High-field and high-temperature magnetoresistance reveals the superconducting behaviour of the stacking faults in multilayer graphene
Authors:
Christian E. Precker,
José Barzola-Quiquia,
Mun K. Chan,
Marcelo Jaime,
Pablo D. Esquinazi
Abstract:
In spite of 40 years of experimental studies and several theoretical proposals, an overall interpretation of the complex behavior of the magnetoresistance (MR) of multilayer graphene, i.e. graphite, at high fields ($B \lesssim 70~$T) and in a broad temperature range is still lacking. Part of the complexity is due to the contribution of stacking faults (SFs), which most of thick enough multilayer g…
▽ More
In spite of 40 years of experimental studies and several theoretical proposals, an overall interpretation of the complex behavior of the magnetoresistance (MR) of multilayer graphene, i.e. graphite, at high fields ($B \lesssim 70~$T) and in a broad temperature range is still lacking. Part of the complexity is due to the contribution of stacking faults (SFs), which most of thick enough multilayer graphene samples have. We propose a procedure that allows us to extract the SF contribution to the MR we have measured at 0.48~K $\leq T \leq$ 250~K and 0~T$\leq B \lesssim$ 65~T. We found that the MR behavior of part of the SFs is similar to that of granular superconductors with a superconducting critical temperature $T_c \sim $ 350~K, in agreement with recent publications. The measurements were done on a multilayer graphene TEM lamella, contacting the edges of the two-dimensional SFs.
△ Less
Submitted 30 September, 2022;
originally announced September 2022.
-
Record-Breaking Magnetoresistance at the Edge of a Microflake of Natural Graphite
Authors:
Christian E. Precker,
Jose Barzola-Quiquia,
Pablo D. Esquinazi,
Markus Stiller,
Mun K. Chan,
Marcelo Jaime,
Zhipeng Zhang,
Marius Grundmann
Abstract:
Placing several electrodes at the edge of a micrometer-size Sri Lankan natural graphite sample at distances comparable to the size of the internal crystalline regions, we found record values for the change of the resistance with magnetic field. At low temperatures and at $B \sim 21$T the magnetoresistance (MR) reaches $\sim 10^7$%. The MR values exceed by far all earlier reported ones for graphite…
▽ More
Placing several electrodes at the edge of a micrometer-size Sri Lankan natural graphite sample at distances comparable to the size of the internal crystalline regions, we found record values for the change of the resistance with magnetic field. At low temperatures and at $B \sim 21$T the magnetoresistance (MR) reaches $\sim 10^7$%. The MR values exceed by far all earlier reported ones for graphite and they are comparable or even larger (at $T > 50$K) than the largest reported in solids including the Weyl semimetals. The origin of this large MR lies in the existence of highly conducting 2D interfaces aligned parallel to the graphene planes.
△ Less
Submitted 13 November, 2019;
originally announced November 2019.
-
Nonintrinsic origin of the magnetic-field-induced metal-insulator and electronic phase transitions in graphite
Authors:
José Barzola-Quiquia,
Pablo D. Esquinazi,
Christian E. Precker,
Markus Stiller,
Mahsa Zoraghi,
Tobias Förster,
Thomas Herrmannsdörfer,
William A. Coniglio
Abstract:
A detailed magnetoresistance study of bulk and microflake samples of highly oriented pyrolytic graphite with a thickness of 25 $μ$m to 23~nm reveals that the usually observed field-induced metal-insulator and electronic phase transitions vanish in thinner samples. The observed suppression is accompanied by orders of magnitude decrease of the magnetoresistance and of the amplitude of the Shubnikov-…
▽ More
A detailed magnetoresistance study of bulk and microflake samples of highly oriented pyrolytic graphite with a thickness of 25 $μ$m to 23~nm reveals that the usually observed field-induced metal-insulator and electronic phase transitions vanish in thinner samples. The observed suppression is accompanied by orders of magnitude decrease of the magnetoresistance and of the amplitude of the Shubnikov-de-Haas oscillations. The overall behavior is related to the decrease in the quantity of two-dimensional interfaces between crystalline regions of the same and different stacking orders present in graphite samples. Our results indicate that these field-induced transitions are not intrinsic to the ideal graphite structure and, therefore, a relevant portion of the published interpretations should be reconsidered.
△ Less
Submitted 1 February, 2019;
originally announced February 2019.
-
Influence of Interfaces on the Transport Properties of Graphite revealed by Nanometer Thickness Reduction
Authors:
Mahsa Zoraghi,
José Barzola-Quiquia,
Markus Stiller,
Pablo D. Esquinazi,
Irina Estrela-Lopis
Abstract:
We investigated the influence of thickness reduction on the transport properties of graphite microflakes. Using oxygen plasma etching we decreased the thickness of highly oriented pyrolytic graphite (HOPG) microflakes from $\sim 100$~nm to $\sim 20$~nm systematically. Kee** current and voltage electrodes intact, the electrical resistance $R(T)$, the magnetoresistance (MR) and Raman spectra were…
▽ More
We investigated the influence of thickness reduction on the transport properties of graphite microflakes. Using oxygen plasma etching we decreased the thickness of highly oriented pyrolytic graphite (HOPG) microflakes from $\sim 100$~nm to $\sim 20$~nm systematically. Kee** current and voltage electrodes intact, the electrical resistance $R(T)$, the magnetoresistance (MR) and Raman spectra were measured in every individual sample and after each etching step of a few nm. The results show that $R(T)$ and MR can increase or decrease with the sample thickness in a non-systematic way. The results indicate that HOPG samples are inhomogeneous materials, in agreement with scanning transmission electron microscopy images and X-ray diffraction data. Our results further indicate that the quantum oscillations in the MR are not an intrinsic property of the ideal graphite structure but their origin is related to internal conducting interfaces.
△ Less
Submitted 24 July, 2018; v1 submitted 19 June, 2018;
originally announced June 2018.
-
Local Magnetic Measurements of Trapped Flux Through a Permanent Current Path in Graphite
Authors:
Markus Stiller,
Pablo D. Esquinazi,
Jose Barzola-Quiquia,
Christian E. Precker
Abstract:
Temperature and field dependent measurements of the electrical resistance of different natural graphite samples, suggest the existence of superconductivity at room temperature in some regions of the samples. To verify whether dissipationless electrical currents are responsible for the trapped magnetic flux inferred from electrical resistance measurements, we localized them using magnetic force mic…
▽ More
Temperature and field dependent measurements of the electrical resistance of different natural graphite samples, suggest the existence of superconductivity at room temperature in some regions of the samples. To verify whether dissipationless electrical currents are responsible for the trapped magnetic flux inferred from electrical resistance measurements, we localized them using magnetic force microscopy on a natural graphite sample in remanent state after applying a magnetic field. The obtained evidence indicates that at room temperature a permanent current flows at the border of the trapped flux region. The current path vanishes at the same transition temperature $T_c\approx370$~K as the one obtained from electrical resistance measurements on the same sample. This sudden decrease of the phase is different from what is expected for a ferromagnetic material. Time dependent measurements of the signal show the typical behavior of flux creep of a permanent current flowing in a superconductor. The overall results support the existence of room-temperature superconductivity at certain regions in the graphite structure and indicate that magnetic force microscopy is suitable to localize them. Magnetic coupling is excluded as origin of the observed phase signal.
