Showing 1–5 of 5 results for author: Čapek, J

The influence of nitrogen ion implantation on the microstructure and chemical composition of a thin layer on the biodegradable Zn-0.8Mg-0.2Sr substrate

Authors: Jan Pinc, Petr Vlcak, Miroslav Lebeda, Vilem Bartunek, Vojtech Smola, Marek Vronka, Jan Drahokoupil, Zdenek Weiss, Petr Svora, Hana Lesakova, Katerina Sindelarova, Orsolya Molnarova, Tomas Horazdovsky, Tomas Studecky, Pavel Salvetr, Jiri Kubasek, Jaroslav Capek, Andrea Skolakova

Abstract: In this research, the influence of the N+ ion implantation process on the microstructure of a biodegradable Zn-0.8Mg-0.2Sr alloy was investigated using various experimental techniques. Microscopic analysis revealed that a fluence of 17x10^17 ions/cm^2 resulted in the oversaturation of pure Zn and Mg2Zn11 surfaces, leading to the formation of nano/micro-porous layers up to 400 nm thick. The behavio… ▽ More In this research, the influence of the N+ ion implantation process on the microstructure of a biodegradable Zn-0.8Mg-0.2Sr alloy was investigated using various experimental techniques. Microscopic analysis revealed that a fluence of 17x10^17 ions/cm^2 resulted in the oversaturation of pure Zn and Mg2Zn11 surfaces, leading to the formation of nano/micro-porous layers up to 400 nm thick. The behavior of the Zn-0.8Mg-0.2Sr alloy was observed to be similar to that of the individual pure phases, albeit without the creation of pore structures. A limited formation of MgO and Mg3N2 was observed on the alloy surface, although the overall presence of Mg significantly increased from 0.8 to 15 wt.%. This increase was caused by the decomposition of the Mg2Zn11 phase during the process and subsequent diffusion of Mg toward the surface. The absence of Zn3N2 within the samples could be explained by the thermodynamic instability and low Zn-N affinity. Despite the absence of zinc nitride, GD-OES confirmed 10 at. % of nitrogen in the pure zinc, suggesting a possible accommodation of N atoms in the interstitial positions. This study points out to the complex nature of the process and highlights other promising directions for future research. △ Less

Submitted 9 July, 2024; originally announced July 2024.

Comments: preprint

Effect of magnetic field configuration on double layer formation and reverse discharge ignition in bipolar HiPIMS

Authors: M. Farahani, T. Kozák, A. D. Pajdarová, J. Čapek

Abstract: The reverse discharge (RD) phenomenon in bipolar HiPIMS has been observed when a sufficiently long positive pulse is applied to the magnetron. Due to the magnetic field, electrons accumulated behind the magnetic trap are prevented from reaching the positive target. Consequently, a space charge double layer (DL) is formed between the positive target and the plasma behind the magnetic trap, leading… ▽ More The reverse discharge (RD) phenomenon in bipolar HiPIMS has been observed when a sufficiently long positive pulse is applied to the magnetron. Due to the magnetic field, electrons accumulated behind the magnetic trap are prevented from reaching the positive target. Consequently, a space charge double layer (DL) is formed between the positive target and the plasma behind the magnetic trap, leading to electron acceleration across the DL and RD ignition. This study reveals the significant impact of the magnetic field configuration on RD ignition. Experiments are performed using a Ti target involving magnetic field variation, wire probe measurements of floating potential, and optical emission spectroscopy imaging. It is found that adjusting the magnetic field to a more balanced configuration leads to earlier RD ignition, while a more unbalanced one delays or even prevents it. Specifically, the time of RD ignition decreases with an increase in the magnetic null point distance from the target. Moreover, the size and shape of optical emission in the RD varies with nearby probe placement, suggesting sensitivity to external electrodes. △ Less

Submitted 23 May, 2024; originally announced May 2024.

