Erosion Study of Tungsten Carbide films under 100 keV Kr+ ion irradiation
Authors:
Shristi Bist,
Ratnesh K. Pandey,
Sejal Shah,
Parswajit Kalita,
Amit Chawla,
D. K. Avasthi
Abstract:
Tungsten carbide (WC) stands out as a crucial material for exploration in extreme environments due to its resistance to radiation and impressive mechanical strength. Widely utilized in cutting tools, high-wear components, and as a potential contender for plasma-facing material in nuclear reactors, WC's erosion behavior under surrogate irradiations is a subject of investigation. In the present work…
▽ More
Tungsten carbide (WC) stands out as a crucial material for exploration in extreme environments due to its resistance to radiation and impressive mechanical strength. Widely utilized in cutting tools, high-wear components, and as a potential contender for plasma-facing material in nuclear reactors, WC's erosion behavior under surrogate irradiations is a subject of investigation. In the present work, WC films were synthesized at two different substrate temperatures of 400 K and 600 K using RF sputtering and were then irradiated with 100 keV Kr1+ ions at a fluence of 1x1017 ions/cm2. The crystalline phases of as deposited WC films were confirmed by glancing incidence X-ray diffraction (GIXRD) measurements. Rutherford Backscattering Spectrometry (RBS) was employed to determine the thicknesses of pristine samples and the sputtering rate by measuring the difference in the areal densities of the pristine and irradiated films. The erosion rate of both types of films was found to be ~ 1.6 atoms per incident Kr+ ion. These findings contribute to a foundational comprehension of the radiation tolerance behavior of WC thin films, crucial for their performance in the demanding conditions of extreme radiation.
△ Less
Submitted 16 February, 2024;
originally announced February 2024.
-
Radiation tolerance: Nano triumphs bulk
Authors:
Parswajit Kalita,
Santanu Ghosh,
Gaëlle Gutierrez,
Parasmani Rajput,
Vinita Grover,
Gaël Sattonnay,
Devesh K. Avasthi
Abstract:
Materials are subjected to energetic particles in a number of radiation environments,and are hence prone to undesirable (radiation) damage.We report here the superiority of the nanocrystalline phase over bulk for radiation tolerance under simultaneous irradiation with high energy (electronic energy loss (Se) dominant) and low energy (nuclear energy loss (Sn) dominant) particles.Nano-crystalline yt…
▽ More
Materials are subjected to energetic particles in a number of radiation environments,and are hence prone to undesirable (radiation) damage.We report here the superiority of the nanocrystalline phase over bulk for radiation tolerance under simultaneous irradiation with high energy (electronic energy loss (Se) dominant) and low energy (nuclear energy loss (Sn) dominant) particles.Nano-crystalline yttria stabilized zirconia is found to exhibit lesser radiation damage (viz.degradation in crystallinity),when compared to its bulklike counterpart,against simultaneous irradiation with high energy 27 MeV Fe and low energy 900 keV I ions.This is interpreted within the framework of the thermal spike model after considering (i) the fact that there is essentially no spatial and time overlap between the damage events of the two simultaneous ion beams,and (ii) the influence of grain size on the radiation damage against separate Sn and Se.The present work besides being of keen interest for fundamental understanding of ion material interactions,also paves the way for the potential application of nanocrystalline materials in the nuclear industry where such simultaneous irradiations are encountered.
△ Less
Submitted 24 December, 2019;
originally announced December 2019.