△ Less
Submitted 26 January, 2018;
originally announced January 2018.
-
Functionalization of atomic force microscopy Akiyama tips for magnetic force microscopy measurements
Authors:
Markus Stiller,
Jose Barzola-Quiquia,
Pablo D. Esquinazi,
Soraya Sangiao,
Jose M. De Teresa,
Jan Meijer,
Bernd Abel
Abstract:
In this work we have used focused electron beam induced deposition of cobalt to functionalize atomic force microscopy Akiyama tips for application in magnetic force microscopy. The grown tips have a content of 90% Co after exposure to ambient air. The magnetic tips were characterized using energy dispersive X-ray spectroscopy and scanning electron microscopy. In order to investigate the magnetic p…
▽ More
In this work we have used focused electron beam induced deposition of cobalt to functionalize atomic force microscopy Akiyama tips for application in magnetic force microscopy. The grown tips have a content of 90% Co after exposure to ambient air. The magnetic tips were characterized using energy dispersive X-ray spectroscopy and scanning electron microscopy. In order to investigate the magnetic properties, current loops were prepared by electron beam lithography. Measurements at room temperature as well as 4.2K were carried out and the coercive field of 68 Oe of the Co tip was estimated by applying several external fields in the opposite direction of the tip magnetization. Magnetic Akiyama tips open new possibilities for low to room-temperature magnetic force microscopy measurements.
△ Less
Submitted 17 September, 2017;
originally announced September 2017.
-
Evidence for room temperature superconductivity at graphite interfaces
Authors:
Pablo D. Esquinazi,
Christian E. Precker,
Markus Stiller,
Tiago R. S. Cordeiro,
Jose Barzola-Quiquia,
Annette Setzer,
Winfried Böhlmann
Abstract:
In the last 43 years several hints were reported suggesting the existence of granular superconductivity above room temperature in different graphite-based systems. In this paper some of the results are reviewed, giving special attention to those obtained in water and n-heptane treated graphite powders, commercial and natural bulk graphite samples with different characteristics as well as transmiss…
▽ More
In the last 43 years several hints were reported suggesting the existence of granular superconductivity above room temperature in different graphite-based systems. In this paper some of the results are reviewed, giving special attention to those obtained in water and n-heptane treated graphite powders, commercial and natural bulk graphite samples with different characteristics as well as transmission electron microscope (TEM) lamellae. The overall results indicate that superconducting regions exist and are localized at certain internal interfaces of the graphite structure. The existence of the rhombohedral graphite phase in all samples with superconducting-like properties suggests its interfaces with the Bernal phase as a possible origin for the high-temperature superconductivity, as theoretical calculations predict. High precision electrical resistance and magnetization measurements were used to identify a transition at $T_c \gtrsim 350~$K. To check for the existence of true zero resistance paths in the samples we used local magnetic measurements, which results support the existence of superconducting regions at such high temperatures.
△ Less
Submitted 1 September, 2017;
originally announced September 2017.
-
Local magnetic measurements of permanent current paths in a natural graphite crystal
Authors:
Markus Stiller,
Pablo D. Esquinazi,
Christian E. Precker,
José Barzola-Quiquia
Abstract:
A recently reported transition in the electrical resistance of different natural graphite samples suggests the existence of superconductivity at room temperature. To check whether dissipationless electrical currents are responsible for the trapped magnetic flux inferred from electrical resistance measurements, we localized them using magnetic force microscopy on a natural graphite sample in remane…
▽ More
A recently reported transition in the electrical resistance of different natural graphite samples suggests the existence of superconductivity at room temperature. To check whether dissipationless electrical currents are responsible for the trapped magnetic flux inferred from electrical resistance measurements, we localized them using magnetic force microscopy on a natural graphite sample in remanent state after applying a magnetic field. The obtained evidence indicates that at room temperature a permanent current flows at the border of the trapped flux region. The current path vanishes at the same transition temperature $T_c \simeq 370~$K as the one obtained from electrical resistance measurements on the same sample. The overall results support the existence of room-temperature superconductivity at certain regions in the graphite structure and show that the used method is suitable to localize the superconducting regions.
△ Less
Submitted 28 May, 2017;
originally announced May 2017.
-
Electrical Transport Properties of Polycrystalline and Amorphous TiO2 Single Nanotubes
Authors:
Markus Stiller,
Jose Barzola-Quiquia,
Pablo Esquinazi,
Seulgi So,
Imgon Hwang,
Patrik Schmuki,
Julia Böttner,
Irina Estrela-Lopis
Abstract:
The electrical transport properties of anodically grown TiO2 nanotubes was investigated. Amorphous nanotubes were anodically grown on titanium foil and transformed through annealing into the anatase phase. Amorphous and polycrystalline single nanotubes were isolated and contacted for measurements of the electrical resistance. Non-linear current-voltage characteristics were explained using the fluc…
▽ More
The electrical transport properties of anodically grown TiO2 nanotubes was investigated. Amorphous nanotubes were anodically grown on titanium foil and transformed through annealing into the anatase phase. Amorphous and polycrystalline single nanotubes were isolated and contacted for measurements of the electrical resistance. Non-linear current-voltage characteristics were explained using the fluctuation induced tunneling conduction model. A clear enhancement of the conductance was induced in an insulating anatase nanotube through low-energy Ar/H ion irradiation. Confocal Raman spectroscopy shows that the annealed samples were in anatase phase and a blueshift due to phonon confinement was observed.
△ Less
Submitted 24 February, 2017;
originally announced February 2017.
-
Fabrication and electrical transport properties of embedded graphite microwires in a diamond matrix
Authors:
J. Barzola-Quiquia,
T. Lühmann,
R. Wunderlich,
M. Stiller,
M. Zoraghi,
J. Meijer,
P. Esquinazi,
J. Böttner,
I. Estrela-Lopis
Abstract:
Micrometer width and nanometer thick wires with different shapes were produced $\approx 3~\upmu$m below the surface of a diamond crystal using a microbeam of He$^+$ ions with 1.8~MeV energy. Initial samples are amorphous and after annealing at $T\approx 1475$~K, the wires crystallized into a graphite-like structures, according to confocal Raman spectroscopy measurements. The electrical resistivity…
▽ More
Micrometer width and nanometer thick wires with different shapes were produced $\approx 3~\upmu$m below the surface of a diamond crystal using a microbeam of He$^+$ ions with 1.8~MeV energy. Initial samples are amorphous and after annealing at $T\approx 1475$~K, the wires crystallized into a graphite-like structures, according to confocal Raman spectroscopy measurements. The electrical resistivity at room temperature is only one order of magnitude larger than the in-plane resistivity of highly oriented pyrolytic bulk graphite and shows a small resistivity ratio($ρ(2{\rm K})/ρ(315{\rm K}) \approx 1.275$). A small negative magnetoresistance below $T=200$~K was measured and can be well understood taking spin-dependent scattering processes into account. The used method provides the means to design and produce millimeter to micrometer sized conducting circuits with arbitrary shape embedded in a diamond matrix.
△ Less
Submitted 13 February, 2017;
originally announced February 2017.
