Showing 1–11 of 11 results for author: Ackerman, K

$\mathcal{L}_1$Quad: $\mathcal{L}_1$ Adaptive Augmentation of Geometric Control for Agile Quadrotors with Performance Guarantees

Authors: Zhuohuan Wu, Sheng Cheng, Pan Zhao, Aditya Gahlawat, Kasey A. Ackerman, Arun Lakshmanan, Chengyu Yang, Jiahao Yu, Naira Hovakimyan

Abstract: Quadrotors that can operate safely in the presence of imperfect model knowledge and external disturbances are crucial in safety-critical applications. We present L1Quad, a control architecture for quadrotors based on the L1 adaptive control. L1Quad enables safe tubes centered around a desired trajectory that the quadrotor is always guaranteed to remain inside. Our design applies to both the rotati… ▽ More Quadrotors that can operate safely in the presence of imperfect model knowledge and external disturbances are crucial in safety-critical applications. We present L1Quad, a control architecture for quadrotors based on the L1 adaptive control. L1Quad enables safe tubes centered around a desired trajectory that the quadrotor is always guaranteed to remain inside. Our design applies to both the rotational and the translational dynamics of the quadrotor. We lump various types of uncertainties and disturbances as unknown nonlinear (time- and state-dependent) forces and moments. Without assuming or enforcing parametric structures, L1Quad can accurately estimate and compensate for these unknown forces and moments. Extensive experimental results demonstrate that L1Quad is able to significantly outperform baseline controllers under a variety of uncertainties with consistently small tracking errors. △ Less

Submitted 14 February, 2023; originally announced February 2023.

Comments: The first two authors contributed equally to this work

The mechanism of twin thickening and the elastic strain state of TWIP steel nanotwins

Authors: T W J Kwok, T P McAuliffe, A K Ackerman, B H Savitzky, M Danaie, C Ophus, D Dye

Abstract: A Twinning Induced Plasticity (TWIP) steel with a nominal composition of Fe-16.4Mn-0.9C-0.5Si-0.05Nb-0.05V was deformed to an engineering strain of 6\%. The strain around the deformation twins were mapped using the 4D-STEM technique. Strain map** showed a large average elastic strain of approximately 6\% in the directions parallel and perpendicular to the twinning direction. However, the large a… ▽ More A Twinning Induced Plasticity (TWIP) steel with a nominal composition of Fe-16.4Mn-0.9C-0.5Si-0.05Nb-0.05V was deformed to an engineering strain of 6\%. The strain around the deformation twins were mapped using the 4D-STEM technique. Strain map** showed a large average elastic strain of approximately 6\% in the directions parallel and perpendicular to the twinning direction. However, the large average strain comprised of several hot spots of even larger strains of up to 12\%. These hot spots could be attributed to a high density of sessile Frank dislocations on the twin boundary and correspond to shear stresses of 1--1.5 GPa. The strain and therefore stress fields are significantly larger than other materials known to twin and are speculated to be responsible for the early thickness saturation of TWIP steel nanotwins. The ability to keep twins extremely thin helps improve grain fragmentation, \textit{i.e.} the dynamic Hall-Petch effect, and underpins the large elongations and strain hardening rates in TWIP steels. △ Less

Submitted 30 September, 2022; originally announced September 2022.

Effect of alloying on the microstructure, phase stability, hardness and partitioning behavior of a new dual-superlattice nickel-based superalloy

Authors: C. Rodenkirchen, A. K. Ackerman, P. M. Mignanelli, A. Cliff, G. J. Wise, J. O. Douglas, P. A. J. Bagot, M. P. Moody, M. Appleton, M. P. Ryan, M. C. Hardy, S. Pedrazzini, H. J. Stone