-
Oxygen vacancy mediated cubic phase stabilization at room temperature in pure nano-crystalline Zirconia films: A combined experimental and first-principles based investigation
Authors:
Parswajit Kalita,
Shikha Saini,
Parasmani Rajput,
S. N. Jha,
D. Bhattacharyya,
Sunil Ojha,
Devesh K. Avasthi,
Saswata Bhattacharya,
Santanu Ghosh
Abstract:
We report the formation of cubic phase, under ambient conditions, in thin films of Zirconia synthesized by electron beam evaporation technique. The stabilization of the cubic phase was achieved without the use of chemical stabilizers and/or concurrent ion beam bombardment. Films of two different thickness (660 nm, 140 nm) were deposited. The 660 nm and 140 nm films were found to be stoichiometric…
▽ More
We report the formation of cubic phase, under ambient conditions, in thin films of Zirconia synthesized by electron beam evaporation technique. The stabilization of the cubic phase was achieved without the use of chemical stabilizers and/or concurrent ion beam bombardment. Films of two different thickness (660 nm, 140 nm) were deposited. The 660 nm and 140 nm films were found to be stoichiometric (ZrO2) and off-stoichiometric (ZrO1.7) respectively by Resonant Rutherford back-scattering spectroscopy. While the 660 nm as-deposited films were in the cubic phase, as indicated by X-ray diffraction and Raman spectroscopy measurements, the 140 nm as-deposited films were amorphous and the transformation to cubic phase was obtained after thermal annealing. Extended X-ray absorption fine structure measurements revealed the existence of Oxygen vacancies in the local structure surrounding Zirconium for all films. However, the amount of these Oxygen vacancies was found to be significantly higher for the amorphous films as compared to the films in the cubic phase (both 660 nm as-deposited and 140 nm annealed films). The cubic phase stabilization is explained on the basis of suppression of the soft X2- mode of vibration of the Oxygen sub-lattice due to the presence of the Oxygen vacancies. Our first-principles modeling under the framework of density functional theory shows that the cubic structure with Oxygen vacancies is indeed more stable at ambient conditions than its pristine (without vacancies) counterpart. The requirement of a critical amount of these vacancies for the stabilization of the cubic phase is also discussed.
△ Less
Submitted 8 April, 2019;
originally announced April 2019.
-
Assessing thermal spike model of swift heavy ion-matter interaction via Pd$_{1-x}$Ni$_x$/Si interface mixing
Authors:
Paramita Patra,
S. A. Khan,
M. Bala,
D. K. Avasthi,
S. K. Srivastava
Abstract:
Thermal spike model (TSM) is presently a widely accepted mechanism of swift heavy ion (SHI) - matter interaction. It provides explanation to various SHI induced effects including mixing across interfaces. The model involves electron-phonon (e-p) coupling to predict the evolution of lattice temperature with time. SHI mixing is considered to be a result of diffusion in transient molten state thus ac…
▽ More
Thermal spike model (TSM) is presently a widely accepted mechanism of swift heavy ion (SHI) - matter interaction. It provides explanation to various SHI induced effects including mixing across interfaces. The model involves electron-phonon (e-p) coupling to predict the evolution of lattice temperature with time. SHI mixing is considered to be a result of diffusion in transient molten state thus achieved. In this work, we assess this conception primarily via tuning the e-p coupling strength by taking a series Pd$_{1-x}$Ni$_x$ of a completely solid soluble binary, and then observing 100 MeV Au ion induced mixing across Pd$_{1-x}$Ni$_x$/Si interfaces. The extent of mixing has been parametrised by the irradiation induced change $Δσ^2$ in variances of Pd and Ni depth profiles derived from X-ray photoelectron spectroscopy. The $x$-dependence of $Δσ^2$ follows a curve that is concave upward with a prominent minimum. Theoretically, e-p coupling strength determined using density functional theory has been used to solve the equations appropriate to TSM, and then an equivalent quantity L$^2$ proportional to $Δσ^2$ has been calculated. L$^2$, however, increases monotonically with $x$ without any minimum, bringing out a convincing disparity between experiment and theory. Perhaps some mechanisms more than the TSM plus the transient molten state diffusion are operative, which can not be foreseen at this point of time.
△ Less
Submitted 11 October, 2018; v1 submitted 10 October, 2018;
originally announced October 2018.
-
Sign Reversal and Tunability of Exchange Bias in Nanoscale AuFe Alloy Film: A New Material for Spintronic Application
Authors:
Compesh Pannu,
Santanu Ghosh,
Pankaj Srivastava,
K Bharuth-Ram,
V. R. Reddy,
Ajay Gupta,
Debdulal Kabiraj,
D. K. Avasthi
Abstract:
We report here sign reversal and tunability of exchange bias in AuFe cosputtered films of thickness about 63 nm. As deposited film exhibits exchange bias effect at room temperature without external triggering field and its magnitude increases gradually with decrease in temperature down to 5 K. Upon irradiation with 100 MeV Au9+ ions at a fluence of 5*1013 ions/cm2, hysteresis loop shifts completel…
▽ More
We report here sign reversal and tunability of exchange bias in AuFe cosputtered films of thickness about 63 nm. As deposited film exhibits exchange bias effect at room temperature without external triggering field and its magnitude increases gradually with decrease in temperature down to 5 K. Upon irradiation with 100 MeV Au9+ ions at a fluence of 5*1013 ions/cm2, hysteresis loop shifts completely from origin towards positive field side at room temperature and reverses sign when temperature is reduced to 5 K as studied by SQUID magnetometry. A well defined uniaxial magnetic anisotropy has been seen by magneto optical Kerr effect (MOKE) in as deposited film as well as in irradiated one. The results are explained on the basis of stress induced magnetic anisotropy in thin films.