-
Identification of a possible superconducting transition above room temperature in natural graphite crystals
Authors:
Christian E. Precker,
Pablo D. Esquinazi,
Ana Champi,
José Barzola-Quiquia,
Mahsa Zoraghi,
Santiago Muiños-Landin,
Annette Setzer,
Winfried Böhlmann,
Daniel Spemann,
Jan Meijer,
Tom Muenster,
Oliver Baehre,
Gert Kloess,
Henning Beth
Abstract:
Measuring with high precision the electrical resistance of highly ordered natural graphite samples from a Brazil mine, we have identified a transition at $\sim$350~K with $\sim$40~K transition width. The step-like change in temperature of the resistance, its magnetic irreversibility and time dependence after a field change, consistent with trapped flux and flux creep, and the partial magnetic flux…
▽ More
Measuring with high precision the electrical resistance of highly ordered natural graphite samples from a Brazil mine, we have identified a transition at $\sim$350~K with $\sim$40~K transition width. The step-like change in temperature of the resistance, its magnetic irreversibility and time dependence after a field change, consistent with trapped flux and flux creep, and the partial magnetic flux expulsion obtained by magnetization measurements, suggest the existence of granular superconductivity below 350~K. The zero-field virgin state can only be reached again after zero field cooling the sample from above the transition. Paradoxically, the extraordinarily high transition temperature we found for this and several other graphite samples is the reason why this transition remained undetected so far. The existence of well ordered rhombohedral graphite phase in all measured samples has been proved by x-rays diffraction measurements, suggesting its interfaces with the Bernal phase as a possible origin for the high-temperature superconductivity, as theoretical studies predicted. The localization of granular superconductivity at these two dimensional interfaces prevents the observation of a zero resistance state or of a full Meissner state.
△ Less
Submitted 30 June, 2016;
originally announced June 2016.
-
Influence of rhombohedral stacking order in the electrical resistance of bulk and mesoscopic graphite
Authors:
M. Zoraghi,
J. Barzola-Quiquia,
M. Stiller,
A. Setzer,
P. Esquinazi,
G. H. Kloess,
T. Muenster,
T. Lühmann,
I. Estrela-Lopis
Abstract:
The electrical, in-plane resistance as a function of temperature $R(T)$ of bulk and mesoscopic thin graphite flakes obtained from the same batch was investigated. Samples thicker than $\sim 30$ nm show metalliclike contribution in a temperature range that increases with the sample thickness, whereas a semiconductinglike behavior was observed for thinner samples. The temperature dependence of the i…
▽ More
The electrical, in-plane resistance as a function of temperature $R(T)$ of bulk and mesoscopic thin graphite flakes obtained from the same batch was investigated. Samples thicker than $\sim 30$ nm show metalliclike contribution in a temperature range that increases with the sample thickness, whereas a semiconductinglike behavior was observed for thinner samples. The temperature dependence of the in-plane resistance of all measured samples and several others from literature can be very well explained between 2 K and 1100 K assuming three contributions in parallel: a metalliclike conducting path at the interfaces between crystalline regions, composed of two semiconducting phases, i.e. Bernal and rhombohedral stacking. From the fits of $R(T)$ we obtain a semiconducting energy gap of $110 \pm 20$meV for the rhombohedral and $38\pm 8 $meV for the Bernal phase. The presence of these crystalline phases was confirmed by x-ray diffraction measurements. We review similar experimental data from literature of the last 33 years and two more theoretical models used to fit $R(T)$.
△ Less
Submitted 25 January, 2017; v1 submitted 21 March, 2016;
originally announced March 2016.
-
Magnetic order and superconductivity observed in bundles of Double-Wall Carbon Nanotubes
Authors:
J. Barzola-Quiquia,
P. Esquinazi,
M. Lindel,
D. Spemann,
M. Muallem,
G. D. Nessim
Abstract:
The magnetotransport properties were studied in hundreds of micrometer length double-wall carbon nanotubes (DWCNT) bundles. Above 15 K the resistance shows an ohmic behavior and its temperature dependence is well described using the variable-range hop** for one-dimensional system. The magnetoresistance is negative and can be explained using an empirical model based on spin-scattering processes i…
▽ More
The magnetotransport properties were studied in hundreds of micrometer length double-wall carbon nanotubes (DWCNT) bundles. Above 15 K the resistance shows an ohmic behavior and its temperature dependence is well described using the variable-range hop** for one-dimensional system. The magnetoresistance is negative and can be explained using an empirical model based on spin-scattering processes indicating the existence of magnetic order up to room temperature. At temperatures between 2 K and 15 K the resistance is non-ohmic and the current-voltage characteristics reveal the appearance of a potential, which can be well described by a fluctuation-induced tunneling conduction model. In this low temperature range and at low enough input current, a positive magnetoresistance appears - in addition to the negative one - with an extraordinary hysteresis in field and vanishes at $T \sim 15 $K, suggesting the existence of a superconducting state. Magnetization results partially support the existence of both phenomena in the DWCNT bundles.
△ Less
Submitted 2 March, 2015;
originally announced March 2015.
-
Topological Insulator Thin Films Starting from the Amorphous Phase - Bi$_2$Se$_3$ as Example
Authors:
J. Barzola-Quiquia,
T. Lehmann,
M. Stiller,
D. Spemann,
P. Esquinazi,
P. Häussler
Abstract:
We present a new method to obtain topological insulator Bi$_2$Se$_3$ thin films with a centimeter large lateral length. To produce amorphous Bi$_2$Se$_3$ thin films we have used a sequential flash-evaporation method at room temperature. Transmission electron microscopy has been used to verify that the prepared samples are in a pure amorphous state. During annealing the samples transform into the r…
▽ More
We present a new method to obtain topological insulator Bi$_2$Se$_3$ thin films with a centimeter large lateral length. To produce amorphous Bi$_2$Se$_3$ thin films we have used a sequential flash-evaporation method at room temperature. Transmission electron microscopy has been used to verify that the prepared samples are in a pure amorphous state. During annealing the samples transform into the rhombohedral Bi$_2$Se$_3$ crystalline strcuture which was confirmed using X-ray diffraction and Raman spectroscopy. Resistance measurements of the amorphous films show the expected Mott variable range hop** conduction process with a high specific resistance compared to the one obtained in the crystalline phase (metallic behavior). We have measured the magnetoresistance (MR) and the Hall effect (HE) at different temperatures between 2 K and 275 K. At temperatures $T \lesssim 50$ K and fields $B \lesssim 1$ T we observe weak anti-localization in the MR; the Hall measurements confirm the n-type character of the samples. All experimental results of our films are in quantitative agreement with results from samples prepared using more sophisticated methods.
△ Less
Submitted 4 February, 2015;
originally announced February 2015.
