Revealing magnetic component in crystalline Fe-gluconate
Authors:
Stanisław M. Dubiel,
Jan Żukrowski,
Maria Bałanda
Abstract:
Low temperature Mössbauer spectroscopic and magnetization measurements were performed on a crystalline sample of Fe-gluconate. Fe atoms were revealed to exist in two phases i.e. a major (90-94 pct.) and a minor (6-10 pct.). Based on values of spectral parameters the former can be regarded as ferrous and the latter as ferric. A sub spectrum associated with the ferric phase shows a significant broad…
▽ More
Low temperature Mössbauer spectroscopic and magnetization measurements were performed on a crystalline sample of Fe-gluconate. Fe atoms were revealed to exist in two phases i.e. a major (90-94 pct.) and a minor (6-10 pct.). Based on values of spectral parameters the former can be regarded as ferrous and the latter as ferric. A sub spectrum associated with the ferric phase shows a significant broadening below ca. 30 K corresponding to 7.5 kGs. A magnetic origin of the effect was confirmed by the magnetization measurements. Evidence on the effect of the magnetism on the lattice vibrations of Fe atoms in both components was found. The Debye temperature, T_D, associated with the vibrations of Fe2+ ions is by a factor of about 2 smaller in the temperature range below ca. 30 K than the one determined from the data measured above ca. 30 K. Interestingly, the T_D-value found for the Fe3+ ions from the data recorded below ca.30 K is about two times smaller than the corresponding value determined for the Fe2+ ions.
△ Less
Submitted 11 February, 2020;
originally announced February 2020.
-
Determination of the magnetic phase diagram in the H-T plane for a sigma-phase Fe47Mo53 alloy
Authors:
Stanisław M. Dubiel,
Maria Bałanda,
Israel Felner
Abstract:
Magnetization measurements were carried out in the in field-cooled (FC) and in zero-field-cooled (ZFC) conditions versus temperature, T, and external magnetic field, H, on a sigma-phase Fe47Mo53 compound. Analysis of the measured M_FC and M_ZFC curves yielded values of characteristic temperatures: magnetic ordering (Curie) temperature, T_C, irreversibility temperature, T_ir, temperature of the max…
▽ More
Magnetization measurements were carried out in the in field-cooled (FC) and in zero-field-cooled (ZFC) conditions versus temperature, T, and external magnetic field, H, on a sigma-phase Fe47Mo53 compound. Analysis of the measured M_FC and M_ZFC curves yielded values of characteristic temperatures: magnetic ordering (Curie) temperature, T_C, irreversibility temperature, T_ir, temperature of the maximum in M_ZFC, T_m, identified as the Nėel (T_N) temperature, and cross-over temperature, T_co. Based on these temperatures a magnetic phase diagram in the H-T plane was outlined. The field dependences of the characteristic temperatures viz. of the irreversibility and of the cross-over temperatures were described in terms of a power law with the exponent 0.5(1). In the whole range of H i.e. up to 800 Oe, except the one H>50 Oe, a rare double re-entrant transition viz. PM-FM-AF-SG takes place. For small fields i.e. H<50 Oe a single re-entrant transition viz. PM-FM-SG is revealed.
△ Less
Submitted 10 February, 2019;
originally announced February 2019.
-
On the magnetism of the C14 Nb0.975Fe2.025 Laves phase compound: Determination of the H-T phase diagram
Authors:
M. Balanda,
S. M. Dubiel
Abstract:
A C14 Nb0.975Fe2.025 Laves phase compound was investigated aimed at determining the H-T magnetic phase diagram. Magnetization, M, and AC magnetic susceptibility measurements were performed. Concerning the former field-cooled and zero-field-cooled M-curves were recorded in the temperature range of 2-200K and in applied magnetic field, H, up to 1000 Oe, isothermal M(H) curves at 2 K, 5 K, 50 K, 80 K…
▽ More
A C14 Nb0.975Fe2.025 Laves phase compound was investigated aimed at determining the H-T magnetic phase diagram. Magnetization, M, and AC magnetic susceptibility measurements were performed. Concerning the former field-cooled and zero-field-cooled M-curves were recorded in the temperature range of 2-200K and in applied magnetic field, H, up to 1000 Oe, isothermal M(H) curves at 2 K, 5 K, 50 K, 80 K and 110 K as well as hysteresis loops at several temperatures over the field range of -10 to +10kOe. Regarding the AC susceptibility, both real and imaginary components were registered as a function of increasing temperature in the interval of 2 K - 150 K at the frequencies of the oscillating field, f, from 3 Hz up to 999 Hz. An influence of the external DC magnetic field, H, on the temperature dependence of the AC susceptibility was investigated, too. The measurements clearly demonstrated that the magnetism of the studied sample is weak, itinerant and has a reentrant character. Based on the obtained results a magnetic phase diagram has been constructed in the H-T coordinates.
