Analysis of a kink pair model applied to a peierls mechanism in basal and prism plane slips in sapphire deformed between 200C and 1800C
Authors:
Miguel Castillo Rodríguez,
Jacques Castaing,
Antonio Muñoz Bernabé,
Patrick Veyssière,
Arturo Domínguez Rodríguez
Abstract:
A model based on dislocation glide controlled by the nucleation and propagation of kink pairs in a high Peierls stress crystal is revisited and modified to account for changes in dislocation densities and segment lengths with temperature and stress. It is applied to the critical resolved shear stress (CRSS) for basal and prism plane slip in sapphire (alpha-Al2O3). According to agreed-upon knowledg…
▽ More
A model based on dislocation glide controlled by the nucleation and propagation of kink pairs in a high Peierls stress crystal is revisited and modified to account for changes in dislocation densities and segment lengths with temperature and stress. It is applied to the critical resolved shear stress (CRSS) for basal and prism plane slip in sapphire (alpha-Al2O3). According to agreed-upon knowledge on dislocations in sapphire, basal slip and prism plane slip are modelled with undissociated and dissociated dislocations, respectively. In the latter case, partial dislocations move independently. Amongst a number of sets of fitting parameters, good fits between experimental and modelled CRSS9s are obtained in the long segment limit over the whole range of temperatures by making use of physically sound parameters, including a stress dependence of the dislocation density.
△ Less
Submitted 4 February, 2024;
originally announced February 2024.
-
Microstructure and high temperature mechanical properties of liquid-phase-sintered $α$-SiC with Y$_2$O$_3$-Al$_2$O$_3$ additions
Authors:
Miguel Castillo Rodríguez,
Antonio Muñoz Bernabé,
Arturo Domínguez Rodríguez
Abstract:
Samples of $α$-SiC have been sintered with liquid phase (LPS) to 1950 $^\circ$C, in atmosphere of argon and processing times between 1 and 7 hours. Using scanning electron microscopy (SEM) the microstructure of the samples has been characterized, being obtained average grain size that grows with the processing time from 0.64 to 1.61 $μ$m. These samples have been deformed in compression under const…
▽ More
Samples of $α$-SiC have been sintered with liquid phase (LPS) to 1950 $^\circ$C, in atmosphere of argon and processing times between 1 and 7 hours. Using scanning electron microscopy (SEM) the microstructure of the samples has been characterized, being obtained average grain size that grows with the processing time from 0.64 to 1.61 $μ$m. These samples have been deformed in compression under constant load, to temperatures between 1450 and 1625 C, stresses between 25 and 450 MPa and strain rate between $4.2\times 10^{-8}$ and $1.5\times 10^{-6}$ s$^{-1}$. The creep parameters have been determined, obtaining for n values between 2.4 0.1 and 4.5 0.2 and Q=680 35 kJ.mol$^{-1}$ in samples sintered during 1 hour and n between 1.2 0.1 and 2.4 0.1 and Q=710 90 kJ.mol$^{-1}$ for samples sintered during 7 hours. These results have been correlated with the microstructure, being the grain boundary sliding (GBS) accommodated by lattice diffusion and the movement of dislocations the possible deformation mechanisms, operating both in a simultaneous way.
△ Less
Submitted 4 February, 2024;
originally announced February 2024.
-
Chromium hardening and Peierls mechanism for basal slip in sapphire at temperatures between 900 and 1500 $^\circ$C
Authors:
Miguel Castillo Rodríguez,
Antonio Muñoz Bernabé,
Jacques Castaing,
Patrick Veyssière,
Arturo Domínguez Rodríguez
Abstract:
The plastic deformation of Cr3+ -doped a-Al2 O3 (ruby) with four distinct Cr concentrations has been studied at temperatures between 900 and 1500 $^\circ$C. The mechanical tests indicate that the processes of dislocation multiplication and the adjustments of the slip velocity of these dislocations to the imposed strain rate in undoped a-Al2 O3 are not significantly affected by the Cr concentra%on.…
▽ More
The plastic deformation of Cr3+ -doped a-Al2 O3 (ruby) with four distinct Cr concentrations has been studied at temperatures between 900 and 1500 $^\circ$C. The mechanical tests indicate that the processes of dislocation multiplication and the adjustments of the slip velocity of these dislocations to the imposed strain rate in undoped a-Al2 O3 are not significantly affected by the Cr concentra%on. The yield stress increment is approximately constant with temperature and the hardening increases with the Cr concentration. The critical resolved shear stress (CRSS) is fixed to a model based on dislocation glide controlled by the nucleation and propagation of kink pairs, modified to include the hardening due to Cr. Satisfactory fits are achieved with adjustable parameters close to those employed for undoped a-Al2 O3 .
△ Less
Submitted 4 February, 2024;
originally announced February 2024.
-
Effect of atmosphere and sintering time on the microstructure and mechanical properties at high temperatures of $α$-SiC sintered with liquid phase Y$_2$O$_3$ and Al$_2$O$_3$
Authors:
Miguel Castillo Rodriguez,
Antonio Munoz Bernabe,
Arturo Dominguez Rodriguez
Abstract:
The influence that the atmosphere (N_2 or Ar) and sintering time have on microstructure evolution in liquid-phase-sintered alpha-sic and on its mechanical properties at high temperature was investigated. The microstructure of the samples sintered in N2 was equiaxed with a grain size of 0.70 μm and a density of 98% of the theoretical value regardless of the sintering time. In contrast, samples sint…
▽ More
The influence that the atmosphere (N_2 or Ar) and sintering time have on microstructure evolution in liquid-phase-sintered alpha-sic and on its mechanical properties at high temperature was investigated. The microstructure of the samples sintered in N2 was equiaxed with a grain size of 0.70 μm and a density of 98% of the theoretical value regardless of the sintering time. In contrast, samples sintered in Ar had an elongated-grain microstructure with a density decreasing from 99% to 95% and a grain size increasing from 0.64 to 1.61 μm as the sintering time increased from 1 to 7 hours. The mechanical behaviour at 1450 °C showed the samples sintered in nitrogen to be brittle and fail at very low strains, with a fracture stress increasing from 400 to 800 MPa as the sintering time increased. In contrast, the samples sintered in Ar were quasi-ductile with increasing strain to failure as the sintering time increased, and a fracture stress strongly linked to the form and size of the grains. These differences in the mechanical properties of the two materials are discussed in the text. During mechanical tests, a loss of intergranular phase takes place in a region, between 50 and 150 μm thick, close to the surface of the samples--the effect being more important in the samples sintered in Ar
△ Less
Submitted 4 February, 2024;
originally announced February 2024.