Epitaxial Growth of Boron Carbide on 4H-SiC
Authors:
Yamina Benamra,
Laurent Auvray,
Jérôme Andrieux,
François Cauwet,
Maria-Paz Alegre,
Fernando Lloret,
Daniel Araujo,
Marina Gutierrez,
Gabriel Ferro
Abstract:
In this work, the successful heteroepitaxial growth of boron carbide (B x C) on 4HSiC(0001) 4{\textdegree} off substrate using chemical vapor deposition (CVD) is reported. Towards this end, a two-step procedure was developed, involving the 4H-SiC substrate boridation under BCl 3 precursor at 1200{\textdegree}C, followed by conventional CVD under BCl 3 + C 3 H 8 at 1600{\textdegree}C. Such a proced…
▽ More
In this work, the successful heteroepitaxial growth of boron carbide (B x C) on 4HSiC(0001) 4{\textdegree} off substrate using chemical vapor deposition (CVD) is reported. Towards this end, a two-step procedure was developed, involving the 4H-SiC substrate boridation under BCl 3 precursor at 1200{\textdegree}C, followed by conventional CVD under BCl 3 + C 3 H 8 at 1600{\textdegree}C. Such a procedure allowed obtaining reproducibly monocrystalline (0001) oriented films of B x C with a step flow morphology at a growth rate of 1.9 $μ$m/h. Without the boridation step, the layers are systematically polycrystalline. The study of the epitaxial growth mechanism shows that a monocrystalline B x C layer is formed after boridation but covered with a B-and Si-containing amorphous layer. Upon heating up to 1600{\textdegree}C, under pure H 2 atmosphere, the amorphous layer was converted into epitaxial B x C and transient surface SiB x and Si crystallites. These crystallites disappear upon CVD growth.
△ Less
Submitted 26 October, 2023;
originally announced October 2023.
In-situ hydrogen charging of zirconium powder to study isothermal percipitation of hydrides and determination of Zr-hydride crystal structure
Authors:
T. Maimaitiyili,
A. Steuwer,
J. Blomquist,
B. Matthew,
Z. Olivier,
J. Andrieux,
C. Bjerken,
R. Fabienne
Abstract:
Zirconium alloys are widely used in the nuclear industry because of their high strength, good corrosion resistance and low neutron absorption cross-section. However, zirconium has strong affinity for hydrogen which leads to hydrogen concentration build-up over time. It is well known that the formation of hydrides will degrade the material and leads to, for example, delayed hydride cracking during…
▽ More
Zirconium alloys are widely used in the nuclear industry because of their high strength, good corrosion resistance and low neutron absorption cross-section. However, zirconium has strong affinity for hydrogen which leads to hydrogen concentration build-up over time. It is well known that the formation of hydrides will degrade the material and leads to, for example, delayed hydride cracking during high burn up. Even though zirconium hydrides have been studied for several decades, there still remain some controversies regarding the formation mechanisms, exact crystal structure, and stability of various hydride phases. This study uses high resolution synchrotron radiation as a probing tool to observe the precipitation and dissolution of hydrides in highly pure zirconium powder during in-situ hydrogen charging. The experiment enabled the direct observation of the hydride formation and phase transformations. It, also, provided high quality data for crystal structure determination.
△ Less
Submitted 20 August, 2014;
originally announced August 2014.