Abstract: A novel y-y'-y" dual-superlattice superalloy, with promising mechanical properties up to elevated temperatures was recently reported. The present work employs state of the art chemical and spatial characterization techniques to study the effect systematic additions of Mo, W and Fe and variations in Nb and Al contents have on the phase fraction, thermal stability, elemental partitioning and mechani… ▽ More A novel y-y'-y" dual-superlattice superalloy, with promising mechanical properties up to elevated temperatures was recently reported. The present work employs state of the art chemical and spatial characterization techniques to study the effect systematic additions of Mo, W and Fe and variations in Nb and Al contents have on the phase fraction, thermal stability, elemental partitioning and mechanical properties. Alloys were produced through arc melting followed by heat treatment. Multi-scale characterization techniques and hardness testing were employed to characterize their microstructure, thermal stability and mechanical properties. Alterations in such properties or in elemental partitioning behaviour were then explained through thermodynamic modelling. A modest addition of 1.8 at.% Mo had a strong effect on the microstructure and thermal stability: it minimized microstructural coarsening during heat treatments while not significantly decreasing the y' solvus temperature. A reduction of Nb by 0.6 at.%, strongly reduced the y" volume fraction, without affecting the y' volume fraction. The reduced precipitate fraction led to a significant reduction in alloy hardness. Fe, added to achieve better processability and reduced material cost, decreased the y' solvus temperature and caused rapid microstructural coarsening during heat treatments, without affecting alloy hardness. A reduction of Al by 0.4 at.%, reduced the y' volume fraction and the y' solvus temperature, also without affecting alloy hardness. The addition of 0.9 at.% W decreased the y' solvus temperature but increased both precipitate volume fractions. These data will be invaluable to optimize current alloy design and to inform future alloy design efforts. △ Less

Submitted 19 September, 2022; originally announced September 2022.

$\mathcal{L}_1$ Adaptive Augmentation for Geometric Tracking Control of Quadrotors

Authors: Zhuohuan Wu, Sheng Cheng, Kasey A. Ackerman, Aditya Gahlawat, Arun Lakshmanan, Pan Zhao, Naira Hovakimyan

Abstract: This paper introduces an $\mathcal{L}_1$ adaptive control augmentation for geometric tracking control of quadrotors. In the proposed design, the $\mathcal{L}_1$ augmentation handles nonlinear (time- and state-dependent) uncertainties in the quadrotor dynamics without assuming or enforcing parametric structures, while the baseline geometric controller achieves stabilization of the known nonlinear m… ▽ More This paper introduces an $\mathcal{L}_1$ adaptive control augmentation for geometric tracking control of quadrotors. In the proposed design, the $\mathcal{L}_1$ augmentation handles nonlinear (time- and state-dependent) uncertainties in the quadrotor dynamics without assuming or enforcing parametric structures, while the baseline geometric controller achieves stabilization of the known nonlinear model of the system dynamics. The $\mathcal{L}_1$ augmentation applies to both the rotational and the translational dynamics. Experimental results demonstrate that the augmented geometric controller shows consistent and (on average five times) smaller trajectory tracking errors compared with the geometric controller alone when tested for different trajectories and under various types of uncertainties/disturbances. △ Less

Submitted 2 March, 2022; v1 submitted 14 September, 2021; originally announced September 2021.

Comments: accepted by ICRA 2022

Tube-Certified Trajectory Tracking for Nonlinear Systems With Robust Control Contraction Metrics

Authors: Pan Zhao, Arun Lakshmanan, Kasey Ackerman, Aditya Gahlawat, Marco Pavone, Naira Hovakimyan