△ Less
Submitted 27 August, 2018;
originally announced August 2018.
-
Enhanced radiation tolerance of YSZ at high temperature against swift heavy ions: key role of interplay between material microstructure and irradiation temperature
Authors:
Parswajit Kalita,
Santanu Ghosh,
Udai B. Singh,
Pawan K. Kulriya,
Vinita Grover,
Rakesh Shukla,
A. K. Tyagi,
Gael Sattonnay,
Devesh K. Avasthi
Abstract:
Yttria stabilized Zirconia (YSZ) pellets with different crystallite sizes were irradiated with 80 MeV Ag$^{6+}$ ions at room temperature and 1000 K to understand the role of crystallite size/material microstructure and irradiation temperature on the radiation tolerance against high electronic energy loss (S$_e$). X-ray diffraction and Raman spectroscopy measurements reveal that, irrespective of th…
▽ More
Yttria stabilized Zirconia (YSZ) pellets with different crystallite sizes were irradiated with 80 MeV Ag$^{6+}$ ions at room temperature and 1000 K to understand the role of crystallite size/material microstructure and irradiation temperature on the radiation tolerance against high electronic energy loss (S$_e$). X-ray diffraction and Raman spectroscopy measurements reveal that, irrespective of the irradiation temperature, the nano-crystalline samples suffered more damage as compared to the bulk-like sample. A reduction in the irradiation damage i.e. improvement in the radiation tolerance, was observed for all the samples irradiated at 1000 K. The reduction in the damage, however, was remarkably higher for the two nano-crystalline samples compared to the bulk-like sample, and hence the difference in the damage between the bulk-like and nano-crystalline samples was also significantly lower at 1000 K than that at room temperature. The irradiation damage, against S$_e$, was thus found to be critically dependent on the interplay between the irradiation temperature and crystallite size. These results are explained with the help of detailed theoretical calculations/simulations based on the 'in-elastic thermal spike' model by taking into consideration the combined effect of crystallite size and environmental (irradiation) temperature on the electron-phonon coupling factor and lattice thermal conductivity (and hence on the resulting thermal spike). Our results are crucial from the fundamental perspective of comprehending the size and temperature dependent radiation damage against S$_e$ ; and also for a number of applications, in various radiation environments, where nano-materials are being envisioned for use.
△ Less
Submitted 27 July, 2018; v1 submitted 26 June, 2018;
originally announced June 2018.
-
Swift heavy ion irradiation induced structural phase transitions in BaTiO3: An in-situ x-ray diffraction study
Authors:
Ravindra Singh Solanki,
Jay Prakash Patel,
Chandana Rath,
Pawan Kumar Kulriya,
Devesh Kumar Avasthi,
Dhananjai Pandey
Abstract:
There is considerable controversy about swift heavy ion (SHI) irradiation induced displacive phase transitions in thermally insulating oxides. We present here unambiguous evidence for tetragonal to monoclinic and rhombohedral to monoclinic phase transitions in BaTiO3 under swift heavy ion irradiation (120MeV 108Ag+9 ions) using in-situ x-ray powder diffraction (XRPD) studies. The anomalous splitti…
▽ More
There is considerable controversy about swift heavy ion (SHI) irradiation induced displacive phase transitions in thermally insulating oxides. We present here unambiguous evidence for tetragonal to monoclinic and rhombohedral to monoclinic phase transitions in BaTiO3 under swift heavy ion irradiation (120MeV 108Ag+9 ions) using in-situ x-ray powder diffraction (XRPD) studies. The anomalous splitting/broadening of 111/222pc, 200pc and 220pc pseudocubic peaks for fluences greater than 3*1012 ions/cm2 reveal structural changes before amorphization at higher fluences. Lebail analysis of XRPD profiles confirm that the monoclinic phase is of MA type in the Cm space group. Shear stress for the structural phase transition is estimated to be ~ 430MPa, which we believe is generated as a result of stop** of the SHI.
