Crystalline phases in Zr9Ni11 and Hf9Ni11 intermetallics; Investigations by perturbed angular correlation spectroscopy and ab initio calculations
Authors:
S. K. Dey,
C. C. Dey,
S. Saha,
G. Bhattacharjee,
J. Belošević-Čavor,
D. Toprek
Abstract:
Crystalline phases formed in stoichiometric Zr$_9$Ni$_{11}$ and Hf$_9$Ni$_{11}$ have been studied by perturbed angular correlation (PAC) spectroscopy, XRD and TEM/SAED measurements. In Zr$_9$Ni$_{11}$, the phases Zr$_9$Ni$_{11}$ ($\sim$89\%) and Zr$_8$Ni$_{21}$ ($\sim$11\%) have been found at room temperature from PAC measurements. At 773 K, Zr$_9$Ni$_{11}$ partially decomposes to Zr$_7$Ni$_{10}$…
▽ More
Crystalline phases formed in stoichiometric Zr$_9$Ni$_{11}$ and Hf$_9$Ni$_{11}$ have been studied by perturbed angular correlation (PAC) spectroscopy, XRD and TEM/SAED measurements. In Zr$_9$Ni$_{11}$, the phases Zr$_9$Ni$_{11}$ ($\sim$89\%) and Zr$_8$Ni$_{21}$ ($\sim$11\%) have been found at room temperature from PAC measurements. At 773 K, Zr$_9$Ni$_{11}$ partially decomposes to Zr$_7$Ni$_{10}$ and at 973 K, it is completely decomposed to ZrNi and Zr$_7$Ni$_{10}$. In Hf$_9$Ni$_{11}$, a predominant phase ($\sim$81\%) due to HfNi is found at room temperature while the phase Hf$_9$Ni$_{11}$ is produced as a minor phase ($\sim$19\%). No compositional phase change at higher temperature is found in Hf$_9$Ni$_{11}$. Phase components found from XRD and TEM/SAED measurements are similar to those observed from PAC measurements. Electric field gradients in Zr$_9$Ni$_{11}$ and Hf$_9$Ni$_{11}$ have been calculated by density functional theory (DFT) using all electron full potential (linearized) augmented plane wave plus local orbitals [FP-(L)APW+lo] method in order to assign the phase components.
△ Less
Submitted 26 October, 2018; v1 submitted 12 December, 2017;
originally announced December 2017.
-
Identification of phase components in Zr-Ni and Hf-Ni intermetallic compounds; Investigations by perturbed angular correlation spectroscopy and first principles calculations
Authors:
S. K. Dey,
C. C. Dey,
S. Saha,
J. Belosevic-Cavor,
D. Toprek
Abstract:
Time-differential perturbed angular correlation (TDPAC) measurements have been carried out in stoichiometric ZrNi$_3$ and HfNi$_3$ intermetallic compounds using $^{181}$Ta probe in the temperature range 77-1073 K considering the immense technological applications of Zr-Ni and Hf-Ni intermetallic compounds. In ZrNi$_3$, four components due to the production of Zr$_2$Ni$_7$, Zr$_8$Ni$_{21}$, Zr$_7$N…
▽ More
Time-differential perturbed angular correlation (TDPAC) measurements have been carried out in stoichiometric ZrNi$_3$ and HfNi$_3$ intermetallic compounds using $^{181}$Ta probe in the temperature range 77-1073 K considering the immense technological applications of Zr-Ni and Hf-Ni intermetallic compounds. In ZrNi$_3$, four components due to the production of Zr$_2$Ni$_7$, Zr$_8$Ni$_{21}$, Zr$_7$Ni$_{10}$ and ZrNi$_3$ have been found at room temperature. The HfNi$_3$ sample produces five electric quadrupole interaction frequencies at room temperature. The phase HfNi$_3$ is strongly produced in stoichiometric sample of HfNi$_3$ where two non-equivalent Hf sites are found to be present. Besides this phase, two other phases due to Hf$_2$Ni$_7$ and Hf$_8$Ni$_{21}$ have been found but, we do not observe any phase due to Hf$_7$Ni$_{10}$. X-ray diffraction, TEM/energy dispersive X-ray spectroscopy (EDX) and TEM-selected area electron diffraction (SAED) measurements were used to further characterize the investigated materials and it was found that these results agree with the TDPAC results. In order to confirm findings from TDPAC measurements, density functional theory (DFT) based calculations of electric field gradients (EFG) and asymmetry parameters at the sites of $^{181}$Ta probe nucleus were performed. Our calculated results are found to be in excellent agreement with the experimental results.
△ Less
Submitted 20 September, 2018; v1 submitted 29 March, 2017;
originally announced March 2017.
-
Electric field gradients in Zr$_8$Ni$_{21}$ and Hf$_8$Ni$_{21}$ intermetallic compounds; Results from perturbed angular correlation measurements and first-principles density functional theory
Authors:
S. K. Dey,
C. C. Dey,
S. Saha,
J. Belošević-Čavor
Abstract:
Numerous technological applications of Ni-based Zr and Hf intermetallic alloys promoted comprehensive studies in Zr$_8$Ni$_{21}$ and Hf$_8$Ni$_{21}$ by perturbed angular correlation (PAC) spectroscopy, which were not studied earlier until this report. The different phases produced in the samples have been identified by PAC and X-ray diffraction (XRD) measurements. Using $^{181}$Hf probe, two non-e…
▽ More
Numerous technological applications of Ni-based Zr and Hf intermetallic alloys promoted comprehensive studies in Zr$_8$Ni$_{21}$ and Hf$_8$Ni$_{21}$ by perturbed angular correlation (PAC) spectroscopy, which were not studied earlier until this report. The different phases produced in the samples have been identified by PAC and X-ray diffraction (XRD) measurements. Using $^{181}$Hf probe, two non-equivalent Zr/Hf sites have been observed in both Zr$_8$Ni$_{21}$ and Hf$_8$Ni$_{21}$ compounds. From present PAC measurements in Zr$_8$Ni$_{21}$, a component due to the production of Zr$_7$Ni$_{10}$ by eutectic reaction from the liquid metals is also observed. The phase Zr$_7$Ni$_{10}$, however, is not found from the XRD measurement. In Zr$_8$Ni$_{21}$, while the results do not change appreciably up to 973 K exhibit drastic changes at 1073 K. In Hf$_8$Ni$_{21}$, similar results for the two non-equivalent sites have been found but site fractions are in reverse order. In this alloy, a different contaminating phase, possibly due to HfNi$_3$, has been found from PAC measurements but is not found from XRD measurement. Density functional theory (DFT) based calculations of electric field gradient (EFG) and asymmetry parameter ($η$) at the sites of $^{181}$Ta probe nucleus allowed us to assign the observed EFG fractions to the various lattice sites in (Zr/Hf)$_8$Ni$_{21}$ compounds.
△ Less
Submitted 29 September, 2018; v1 submitted 5 October, 2016;
originally announced October 2016.