, which belongs to a special class of spinel, known as chromite. Bulk MnCr$_2$O$_4$ shows a sequence of magnetic states, which follows paramagnetic (PM) to collinear ferrimagnetic (FM) state below T$_C$ $\sim$ 45 K and collinear FM state to non-collinear FM state below T$_S$ $\sim$ 18 K. The non-collinear spin structure has been modified on decreasing…
▽ More
We report magnetic behaviour of MnCr$_2$O$_4$, which belongs to a special class of spinel, known as chromite. Bulk MnCr$_2$O$_4$ shows a sequence of magnetic states, which follows paramagnetic (PM) to collinear ferrimagnetic (FM) state below T$_C$ $\sim$ 45 K and collinear FM state to non-collinear FM state below T$_S$ $\sim$ 18 K. The non-collinear spin structure has been modified on decreasing the particle size, and magnetic transition at T$_S$ decreases in nanoparticle samples. However, ferrimagnetic order is still dominating in nanoparticles, except the observation of superparamagnetic like blocking and decrease of spontaneous magnetization for nanoparticle. This may, according to the core-shell model of ferrimagnetic nanoparticle, be the surface disorder effect of nanoparticle. The system also show the increase of T$_C$ in nanoparticle samples, which is not consistent with the core-shell model. The analysis of the M(T) data, applying spin wave theory, has shown an unusual Bloch exponent value 3.35 for bulk MnCr$_2$O$_4$, which decreases and approaches to 1.5, a typical value for any standard ferromagnet, with decreasing the particle size. MnCr$_2$O$_4$ has shown a few more unusual behaviour. For example, lattice expansion in nanoparticle samples. The present work demonstrates the correlation between a systematic increase of lattice parameter and the gradual decrease of B site non-collinear spin structure in the light of magnetism of MnCr$_2$O$_4$ nanoparticles.
△ Less
Submitted 30 October, 2005;
originally announced October 2005.
-
Static magnetic response of clusters in Co_{0.2}Zn_{0.8}Fe_{1.95}Ho_{0.05}O_{4} spinel oxide
Authors:
R. N. Bhowmik,
R. Ranganathan,
R. Nagarajan
Abstract:
Earlier investigation of Co_{0.2}Zn_{0.8}Fe_{1.95}Ho_{0.05}O_{4} spinel has shown the existence of "super-ferromagnetic " clusters containing Fe^{3+} and Ho^{3+} ions along with small size clusters of Fe^{3+} ions (Bhowmik et al, J. Magn. Magn. Mater. {247}, 83 (2002)). Here, We report the static magnetic response of these clusters. The experimental data suggests some interesting magnetic featur…
▽ More
Earlier investigation of Co_{0.2}Zn_{0.8}Fe_{1.95}Ho_{0.05}O_{4} spinel has shown the existence of "super-ferromagnetic " clusters containing Fe^{3+} and Ho^{3+} ions along with small size clusters of Fe^{3+} ions (Bhowmik et al, J. Magn. Magn. Mater. {247}, 83 (2002)). Here, We report the static magnetic response of these clusters. The experimental data suggests some interesting magnetic features, such as, enhancement of magnetization; re-entrant magnetic transitions with paramagnetic to ferromagnetic state below 225 K and ferromagnetic to spin glass state below 120 K; appearance of field induced ferromagnetism. We also observe an unusual maximum in the thermoremanent magnetization (TRM) vs temperature data. Our measurements suggest that this unusuality in TRM is related to the blocking of "super-ferromagnetic" clusters ,out of the ferromagnetic state, along their local anisotropy axis.
△ Less
Submitted 25 June, 2003;
originally announced June 2003.