-
On the low-field Hall coefficient of graphite
Authors:
P. Esquinazi,
J. Krüger,
J. Barzola-Quiquia,
R. Schönemann,
T. Herrmannsdörfer,
N. García
Abstract:
We have measured the temperature and magnetic field dependence of the Hall coefficient ($R_{\rm H}$) in three, several micrometer long multigraphene samples of thickness between $\sim 9~$to $\sim 30$~nm in the temperature range 0.1 to 200~K and up to 0.2~T field. The temperature dependence of the longitudinal resistance of two of the samples indicates the contribution from embedded interfaces runn…
▽ More
We have measured the temperature and magnetic field dependence of the Hall coefficient ($R_{\rm H}$) in three, several micrometer long multigraphene samples of thickness between $\sim 9~$to $\sim 30$~nm in the temperature range 0.1 to 200~K and up to 0.2~T field. The temperature dependence of the longitudinal resistance of two of the samples indicates the contribution from embedded interfaces running parallel to the graphene layers. At low enough temperatures and fields $R_{\rm H}$ is positive in all samples, showing a crossover to negative values at high enough fields and/or temperatures in samples with interfaces contribution. The overall results are compatible with the reported superconducting behavior of embedded interfaces in the graphite structure and indicate that the negative low magnetic field Hall coefficient is not intrinsic of the ideal graphite structure.
△ Less
Submitted 6 November, 2014; v1 submitted 28 July, 2014;
originally announced July 2014.
-
Mott Variable Range Hop** and Weak Antilocalization Effect in Heteroepitaxial Na2IrO3 Thin Films
Authors:
Marcus Jenderka,
José Barzola-Quiquia,
Zhipeng Zhang,
Heiko Frenzel,
Marius Grundmann,
Michael Lorenz
Abstract:
Iridate thin films are a prerequisite for any application utilizing their cooperative effects resulting from the interplay of stron spin-orbit coupling and electronic correlations. Here, heteroepitaxial Na2IrO3 thin films with excellent (001) out-of-plane crystalline orientation and well defined in-plane epitaxial relationship are presented on various oxide substrates. Resistivity is dominated by…
▽ More
Iridate thin films are a prerequisite for any application utilizing their cooperative effects resulting from the interplay of stron spin-orbit coupling and electronic correlations. Here, heteroepitaxial Na2IrO3 thin films with excellent (001) out-of-plane crystalline orientation and well defined in-plane epitaxial relationship are presented on various oxide substrates. Resistivity is dominated by a three-dimensional variable range hop** mechanism in a large temperature range between 300 K and 40 K. Optical experiments show the onset of a small optical gap of about 200 meV and a splitting of the Ir 5d-t2g manifold. Positive magnetoresistance below 3 T and 25 K shows signatures of a weak antilocalization effect. This effect can be associated with surface states in a topological insulator and hence supports proposals for a topological insulator phase present in Na2IrO3.
△ Less
Submitted 21 March, 2013;
originally announced March 2013.
-
Can do** graphite trigger room temperature superconductivity? Evidence for granular high-temperature superconductivity in water-treated graphite powder
Authors:
T. Scheike,
W. Böhlmann,
P. Esquinazi,
J. Barzola-Quiquia,
A. Ballestar,
A. Setzer
Abstract:
Trying to dope graphite flakes we found that the magnetization of pure, several tens of micrometers grain size graphite powder and after a simple treatment with pure water shows clear and reproducible granular superconducting behavior with a critical temperature above 300K. The observed magnetic characteristics as a function of temperature, magnetic field and time, provide evidence for weakly coup…
▽ More
Trying to dope graphite flakes we found that the magnetization of pure, several tens of micrometers grain size graphite powder and after a simple treatment with pure water shows clear and reproducible granular superconducting behavior with a critical temperature above 300K. The observed magnetic characteristics as a function of temperature, magnetic field and time, provide evidence for weakly coupled grains through Josephson interaction, revealing the existence of superconducting vortices.
△ Less
Submitted 10 September, 2012;
originally announced September 2012.
-
Revealing the origin of the vertical hysteresis loop shifts in an exchange biased Co/YMnO$_3$ bilayer
Authors:
J. Barzola-Quiquia,
A. Lessig,
A. Ballestar,
C. Zandalazini,
G. Bridoux,
F. Bern,
P. Esquinazi
Abstract:
We have investigated exchange bias effects in bilayers composed by the antiferromagnetic o-YMnO$_3$ and ferromagnetic Co thin film by means of SQUID magnetometry, magnetoresistance, anisotropic magnetoresistance and planar Hall effect. The magnetization and magnetotransport properties show pronounced asymmetries in the field and magnetization axes of the field hysteresis loops. Both exchange bias…
▽ More
We have investigated exchange bias effects in bilayers composed by the antiferromagnetic o-YMnO$_3$ and ferromagnetic Co thin film by means of SQUID magnetometry, magnetoresistance, anisotropic magnetoresistance and planar Hall effect. The magnetization and magnetotransport properties show pronounced asymmetries in the field and magnetization axes of the field hysteresis loops. Both exchange bias parameters, the exchange bias field $H_{E}(T)$ as well as the magnetization shift $M_E(T)$, vanish around the Néel temperature $T_N \simeq 45$ K. We show that the magnetization shift $M_E(T)$ is also measured by a shift in the anisotropic magnetoresistance and planar Hall resistance having those a similar temperature dependence as the one obtained from magnetization measurements. Because the o-YMnO$_3$ film is highly insulating, our results demonstrate that the $M_E(T)$ shift originates at the interface within the ferromagnetic Co layer. To show that the main results obtained are general and not because of some special characteristics of the o-YMO$_3$ layer, similar measurements were done in Co/CoO micro-wires. The transport and magnetization characterization of the micro-wires supports the main conclusion that these effects are related to the response of the ferromagnetic Co layer at the interface.
△ Less
Submitted 9 August, 2012;
originally announced August 2012.
-
Evidence of Josephson-coupled superconducting regions at the interfaces of Highly Oriented Pyrolytic Graphite
Authors:
A. Ballestar,
J. Barzola-Quiquia,
P. Esquinazi
Abstract:
Transport properties of a few hundreds of nanometers thick (in the graphene plane direction) lamellae of highly oriented pyrolytic graphite (HOPG) have been investigated. Current-Voltage characteristics as well as the temperature dependence of the voltage at different fixed input currents provide evidence for Josephson-coupled superconducting regions embedded in the internal two-dimensional interf…
▽ More
Transport properties of a few hundreds of nanometers thick (in the graphene plane direction) lamellae of highly oriented pyrolytic graphite (HOPG) have been investigated. Current-Voltage characteristics as well as the temperature dependence of the voltage at different fixed input currents provide evidence for Josephson-coupled superconducting regions embedded in the internal two-dimensional interfaces, reaching zero resistance at low enough temperatures. The overall behavior indicates the existence of superconducting regions with critical temperatures above 100 K at the internal interfaces of oriented pyrolytic graphite.
△ Less
Submitted 13 June, 2012; v1 submitted 12 June, 2012;
originally announced June 2012.
-
Possible superconductivity in multi-layer-graphene by application of a gate voltage
Authors:
A. Ballestar,
P. Esquinazi,
J. Barzola-Quiquia,
S. Dusari,
F. Bern,
R. R. da Silva,
Y. Kopelevich
Abstract:
The carrier density in tens of nanometers thick graphite samples (multi-layer-graphene, MLG) has been modified by applying a gate voltage ($V_g$) perpendicular to the graphene planes. Surface potential microscopy shows inhomogeneities in the carrier density ($n$) in the sample near surface region and under different values of $V_g$ at room temperature. Transport measurements on different MLG sampl…
▽ More
The carrier density in tens of nanometers thick graphite samples (multi-layer-graphene, MLG) has been modified by applying a gate voltage ($V_g$) perpendicular to the graphene planes. Surface potential microscopy shows inhomogeneities in the carrier density ($n$) in the sample near surface region and under different values of $V_g$ at room temperature. Transport measurements on different MLG samples reveal that under a large enough applied electric field these regions undergo a superconducting-like transition at $T \lesssim 17$ K. A magnetic field applied parallel or normal to the graphene layers suppresses the transition without changing appreciably the transition temperature.