Abstract: This paper presents an approach towards guaranteed trajectory tracking for nonlinear control-affine systems subject to external disturbances based on robust control contraction metrics (CCM) that aims to minimize the $\mathcal L_\infty$ gain from the disturbances to nominal-actual trajectory deviations. The guarantee is in the form of invariant tubes, computed offline and valid for any nominal tra… ▽ More This paper presents an approach towards guaranteed trajectory tracking for nonlinear control-affine systems subject to external disturbances based on robust control contraction metrics (CCM) that aims to minimize the $\mathcal L_\infty$ gain from the disturbances to nominal-actual trajectory deviations. The guarantee is in the form of invariant tubes, computed offline and valid for any nominal trajectories, in which the actual states and inputs of the system are guaranteed to stay despite disturbances. Under mild assumptions, we prove that the proposed robust CCM (RCCM) approach yields tighter tubes than an existing approach based on CCM and input-to-state stability analysis. We show how the RCCM-based tracking controller together with tubes can be incorporated into a feedback motion planning framework to plan safe trajectories for robotic systems. Simulation results illustrate the effectiveness of the proposed method and empirically demonstrate reduced conservatism compared to the CCM-based approach. △ Less

Submitted 6 July, 2023; v1 submitted 9 September, 2021; originally announced September 2021.

Comments: Extended version of a paper published in IEEE Robotics and Automation Letters (2022). 13 pages, 6 figures

Effect of bed temperature on solute segregation and mechanical properties in Ti-6Al-4V produced by selective laser melting

Authors: S. Pedrazzini, M. E. Pek, A. K. Ackerman, Q. Cheng, H. Ali, H. Ghadbeigi, K. Mumtaz, T. Dessolier, T. B. Britton, P. Bajaj, E. Jägle, B. Gault, A. J. London, E. Galindo-Nava

Abstract: Advanced characterisation techniques were used on LPBF Ti-6Al-4V samples produced on a heated base plate. When the substrate temperature is 100°C the elongation is 6\%, which increases and peaks at 10\% at 570°C, then sharply decreases to zero ductility at 770°C. At 100°C, a heavily strained and twinned microstructure, primarily composed of α+α', was observed and it was comparable to asbuilt micro… ▽ More Advanced characterisation techniques were used on LPBF Ti-6Al-4V samples produced on a heated base plate. When the substrate temperature is 100°C the elongation is 6\%, which increases and peaks at 10\% at 570°C, then sharply decreases to zero ductility at 770°C. At 100°C, a heavily strained and twinned microstructure, primarily composed of α+α', was observed and it was comparable to asbuilt microstructures obtained by conventional LPBF methods. At higher temperatures, twins are no longer present and instead nano-scale β precipitates are observed within α' and α, as well as dislocation networks (570°C) and tangles (770°C). Solute segregation at crystal defects was observed in all pre-heating conditions. Al and V segregation at microtwins was observed in the 100°C sample, reporting for the first time `selective' and mutually exclusive Al- and V-rich regions forming in adjacent twins. V segregation at dislocations was observed in the 570°C and 770°C samples, consistent with the higher preheating temperatures. High O contents were measured in all samples but with apparent opposing effects. At 100°C and 570°C was estimated to be below the critical threshold for O embrittlement and locally aids in maintaining a strength high by solid solution strengthening, whereas at 770°C it was above the threshold, therefore failing in a brittle fashion. Based on these observations, the initial increase in ductility from 100°C to 570°C is attributed to a reduction in microtwins and the dislocation networks acting as `soft barriers' for slip within a coarser microstructure. The lack of ductility at 770°C was attributed to local solute redistribution causing dislocation pinning and an increase of O content in this sample. △ Less

Submitted 1 December, 2020; v1 submitted 15 June, 2020; originally announced June 2020.

