On Curie temperature of B20-MnSi films
Authors:
Zichao Li,
Ye Yuan,
Viktor Begeza,
Lars Rebohle,
Manfred Helm,
Kornelius Nielsch,
Slawomir Prucnal,
Shengqiang Zhou
Abstract:
B20-type MnSi is the prototype magnetic skyrmion material. Thin films of MnSi show a higher Curie temperature than their bulk counterpart. However, it is not yet clear what mechanism leads to the increase of the Curie temperature. In this work, we grow MnSi films on Si(100) and Si(111) substrates with a broad variation in their structures. By controlling the Mn thickness and annealing parameters,…
▽ More
B20-type MnSi is the prototype magnetic skyrmion material. Thin films of MnSi show a higher Curie temperature than their bulk counterpart. However, it is not yet clear what mechanism leads to the increase of the Curie temperature. In this work, we grow MnSi films on Si(100) and Si(111) substrates with a broad variation in their structures. By controlling the Mn thickness and annealing parameters, the pure MnSi phase of polycrystalline and textured nature as well as the mixed phase of MnSi and MnSi1.7 are obtained. Surprisingly, all these MnSi films show an increased Curie temperature of up to around 43 K. The Curie temperature is likely independent of the structural parameters within our accessibility including the film thickness above a threshold, strain, cell volume and the mixture with MnSi1.7. However, a pronounced phonon softening is observed for all samples, which can tentatively be attributed to slight Mn excess from stoichiometry, leading to the increased Curie temperature.
△ Less
Submitted 7 October, 2022;
originally announced October 2022.
B20-MnSi films grown on Si(100) substrates with magnetic skyrmion signature
Authors:
Zichao Li,
Ye Yuan,
René Hübner,
Viktor Begeza,
Thomas Naumann,
Lars Rebohle,
Olav Hellwig,
Manfred Helm,
Kornelius Nielsch,
Slawomir Prucnal,
Shengqiang Zhou
Abstract:
Magnetic skyrmions have been suggested as information carriers for future spintronic devices. As the first material with experimentally confirmed skyrmions, B20-type MnSi was the research focus for decades. Although B20-MnSi films have been successfully grown on Si(111) substrates, there is no report about B20-MnSi films on Si(100) substrates, which would be more preferred for practical applicatio…
▽ More
Magnetic skyrmions have been suggested as information carriers for future spintronic devices. As the first material with experimentally confirmed skyrmions, B20-type MnSi was the research focus for decades. Although B20-MnSi films have been successfully grown on Si(111) substrates, there is no report about B20-MnSi films on Si(100) substrates, which would be more preferred for practical applications. In this letter, we present the first preparation of B20-MnSi on Si(100) substrates. It is realized by sub-second solid-state reaction between Mn and Si via flash-lamp annealing at ambient pressure. The regrown layer shows an enhanced Curie temperature of 43 K compared with bulk B20-MnSi. The magnetic skyrmion signature is proved in our films by magnetic and transport measurements. The millisecond-range flash annealing provides a promising avenue for the fabrication of Si-based skyrmionic devices.
△ Less
Submitted 24 September, 2021;
originally announced September 2021.