△ Less
Submitted 3 February, 2014; v1 submitted 15 February, 2012;
originally announced February 2012.
-
Length dependence of the resistance in graphite: Influence of ballistic transport
Authors:
P. Esquinazi,
J. Barzola-Quiquia,
S. Dusari,
N. García
Abstract:
Using a linear array of voltage electrodes with a separation of several micrometers on a $20 $nm thick and 30 $μ$m long multigraphene sample we show that the measured resistance does not follow the usual length dependence according to Ohm's law. The deviations can be quantitatively explained taking into account Sharvin-Knudsen formula for ballistic transport. This allows us to obtain without free…
▽ More
Using a linear array of voltage electrodes with a separation of several micrometers on a $20 $nm thick and 30 $μ$m long multigraphene sample we show that the measured resistance does not follow the usual length dependence according to Ohm's law. The deviations can be quantitatively explained taking into account Sharvin-Knudsen formula for ballistic transport. This allows us to obtain without free parameters the mean free path of the carriers in the sample at different temperatures. In agreement with recently reported values obtained with a different experimental method, we obtain that the carrier mean free path is of the order of $\sim 2 μ$m with a mobility $μ\sim 10^7 $cm$^{2}$V$^{-1}$s$^{-1}$. The results indicate that the usual Ohm's law is not adequate to calculate the absolute resistivity of mesoscopic graphite samples.
△ Less
Submitted 14 January, 2012;
originally announced January 2012.
-
Large local Hall effect in pin-hole dominated multigraphene spin-valves
Authors:
P. K. Muduli,
J. Barzola-Quiquia,
S. Dusari,
Ana Ballestar,
F. Bern,
W. Bohlmann,
P. Esquinazi
Abstract:
We report local and non-local measurements in pin-hole dominated mesoscopic multigraphene spin-valves. Local spin-valve measurements show spurious switching behavior in resistance during magnetic field swee** similar to the signal observed due to spin-injection into multigraphene. The switching behavior has been explained in terms of local Hall effect due to thickness irregularity of the tunnel…
▽ More
We report local and non-local measurements in pin-hole dominated mesoscopic multigraphene spin-valves. Local spin-valve measurements show spurious switching behavior in resistance during magnetic field swee** similar to the signal observed due to spin-injection into multigraphene. The switching behavior has been explained in terms of local Hall effect due to thickness irregularity of the tunnel barrier. Local Hall effect appears due to large local magnetostatic field produced at the roughness in the AlO$_x$ tunnel barrier. The effect of this local Hall effect is found to reduce as temperature is increased above 75 K. The strong local Hall effect hinders spin-injection into multigraphene resulting in no spin signal in non-local measurements.
△ Less
Submitted 23 July, 2012; v1 submitted 10 November, 2011;
originally announced November 2011.
-
Experimental Study of the Intrinsic and Extrinsic Transport Properties of Graphite and Multigraphene Samples
Authors:
J. Barzola-Quiquia,
A. Ballestar,
S. Dusari,
P. Esquinazi
Abstract:
This work deals with the intrinsic and extrinsic properties of the graphene layers inside the graphite structure, in particular the influence of defects and interfaces. We discuss the evidence for ballistic transport found in mesoscopic graphite samples and the possibility to obtain the intrinsic carrier density of graphite, without the need of free parameters or arbitrary assumptions. The influen…
▽ More
This work deals with the intrinsic and extrinsic properties of the graphene layers inside the graphite structure, in particular the influence of defects and interfaces. We discuss the evidence for ballistic transport found in mesoscopic graphite samples and the possibility to obtain the intrinsic carrier density of graphite, without the need of free parameters or arbitrary assumptions. The influence of internal interfaces on the transport properties of bulk graphite is described in detail. We show that in specially prepared multigraphene samples the transport properties show clear signs for the existence of granular superconductivity within the graphite interfaces. We argue that the superconducting-insulator or metal-insulator transition (MIT) reported in the literature for bulk graphite is not intrinsic of the graphite structure but it is due to the influence of these interfaces. Current-Voltage characteristics curves reveal Josephson-like behavior at the interfaces with superconducting critical temperatures above 150K.
△ Less
Submitted 2 August, 2011;
originally announced August 2011.
-
Evidence for semiconducting behavior with a narrow band gap of Bernal graphite
Authors:
N. García,
P. Esquinazi,
J. Barzola-Quiquia,
S. Dusari
Abstract:
We have studied the resistivity of a large number of highly oriented graphite samples with areas ranging from several mm$^2$ to a few $μ$m$^2$ and thickness from $\sim 10 $nm to several tens of micrometers. The measured resistance can be explained by the parallel contribution of semiconducting graphene layers with low carrier density $< 10^9$ cm$^{-2}$ and the one from metallic-like internal inter…
▽ More
We have studied the resistivity of a large number of highly oriented graphite samples with areas ranging from several mm$^2$ to a few $μ$m$^2$ and thickness from $\sim 10 $nm to several tens of micrometers. The measured resistance can be explained by the parallel contribution of semiconducting graphene layers with low carrier density $< 10^9$ cm$^{-2}$ and the one from metallic-like internal interfaces. The results indicate that ideal graphite with Bernal stacking structure is a narrow-gap semiconductor with an energy gap $E_g \sim 40 $meV.
△ Less
Submitted 30 April, 2012; v1 submitted 2 June, 2011;
originally announced June 2011.
-
Enhancement of the ferromagnetic order of graphite after sulphuric acid treatment
Authors:
J. Barzola-Quiquia,
W. Böhlmann,
P. Esquinazi,
A. Schadewitz,
A. Ballestar,
S. Dusari,
L. Schultze-Nobre,
B. Kersting
Abstract:
We have studied the changes in the ferromagnetic behavior of graphite powder and graphite flakes after treatment with diluted sulphuric acid. We show that this kind of acid treatment enhances substantially the ferromagnetic magnetization of virgin graphite micrometer size powder as well as in graphite flakes. The anisotropic magnetoresistance (AMR) amplitude at 300 K measured in a micrometer size…
▽ More
We have studied the changes in the ferromagnetic behavior of graphite powder and graphite flakes after treatment with diluted sulphuric acid. We show that this kind of acid treatment enhances substantially the ferromagnetic magnetization of virgin graphite micrometer size powder as well as in graphite flakes. The anisotropic magnetoresistance (AMR) amplitude at 300 K measured in a micrometer size thin graphite flake after acid treatment reaches values comparable to polycrystalline cobalt.
△ Less
Submitted 5 April, 2011;
originally announced April 2011.