△ Less
Submitted 9 January, 2018; v1 submitted 23 September, 2017;
originally announced September 2017.
-
Magnetism of a sigma-phase Fe60V40 alloy: magnetic susceptibilities and magnetocaloric effect studies
Authors:
M. Balanda,
S. M. Dubiel,
R. Pelka
Abstract:
Magnetic properties of a sigma-phase Fe60V40 intermetallic compound were studied by means of ac and dc magnetic susceptibility and magnetocaloric effect measurements. The compound is a soft magnet yet it was found to behave like a re-entrant spin-glass system. The magnetic ordering temperature was found to be T_C ca.170 K, while the spin-freezing temperature was ca.164 K. Its relative shift per de…
▽ More
Magnetic properties of a sigma-phase Fe60V40 intermetallic compound were studied by means of ac and dc magnetic susceptibility and magnetocaloric effect measurements. The compound is a soft magnet yet it was found to behave like a re-entrant spin-glass system. The magnetic ordering temperature was found to be T_C ca.170 K, while the spin-freezing temperature was ca.164 K. Its relative shift per decade of ac frequency was 0.002, a value smaller than that typical of canonical spin-glasses. Magnetic entropy change, DeltaS, in the vicinity of T_C was determined for magnetic field, H, ranging between 5 and 50 kOe. Analysis of DeltaS in terms of the power law yielded the critical exponent, n, vs. temperature with the minimum value of 0.75 at T_C, while from the analysis of a relative shift of the maximum value of DeltaS with the field a critical exponent Delta=1.7 was obtained. Based on scaling laws relationships values of other two exponents viz. betha=0.6 and gamma=1 were determined.
△ Less
Submitted 28 November, 2016;
originally announced November 2016.
-
AC magnetic susceptibility study of a sigma-phase Fe65.9V34.1 alloy
Authors:
Maria Balanda,
Stanislaw M. Dubiel
Abstract:
A sigma-phase Fe65.9V34.1 alloy was investigated with the AC magnetic susceptibility as a function of temperature, frequency and external magnetic field. An evidence was found that its magnetism shows features characteristic of a reentrant behavior viz. two transitions: first at TC ca.312K from the paramagnetic state into the collinear ferromagnetic one, and second at Tf ca.302K to a mixed state (…
▽ More
A sigma-phase Fe65.9V34.1 alloy was investigated with the AC magnetic susceptibility as a function of temperature, frequency and external magnetic field. An evidence was found that its magnetism shows features characteristic of a reentrant behavior viz. two transitions: first at TC ca.312K from the paramagnetic state into the collinear ferromagnetic one, and second at Tf ca.302K to a mixed state (sometimes termed as a ferromagnetic re-entrant spin glass) which, finally, at a lower temperature (TRSG ca.60K) transforms to a state where replica symmetry is broken. The frequency dependence of Tf is lower than that of canonical spin glasses, a feature, that in the light of a high concentration of magnetic carriers, can be understood in terms of a weak coupling between magnetic clusters.
△ Less
Submitted 12 September, 2015;
originally announced September 2015.
-
Magnetic systems at criticality: different signatures of scaling
Authors:
R. Pelka,
P. Konieczny,
M. Fitta,
M. Czapla,
P. M. Zielinski,
M. Balanda,
T. Wasiutynski,
Y. Miyazaki,
A. Inaba,
D. Pinkowicz,
B. Sieklucka
Abstract:
Different aspects of critical behaviour of magnetic materials are presented and discussed. The scaling ideas are shown to arise in the context of purely magnetic properties as well as in that of thermal properties as demonstrated by magnetocaloric effect or combined scaling of excess entropy and order parameter. Two non-standard approaches to scaling phenomena are described. The presented concepts…
▽ More
Different aspects of critical behaviour of magnetic materials are presented and discussed. The scaling ideas are shown to arise in the context of purely magnetic properties as well as in that of thermal properties as demonstrated by magnetocaloric effect or combined scaling of excess entropy and order parameter. Two non-standard approaches to scaling phenomena are described. The presented concepts are exemplified by experimental data gathered on four representatives of molecular magnets.
△ Less
Submitted 3 December, 2013;
originally announced December 2013.