On double-layer and reverse discharge creation during long positive voltage pulses in a bipolar HiPIMS discharge

Authors: Andrea Dagmar Pajdarová, Tomáš Kozák, Tomáš Tölg, Jiří Čapek

Abstract: Time-resolved Langmuir probe diagnostics at the discharge centerline and at three distances from the target (35mm, 60mm, and 100mm) was carried out during long positive voltage pulses (a duration of 500$μ$s and a preset positive voltage of 100V) in bipolar High-Power Impulse Magnetron Sputtering of a Ti target (a diameter of 100mm) using an unbalanced magnetron. Fast-camera spectroscopy imaging re… ▽ More Time-resolved Langmuir probe diagnostics at the discharge centerline and at three distances from the target (35mm, 60mm, and 100mm) was carried out during long positive voltage pulses (a duration of 500$μ$s and a preset positive voltage of 100V) in bipolar High-Power Impulse Magnetron Sputtering of a Ti target (a diameter of 100mm) using an unbalanced magnetron. Fast-camera spectroscopy imaging recorded light emission from Ar and Ti atoms and singly charged ions during positive voltage pulses. It was found that during the long positive voltage pulse, the floating and the plasma potentials suddenly decrease, which is accompanied by the presence of anode light located on the discharge centerline between the target center and the magnetic null of the magnetron's magnetic field. These light patterns are related to the ignition of a reverse discharge, which leads to the subsequent rise in the plasma and the floating potentials. The reversed discharge is burning up to the end of the positive voltage pulse, but the plasma and floating potentials have lower values than the values from the initial part of the positive voltage pulse. Secondary electron emission induced by the im**ing Ar$^+$ ions to the grounded surfaces in the vicinity of the discharge plasma together with the mirror configuration of the magnetron magnetic field are identified as the probable causes of the charge double-layer structure formation in front of the target and the ignition of the reverse discharge. △ Less

Submitted 27 March, 2024; originally announced March 2024.

High Ductility and Transformation-Induced-Plasticity in Metastable Stainless Steel Processed by Selective Laser Melting with Low Power

Authors: E. Polatidis, J. Capek, A. Arabi-Hashemi, C. Leinenbach, M. Strobl

Abstract: A metastable austenitic Fe-Cr-Ni steel was processed by selective laser melting with low power, resulting in nearly random crystallographic texture. In-situ tensile loading and neutron diffraction experiments were undertaken and the results indicate high ductility, despite the presence of porosity, and pronounced strain-induced martensitic transformation. A secondary hardening is observed in the m… ▽ More A metastable austenitic Fe-Cr-Ni steel was processed by selective laser melting with low power, resulting in nearly random crystallographic texture. In-situ tensile loading and neutron diffraction experiments were undertaken and the results indicate high ductility, despite the presence of porosity, and pronounced strain-induced martensitic transformation. A secondary hardening is observed in the mechanical data due to the martensite carrying significant load, upon its formation. The pronounced martensitic transformation is discussed with respect to the initial and the evolving deformation texture and its affinity for forming martensite under uniaxial tensile loading. △ Less

Submitted 3 October, 2019; v1 submitted 2 October, 2019; originally announced October 2019.

Comments: As accepted version to Scripta Materialia

Achromatic Non-Interferometric Single Grating Neutron Phase Imaging

Authors: Markus Strobl, Jacopo Valsecchi, Ralph . P. Harti, Pavel Trtik, Aanders Kaestner, Christian Gruenzweig, Efthymios Polatidis, Jan Capek

Abstract: We demonstrate a simple single grating beam modulation technique, which enables the use of a highly intense neutron beam for phase imaging and thus spatially resolved structural correlation measurements in full analogy to quantum interference based methods. In contrast to interferometric approaches our method is intrinsically achromatic and provides unprecedented flexibility in the choice of exper… ▽ More We demonstrate a simple single grating beam modulation technique, which enables the use of a highly intense neutron beam for phase imaging and thus spatially resolved structural correlation measurements in full analogy to quantum interference based methods. In contrast to interferometric approaches our method is intrinsically achromatic and provides unprecedented flexibility in the choice of experimental parameters. Utilizing merely a macroscopic absorption mask unparalleled length scales become accessible. The results presented, including application to a variety of materials, establish a paradigm shift in phase imaging. △ Less

Submitted 23 March, 2019; originally announced March 2019.