-
Ballistic transport at room temperature in micrometer size multigraphene
Authors:
S. Dusari,
J. Barzola-Quiquia,
P. Esquinazi,
N. García
Abstract:
The intrinsic values of the carriers mobility and density of the graphene layers inside graphite, the well known structure built on these layers in the Bernal stacking configuration, are not well known mainly because most of the research was done in rather bulk samples where lattice defects hide their intrinsic values. By measuring the electrical resistance through microfabricated constrictions in…
▽ More
The intrinsic values of the carriers mobility and density of the graphene layers inside graphite, the well known structure built on these layers in the Bernal stacking configuration, are not well known mainly because most of the research was done in rather bulk samples where lattice defects hide their intrinsic values. By measuring the electrical resistance through microfabricated constrictions in micrometer small graphite flakes of a few tens of nanometers thickness we studied the ballistic behavior of the carriers. We found that the carriers' mean free path is micrometer large with a mobility $μ\simeq 6 \times 10^6 $cm$^2$/Vs and a carrier density $n \simeq 7 \times 10^8 $cm$^{-2}$ per graphene layer at room temperature. These distinctive transport and ballistic properties have important implications for understanding the values obtained in single graphene and in graphite as well as for implementing this last in nanoelectronic devices.
△ Less
Submitted 6 December, 2010;
originally announced December 2010.
-
Uncompensated magnetization and exchange-bias field in La$_{0.7}$Sr$_{0.3}$MnO$_3$/YMnO$_3$ bilayers: The influence of the ferromagnetic layer
Authors:
C. Zandalazini,
P. Esquinazi,
G. Bridoux,
J. Barzola-Quiquia,
H. Ohldag,
E. Arenholz
Abstract:
We studied the magnetic behavior of bilayers of multiferroic and nominally antiferromagnetic o-YMnO$_3$ (375~nm thick) and ferromagnetic La$_{0.7}$Sr$_{0.3}$MnO$_3$ and La$_{0.67}$Ca$_{0.33}$MnO$_3$ ($8 \ldots 225~$nm), in particular the vertical magnetization shift $M_E$ and exchange bias field $H_E$ for different thickness and magnetic dilution of the ferromagnetic layer at different temperature…
▽ More
We studied the magnetic behavior of bilayers of multiferroic and nominally antiferromagnetic o-YMnO$_3$ (375~nm thick) and ferromagnetic La$_{0.7}$Sr$_{0.3}$MnO$_3$ and La$_{0.67}$Ca$_{0.33}$MnO$_3$ ($8 \ldots 225~$nm), in particular the vertical magnetization shift $M_E$ and exchange bias field $H_E$ for different thickness and magnetic dilution of the ferromagnetic layer at different temperatures and cooling fields. We have found very large $M_E$ shifts equivalent to up to 100\% of the saturation value of the o-YMO layer alone. The overall behavior indicates that the properties of the ferromagnetic layer contribute substantially to the $M_E$ shift and that this does not correlate straightforwardly with the measured exchange bias field $H_E$.
△ Less
Submitted 14 September, 2010;
originally announced September 2010.
-
ZnO:Co Diluted Magnetic Semiconductor or Hybrid Nanostructure for Spintronics?
Authors:
F. Golmar,
M. Villafuerte,
A. Mudarra Navarro,
C. E. Rodrıguez Torres,
J. Barzola-Quiquia,
P. Esquinazi,
S. P. Heluani
Abstract:
We have studied the influence of intrinsic and extrinsic defects in the magnetic and electrical transport properties of Co-doped ZnO thin films. X ray absorption measurements show that Co substitute Zn in the ZnO structure and it is in the 2+ oxidation state. Magnetization (M) measurements show that doped samples are mainly paramagnetic. From M vs. H loops measured at 5 K we found that the values…
▽ More
We have studied the influence of intrinsic and extrinsic defects in the magnetic and electrical transport properties of Co-doped ZnO thin films. X ray absorption measurements show that Co substitute Zn in the ZnO structure and it is in the 2+ oxidation state. Magnetization (M) measurements show that doped samples are mainly paramagnetic. From M vs. H loops measured at 5 K we found that the values of the orbital L and spin S numbers are between 1 and 1.3 for L and S = 3/2, in agreement with the representative values for isolated Co 2+. The obtained negative values of the Curie-Weiss temperatures indicate the existence of antiferromagnetic interactions between transition metal atoms.
△ Less
Submitted 1 July, 2010;
originally announced July 2010.
-
The influence of Ga$^+$-irradiation on the transport properties of mesoscopic conducting thin films
Authors:
J. Barzola-Quiquia,
S. Dusari,
G. Bridoux,
F. Bern,
A. Molle,
P. Esquinazi
Abstract:
We studied the influence of 30keV Ga$^+$-ions -- commonly used in focused ion beam (FIB) devices -- on the transport properties of thin crystalline graphite flake, La$_{0.7}$Ca$_{0.3}$MnO$_3$ and Co thin films. The changes of the electrical resistance were measured in-situ during irradiation and also the temperature and magnetic field dependence before and after irradiation. Our results show tha…
▽ More
We studied the influence of 30keV Ga$^+$-ions -- commonly used in focused ion beam (FIB) devices -- on the transport properties of thin crystalline graphite flake, La$_{0.7}$Ca$_{0.3}$MnO$_3$ and Co thin films. The changes of the electrical resistance were measured in-situ during irradiation and also the temperature and magnetic field dependence before and after irradiation. Our results show that the transport properties of these materials strongly change at Ga$^+$ fluences much below those used for patterning and ion beam induced deposition (IBID), limiting seriously the use of FIB when the intrinsic properties of the materials of interest are of importance. We present a method that can be used to protect the sample as well as to produce selectively irradiation-induced changes.
△ Less
Submitted 18 February, 2010;
originally announced February 2010.
-
Andreev reflection measurements in nanostructures with amorphous WC$_x$ superconducting contacts
Authors:
J. Barzola-Quiquia,
M. Ziese,
P. Esquinazi,
N. Garcia
Abstract:
Point-contact Andreev reflection measurements of Co/ and Cu/tungsten-carbide (WC$_x$) contacts are presented. Metallic thin films were patterned by e-beam-lithography and lift-off; tungsten carbide superconducting tips were grown directly on the pre-patterned samples by decomposition of a metallo-organic vapour (tungsten hexacarbonyl) under a focused Ga$^+$-ion beam (FIB). Current-voltage measur…
▽ More
Point-contact Andreev reflection measurements of Co/ and Cu/tungsten-carbide (WC$_x$) contacts are presented. Metallic thin films were patterned by e-beam-lithography and lift-off; tungsten carbide superconducting tips were grown directly on the pre-patterned samples by decomposition of a metallo-organic vapour (tungsten hexacarbonyl) under a focused Ga$^+$-ion beam (FIB). Current-voltage measurements as a function of temperature and magnetic field clearly showed the signatures of Andreev reflection. The experimental conductance-voltage curves were analyzed within the Blonder-Tinkham-Klapwijk theory. The results highlight the possibilities, advantages and disadvantages of using FIB-produced amorphous WC$_x$ tips for point-contact spectroscopy in metallic nanostructures.
△ Less
Submitted 7 December, 2009;
originally announced December 2009.
