Pressure Induced Changes in the Antiferromagnetic Superconductor YbPd2Sn
Authors:
A-M. Cumberlidge,
P. L. Alireza,
A. F. Kusmartseva,
E. E. Pearson,
G. G. Lonzarich,
N. R. Bernhoeft,
B. Roessli
Abstract:
Low temperature ac magnetic susceptibility measurements of the coexistent antiferromagnetic superconductor YbPd2Sn have been made in hydrostatic pressures < 74 kbar in moissanite anvil cells. The superconducting transition temperature is forced to T(SC) = 0 K at a pressure of 58 kbar. The initial suppression of the superconducting transition temperature is corroborated by lower hydrostatic press…
▽ More
Low temperature ac magnetic susceptibility measurements of the coexistent antiferromagnetic superconductor YbPd2Sn have been made in hydrostatic pressures < 74 kbar in moissanite anvil cells. The superconducting transition temperature is forced to T(SC) = 0 K at a pressure of 58 kbar. The initial suppression of the superconducting transition temperature is corroborated by lower hydrostatic pressure (p < 16 kbar) four point resisitivity measurements, made in a piston cylinder pressure cell. At ambient pressure, in a modest magnetic field of ~ 500 G, this compound displays reentrant superconducting behaviour. This reentrant superconductivity is suppressed to lower temperature and lower magnetic field as pressure is increased. The antiferromagnetic ordering temperature, which was measured at T(N) = 0.12 K at ambient pressure is enhanced, to reach T(N) = 0.58 K at p = 74 kbar. The reasons for the coexistence of superconductivity and antiferromagnetism is discussed in the light of these and previous findings. Also considered is why superconductivity on the border of long range magnetic order is so much rarer in Yb compounds than in Ce compounds. The presence of a new transition visible by ac magnetic susceptibility under pressure and in magnetic fields greater than 1.5 kG is suggested.
△ Less
Submitted 17 May, 2006;
originally announced May 2006.
Superconductivity induced by spark erosion in ZrZn2
Authors:
E. A. Yelland,
S. M. Hayden,
S. J. C. Yates,
C. Pfleiderer,
M. Uhlarz,
R. Vollmer,
H. v. Lohneysen,
N. R. Bernhoeft,
R. P. Smith,
S. S. Saxena,
N. Kimura
Abstract:
We show that the superconductivity observed recently in the weak itinerant ferromagnet ZrZn2 [C. Pfleiderer et al., Nature (London) 412, 58 (2001)] is due to remnants of a superconducting layer induced by spark erosion. Results of resistivity, susceptibility, specific heat and surface analysis measurements on high-quality ZrZn2 crystals show that cutting by spark erosion leaves a superconducting…
▽ More
We show that the superconductivity observed recently in the weak itinerant ferromagnet ZrZn2 [C. Pfleiderer et al., Nature (London) 412, 58 (2001)] is due to remnants of a superconducting layer induced by spark erosion. Results of resistivity, susceptibility, specific heat and surface analysis measurements on high-quality ZrZn2 crystals show that cutting by spark erosion leaves a superconducting surface layer. The resistive superconducting transition is destroyed by chemically etching a layer of 5 microns from the sample. No signature of superconductivity is observed in rho(T) of etched samples at the lowest current density measured, J=675 Am-2, and at T < 45 mK. EDX analysis shows that spark-eroded surfaces are strongly Zn depleted. The simplest explanation of our results is that the superconductivity results from an alloy with higher Zr content than ZrZn2.
△ Less
Submitted 8 January, 2006; v1 submitted 14 February, 2005;
originally announced February 2005.