Spin-carrier coupling induced ferromagnetism and giant resistivity peak in EuCd$_2$P$_2$
Authors:
Veronika Sunko,
Yue Sun,
Mayia Vranas,
Christopher C. Homes,
Changmin Lee,
Elizabeth Donoway,
Zhi-Cheng Wang,
Sudhaman Balguri,
Mira B. Mahendru,
Alejandro Ruiz,
Brandon Gunn,
Rourav Basak,
Enrico Schierle,
Eugene Weschke,
Fazel Tafti,
Alex Frano,
Joseph Orenstein
Abstract:
EuCd$_2$P$_2$ is notable for its unconventional transport: upon cooling the metallic resistivity changes slope and begins to increase, ultimately 100-fold, before returning to its metallic value. Surprisingly, this giant peak occurs at 18K, well above the Néel temperature ($T_N$) of 11.5K. Using a suite of sensitive probes of magnetism, including resonant x-ray scattering and magneto-optical polar…
▽ More
EuCd$_2$P$_2$ is notable for its unconventional transport: upon cooling the metallic resistivity changes slope and begins to increase, ultimately 100-fold, before returning to its metallic value. Surprisingly, this giant peak occurs at 18K, well above the Néel temperature ($T_N$) of 11.5K. Using a suite of sensitive probes of magnetism, including resonant x-ray scattering and magneto-optical polarimetry, we have discovered that ferromagnetic order onsets above $T_N$ in the temperature range of the resistivity peak. The observation of inverted hysteresis in this regime shows that ferromagnetism is promoted by coupling of localized spins and itinerant carriers. The resulting carrier localization is confirmed by optical conductivity measurements.
△ Less
Submitted 10 August, 2022;
originally announced August 2022.
Diclofenac sodium ion exchange resin complex loaded melt cast films for sustained release ocular delivery
Authors:
Goutham R. Adelli,
Sai Prachetan Balguri,
Prakash Bhagav,
Vijayasankar Raman,
Soumyajit Majumdar
Abstract:
The goal of the present study is to develop polymeric matrix films loaded with a combination of free diclofenac sodium (DFSfree) and DFS:Ion exchange resin complexes (DFS:IR) for immediate and sustained release profiles, respectively. Effect of ratio of DFS and IR on the DFS:IR complexation efficiency was studied using batch processing. DFS:IR complex, DFSfree, or a combination of DFSfree+DFS:IR l…
▽ More
The goal of the present study is to develop polymeric matrix films loaded with a combination of free diclofenac sodium (DFSfree) and DFS:Ion exchange resin complexes (DFS:IR) for immediate and sustained release profiles, respectively. Effect of ratio of DFS and IR on the DFS:IR complexation efficiency was studied using batch processing. DFS:IR complex, DFSfree, or a combination of DFSfree+DFS:IR loaded matrix films were prepared by melt-cast technology. DFS content was 20% w/w in these matrix films. In vitro transcorneal permeability from the film formulations were compared against DFS solution, using a side-by-side diffusion apparatus, over a 6 h period. Ocular disposition of DFS from the solution, films and corresponding suspensions were evaluated in conscious New Zealand albino rabbits, 4 h and 8 h post-topical administration. All in vivo studies were carried out as per the University of Mississippi IACUC approved protocol. Complexation efficiency of DFS:IR was found to be 99% with a 1:1 ratio of DFS:IR. DFS release from DFS:IR suspension and the film were best-fit to a Higuchi model. In vitro transcorneal flux with the DFSfree+DFS:IR(1:1)(1 + 1) was twice that of only DFS:IR(1:1) film. In vivo, DFS solution and DFS:IR(1:1) suspension formulations were not able to maintain therapeutic DFS levels in the aqueous humor (AH). Both DFSfree and DFSfree+DFS:IR(1:1)(3 + 1) loaded matrix films were able to achieve and maintain high DFS concentrations in the AH, but elimination of DFS from the ocular tissues was much faster with the DFSfree formulation. DFSfree+DFS:IR combination loaded matrix films were able to deliver and maintain therapeutic DFS concentrations in the anterior ocular chamber for up to 8 h. Thus, free drug/IR complex loaded matrix films could be a potential topical ocular delivery platform for achieving immediate and sustained release characteristics.
△ Less
Submitted 10 July, 2017;
originally announced July 2017.