-
Changes in the electrical transport of ZnO under visible light
Authors:
S. Dusari,
J. Barzola-Quiquia,
P. Esquinazi,
S. P. Heluani
Abstract:
Complex impedance spectroscopy data in the frequency range 16Hz < f < 3 MHz at room temperature were acquired on pure ZnO single crystal and thin film. The measured impedance of the ZnO samples shows large changes with time after exposure to or covering them from visible light. At fixed times Cole-Cole-diagrams indicate the presence of a single relaxation process. A simple analysis of the impeda…
▽ More
Complex impedance spectroscopy data in the frequency range 16Hz < f < 3 MHz at room temperature were acquired on pure ZnO single crystal and thin film. The measured impedance of the ZnO samples shows large changes with time after exposure to or covering them from visible light. At fixed times Cole-Cole-diagrams indicate the presence of a single relaxation process. A simple analysis of the impedance data allows us to obtain two main relaxation times. The behavior for both, ZnO crystal and thin film, is similar but the thin film shows shorter relaxation times. The analysis indicates the existence of two different photo-active defects with activation energies between ~0.8 eV and ~1.1 eV.
△ Less
Submitted 14 October, 2009;
originally announced October 2009.
-
On the origin of the electric carrier concentration in graphite
Authors:
A. Arndt,
D. Spoddig,
P. Esquinazi,
J. Barzola-Quiquia,
T. Butz
Abstract:
We investigate the dependence of the electrical resistivity of $\sim 60 $nm thick single crystalline graphite samples on the defect concentration produced by proton irradiation at very low fluences. We show that the resistivity decreases few percent at room temperature after inducing defects at concentrations as low as $\sim 0.1 $ppm due to the increase in the carrier density, in agreement with…
▽ More
We investigate the dependence of the electrical resistivity of $\sim 60 $nm thick single crystalline graphite samples on the defect concentration produced by proton irradiation at very low fluences. We show that the resistivity decreases few percent at room temperature after inducing defects at concentrations as low as $\sim 0.1 $ppm due to the increase in the carrier density, in agreement with theoretical estimates. The overall results indicate that the carrier densities measured in graphite are not intrinsic but related to defects and impurities.
△ Less
Submitted 4 September, 2009; v1 submitted 18 May, 2009;
originally announced May 2009.
-
Disordered Electrical Potential Observed on the Surface of SiO$_2$ by Electric Field Microscopy
Authors:
N. García,
Zang Yan,
A. Ballestar,
J. Barzola-Quiquia,
F. Bern,
P. Esquinazi
Abstract:
The electrical potential on the surface of $\sim 300$ nm thick SiO$_2$ grown on single crystalline Si substrates has been characterized at ambient conditions using electric field microscopy. Our results show an inhomogeneous potential distribution with fluctuations up to $\sim 0.4 $V within regions of $1 μ$m. The potential fluctuations observed at the surface of these usual dielectric holders of…
▽ More
The electrical potential on the surface of $\sim 300$ nm thick SiO$_2$ grown on single crystalline Si substrates has been characterized at ambient conditions using electric field microscopy. Our results show an inhomogeneous potential distribution with fluctuations up to $\sim 0.4 $V within regions of $1 μ$m. The potential fluctuations observed at the surface of these usual dielectric holders of graphene sheets should induce strong variations in the graphene charge densities and provide a simple explanation for some of the anomalous behaviors of the transport properties of graphene.
△ Less
Submitted 17 July, 2009; v1 submitted 18 May, 2009;
originally announced May 2009.
-
Ferromagnetic- and superconducting-like behavior of the electrical resistance of inhomogeneous graphite flake
Authors:
J. Barzola-Quiquia,
P. Esquinazi
Abstract:
We have measured the magnetic field and temperature dependence of the resistivity of several micrometers long and heterogeneously thick graphite sample. The magnetoresistance results for fields applied nearly parallel to the graphene planes show both a granular superconducting behavior as well as the existence of magnetic order in the sample.
We have measured the magnetic field and temperature dependence of the resistivity of several micrometers long and heterogeneously thick graphite sample. The magnetoresistance results for fields applied nearly parallel to the graphene planes show both a granular superconducting behavior as well as the existence of magnetic order in the sample.
△ Less
Submitted 17 July, 2009; v1 submitted 19 March, 2009;
originally announced March 2009.
-
Magnetic order in Graphite: Experimental evidence, intrinsic and extrinsic difficulties
Authors:
P. Esquinazi,
J. Barzola-Quiquia,
D. Spemann,
M. Rothermel,
H. Ohldag,
N. García,
A. Setzer,
T. Butz
Abstract:
We discuss recently obtained data using different experimental methods including magnetoresistance measurements that indicate the existence of metal-free high-temperature magnetic order in graphite. Intrinsic as well as extrinsic difficulties to trigger magnetic order by irradiation of graphite are discussed in view of recently published theoretical work.
We discuss recently obtained data using different experimental methods including magnetoresistance measurements that indicate the existence of metal-free high-temperature magnetic order in graphite. Intrinsic as well as extrinsic difficulties to trigger magnetic order by irradiation of graphite are discussed in view of recently published theoretical work.
△ Less
Submitted 10 February, 2009;
originally announced February 2009.
-
Sample Size Effects on the Transport Characteristics of Mesoscopic Graphite Samples
Authors:
J. Barzola-Quiquia,
J. -L. Yao,
P. Rödiger,
K. Schindler,
P. Esquinazi
Abstract:
In this work we investigated correlations between the internal microstructure and sample size (lateral as well as thickness) of mesoscopic, tens of nanometer thick graphite (multigraphene) samples and the temperature $(T)$ and field $(B)$ dependence of their electrical resistivity $ρ(T,B)$. Low energy transmission electron microscopy reveals that the original highly oriented pyrolytic graphite m…
▽ More
In this work we investigated correlations between the internal microstructure and sample size (lateral as well as thickness) of mesoscopic, tens of nanometer thick graphite (multigraphene) samples and the temperature $(T)$ and field $(B)$ dependence of their electrical resistivity $ρ(T,B)$. Low energy transmission electron microscopy reveals that the original highly oriented pyrolytic graphite material -- from which the multigraphene samples were obtained by exfoliation -- is composed of a stack of $\sim 50 $nm thick and micrometer long crystalline regions separated by interfaces running parallel to the graphene planes. We found a qualitative and quantitative change in the behavior of $ρ(T,B)$ upon thickness of the multigraphene samples, indicating that their internal microstructure is important.} {The overall results indicate that the metallic-like behavior of $ρ(T)$ at zero field measured for bulk graphite samples is not intrinsic of ideal graphite. The results suggest that the interfaces between crystalline regions may be responsible for the superconducting-like properties observed in graphite. Our transport measurements also show that reducing the sample lateral size as well as the length between voltage electrodes decreases the magnetoresistance, in agreement with recently published results. The magnetoresistance of the multigraphene samples shows a scaling of the form ($(R(B) - R(0))/R(0))/T^α= f(B/T)$ with a sample dependent exponent $α\sim 1$, which applies in the whole temperature 2 K $\le T \le 270$K and magnetic field range $B \le 8 $T.
△ Less
Submitted 19 September, 2008;
originally announced September 2008.