-
Particle size effects in the antiferromagnetic spinel CoRh$_2$O$_4$
Authors:
R. N. Bhowmik,
R. Nagarajan,
R. Ranganathan
Abstract:
We report the particle size dependent magnetic behaviour in the antiferromagnetic spinel CoRh2O4. The nanoparticles were obtained by mechanical milling of bulk material, prepared under sintering method. The XRD spectra show that the samples are retaining the spinel structure. The particle size decreases from 70 nm to 16 nm as the milling time increases from 12 hours to 60 hours. The magnetic mea…
▽ More
We report the particle size dependent magnetic behaviour in the antiferromagnetic spinel CoRh2O4. The nanoparticles were obtained by mechanical milling of bulk material, prepared under sintering method. The XRD spectra show that the samples are retaining the spinel structure. The particle size decreases from 70 nm to 16 nm as the milling time increases from 12 hours to 60 hours. The magnetic measurements suggest that the antiferromagnetic ordering at T$_N$ $\approx$ 27K exists in bulk as well as in nanoparticle samples. However, the magnitude of the magnetization below T$_N$ increases with decreasing particle size.
△ Less
Submitted 30 October, 2002;
originally announced October 2002.
-
Re-entrant spin glass and magnetoresistance in Co_{0.2}Zn_{0.8}Fe_{1.6}Ti_{0.4}O_4 spinel oxide
Authors:
R. N. Bhowmik,
R. Ranganathan
Abstract:
We have investigated the static and dynamic response of magnetic clusters in Co_{0.2}Zn_{0.8}Fe_{1.6}Ti_{0.4}O_4 spinel oxide, where a sequence of magnetic phase transitions, i.e., paramagnetic (PM) to ferromagnetic at T_{C} $\leq$ 270K and ferromagnetic to canted spin glass state at T_f$ $\leq$ 125K is observed.
We have investigated the static and dynamic response of magnetic clusters in Co_{0.2}Zn_{0.8}Fe_{1.6}Ti_{0.4}O_4 spinel oxide, where a sequence of magnetic phase transitions, i.e., paramagnetic (PM) to ferromagnetic at T_{C} $\leq$ 270K and ferromagnetic to canted spin glass state at T_f$ $\leq$ 125K is observed.
△ Less
Submitted 21 August, 2002;
originally announced August 2002.
-
Magnetic enhancement of Co$_{0.2}$Zn$_{0.8}$Fe$_2$O$_4$ spinel oxide by mechanical milling
Authors:
R. N. Bhowmik,
R. Ranganathan,
S. sarkar,
C. Bansal,
R. Nagarajan
Abstract:
We report the magnetic properties of mechanically milled Co$_{0.2}$Zn$_{0.8}$Fe$_2$O$_4$ spinel oxide. After 24 hours milling of the bulk sample, the XRD spectra show nanostructure with average particle size $\approx$ 20 nm. The as milled sample shows an enhancement in magnetization and ordering temperature compared to the bulk sample. If the as milled sample is annealed at different temperature…
▽ More
We report the magnetic properties of mechanically milled Co$_{0.2}$Zn$_{0.8}$Fe$_2$O$_4$ spinel oxide. After 24 hours milling of the bulk sample, the XRD spectra show nanostructure with average particle size $\approx$ 20 nm. The as milled sample shows an enhancement in magnetization and ordering temperature compared to the bulk sample. If the as milled sample is annealed at different temperatures for the same duration, recrystallization process occurs and approaches to the bulk structure on increasing the annealing temperatures. The magnetization of the annealed samples first increases and then decreases. At higher annealing temperature ($\sim$ 1000$^{0}$C) the system shows two coexisting magnetic phases {\it i.e.}, spin glass state and ferrimagnetic state, similar to the as prepared bulk sample. The room temperature Mössbauer spectra of the as milled sample, annealed at 300$^{0}$C for different durations (upto 575 hours), suggest that the observed change in magnetic behaviour is strongly related with cations redistribution between tetrahedral (A) and octahedral (O) sites in the spinel structure. Apart from the cation redistribution, we suggest that the enhancement of magnetization and ordering temperature is related with the reduction of B site spin canting and increase of strain induced anisotropic energy during mechanical milling.
△ Less
Submitted 3 July, 2002;
originally announced July 2002.