Achieving the depairing limit along $c$ axis in Fe$_{1+y}$Te$_{1-x}$Se$_x$ single crystals
Authors:
Yue Sun,
Haruka Ohnuma,
Shin-ya Ayukawa,
Takashi Noji,
Yoji Koike,
Tsuyoshi Tamegai,
Haruhisa Kitano
Abstract:
We report the achieving of depairing current limit along $c$-axis in Fe$_{1+y}$Te$_{1-x}$Se$_x$ single crystals. A series of crystals with $T_{\rm{c}}$ ranging from 8.6 K to 13.7 K (different amount of excess Fe, $y$) were fabricated into $c$-axis bridges with a square-micrometer cross-section. The critical current density, $J_{\rm{c}}$, was directly estimated from the transport current-voltage me…
▽ More
We report the achieving of depairing current limit along $c$-axis in Fe$_{1+y}$Te$_{1-x}$Se$_x$ single crystals. A series of crystals with $T_{\rm{c}}$ ranging from 8.6 K to 13.7 K (different amount of excess Fe, $y$) were fabricated into $c$-axis bridges with a square-micrometer cross-section. The critical current density, $J_{\rm{c}}$, was directly estimated from the transport current-voltage measurements. The transport $J_{\rm{c}}$ reaches a very large value, which is about one order of magnitude larger than the depinning $J_{\rm{c}}$, but comparable to the calculated depairing $J_{\rm{c}}$ $\sim$ 2 $\times$ 10$^6$ A/cm$^2$ at 0 K, based on the Ginzburg-Landau (GL) theory. The temperature dependence of the depairing $J_{\rm{c}}$ follows the GL-theory ($\propto$ (1-$T/T_{\rm{c}}$)$^{3/2}$) down to $\sim$ 0.83 $T_{\rm{c}}$, then increases with a reduced slope at low temperatures, which can be qualitatively described by the Kupriyanov-Lukichev theory. Our study provides a new route to understand the behavior of depairing $J_{\rm{c}}$ in iron-based superconductors in a wide temperature range.
△ Less
Submitted 28 April, 2020; v1 submitted 2 November, 2019;
originally announced November 2019.
-
Superconductivity in BaPtSb with an Ordered Honeycomb Network
Authors:
Kazutaka Kudo,
Yuki Saito,
Takaaki Takeuchi,
Shin-ya Ayukawa,
Takayuki Kawamata,
Shinichiro Nakamura,
Yoji Koike,
Minoru Nohara
Abstract:
Superconductivity in BaPtSb with the SrPtSb-type structure (space group $P\bar{6}m2$, $D_{3h}^1$, No. 187) is reported. The structure consists of a PtSb ordered honeycomb network that stacks along the $c$-axis so that spatial inversion symmetry is broken globally. Electrical resistivity and specific-heat measurements revealed that the compound exhibited superconductivity at 1.64 K. The noncentrosy…
▽ More
Superconductivity in BaPtSb with the SrPtSb-type structure (space group $P\bar{6}m2$, $D_{3h}^1$, No. 187) is reported. The structure consists of a PtSb ordered honeycomb network that stacks along the $c$-axis so that spatial inversion symmetry is broken globally. Electrical resistivity and specific-heat measurements revealed that the compound exhibited superconductivity at 1.64 K. The noncentrosymmetric structure and the strong spin-orbit coupling of Pt and Sb make BaPtSb an attractive compound for studying the exotic superconductivity predicted for a honeycomb network.
△ Less
Submitted 3 September, 2018;
originally announced September 2018.
-
Superconductivity in Hexagonal BaPtAs: SrPtSb- and YPtAs-type Structures with Ordered Honeycomb Network
Authors:
Kazutaka Kudo,
Takaaki Takeuchi,
Hiromi Ota,
Yuki Saito,
Shin-ya Ayukawa,
Kazunori Fujimura,
Minoru Nohara
Abstract:
The crystal structure and superconductivity of hexagonal BaPtAs are reported. Single-crystal X-ray diffraction, magnetization, electrical resistivity, and specific heat measurements were performed in this study. Two hexagonal structures with different PtAs honeycomb network stacking sequences, namely, SrPtSb- (space group $P\bar{6}m2$, $D_{3h}^1$, No. 187) and YPtAs-type ($P6_3/mmc$, $D_{6h}^4$, N…
▽ More
The crystal structure and superconductivity of hexagonal BaPtAs are reported. Single-crystal X-ray diffraction, magnetization, electrical resistivity, and specific heat measurements were performed in this study. Two hexagonal structures with different PtAs honeycomb network stacking sequences, namely, SrPtSb- (space group $P\bar{6}m2$, $D_{3h}^1$, No. 187) and YPtAs-type ($P6_3/mmc$, $D_{6h}^4$, No. 194) structures, were identified and found to exhibit superconductivity at 2.8 and 2.1-3.0 K, respectively. In contrast, the cubic LaIrSi-type structure ($P2_13$, $T^4$, No. 198) did not exhibit superconductivity above 0.1 K. BaPtAs provides a unique opportunity to study superconductivity with broken and preserved spatial inversion symmetry.
△ Less
Submitted 3 September, 2018;
originally announced September 2018.