-
From Ohmic to Ballistic Transport in Oriented Graphite
Authors:
N. García,
P. Esquinazi,
J. Barzola-Quiquia,
B. Ming,
D. Spoddig
Abstract:
In this work we show that for a quasi-2D system of size $Ω$ and thickness $t$ the resistance goes as $(2ρ/πt)\ln(Ω/W)$, diverging logarithmically with the size. Measurements in highly oriented pyrolytic graphite (HOPG) as well as numerical simulations confirm this relation. Furthermore, we present an experimental method that allows us to obtain the carriers mean free path $l(T)$, the Fermi wavel…
▽ More
In this work we show that for a quasi-2D system of size $Ω$ and thickness $t$ the resistance goes as $(2ρ/πt)\ln(Ω/W)$, diverging logarithmically with the size. Measurements in highly oriented pyrolytic graphite (HOPG) as well as numerical simulations confirm this relation. Furthermore, we present an experimental method that allows us to obtain the carriers mean free path $l(T)$, the Fermi wavelength $λ(T)$ and the mobility $μ(T)$ directly from experiments without adjustable parameters. Measuring the electrical resistance through microfabricated constrictions in HOPG and observing the transition from ohmic to ballistic regime we obtain that $0.2 μ$m $\lesssim l \lesssim 10 μ$m, $0.1 μ$m $\lesssim λ\lesssim 2 μ$m and a mobility $5 \times 10^4$ cm$^2$/Vs $ \lesssim μ\lesssim 4 \times 10^7$ cm$^2$/Vs when the temperature decreases from 270K to 3K. A comparison of these results with those from literature indicates that conventional, multiband Boltzmann-Drude approaches are inadequate for oriented graphite. The upper value obtained for the mobility is much larger than the mobility graphene samples of micrometer size can have.
△ Less
Submitted 28 May, 2008; v1 submitted 14 March, 2008;
originally announced March 2008.
-
A comparison of the magnetic properties of Proton- and Iron-implanted graphite
Authors:
J. Barzola-Quiquia,
R. Höhne,
M. Rothermel,
A. Setzer,
P. Esquinazi,
V. Heera
Abstract:
In this work we have investigated the changes of the magnetic properties of highly oriented pyrolytic graphite samples after irradiation either with $\sim 3 \times 10^{14}$ protons or $ 3.5 \times 10^{13} ... 3.5 \times 10^{14}$ iron ions with energies in the MeV range. Our results show that iron and proton irradiations can produce similar paramagnetic contributions depending on the implantation…
▽ More
In this work we have investigated the changes of the magnetic properties of highly oriented pyrolytic graphite samples after irradiation either with $\sim 3 \times 10^{14}$ protons or $ 3.5 \times 10^{13} ... 3.5 \times 10^{14}$ iron ions with energies in the MeV range. Our results show that iron and proton irradiations can produce similar paramagnetic contributions depending on the implantation temperature. However, only protons induce a ferromagnetic effect.
△ Less
Submitted 6 January, 2008;
originally announced January 2008.
-
Intrinsic Superconductivity at 25 K in Highly Oriented Pyrolytic Graphite
Authors:
P. Esquinazi,
N. García,
J. Barzola-Quiquia,
J. C. González,
M. Muñoz,
P. Rödiger,
K. Schindler,
J. -L. Yao,
M. Ziese
Abstract:
High resolution magnetoresistance data in highly oriented pyrolytic graphite thin samples manifest non-homogenous superconductivity with critical temperature $T_c \sim 25 $K. These data exhibit: i) hysteretic loops of resistance versus magnetic field similar to Josephson-coupled grains, ii) quantum Andreev's resonances and iii) absence of the Schubnikov-de Haas oscillations. The results indicate…
▽ More
High resolution magnetoresistance data in highly oriented pyrolytic graphite thin samples manifest non-homogenous superconductivity with critical temperature $T_c \sim 25 $K. These data exhibit: i) hysteretic loops of resistance versus magnetic field similar to Josephson-coupled grains, ii) quantum Andreev's resonances and iii) absence of the Schubnikov-de Haas oscillations. The results indicate that graphite is a system with non-percolative superconducting domains immersed in a semiconducting-like matrix. As possible origin of the superconductivity in graphite we discuss interior-gap superconductivity when two very different electronic masses are present.
△ Less
Submitted 22 November, 2007;
originally announced November 2007.
-
Size Effects in the Magnetoresistance of Graphite: Absence of Magnetoresistance in Micrometer size Samples
Authors:
J. C. González,
M. Muñoz,
N. García,
J. Barzola-Quiquia,
D. Spoddig,
K. Schindler,
P. Esquinazi
Abstract:
We present a study of the magnetoresistance of highly oriented pyrolytic graphite (HOPG) as a function of the sample size. Our results show unequivocally that the magnetoresistance reduces with the sample size even for samples of hundreds of micrometers size. This sample size effect is due the large mean free path and Fermi wavelength of carriers in graphite and may explain the observed practica…
▽ More
We present a study of the magnetoresistance of highly oriented pyrolytic graphite (HOPG) as a function of the sample size. Our results show unequivocally that the magnetoresistance reduces with the sample size even for samples of hundreds of micrometers size. This sample size effect is due the large mean free path and Fermi wavelength of carriers in graphite and may explain the observed practically absence of magnetoresistance in micrometer confined small graphene samples where quantum effects should be at hand. These were not taken into account in the literature yet and ask for a revision of experimental and theoretical work on graphite.
△ Less
Submitted 20 June, 2007;
originally announced June 2007.
-
Experimental Evidence for Two-Dimensional Magnetic Order in Proton Bombarded Graphite
Authors:
J. Barzola-Quiquia,
P. Esquinazi,
M. Rothermel,
D. Spemann,
T. Butz,
N. García
Abstract:
We have prepared magnetic graphite samples bombarded by protons at low temperatures and low fluences to attenuate the large thermal annealing produced during irradiation. An overall optimization of sample handling allowed us to find Curie temperatures $ T_c \gtrsim 350$ K at the used fluences. The magnetization versus temperature shows unequivocally a linear dependence, which can be interpreted…
▽ More
We have prepared magnetic graphite samples bombarded by protons at low temperatures and low fluences to attenuate the large thermal annealing produced during irradiation. An overall optimization of sample handling allowed us to find Curie temperatures $ T_c \gtrsim 350$ K at the used fluences. The magnetization versus temperature shows unequivocally a linear dependence, which can be interpreted as due to excitations of spin waves in a two dimensional Heisenberg model with a weak uniaxial anisotropy.
△ Less
Submitted 16 June, 2007;
originally announced June 2007.
-
Proton-induced magnetic order in carbon: SQUID measurements
Authors:
J. Barzola-Quiquia,
S. Petriconi,
P. Esquinazi,
M. Rothermel,
D. Spemann,
A. Setzer,
T. Butz
Abstract:
In this work we have studied systematically the changes in the magnetic behavior of highly oriented pyrolytic graphite (HOPG) samples after proton irradiation in the MeV energy range. Superconducting quantum interferometer device (SQUID) results obtained from samples with thousands of localized spots of micrometer size as well on samples irradiated with a broad beam confirm previously reported r…
▽ More
In this work we have studied systematically the changes in the magnetic behavior of highly oriented pyrolytic graphite (HOPG) samples after proton irradiation in the MeV energy range. Superconducting quantum interferometer device (SQUID) results obtained from samples with thousands of localized spots of micrometer size as well on samples irradiated with a broad beam confirm previously reported results. Both, the para- and ferromagnetic contributions depend strongly on the irradiation details. The results indicate that the magnetic moment at saturation of spots of micrometer size is of the order of $10^{-10}$ emu.
△ Less
Submitted 11 October, 2006;
originally announced October 2006.