△ Less
Submitted 7 March, 2017;
originally announced March 2017.
-
Field emission characteristics of carbon nanotubes according to the high energy ion irradiation
Authors:
P. M. Koinkar,
A. Kumar,
D. K. Avasthi,
M. A. More,
Ri-ichi Murakami
Abstract:
The field emission properties of ion irradiated multiwalled carbon nanotubes (MWCNTs) and doublewalled carbon nanotubes (DWCNTs) have been studied. The carbon nanotubes synthesized by a chemical vapor deposition method were irradiated by high energy (90 MeV) Au ions with different ion fluence from 4x1011 to 1x1013 ions/cm2 . After ion irradiation, the field emission properties of MWCNTs and DWCNTs…
▽ More
The field emission properties of ion irradiated multiwalled carbon nanotubes (MWCNTs) and doublewalled carbon nanotubes (DWCNTs) have been studied. The carbon nanotubes synthesized by a chemical vapor deposition method were irradiated by high energy (90 MeV) Au ions with different ion fluence from 4x1011 to 1x1013 ions/cm2 . After ion irradiation, the field emission properties of MWCNTs and DWCNTs were greatly influenced. The change in the emission characteristics is due to structural defects caused by the high energy ion irradiation. The emission characteristic of MWCNTs was improved and turn-on field decreased from 5.43 to 3.10 V/m by ion irradiation. Noticeable improvement in emission characteristics of MWCNTs was observed at a fluence of 1x 10 13 ions/cm2. The emission characteristics of DWCNTs deteriorated and the turn-on field was increased from 2.44 to 7.76 V/m. This results show the distinctly different behavior of ion irradiated MWCNTs and DWCNTs.
△ Less
Submitted 25 April, 2014;
originally announced April 2014.
-
Nano tracks in fullerene film by dense electronic excitations
Authors:
P. Kumar,
D. K. Avasthi,
J. Ghatak,
P. V. Satyam,
R. Prakash,
A. Kumar
Abstract:
In the present work, we investigate the formation of nano tracks by cluster and mono-atomic ion beams in the fullerene (C60) thin films by High Resolution Transmission Electron Microscopy (HRTEM). The fullerene films on carbon coated grids were irradiated by 30 MeV C60 cluster beam and 120 MeV Au mono-atomic beams at normal and grazing angle to the incident ion beams. The studies show that the clu…
▽ More
In the present work, we investigate the formation of nano tracks by cluster and mono-atomic ion beams in the fullerene (C60) thin films by High Resolution Transmission Electron Microscopy (HRTEM). The fullerene films on carbon coated grids were irradiated by 30 MeV C60 cluster beam and 120 MeV Au mono-atomic beams at normal and grazing angle to the incident ion beams. The studies show that the cluster beam creates latent tracks of an average diameter of around 20 nm. The formation of large size nano tracks by cluster beam is attributed to the deposition of large electronic energy density as compared to mono-atomic beams.
△ Less
Submitted 25 April, 2014; v1 submitted 2 February, 2014;
originally announced February 2014.
-
Swift Heavy Ion Induced Modification Studies of C60 Thin Films
Authors:
Navdeep Bajwa,
Alka Ingale,
D. K. Avasthi,
Ravi Kumar,
K. Dharamvir,
V. K. **dal
Abstract:
Modification induced by 110 MeV Ni ion irradiated thin film samples of C60 on Si and quartz substrates were studied at various fluences. The pristine and irradiated samples were investigated using Raman spectroscopy, electrical conductivity and optical absorption spectroscopy. The Raman data and band gap measurements indicate that swift ions at low fluences result in formations that involve mult…
▽ More
Modification induced by 110 MeV Ni ion irradiated thin film samples of C60 on Si and quartz substrates were studied at various fluences. The pristine and irradiated samples were investigated using Raman spectroscopy, electrical conductivity and optical absorption spectroscopy. The Raman data and band gap measurements indicate that swift ions at low fluences result in formations that involve multiple molecular units like dimer or polymer. High fluence irradiation resulted in sub-molecular formations and amorphous semiconducting carbon, indicating overall damage of the fullerene molecules. These sub-molecular units have been identified with nanocrystalline diamond and nanocrystalline graphite like formations.
△ Less
Submitted 25 July, 2002;
originally announced July 2002.