4D-STEM elastic stress state characterisation of a TWIP steel nanotwin

Authors: T P McAuliffe, A K Ackerman, B H Savitzky, T W J Kwok, M Danaie, C Ophus, D Dye

Abstract: We measure the stress state in and around a deformation nanotwin in a twinning-induced plasticity (TWIP) steel. Using four-dimensional scanning transmission electron microscopy (4D-STEM), we measure the elastic strain field in a 68.2-by-83.1 nm area of interest with a scan step of 0.36 nm and a diffraction limit resolution of 0.73 nm. The stress field in and surrounding the twin matches the form e… ▽ More We measure the stress state in and around a deformation nanotwin in a twinning-induced plasticity (TWIP) steel. Using four-dimensional scanning transmission electron microscopy (4D-STEM), we measure the elastic strain field in a 68.2-by-83.1 nm area of interest with a scan step of 0.36 nm and a diffraction limit resolution of 0.73 nm. The stress field in and surrounding the twin matches the form expected from analytical theory and is on the order of 15 GPa, close to the theoretical strength of the material. We infer that the measured back-stress limits twin thickening, providing a rationale for why TWIP steel twins remain thin during deformation, continuously dividing grains to give substantial work hardening. Our results support modern mechanistic understanding of the influence of twinning on crack propagation and embrittlement in TWIP steels. △ Less

Submitted 20 October, 2020; v1 submitted 8 April, 2020; originally announced April 2020.

Comments: After peer review comments and resubmission

L1-Adaptive MPPI Architecture for Robust and Agile Control of Multirotors

Authors: **tasit Pravitra, Kasey A. Ackerman, Chengyu Cao, Naira Hovakimyan, Evangelos A. Theodorou

Abstract: This paper presents a multirotor control architecture, where Model Predictive Path Integral Control (MPPI) and L1 adaptive control are combined to achieve both fast model predictive trajectory planning and robust trajectory tracking. MPPI provides a framework to solve nonlinear MPC with complex cost functions in real-time. However, it often lacks robustness, especially when the simulated dynamics… ▽ More This paper presents a multirotor control architecture, where Model Predictive Path Integral Control (MPPI) and L1 adaptive control are combined to achieve both fast model predictive trajectory planning and robust trajectory tracking. MPPI provides a framework to solve nonlinear MPC with complex cost functions in real-time. However, it often lacks robustness, especially when the simulated dynamics are different from the true dynamics. We show that the L1 adaptive controller robustifies the architecture, allowing the overall system to behave similar to the nominal system simulated with MPPI. The architecture is validated in a simulated multirotor racing environment. △ Less

Submitted 31 March, 2020; originally announced April 2020.

Comments: Submitted to 2020 IEEE/RSJ International Conference on Intelligent Robots and Systems

The Kinetics of Primary Alpha Plate Growth in Titanium Alloys

Authors: Abigail K Ackerman, Alexander J. Knowles, Hazel M. Gardner, Andre A N Nemeth, Ioannis Bantounas, Anna Radecka, Michael P. Moody, Paul A. J. Bagot, Roger C. Reed, David Rugg, David Dye

Abstract: The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is availab… ▽ More The kinetics of primary alpha-Ti colony/Widmanstatten plate growth from the beta are examined, comparing model to experiment. The plate growth velocity depends sensitively both on the diffusivity D(T) of the rate-limiting species and on the supersaturation around the growing plate. These result in a maxima in growth velocity around 40 K below the transus, once sufficient supersaturation is available to drive plate growth. In Ti-6246, the plate growth velocity was found to be around 0.32 um min-1 at 850 oC, which was in good agreement with the model prediction of 0.36 um min-1 . The solute field around the growing plates, and the plate thickness, was found to be quite variable, due to the intergrowth of plates and soft im**ement. This solute field was found to extend to up to 30 nm, and the interface concentration in the beta was found to be around 6.4 at.% Mo. It was found that increasing O content will have minimal effect on the plate lengths expected during continuous cooling; in contrast, Mo approximately doubles the plate lengths obtained for every 2 wt.% Mo reduction. Alloys using V as the beta stabiliser instead of Mo are expected to have much faster plate growth kinetics at nominally equivalent V contents. These findings will provide a useful tool for the integrated design of alloys and process routes to achieve tailored microstructures. △ Less

Submitted 31 July, 2019; v1 submitted 24 May, 2018; originally announced May 2018.

Comments: Revised version resubmitted to journal

Interface characteristics in an α+β titanium alloy

Authors: Abigail K. Ackerman, Vassili A. Vorontsov, Ioannis Bantounas, Yufeng Zheng, Thomas McAuliffe, William A. Clark, Hamish L. Fraser, David Rugg, David Dye

Abstract: The alpha/beta interface in Ti-6Al-2Sn-4Zr-6Mo (Ti-6246) is investigated via centre of symmetry analysis, both as-grown and after 10% cold work. Semi-coherent interface steps are observed at a spacing of 4.5 +/-1.13 atoms in the as-grown condition, in good agreement with theory prediction (4.37 atoms). Lattice accommodation is observed, with elongation along [-1 2 -1 0]alpha and contraction along… ▽ More The alpha/beta interface in Ti-6Al-2Sn-4Zr-6Mo (Ti-6246) is investigated via centre of symmetry analysis, both as-grown and after 10% cold work. Semi-coherent interface steps are observed at a spacing of 4.5 +/-1.13 atoms in the as-grown condition, in good agreement with theory prediction (4.37 atoms). Lattice accommodation is observed, with elongation along [-1 2 -1 0]alpha and contraction along [1 0 -1 0]alpha . Deformed alpha exhibited larger, less coherent steps with slip bands lying in {110}beta. This indicates dislocation pile-up at the grain boundary, a precursor to globularisation, offering insight into the effect of deformation processing on the interface, which is important for titanium alloy processing route design. △ Less

Submitted 18 December, 2019; v1 submitted 24 May, 2018; originally announced May 2018.

Comments: Revised after review

Journal ref: Phys. Rev. Materials 4, 013602 (2020)

Using transmission Kikuchi diffraction to characterise α variants in an α + β titanium alloy

Authors: Vivian Tong, Sudha Joseph, Abigail K. Ackerman, David Dye, T. Ben Britton

Abstract: Two phase titanium alloys are important for high performance engineering components, such as aeroengine discs. The microstructures of these alloys are tailored during thermomechanical processing to precisely control phase factions, morphology and crystallographic orientations. In bimodal two phase (α + β) Ti-6Al-2Sn-4Zr-2Mo (Ti-6242) alloys there are often three microstructural lengthscales to con… ▽ More Two phase titanium alloys are important for high performance engineering components, such as aeroengine discs. The microstructures of these alloys are tailored during thermomechanical processing to precisely control phase factions, morphology and crystallographic orientations. In bimodal two phase (α + β) Ti-6Al-2Sn-4Zr-2Mo (Ti-6242) alloys there are often three microstructural lengthscales to consider: large (~10 μm) equiaxed primary α; >200 nm thick plate α with a basketweave morphology; and very fine scaled (>50 nm plate thickness) secondary α that grows between the larger α plates surrounded by retained β. In this work, we utilise high spatial resolution transmission Kikuchi diffraction (TKD, also known as transmission based electron backscatter diffraction, t-EBSD) and scanning electron microscopy (SEM) based forward scattering electron imaging to resolve the structures and orientations of basketweave and secondary α in Ti-6242. We analyse the α variants formed within one prior β grain, and test whether existing theories of habit planes of the phase transformation are upheld. Our analysis is important in understanding both the thermomechanical processing strategy of new bimodal two-phase titanium alloys, as well the ultimate performance of these alloys in complex loading regimes such as dwell fatigue. Our paper champions the significant increase in spatial resolution afforded using transmission techniques, combined with the ease of SEM based analysis using conventional electron backscatter diffraction (EBSD) systems and forescatter detector (FSD) imaging, to study the nanostructure of real-world engineering alloys. △ Less

Submitted 4 April, 2017; v1 submitted 11 January, 2017; originally announced January 2017.

Comments: This is an accepted version of the article which is due to be published in Journal of Microscopy

Journal ref: Journal of Microscopy (2017)